CN105418051A - Environment-friendly building material - Google Patents
Environment-friendly building material Download PDFInfo
- Publication number
- CN105418051A CN105418051A CN201510903958.6A CN201510903958A CN105418051A CN 105418051 A CN105418051 A CN 105418051A CN 201510903958 A CN201510903958 A CN 201510903958A CN 105418051 A CN105418051 A CN 105418051A
- Authority
- CN
- China
- Prior art keywords
- parts
- environmental
- construction material
- friendly construction
- building material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environment-friendly building material which comprises, by weight parts, 12-20 parts of ardealite, 4-8 parts of plaster of paris, 5-15 parts of modified wollastonite, 5-15 parts of polyester fiber, 10-15 parts of magnesium hypophosphite, 10-15 parts of carbamate, 1-5 parts of polyvinyl chloride, 1-5 parts of polyvinyl alcohol, 6-8 parts of talcum powder, 5-10 parts of limestone, 1-5 parts of foaming agent, 5-10 parts of addition agent and 20-40 parts of water. The environment-friendly building material is used as a building material, is extremely good in environmental protection performance, compact in texture and good in heat insulation and sound insulation effect and conforms to the national standard. Compared with an existing building material, the environment-friendly building material is lighter and higher in intensity, can meet the external wall and internal wall building requirements simultaneously and has wide market prospects.
Description
Technical field
The present invention relates to Material Field, particularly relate to a kind of environmental-friendly construction material.
Background technology
Along with saving energy sense is rooted in the hearts of the people, higher requirement is also proposed to building energy conservation.Thus building energy conservation environment-friendly materials are also more and more is developed and applies, but at present environmental-friendly construction material not only type is few, environment-friendly function is weak, and cost is high, cannot compare with the conventional material such as concrete.
Therefore, prior art also needs to further develop and improve.
Summary of the invention
The object of the present invention is to provide a kind of environmental-friendly construction material, be intended to solve current effect of heat insulation for building material poor, not environmentally, the problem that cost is high.
Technical scheme of the present invention is as follows:
A kind of environmental-friendly construction material, wherein: described environmental-friendly construction material is composed of the following components according to parts by weight:
Phosphogypsum 12 ~ 20 parts;
Gesso 4 ~ 8 parts;
Modified grammite 5 ~ 15 parts;
5 ~ 15 parts, trevira;
Magnesium hypophosphite 10 ~ 15 parts;
Carbamate 10 ~ 15 parts
Polyvinyl chloride 1 ~ 5 part;
Polyvinyl alcohol 1 ~ 5 part;
Talcum powder 6 ~ 8 parts;
5 ~ 10 parts, Wingdale;
Whipping agent 1 ~ 5 part;
Auxiliary agent 5 ~ 10 parts;
20 ~ 40 parts, water.
Described environmental-friendly construction material, wherein: described auxiliary agent is made up of sodium lignosulfonate, titanium dioxide, ferrous sulfate and lubricant.
Described environmental-friendly construction material, wherein: the weight ratio of using forming each component sodium lignosulfonate of auxiliary agent, titanium dioxide, ferrous sulfate and lubricant is 1:1:1:2.
Described environmental-friendly construction material, wherein: described whipping agent is for being that 1:1 configures and forms by gelatin and rosin according to weight ratio.
Described environmental-friendly construction material, wherein: described environmental-friendly construction material is composed of the following components according to parts by weight:
Phosphogypsum 16 parts;
Gesso 6 parts;
Modified grammite 10 parts;
10 parts, trevira;
Magnesium hypophosphite 10 parts;
Carbamate 15 parts
Polyvinyl chloride 5 parts;
Polyvinyl alcohol 1 part;
Talcum powder 7 parts;
5 parts, Wingdale;
Whipping agent 5 parts;
Auxiliary agent 10 parts;
30 parts, water.
Beneficial effect: the invention provides a kind of environmental-friendly construction material, this material uses as material of construction, there is splendid environmental-protecting performance, its quality is fine and close, and heat-insulating sound-insulating is effective, meets national standard, relative to existing material of construction, its lighter intensity is higher, can be full of the building needs of exterior wall and interior wall simultaneously, have wide market outlook.
Embodiment
For making object of the present invention, technical scheme and advantage clearly, clearly, the present invention is described in more detail below.
The invention provides a kind of environmental-friendly construction material, wherein: described environmental-friendly construction material is composed of the following components according to parts by weight:
Phosphogypsum 12 ~ 20 parts;
Gesso 4 ~ 8 parts;
Modified grammite 5 ~ 15 parts;
5 ~ 15 parts, trevira;
Magnesium hypophosphite 10 ~ 15 parts;
Carbamate 10 ~ 15 parts
Polyvinyl chloride 1 ~ 5 part;
Polyvinyl alcohol 1 ~ 5 part;
Talcum powder 6 ~ 8 parts;
5 ~ 10 parts, Wingdale;
Whipping agent 1 ~ 5 part;
Auxiliary agent 5 ~ 10 parts;
20 ~ 40 parts, water.
Wherein, described auxiliary agent is made up of sodium lignosulfonate, titanium dioxide, ferrous sulfate and lubricant.Further, in preferred embodiment, the weight ratio of using forming each component sodium lignosulfonate of auxiliary agent, titanium dioxide, ferrous sulfate and lubricant is 1:1:1:2.The auxiliary agent of this proportioning can make final driving be that the environmental-friendly construction material formed has the finest and close structure, and intensity is the highest.
