CN105419663A - High-temperature-resistant pressure sensitive adhesive tape and preparation method thereof - Google Patents
High-temperature-resistant pressure sensitive adhesive tape and preparation method thereof Download PDFInfo
- Publication number
- CN105419663A CN105419663A CN201510944700.0A CN201510944700A CN105419663A CN 105419663 A CN105419663 A CN 105419663A CN 201510944700 A CN201510944700 A CN 201510944700A CN 105419663 A CN105419663 A CN 105419663A
- Authority
- CN
- China
- Prior art keywords
- parts
- pressure sensitive
- sensitive adhesive
- resistant pressure
- vinylformic acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-temperature-resistant pressure sensitive adhesive tape. The adhesive tape comprises raw materials in parts by weight as follows: 100-120 parts of natural rubber, 80-100 parts of acrylic acid isononyl ester, 75-95 parts of acrylic acid, 75-95 parts of zinc oxide, 70-90 parts of ethyl acetate, 40-60 parts of silicone oil, 40-60 parts of rosin, 30-50 parts of an emulsifier, 20-40 parts of sodium bicarbonate, 10-30 parts of a gasoline-methylbenzene mixture solvent, 2-4 parts of a cross-linking agent and 1-2 parts of an anti-aging agent D. The invention further provides a preparation method of the high-temperature-resistant pressure sensitive adhesive tape. The preparation method comprises steps as follows: S1, 100-120 parts of natural rubber, 80-100 parts of acrylic acid isononyl ester and 75-95 parts of acrylic acid are weighed in weight proportion, natural rubber and acrylic acid isononyl ester are sufficiently mixed and then put into an internal mixer, acrylic acid is added, the mixture is mixed at the temperature of 50-70 DEG C for 0.5-1 h, and a mixed compound A is obtained. The high-temperature-resistant pressure sensitive adhesive tape is simple to prepare, has high high-temperature resistance and is multipurpose and suitable for popularization.
Description
Technical field
The present invention relates to high temperature resistant pressure sensitive adhesive band technical field, particularly relate to a kind of high temperature resistant pressure sensitive adhesive band and preparation method thereof.
Background technology
Along with the quick raising of social economy and people's living standard, adhesive tape has been dissolved in the use of all trades and professions and people's daily life completely.Adhesive tape is not only widely used, kind is also very many, as: the High temperature-resistanadhesive adhesive tape used under high-temperature service environment, this kind of adhesive tape is mainly used in electronic industry purposes, heat resistance, usually between 120 degree to 260 degree, is usually used in spraying paint, baking vanish leather processing, application covers and cover with fixing, printed circuit board (PCB) in electronic component processing procedure and pyroprocessing.
In prior art, common pressure sensitive adhesive resistance toheat is general, at relatively high temperatures, heatproof air aging performance is poor, easily lose pressure-sensitive, present stage, market is compared the pressure sensitive adhesive that shortage possesses high-peeling strength, high just viscous force, wide in range use temperature simultaneously, we have proposed a kind of high temperature resistant pressure sensitive adhesive band and preparation method thereof for this reason.
Summary of the invention
Based on the technical problem that background technology exists, the present invention proposes a kind of high temperature resistant pressure sensitive adhesive band and preparation method thereof.
A kind of high temperature resistant pressure sensitive adhesive band that the present invention proposes, comprises the raw material of following weight part: natural rubber 100-120 part, vinylformic acid different nonyl ester 80-100 part, vinylformic acid 75-95 part, zinc oxide 75-95 part, ethyl acetate 70-90 part, silicone oil 40-60 part, rosin 40-60 part, emulsifying agent 30-50 part, sodium bicarbonate 20-40 part, gasoline-toluene Mixed Solvent 10-30 part, linking agent 2-4 part, antioxidant D 1-2 part.
Preferably, described linking agent is the one in dicumyl peroxide, ditertiary butyl peroxide, di-isopropylbenzene hydroperoxide.
