CN105442142A - Chemical-corrosion-resistant woven fabric and making method thereof - Google Patents
Chemical-corrosion-resistant woven fabric and making method thereof Download PDFInfo
- Publication number
- CN105442142A CN105442142A CN201510912232.9A CN201510912232A CN105442142A CN 105442142 A CN105442142 A CN 105442142A CN 201510912232 A CN201510912232 A CN 201510912232A CN 105442142 A CN105442142 A CN 105442142A
- Authority
- CN
- China
- Prior art keywords
- parts
- hour
- woven fabric
- chemical
- corrosion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a chemical-corrosion-resistant woven fabric and a making method thereof. The chemical-corrosion-resistant woven fabric is formed by weaving warp yarn and weft yarn through an air jet loom and is characterized in that the raw materials of the warp yarn and the weft yarn are prepared from, by weight, 24-29 parts of syndiotatic polypropylene, 0.4-0.8 part of magnesium sulfate, 23-28 parts of natural bamboo fibers, 30-35 parts of polysulphonamide fibers, 14-19 parts of jade fibers, 17-23 parts of ceiba fibers, 4-7 parts of sawdust, 3-6 parts of pine needles, 2-5 parts of dicyclohexyl phthalate, 7-12 parts of diethyl oxalate, 2-4 parts of ephedra, 3-5 parts of folium isatidis, 85-105 parts of 1-butyl-3-methyl imidazole acetate, 95-110 parts of 1-allyl-3-methyl imidazole chloride salt, 5-8 parts of auxiliaries and a proper amount of water. The chemical-corrosion-resistant woven fabric has the functions of antibiosis and acarus killing, deodorization and inflaming retarding, chemical corrosion resistance, sound insulation, warm keeping and the like.
Description
Technical field
The present invention relates to woven fabric production technology, be specifically related to a kind of resist chemical woven fabric and preparation method thereof.
Background technology
Communications and transportation plays vital effect in the national economic development, the vehicles such as automobile, train, aircraft, steamer also more and more go deep into the life of people, particularly automobile, become the indispensability trip instrument in nowadays people's life, along with developing rapidly of auto industry, textile for automobile also develops thereupon.Consider health, for textile for automobile, gas permeability, comfortableness, aesthetic property, smell, antibacterial and antimildew function and attraction noise reduction etc. have strict demand, especially automotive trim textiles.What textile for automobile application was more is exactly woven fabric, is mainly used in door internal decoration plate, carpet, ceiling, seat etc.
Woven fabric is by the mutually vertical yarn of two or more than two, to be interwoven fabric as longitude and latitude with an angle of 90 degrees, the woven fabric of prior art has that composition is more single, function simple, sound-absorbing antimildew and antibacterial function not significantly, the low defect such as not to be durable of ABRASION RESISTANCE, the multi-functional demand of people for automotive trim woven fabric cannot be met.
Summary of the invention
Object of the present invention is just to provide a kind of resist chemical woven fabric and preparation method thereof, to overcome the deficiencies in the prior art.
The object of the present invention is achieved like this:
A kind of resist chemical woven fabric, formed through air-jet loom braiding by warp thread and weft yarn, it is characterized in that, the raw material of described warp thread and weft yarn is made up of the raw material of following weight portion: syndiotactic polypropylene 24-29, magnesium sulfate 0.4-0.8, natural bamboo fiber 23-28, polysulphonamide fiber 30-35, jade fiber 14-19, bombax cotton 17-23, wood sawdust 4-7, pine needle 3-6, dicyclohexyl phthalate 2-5, diethyl oxalate 7-12, Chinese ephedra 2-4, folium isatidis 3-5, 1-butyl-3-N-Methylimidazoleacetic salt 85-105, 1-allyl-3-methylimidazole villaumite 95-110, auxiliary agent 5-8, suitable quantity of water.
