CN104652016A - Waterproof noise-reduction multifunctional woven fabric and production method thereof - Google Patents
Waterproof noise-reduction multifunctional woven fabric and production method thereof Download PDFInfo
- Publication number
- CN104652016A CN104652016A CN201510074345.6A CN201510074345A CN104652016A CN 104652016 A CN104652016 A CN 104652016A CN 201510074345 A CN201510074345 A CN 201510074345A CN 104652016 A CN104652016 A CN 104652016A
- Authority
- CN
- China
- Prior art keywords
- parts
- hour
- add
- grinding
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a waterproof noise-reduction multifunctional woven fabric which is formed by weaving warp yarns and weft yarns by an air-jet loom, wherein the warp yarns and the weft yarns are prepared from the following raw materials in parts by weight: 30 to 36 parts of isotatic polypropylene, 10 to 14 parts of polyvinyl chloride, 20 to 24 parts of cowhair, 17 to 19 parts of alpinia fiber, 22 to 26 parts of kenaf fiber, 18 to 23 parts of cotton pulp, 7 to 9 parts of liquid paraffin, 8 to 10 parts of ethyl carbamate, 7 to 11 parts of polytetramethylene glycol, 1.1 to 2.5 parts of benzoyl peroxide, 2.1 to 3.2 parts of chitosan, 0.3 to 0.5 part of magnesium acetate, 2 to 4 parts of shell powder, 1 to 3 parts of rhizoma, 2 to 5 parts of mangnolia officinalis, 85 to 95 parts of 1-butyl-3-methyl imidazole acetate, 95 to 105 parts of 1-allyl-3-methyl imidazole chloride salt, a proper amount of water and 4 to 7 parts of assistant. The woven fabric has the advantages of warmth keeping, ventilation, wear resistance, antibacterial performance and the like.
Description
Technical field
The present invention relates to woven fabric production technology, be specifically related to a kind of water-proof noise reducing Multi Role Aircraft knitted fabric and preparation method thereof.
Background technology
Communications and transportation plays vital effect in the national economic development, the vehicles such as automobile, train, aircraft, steamer also more and more go deep into the life of people, particularly automobile, become the indispensability trip instrument in nowadays people's life, along with developing rapidly of auto industry, textile for automobile also develops thereupon.Consider health, for textile for automobile, gas permeability, comfortableness, aesthetic property, smell, antibacterial and antimildew function and attraction noise reduction etc. have strict demand, especially automotive trim textiles.What textile for automobile application was more is exactly woven fabric, is mainly used in door internal decoration plate, carpet, ceiling, seat etc.
Woven fabric is by the mutually vertical yarn of two or more than two, to be interwoven fabric as longitude and latitude with an angle of 90 degrees, the woven fabric of prior art has that composition is more single, function simple, sound-absorbing antimildew and antibacterial function not significantly, the low defect such as not to be durable of ABRASION RESISTANCE, the multi-functional demand of people for automotive trim woven fabric cannot be met.
Summary of the invention
Object of the present invention is just to provide a kind of water-proof noise reducing Multi Role Aircraft knitted fabric and preparation method thereof, to overcome the deficiencies in the prior art.
The object of the present invention is achieved like this:
A kind of water-proof noise reducing Multi Role Aircraft knitted fabric, formed through air-jet loom braiding by warp thread and weft yarn, it is characterized in that, the raw material of described warp thread and weft yarn is made up of the raw material of following weight portion: isotactic polypropylene 30-36, polyvinyl chloride 10-14, ox hair 20-24, moon peach fiber 17-19, kenaf 22-26, Cotton Pulp 18-23, atoleine 7-9, urethanes 8-10, polytetramethylene glycol 7-11, benzoyl peroxide 1.1-2.5, shitosan 2.1-3.2, magnesium acetate 0.3-0.5, oyster shell whiting 2-4, rattletop 1-3, bark of official magnolia 2-5, 1-butyl-3-N-Methylimidazoleacetic salt 85-95, 1-allyl-3-methylimidazole villaumite 95-105, suitable quantity of water, auxiliary agent 4-7.