Preferably, described natural rubber, vinylformic acid different nonyl ester, acrylic acid weight ratio are 105-115:85-95:80-90.
The invention allows for a kind of preparation method of high temperature resistant pressure sensitive adhesive band, comprise the following steps:
S1, natural rubber 100-120 part, vinylformic acid different nonyl ester 80-100 part, vinylformic acid 75-95 part is taken according to deal proportioning, Banbury mixer is put into after natural rubber and the different nonyl ester of vinylformic acid fully being mixed, put into vinylformic acid again, carry out mixing at the temperature of 50-70 DEG C, continue 0.5-1h, obtain rubber unvulcanizate A;
S2, zinc oxide 75-95 part, ethyl acetate 70-90 part, silicone oil 40-60 part, rosin 40-60 part, emulsifying agent 30-50 part, sodium bicarbonate 20-40 part, gasoline-toluene Mixed Solvent 10-30 part, linking agent 2-4 part, antioxidant D 1-2 part is taken according to deal proportioning, above-mentioned raw materials is put into reactor, at the temperature of 40-50 DEG C, react 2-3h, obtain mixture B;
S3, is extruded rubber unvulcanizate A by Rubber Extruder and obtains flap C, uses coating machine by mixture B uniform application on the surface of flap C, and at the temperature of 20-30 DEG C, standing 3-4h, obtains sheet adhesive tape D;
S4, sends into sheet adhesive tape D in drying tunnel, with the hot blast drying of 60-70 DEG C, then carries out rolling and cuts, can obtain a kind of high temperature resistant pressure sensitive adhesive band.
Preferably, the weight ratio of described zinc oxide, ethyl acetate, silicone oil is 80-90:75-85:45-55.
Preferably, coating machine is used in described S3 by mixture B uniform application in the side surface of flap C or both side surface.
In the present invention, the natural high moleculer eompound of natural rubber to be a kind of with polyisoprene be main component, in its composition, 91-94% is rubber hydrocarbon, because there is unsaturated double-bond, natural rubber is the material that a kind of chemical reaction ability is stronger, by can effectively prevent natural rubber aging with the reaction of vinylformic acid different nonyl ester, vinylformic acid, react cooperation between zinc oxide and ethyl acetate and can improve pressure sensitive adhesive resistance to elevated temperatures, adopt linking agent can improve heat resistance and the moisture resistance properties of pressure sensitive adhesive, adopt anti-aging agent that pressure sensitive adhesive can be prevented aging, the over-all properties of pressure sensitive adhesive effectively can be improved after adopting raw material of the present invention to react, the present invention prepares simply, the pressure sensitive adhesive resistance to elevated temperatures of preparation is strong, can multi-usage use, be applicable to promoting.
Embodiment
Below in conjunction with specific embodiment, further explanation is done to the present invention.
Embodiment one
A kind of high temperature resistant pressure sensitive adhesive band that the present invention proposes, comprises the raw material of following weight part: the different nonyl ester of natural rubber 100 parts, vinylformic acid 80 parts, 75 parts, vinylformic acid, 75 parts, zinc oxide, ethyl acetate 70 parts, silicone oil 40 parts, rosin 40 parts, emulsifying agent 30 parts, sodium bicarbonate 20 parts, gasoline-toluene Mixed Solvent 10 parts, linking agent 2 parts, antioxidant D 1 part.