Described auxiliary agent is made up of following raw materials in part by weight: boric acid 0.2-0.5, Tea Saponin 0.04-0.08, glycerine 15-19, benzoic acid 16-22, ethylene glycol 18-26, ethylenediamine 2-4, nano silicon 1.2-2.3, mica powder 3-5, dimethyl carbonate 13-17, single palmitic acid 12-14, palm oil 7-10, marigold essential oil 0.05-0.15, ESCALOL 567 0.1-0.3, its preparation method is by glycerine, benzoic acid, ethylene glycol is put into reactor and is stirred and evenly mixed, be warming up to 200-210 DEG C and keep temperature, add boric acid, Tea Saponin reaction 3-5 hour, be cooled to 80-90 DEG C, add dimethyl carbonate, single palmitic acid, ethylenediamine stirring reaction 2-3 hour, finally be cooled to room temperature, instillation marigold essential oil and other residual componentss are ground pulping and get final product.
The preparation method of described a kind of resist chemical woven fabric, is characterized in that comprising the following steps:
(1) by Chinese ephedra, folium isatidis boiling 4-6 hour, filter, in filtrate, drop into natural bamboo fiber, polysulphonamide fiber, jade fiber, bombax cotton immersion 10-13 hour, pull oven dry, ultra-fine grinding out;
(2) wood sawdust, pine needle to be added water grinding pulping after drying charing, add magnesium sulfate and stir and evenly mix and put into Ultrasonic machining groove, concussion 6-12 hour, dry grinding 2-4 hour;
(3) syndiotactic polypropylene is heated to molten condition, adds step (2) product, dicyclohexyl phthalate, diethyl oxalate, agitation grinding 4-6 hour;
(4) take 1-butyl-3-N-Methylimidazoleacetic salt, 1-allyl-3-methylimidazole villaumite drops in reactor and stirs and evenly mixs, add step (1), (3) product grinding 20-40 minute, be heated to 95-110 DEG C, add other residual components stirring reaction 50-70 minute, obtained spinning solution, through spinning, spinning discharging.
The present invention has following beneficial effect: preparation section of the present invention is easy, easy to implement, by the choose reasonable of raw material and the proportion design of science, and obtained woven fabric complete function; By natural bamboo fiber, polysulphonamide fiber, jade fiber, bombax cotton after medicinal herb soak process and polypropylene fibre blending, not only increase spinnability and the spinning quality of string, also improve all technical of woven fabric, there is the functions such as antibacterial mite-removing, deodorization are fire-retardant, chemicals-resistant burn into sound-insulation and heat-insulation.
Detailed description of the invention
Described a kind of resist chemical woven fabric, formed through air-jet loom braiding by warp thread and weft yarn, it is characterized in that, the raw material of described warp thread and weft yarn is made up of the raw material of following weight portion: syndiotactic polypropylene 26, magnesium sulfate 0.4, natural bamboo fiber 27, polysulphonamide fiber 32, jade fiber 16, bombax cotton 17, wood sawdust 4, pine needle 3, dicyclohexyl phthalate 4, diethyl oxalate 8, Chinese ephedra 2, folium isatidis 5,1-butyl-3-N-Methylimidazoleacetic salt 89,1-allyl-3-methylimidazole villaumite 99, auxiliary agent 7, suitable quantity of water.
Described auxiliary agent is made up of following raw materials in part by weight: boric acid 0.4, Tea Saponin 0.07, glycerine 18, benzoic acid 16, ethylene glycol 18, ethylenediamine 3, nano silicon 1.7, mica powder 3, dimethyl carbonate 15, single palmitic acid 13, palm oil 9, marigold essential oil 0.15, ESCALOL 567 0.1, its preparation method is by glycerine, benzoic acid, ethylene glycol is put into reactor and is stirred and evenly mixed, be warming up to 200-210 DEG C and keep temperature, add boric acid, Tea Saponin reaction 3-5 hour, be cooled to 80-90 DEG C, add dimethyl carbonate, single palmitic acid, ethylenediamine stirring reaction 2-3 hour, finally be cooled to room temperature, instillation marigold essential oil and other residual componentss are ground pulping and get final product.
