CN105419588A - Mixed coating of alkyd resin and modified acrylic resin - Google Patents
Mixed coating of alkyd resin and modified acrylic resin Download PDFInfo
- Publication number
- CN105419588A CN105419588A CN201510949175.1A CN201510949175A CN105419588A CN 105419588 A CN105419588 A CN 105419588A CN 201510949175 A CN201510949175 A CN 201510949175A CN 105419588 A CN105419588 A CN 105419588A
- Authority
- CN
- China
- Prior art keywords
- parts
- acrylic resin
- modified acrylic
- mixed coating
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a mixed coating of alkyd resin and modified acrylic resin. The mixed coating is prepared from the following raw materials in parts by weight: 32 to 38 parts of alkyd resin, 28 to 30 parts of modified acrylic resin, 6 to 10 parts of methacrylamide, 6 to 8 parts of crylic acid, 1 to 4 parts of barium sulfate, 2 to 4 parts of zinc sulfate, 3 to 5 parts of DMC (dimethyl carbonate), 3 to 5 parts of organobentonite, 2 to 6 parts of nano-silica, 2 to 6 parts of iron oxide red, 8 to 10 parts of glycerine, 8 to 12 parts of pentaerythritol, 1 to 4 parts of phosphate ester and 2 to 4 parts of defoamer. The mixed coating of the alkyd resin and the modified acrylic resin, disclosed by the invention, is rapid in drying speed, strong in adhesive force, good in color retention, and superior in water resistance and alkali resistance, and is ageing resistant.
Description
Technical field
The invention belongs to paint field, be specifically related to a kind of Synolac and acrylic resin modified compo.
Background technology
Alkydpaints take Synolac as the synthetic resin coating of main film forming substance, phthalic resin coating is all better than oil-base paint in drying rate, sticking power, hardness, gloss, weathering resistance and gloss retention etc., and easy construction, but film is softer, water-fast, alkali resistance is not good enough.Acrylic coating take acrylic resin as the synthetic resin coating of main film forming substance, and rate of drying is slow, weathering resistance is poor.
Summary of the invention
For the deficiencies in the prior art, the invention provides a kind of Synolac and acrylic resin modified compo, rate of drying is fast, and strong adhesion, unfading is good, and water tolerance, alkaline resistance properties are superior, anti-aging.
Technical scheme of the present invention is: a kind of Synolac and acrylic resin modified compo, be made up of the raw material of following parts by weight: Synolac 32-38 part, acrylic resin modified 28-30 part, Methacrylamide 6-10 part, vinylformic acid 6-8 part, barium sulfate 1-4 part, zinc sulfate 2-4 part, methylcarbonate 3-5 part, organobentonite 3-5 part, nano silicon 2-6 part, iron oxide red 2-6 part, glycerol 8-10 part, tetramethylolmethane 8-12 part, phosphoric acid ester 1-4 part, defoamer 2-4 part.
Compared with prior art, the invention has the advantages that: rate of drying is fast, strong adhesion, and unfading is good; Water tolerance, alkaline resistance properties are superior, anti-aging.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in further detail.
Embodiment 1
A kind of Synolac and acrylic resin modified compo, be made up of the raw material of following parts by weight: Synolac 32 parts, acrylic resin modified 28 parts, Methacrylamide 6 parts, 6 parts, vinylformic acid, 1 part, barium sulfate, 2 parts, zinc sulfate, methylcarbonate 3 parts, organobentonite 3 parts, nano silicon 2 parts, iron oxide red 2 parts, glycerol 8 parts, tetramethylolmethane 8 parts, phosphoric acid ester 1 part, defoamer 2 parts.
Embodiment 2
A kind of Synolac and acrylic resin modified compo, be made up of the raw material of following parts by weight: Synolac 35 parts, acrylic resin modified 29 parts, Methacrylamide 8 parts, 7 parts, vinylformic acid, 2 parts, barium sulfate, 3 parts, zinc sulfate, methylcarbonate 4 parts, organobentonite 4 parts, nano silicon 4 parts, iron oxide red 4 parts, glycerol 9 parts, tetramethylolmethane 10 parts, phosphoric acid ester 3 parts, defoamer 3 parts.
Embodiment 3
A kind of Synolac and acrylic resin modified compo, be made up of the raw material of following parts by weight: Synolac 38 parts, acrylic resin modified 30 parts, Methacrylamide 10 parts, 8 parts, vinylformic acid, 4 parts, barium sulfate, 4 parts, zinc sulfate, methylcarbonate 5 parts, organobentonite 5 parts, nano silicon 6 parts, iron oxide red 6 parts, glycerol 10 parts, tetramethylolmethane 12 parts, phosphoric acid ester 4 parts, defoamer 4 parts.
Describe the present invention by way of example above, but the invention is not restricted to above-mentioned specific embodiment, all any changes of doing based on the present invention or modification all belong to the scope of protection of present invention.
Claims (1)
1. Synolac and an acrylic resin modified compo, is characterized in that: be made up of the raw material of following parts by weight: Synolac 32-38 part, acrylic resin modified 28-30 part, Methacrylamide 6-10 part, vinylformic acid 6-8 part, barium sulfate 1-4 part, zinc sulfate 2-4 part, methylcarbonate 3-5 part, organobentonite 3-5 part, nano silicon 2-6 part, iron oxide red 2-6 part, glycerol 8-10 part, tetramethylolmethane 8-12 part, phosphoric acid ester 1-4 part, defoamer 2-4 part.