The invention allows for a kind of preparation method of high temperature resistant pressure sensitive adhesive band, comprise the following steps:
S1, takes natural rubber 100 parts, the different nonyl ester of vinylformic acid 80 parts, 75 parts, vinylformic acid according to deal proportioning, puts into Banbury mixer after natural rubber and the different nonyl ester of vinylformic acid fully being mixed, put into vinylformic acid again, carry out mixing at the temperature of 50 DEG C, continue 0.5h, obtain rubber unvulcanizate A;
S2,75 parts, zinc oxide, ethyl acetate 70 parts, silicone oil 40 parts, rosin 40 parts, emulsifying agent 30 parts, sodium bicarbonate 20 parts, gasoline-toluene Mixed Solvent 10 parts, linking agent 2 parts, antioxidant D 1 part is taken according to deal proportioning, above-mentioned raw materials is put into reactor, at the temperature of 40 DEG C, react 2h, obtain mixture B;
S3, is extruded rubber unvulcanizate A by Rubber Extruder and obtains flap C, uses coating machine by mixture B uniform application on the surface of flap C, and at the temperature of 20 DEG C, standing 3h, obtains sheet adhesive tape D;
S4, sends into sheet adhesive tape D in drying tunnel, with the hot blast drying of 60 DEG C, then carries out rolling and cuts, can obtain a kind of high temperature resistant pressure sensitive adhesive band.
Embodiment two
A kind of high temperature resistant pressure sensitive adhesive band that the present invention proposes, comprises the raw material of following weight part: the different nonyl ester of natural rubber 105 parts, vinylformic acid 85 parts, 80 parts, vinylformic acid, 80 parts, zinc oxide, ethyl acetate 75 parts, silicone oil 45 parts, rosin 45 parts, emulsifying agent 35 parts, sodium bicarbonate 25 parts, gasoline-toluene Mixed Solvent 15 parts, linking agent 2.5 parts, antioxidant D 1.25 parts.
The invention allows for a kind of preparation method of high temperature resistant pressure sensitive adhesive band, comprise the following steps:
S1, takes natural rubber 105 parts, the different nonyl ester of vinylformic acid 85 parts, 80 parts, vinylformic acid according to deal proportioning, puts into Banbury mixer after natural rubber and the different nonyl ester of vinylformic acid fully being mixed, put into vinylformic acid again, carry out mixing at the temperature of 55 DEG C, continue 0.6h, obtain rubber unvulcanizate A;
S2,80 parts, zinc oxide, ethyl acetate 75 parts, silicone oil 45 parts, rosin 45 parts, emulsifying agent 35 parts, sodium bicarbonate 25 parts, gasoline-toluene Mixed Solvent 15 parts, linking agent 2.5 parts, antioxidant D 1.25 parts is taken according to deal proportioning, above-mentioned raw materials is put into reactor, at the temperature of 42.5 DEG C, react 2.25h, obtain mixture B;
S3, is extruded rubber unvulcanizate A by Rubber Extruder and obtains flap C, uses coating machine by mixture B uniform application on the surface of flap C, and at the temperature of 22.5 DEG C, standing 3.25h, obtains sheet adhesive tape D;
S4, sends into sheet adhesive tape D in drying tunnel, with the hot blast drying of 62.5 DEG C, then carries out rolling and cuts, can obtain a kind of high temperature resistant pressure sensitive adhesive band.
Embodiment three
A kind of high temperature resistant pressure sensitive adhesive band that the present invention proposes, comprises the raw material of following weight part: the different nonyl ester of natural rubber 110 parts, vinylformic acid 90 parts, 85 parts, vinylformic acid, 85 parts, zinc oxide, ethyl acetate 80 parts, silicone oil 50 parts, rosin 50 parts, emulsifying agent 40 parts, sodium bicarbonate 30 parts, gasoline-toluene Mixed Solvent 20 parts, linking agent 3 parts, antioxidant D 1.5 parts.