Described auxiliary agent is made up of following raw materials in part by weight: lanolin 12-16, lithium soap stone flour 1-3, gallic acid 2.3-4.7, linoleic acid 7-10, phenylalanine 17-22, pentaerythrite 15-18, methyl methacrylate 13-17, diethylenetriamine 3-5, cyanidenon 0.1-0.3, potassium oleate 0.2-0.4, linen softening oil 6-9, active fruit shell carbon 4-7, polymethyl hydrogen siloxane 1.1-2.5, its preparation method is by linoleic acid, phenylalanine, pentaerythrite is put into reactor and is stirred and evenly mixed, be warming up to 210-220 DEG C and keep temperature, add gallic acid, potassium oleate reaction 3-5 hour, be cooled to 80-95 DEG C, add methyl methacrylate, diethylenetriamine, polymethyl hydrogen siloxane stirring reaction 2-3 hour, finally be cooled to room temperature, instillation marigold essential oil and other residual componentss are ground pulping and get final product.
The preparation method of described a kind of water-proof noise reducing Multi Role Aircraft knitted fabric, is characterized in that comprising the following steps:
(1) by rattletop, bark of official magnolia boiling 4-6 hour, filter, drop into toward filtrate in ox hair, the moon peach fiber, kenaf immersion 10-13 hour, pull oven dry, ultra-fine grinding out;
(2) add water oyster shell whiting grinding pulping, adds shitosan, magnesium acetate, Cotton Pulp stir and evenly mix and put into Ultrasonic machining groove, concussion 6-12 hour, dry grinding 2-4 hour obtained modification oyster shell whiting;
(3) isotactic polypropylene is heated to molten condition, adds modification oyster shell whiting, polyvinyl chloride, atoleine, urethanes, polytetramethylene glycol, abundant agitation grinding 3-6 hour;
(4) take 1-butyl-3-N-Methylimidazoleacetic salt, 1-allyl-3-methylimidazole villaumite drops in reactor and stirs and evenly mixs, add step (1), (3) product grinding 20-40 minute, be heated to 100-120 DEG C, add other residual components stirring reaction 50-70 minute, obtained spinning solution, through spinning, spinning discharging.
The present invention has following beneficial effect: the present invention by ox hair, the moon peach fiber, kenaf is after medicinal herb soak process and polypropylene fibre blending, not only increase spinnability and the spinning quality of string, also improve the water-proof noise reducing function of woven fabric, modified for oyster shell whiting and other active ingredients are added in raw material by the present invention simultaneously, the binding ability of oyster shell whiting particulate and fiber can be improved and improve the properties of product, there is the advantage such as heat-insulation breathable, wear-resistant antibacterial.
Detailed description of the invention
Described a kind of water-proof noise reducing Multi Role Aircraft knitted fabric, formed through air-jet loom braiding by warp thread and weft yarn, it is characterized in that, the raw material of described warp thread and weft yarn is made up of the raw material of following weight portion: isotactic polypropylene 32, polyvinyl chloride 13, ox hair 21, month peach fiber 17, kenaf 24, Cotton Pulp 19, atoleine 8, urethanes 8, polytetramethylene glycol 7, benzoyl peroxide 1.8, shitosan 2.7, magnesium acetate 0.3, oyster shell whiting 2, rattletop 1, the bark of official magnolia 4, 1-butyl-3-N-Methylimidazoleacetic salt 89, 1-allyl-3-methylimidazole villaumite 102, suitable quantity of water, auxiliary agent 5.
Described auxiliary agent is made up of following raw materials in part by weight: lanolin 14, lithium soap stone flour 1, gallic acid 2.7, linoleic acid 7, phenylalanine 18, pentaerythrite 16, methyl methacrylate 15, diethylenetriamine 4, cyanidenon 0.2, potassium oleate 0.3, linen softening oil 8, active fruit shell carbon 7, polymethyl hydrogen siloxane 1.9, its preparation method is by linoleic acid, phenylalanine, pentaerythrite is put into reactor and is stirred and evenly mixed, be warming up to 210-220 DEG C and keep temperature, add gallic acid, potassium oleate reaction 3-5 hour, be cooled to 80-95 DEG C, add methyl methacrylate, diethylenetriamine, polymethyl hydrogen siloxane stirring reaction 2-3 hour, finally be cooled to room temperature, instillation marigold essential oil and other residual componentss are ground pulping and get final product.
