CN105440585A - Fire and flame resisting material - Google Patents
Fire and flame resisting material Download PDFInfo
- Publication number
- CN105440585A CN105440585A CN201510935236.9A CN201510935236A CN105440585A CN 105440585 A CN105440585 A CN 105440585A CN 201510935236 A CN201510935236 A CN 201510935236A CN 105440585 A CN105440585 A CN 105440585A
- Authority
- CN
- China
- Prior art keywords
- parts
- fire
- flame
- resisting material
- gypsum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a fire and flame resisting material. The fire and flame resisting material is prepared from, by weight, 8-9 parts of flame retardation polyether, 13-15 parts of calcium carbonate, 3-5 parts of molybdenum trioxide, 4-6 parts of polycarbonate, 8-11 parts of pentaerythritol, 7-9 parts of silica, 3-5 parts of magnesium hydroxide, 30-42 parts of epoxy resin, 12-14 parts of potato starch, 5-8 parts of diethyl phthalate, 6-10 parts of stearic acid and 12-15 parts of gypsum. The fire and flame resisting material has the advantages of good fire resistance, strong flame retardation capability, no toxic substances, substantial environmental protection performance, and no decomposition of toxic substances in the high temperature process.
Description
Technical field
The present invention relates to technical field of flame retardant, particularly relate to a kind of applied fireproofing.
Background technology
All physical and chemical changes that the combustionproperty of material of construction occurs when referring to its burning or meet fire, and material of construction inside fitting design should deal carefully with the contradiction of finishing effect and use safety, active adoption non-combustible material and flame retardant material, avoid adopting the material producing a large amount of dense smoke or toxic gas when burning as far as possible, accomplish safe and applicable, advanced technology, economical rationality.Current most of material of construction, without any flame retardant effect, very easily burns, and fire hazard is very large.
Summary of the invention
For solving above-mentioned Problems existing, the invention provides a kind of fire line good, fire retardancy is strong, and without toxic substance, environmental-protecting performance is remarkable, without the applied fireproofing that toxic substance decomposes in pyroprocess.
The technical scheme that the present invention solves the problems of the technologies described above employing is: a kind of applied fireproofing, is prepared by the raw material of following weight part:
Flame retarding polyether 8-9 part, calcium carbonate 13-15 part, molybdic oxide 3-5 part, polycarbonate 4-6 part, tetramethylolmethane 8-11 part, silicon-dioxide 7-9 part, magnesium hydroxide 3-5 part, epoxy resin 30-42 part, Cornstarch 12-14 part, diethyl phthalate 5-8 part, stearic acid 6-10 part, gypsum 12-15 part.
Above-mentioned applied fireproofing, prepared by the raw material of following weight part:
Flame retarding polyether 8.5 parts, 14 parts, calcium carbonate, molybdic oxide 4 parts, polycarbonate 5 parts, tetramethylolmethane 10 parts, silicon-dioxide 8 parts, magnesium hydroxide 4 parts, epoxy resin 36 parts, Cornstarch 13 parts, diethyl phthalate 6 parts, stearic acid 8 parts, 13 parts, gypsum.
The beneficial effect that technical solution problem of the present invention is brought is: fire line of the present invention is good, and fire retardancy is strong, and without toxic substance, environmental-protecting performance is remarkable, decomposes in pyroprocess without toxic substance.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in further details.
Embodiment 1
A kind of applied fireproofing, prepared by the raw material of following weight part:
Flame retarding polyether 8 parts, 13 parts, calcium carbonate, molybdic oxide 3 parts, polycarbonate 4 parts, tetramethylolmethane 8 parts, silicon-dioxide 7 parts, magnesium hydroxide 3 parts, epoxy resin 30 parts, Cornstarch 12 parts, diethyl phthalate 5 parts, stearic acid 6 parts, 12 parts, gypsum.
Embodiment 2
A kind of applied fireproofing, prepared by the raw material of following weight part:
Flame retarding polyether 8.5 parts, 14 parts, calcium carbonate, molybdic oxide 4 parts, polycarbonate 5 parts, tetramethylolmethane 10 parts, silicon-dioxide 8 parts, magnesium hydroxide 4 parts, epoxy resin 36 parts, Cornstarch 13 parts, diethyl phthalate 6 parts, stearic acid 8 parts, 13 parts, gypsum.
Embodiment 3
A kind of applied fireproofing, prepared by the raw material of following weight part:
Flame retarding polyether 9 parts, 15 parts, calcium carbonate, molybdic oxide 5 parts, polycarbonate 6 parts, tetramethylolmethane 11 parts, silicon-dioxide 9 parts, magnesium hydroxide 5 parts, epoxy resin 42 parts, Cornstarch 14 parts, diethyl phthalate 8 parts, stearic acid 10 parts, 15 parts, gypsum.
Although above-mentioned, the specific embodiment of the present invention is described; but not limiting the scope of the invention; one of ordinary skill in the art should be understood that; on the basis of technical scheme of the present invention, those skilled in the art do not need to pay various amendment or distortion that creative work can make still within protection scope of the present invention.
Claims (2)
1. an applied fireproofing, is characterized in that, is prepared by the raw material of following weight part:
Flame retarding polyether 8-9 part, calcium carbonate 13-15 part, molybdic oxide 3-5 part, polycarbonate 4-6 part, tetramethylolmethane 8-11 part, silicon-dioxide 7-9 part, magnesium hydroxide 3-5 part, epoxy resin 30-42 part, Cornstarch 12-14 part, diethyl phthalate 5-8 part, stearic acid 6-10 part, gypsum 12-15 part.
2. applied fireproofing according to claim 1, is characterized in that, is prepared by the raw material of following weight part:
Flame retarding polyether 8.5 parts, 14 parts, calcium carbonate, molybdic oxide 4 parts, polycarbonate 5 parts, tetramethylolmethane 10 parts, silicon-dioxide 8 parts, magnesium hydroxide 4 parts, epoxy resin 36 parts, Cornstarch 13 parts, diethyl phthalate 6 parts, stearic acid 8 parts, 13 parts, gypsum.