The invention allows for a kind of preparation method of high temperature resistant pressure sensitive adhesive band, comprise the following steps:
S1, takes natural rubber 110 parts, the different nonyl ester of vinylformic acid 90 parts, 85 parts, vinylformic acid according to deal proportioning, puts into Banbury mixer after natural rubber and the different nonyl ester of vinylformic acid fully being mixed, put into vinylformic acid again, carry out mixing at the temperature of 60 DEG C, continue 0.75h, obtain rubber unvulcanizate A;
S2,85 parts, zinc oxide, ethyl acetate 80 parts, silicone oil 50 parts, rosin 50 parts, emulsifying agent 40 parts, sodium bicarbonate 30 parts, gasoline-toluene Mixed Solvent 20 parts, linking agent 3 parts, antioxidant D 1.5 parts is taken according to deal proportioning, above-mentioned raw materials is put into reactor, at the temperature of 45 DEG C, react 2.5h, obtain mixture B;
S3, is extruded rubber unvulcanizate A by Rubber Extruder and obtains flap C, uses coating machine by mixture B uniform application on the surface of flap C, and at the temperature of 25 DEG C, standing 3.5h, obtains sheet adhesive tape D;
S4, sends into sheet adhesive tape D in drying tunnel, with the hot blast drying of 65 DEG C, then carries out rolling and cuts, can obtain a kind of high temperature resistant pressure sensitive adhesive band.
Embodiment four
A kind of high temperature resistant pressure sensitive adhesive band that the present invention proposes, comprises the raw material of following weight part: the different nonyl ester of natural rubber 115 parts, vinylformic acid 95 parts, 90 parts, vinylformic acid, 90 parts, zinc oxide, ethyl acetate 85 parts, silicone oil 55 parts, rosin 55 parts, emulsifying agent 45 parts, sodium bicarbonate 35 parts, gasoline-toluene Mixed Solvent 25 parts, linking agent 3.5 parts, antioxidant D 1.75 parts.
The invention allows for a kind of preparation method of high temperature resistant pressure sensitive adhesive band, comprise the following steps:
S1, takes natural rubber 115 parts, the different nonyl ester of vinylformic acid 95 parts, 90 parts, vinylformic acid according to deal proportioning, puts into Banbury mixer after natural rubber and the different nonyl ester of vinylformic acid fully being mixed, put into vinylformic acid again, carry out mixing at the temperature of 65 DEG C, continue 0.9h, obtain rubber unvulcanizate A;
S2,90 parts, zinc oxide, ethyl acetate 85 parts, silicone oil 55 parts, rosin 55 parts, emulsifying agent 45 parts, sodium bicarbonate 35 parts, gasoline-toluene Mixed Solvent 25 parts, linking agent 3.5 parts, antioxidant D 1.75 parts is taken according to deal proportioning, above-mentioned raw materials is put into reactor, at the temperature of 40-50 DEG C, react 2.75h, obtain mixture B;
S3, is extruded rubber unvulcanizate A by Rubber Extruder and obtains flap C, uses coating machine by mixture B uniform application on the surface of flap C, and at the temperature of 27.5 DEG C, standing 3.75h, obtains sheet adhesive tape D;
S4, sends into sheet adhesive tape D in drying tunnel, with the hot blast drying of 67.5 DEG C, then carries out rolling and cuts, can obtain a kind of high temperature resistant pressure sensitive adhesive band.
Embodiment five
A kind of high temperature resistant pressure sensitive adhesive band that the present invention proposes, comprises the raw material of following weight part: the different nonyl ester of natural rubber 120 parts, vinylformic acid 100 parts, 95 parts, vinylformic acid, 95 parts, zinc oxide, ethyl acetate 90 parts, silicone oil 60 parts, rosin 60 parts, emulsifying agent 50 parts, sodium bicarbonate 40 parts, gasoline-toluene Mixed Solvent 30 parts, linking agent 4 parts, antioxidant D 2 parts.