Preparation method comprises the following steps:
(1) by rattletop, bark of official magnolia boiling 4-6 hour, filter, drop into toward filtrate in ox hair, the moon peach fiber, kenaf immersion 10-13 hour, pull oven dry, ultra-fine grinding out;
(2) add water oyster shell whiting grinding pulping, adds shitosan, magnesium acetate, Cotton Pulp stir and evenly mix and put into Ultrasonic machining groove, concussion 6-12 hour, dry grinding 2-4 hour obtained modification oyster shell whiting;
(3) isotactic polypropylene is heated to molten condition, adds modification oyster shell whiting, polyvinyl chloride, atoleine, urethanes, polytetramethylene glycol, abundant agitation grinding 3-6 hour;
(4) take 1-butyl-3-N-Methylimidazoleacetic salt, 1-allyl-3-methylimidazole villaumite drops in reactor and stirs and evenly mixs, add step (1), (3) product grinding 20-40 minute, be heated to 100-120 DEG C, add other residual components stirring reaction 50-70 minute, obtained spinning solution, through spinning, spinning discharging.
The woven fabric using the present invention to produce has following performance indications:
(1) light weight, warming, gas permeability is good, wear-resisting;
(2) after 20 washings, antibiotic rate still reaches 96.4%;
(3) noise reduction coefficient is 0.88.
Claims (2)
1. a water-proof noise reducing Multi Role Aircraft knitted fabric, formed through air-jet loom braiding by warp thread and weft yarn, it is characterized in that, the raw material of described warp thread and weft yarn is made up of the raw material of following weight portion: isotactic polypropylene 30-36, polyvinyl chloride 10-14, ox hair 20-24, moon peach fiber 17-19, kenaf 22-26, Cotton Pulp 18-23, atoleine 7-9, urethanes 8-10, polytetramethylene glycol 7-11, benzoyl peroxide 1.1-2.5, shitosan 2.1-3.2, magnesium acetate 0.3-0.5, oyster shell whiting 2-4, rattletop 1-3, bark of official magnolia 2-5, 1-butyl-3-N-Methylimidazoleacetic salt 85-95, 1-allyl-3-methylimidazole villaumite 95-105, suitable quantity of water, auxiliary agent 4-7, described auxiliary agent is made up of following raw materials in part by weight: lanolin 12-16, lithium soap stone flour 1-3, gallic acid 2.3-4.7, linoleic acid 7-10, phenylalanine 17-22, pentaerythrite 15-18, methyl methacrylate 13-17, diethylenetriamine 3-5, cyanidenon 0.1-0.3, potassium oleate 0.2-0.4, linen softening oil 6-9, active fruit shell carbon 4-7, polymethyl hydrogen siloxane 1.1-2.5, its preparation method is by linoleic acid, phenylalanine, pentaerythrite is put into reactor and is stirred and evenly mixed, be warming up to 210-220 DEG C and keep temperature, add gallic acid, potassium oleate reaction 3-5 hour, be cooled to 80-95 DEG C, add methyl methacrylate, diethylenetriamine, polymethyl hydrogen siloxane stirring reaction 2-3 hour, finally be cooled to room temperature, instillation marigold essential oil and other residual componentss are ground pulping and get final product.
2. the preparation method of a kind of water-proof noise reducing Multi Role Aircraft knitted fabric according to claim 1, is characterized in that comprising the following steps:
(1) by rattletop, bark of official magnolia boiling 4-6 hour, filter, drop into toward filtrate in ox hair, the moon peach fiber, kenaf immersion 10-13 hour, pull oven dry, ultra-fine grinding out;
(2) add water oyster shell whiting grinding pulping, adds shitosan, magnesium acetate, Cotton Pulp stir and evenly mix and put into Ultrasonic machining groove, concussion 6-12 hour, dry grinding 2-4 hour obtained modification oyster shell whiting;
(3) isotactic polypropylene is heated to molten condition, adds modification oyster shell whiting, polyvinyl chloride, atoleine, urethanes, polytetramethylene glycol, abundant agitation grinding 3-6 hour;
(4) take 1-butyl-3-N-Methylimidazoleacetic salt, 1-allyl-3-methylimidazole villaumite drops in reactor and stirs and evenly mixs, add step (1), (3) product grinding 20-40 minute, be heated to 100-120 DEG C, add other residual components stirring reaction 50-70 minute, obtained spinning solution, through spinning, spinning discharging.