Preparation method comprises the following steps:
(1) by Chinese ephedra, folium isatidis boiling 4-6 hour, filter, in filtrate, drop into natural bamboo fiber, polysulphonamide fiber, jade fiber, bombax cotton immersion 10-13 hour, pull oven dry, ultra-fine grinding out;
(2) wood sawdust, pine needle to be added water grinding pulping after drying charing, add magnesium sulfate and stir and evenly mix and put into Ultrasonic machining groove, concussion 6-12 hour, dry grinding 2-4 hour;
(3) syndiotactic polypropylene is heated to molten condition, adds step (2) product, dicyclohexyl phthalate, diethyl oxalate, agitation grinding 4-6 hour;
(4) take 1-butyl-3-N-Methylimidazoleacetic salt, 1-allyl-3-methylimidazole villaumite drops in reactor and stirs and evenly mixs, add step (1), (3) product grinding 20-40 minute, be heated to 95-110 DEG C, add other residual components stirring reaction 50-70 minute, obtained spinning solution, through spinning, spinning discharging.
The woven fabric using the present invention to produce has following performance indications:
(1) light weight, warming, gas permeability is good, wear-resisting, flame retardant effect is excellent;
(2) after 30 washings, antibiotic rate still reaches 96.9%;
(3) coefficient of heat conduction is 4.748W/ (m
2dEG C), noise reduction coefficient is 0.863.
Claims (2)
1. a resist chemical woven fabric, formed through air-jet loom braiding by warp thread and weft yarn, it is characterized in that, the raw material of described warp thread and weft yarn is made up of the raw material of following weight portion: syndiotactic polypropylene 24-29, magnesium sulfate 0.4-0.8, natural bamboo fiber 23-28, polysulphonamide fiber 30-35, jade fiber 14-19, bombax cotton 17-23, wood sawdust 4-7, pine needle 3-6, dicyclohexyl phthalate 2-5, diethyl oxalate 7-12, Chinese ephedra 2-4, folium isatidis 3-5, 1-butyl-3-N-Methylimidazoleacetic salt 85-105, 1-allyl-3-methylimidazole villaumite 95-110, auxiliary agent 5-8, suitable quantity of water, described auxiliary agent is made up of following raw materials in part by weight: boric acid 0.2-0.5, Tea Saponin 0.04-0.08, glycerine 15-19, benzoic acid 16-22, ethylene glycol 18-26, ethylenediamine 2-4, nano silicon 1.2-2.3, mica powder 3-5, dimethyl carbonate 13-17, single palmitic acid 12-14, palm oil 7-10, marigold essential oil 0.05-0.15, ESCALOL 567 0.1-0.3, its preparation method is by glycerine, benzoic acid, ethylene glycol is put into reactor and is stirred and evenly mixed, be warming up to 200-210 DEG C and keep temperature, add boric acid, Tea Saponin reaction 3-5 hour, be cooled to 80-90 DEG C, add dimethyl carbonate, single palmitic acid, ethylenediamine stirring reaction 2-3 hour, finally be cooled to room temperature, instillation marigold essential oil and other residual componentss are ground pulping and get final product.
2. the preparation method of a kind of resist chemical woven fabric according to claim 1, is characterized in that comprising the following steps:
(1) by Chinese ephedra, folium isatidis boiling 4-6 hour, filter, in filtrate, drop into natural bamboo fiber, polysulphonamide fiber, jade fiber, bombax cotton immersion 10-13 hour, pull oven dry, ultra-fine grinding out;
(2) wood sawdust, pine needle to be added water grinding pulping after drying charing, add magnesium sulfate and stir and evenly mix and put into Ultrasonic machining groove, concussion 6-12 hour, dry grinding 2-4 hour;
(3) syndiotactic polypropylene is heated to molten condition, adds step (2) product, dicyclohexyl phthalate, diethyl oxalate, agitation grinding 4-6 hour;
(4) take 1-butyl-3-N-Methylimidazoleacetic salt, 1-allyl-3-methylimidazole villaumite drops in reactor and stirs and evenly mixs, add step (1), (3) product grinding 20-40 minute, be heated to 95-110 DEG C, add other residual components stirring reaction 50-70 minute, obtained spinning solution, through spinning, spinning discharging.