The invention allows for a kind of preparation method of high temperature resistant pressure sensitive adhesive band, comprise the following steps:
S1, takes natural rubber 120 parts, the different nonyl ester of vinylformic acid 100 parts, 95 parts, vinylformic acid according to deal proportioning, puts into Banbury mixer after natural rubber and the different nonyl ester of vinylformic acid fully being mixed, put into vinylformic acid again, carry out mixing at the temperature of 70 DEG C, continue 1h, obtain rubber unvulcanizate A;
S2,95 parts, zinc oxide, ethyl acetate 90 parts, silicone oil 60 parts, rosin 60 parts, emulsifying agent 50 parts, sodium bicarbonate 40 parts, gasoline-toluene Mixed Solvent 30 parts, linking agent 4 parts, antioxidant D 2 parts is taken according to deal proportioning, above-mentioned raw materials is put into reactor, at the temperature of 50 DEG C, react 3h, obtain mixture B;
S3, is extruded rubber unvulcanizate A by Rubber Extruder and obtains flap C, uses coating machine by mixture B uniform application on the surface of flap C, and at the temperature of 30 DEG C, standing 4h, obtains sheet adhesive tape D;
S4, sends into sheet adhesive tape D in drying tunnel, with the hot blast drying of 70 DEG C, then carries out rolling and cuts, can obtain a kind of high temperature resistant pressure sensitive adhesive band.
The above; be only the present invention's preferably embodiment; but protection scope of the present invention is not limited thereto; anyly be familiar with those skilled in the art in the technical scope that the present invention discloses; be equal to according to technical scheme of the present invention and inventive concept thereof and replace or change, all should be encompassed within protection scope of the present invention.
Claims (6)
1. a high temperature resistant pressure sensitive adhesive band, it is characterized in that, comprise the raw material of following weight part: natural rubber 100-120 part, vinylformic acid different nonyl ester 80-100 part, vinylformic acid 75-95 part, zinc oxide 75-95 part, ethyl acetate 70-90 part, silicone oil 40-60 part, rosin 40-60 part, emulsifying agent 30-50 part, sodium bicarbonate 20-40 part, gasoline-toluene Mixed Solvent 10-30 part, linking agent 2-4 part, antioxidant D 1-2 part.
2. a kind of high temperature resistant pressure sensitive adhesive band according to claim 1, is characterized in that, described linking agent is the one in dicumyl peroxide, ditertiary butyl peroxide, di-isopropylbenzene hydroperoxide.
3. a kind of high temperature resistant pressure sensitive adhesive band according to claim 1, is characterized in that, described natural rubber, vinylformic acid different nonyl ester, acrylic acid weight ratio are 105-115:85-95:80-90.
4. a kind of high temperature resistant pressure sensitive adhesive band according to claim 1, is characterized in that, the weight ratio of described zinc oxide, ethyl acetate, silicone oil is 80-90:75-85:45-55.
5. a preparation method for high temperature resistant pressure sensitive adhesive band, is characterized in that, comprises the following steps:
S1, natural rubber 100-120 part, vinylformic acid different nonyl ester 80-100 part, vinylformic acid 75-95 part is taken according to deal proportioning, Banbury mixer is put into after natural rubber and the different nonyl ester of vinylformic acid fully being mixed, put into vinylformic acid again, carry out mixing at the temperature of 50-70 DEG C, continue 0.5-1h, obtain rubber unvulcanizate A;
S2, zinc oxide 75-95 part, ethyl acetate 70-90 part, silicone oil 40-60 part, rosin 40-60 part, emulsifying agent 30-50 part, sodium bicarbonate 20-40 part, gasoline-toluene Mixed Solvent 10-30 part, linking agent 2-4 part, antioxidant D 1-2 part is taken according to deal proportioning, above-mentioned raw materials is put into reactor, at the temperature of 40-50 DEG C, react 2-3h, obtain mixture B;
S3, is extruded rubber unvulcanizate A by Rubber Extruder and obtains flap C, uses coating machine by mixture B uniform application on the surface of flap C, and at the temperature of 20-30 DEG C, standing 3-4h, obtains sheet adhesive tape D;
S4, sends into sheet adhesive tape D in drying tunnel, with the hot blast drying of 60-70 DEG C, then carries out rolling and cuts, can obtain a kind of high temperature resistant pressure sensitive adhesive band.
6. the preparation method of a kind of high temperature resistant pressure sensitive adhesive band according to claim 5, is characterized in that, uses coating machine by mixture B uniform application in the side surface of flap C or both side surface in described S3.