Preferably, described whipping agent is for being that 1:1 configures and forms by gelatin and rosin according to weight ratio.
Below by embodiment, explanation is further explained to the present invention program.
Embodiment 1
Described environmental-friendly construction material, wherein: described environmental-friendly construction material is composed of the following components according to parts by weight:
Phosphogypsum 16 parts;
Gesso 6 parts;
Modified grammite 10 parts;
10 parts, trevira;
Magnesium hypophosphite 10 parts;
Carbamate 15 parts
Polyvinyl chloride 5 parts;
Polyvinyl alcohol 1 part;
Talcum powder 7 parts;
5 parts, Wingdale;
Whipping agent 5 parts;
Auxiliary agent 10 parts;
30 parts, water.
Described auxiliary agent is that 1:1:1:2 forms by sodium lignosulfonate, titanium dioxide, ferrous sulfate and lubricant according to using weight ratio.
Environmental-friendly construction material manufacture method of the present invention in turn includes the following steps:
(1), above-mentioned each component is taken by above-mentioned weight part;
(2) by modified grammite, Wingdale, talcum powder grinding is made Powdered, then adds phosphogypsum, gesso and trevira, after fully mixing, makes powdery dry batch mixing;
(3) magnesium hypophosphite, polyvinyl chloride, polyvinyl alcohol and carbamate are mixed with appropriate water, make mixed solution;
(4) whipping agent, auxiliary agent and obtained mixed solution and dry blend are fully mixed, be configured to slurry, solidification mortar obtains environmental-friendly construction material.
Measure the performance of the environmental-friendly construction material that embodiment 1 obtains, measurement result is as follows: thermal conductivity≤0.12W/mK, GB/T10294-2008.Said determination result shows that environmental-friendly construction material of the present invention has excellent heat insulation performance, and it has good weathering resistance simultaneously, meets the needs of Discussion on architecture body of wall.
Embodiment 2
Described environmental-friendly construction material, wherein: described environmental-friendly construction material is composed of the following components according to parts by weight:
Phosphogypsum 20 parts;
Gesso 8 parts;
Modified grammite 5 parts;
5 parts, trevira;
Magnesium hypophosphite 15 parts;
Carbamate 15 parts
Polyvinyl chloride 1 part;
Polyvinyl alcohol 5 parts;
Talcum powder 8 parts;
5 parts, Wingdale;
Whipping agent 1 part;
Auxiliary agent 5 parts;
40 parts, water.
Described auxiliary agent is that 1:1:1:2 forms by sodium lignosulfonate, titanium dioxide, ferrous sulfate and lubricant according to using weight ratio.
Environmental-friendly construction material manufacture method of the present invention in turn includes the following steps:
(1), above-mentioned each component is taken by above-mentioned weight part;
(2) by modified grammite, Wingdale, talcum powder grinding is made Powdered, then adds phosphogypsum, gesso and trevira, after fully mixing, makes powdery dry batch mixing;
(3) magnesium hypophosphite, polyvinyl chloride, polyvinyl alcohol and carbamate are mixed with appropriate water, make mixed solution;
(4) whipping agent, auxiliary agent and obtained mixed solution and dry blend are fully mixed, be configured to slurry, solidification mortar obtains environmental protection lagging material.
Measure the performance of the environmental-friendly construction material that embodiment 2 obtains, measurement result is as follows: thermal conductivity≤0.14W/mK, GB/T10294-2008.Said determination result shows that environmental-friendly construction material of the present invention has excellent heat insulation performance, and it has good weathering resistance simultaneously, meets the needs of Discussion on architecture body of wall.
The invention provides a kind of environmental-friendly construction material, this material uses as material of construction, there is splendid environmental-protecting performance, its quality is fine and close, and heat-insulating sound-insulating is effective, meets national standard, relative to existing material of construction, its lighter intensity is higher, can be full of the building needs of exterior wall and interior wall simultaneously, have wide market outlook.
Should be understood that, application of the present invention is not limited to above-mentioned citing, for those of ordinary skills, can be improved according to the above description or convert, and all these improve and convert the protection domain that all should belong to claims of the present invention.
Claims (5)
1. an environmental-friendly construction material, is characterized in that: described environmental-friendly construction material is composed of the following components according to parts by weight:
Phosphogypsum 12 ~ 20 parts;
Gesso 4 ~ 8 parts;
Modified grammite 5 ~ 15 parts;
5 ~ 15 parts, trevira;
Magnesium hypophosphite 10 ~ 15 parts;
Carbamate 10 ~ 15 parts
Polyvinyl chloride 1 ~ 5 part;
Polyvinyl alcohol 1 ~ 5 part;
Talcum powder 6 ~ 8 parts;
5 ~ 10 parts, Wingdale;
Whipping agent 1 ~ 5 part;
Auxiliary agent 5 ~ 10 parts;
20 ~ 40 parts, water.
2. environmental-friendly construction material as claimed in claim 1, is characterized in that: described auxiliary agent is made up of sodium lignosulfonate, titanium dioxide, ferrous sulfate and lubricant.
3. environmental-friendly construction material as claimed in claim 2, is characterized in that: the weight ratio of using forming each component sodium lignosulfonate of auxiliary agent, titanium dioxide, ferrous sulfate and lubricant is 1:1:1:2.
4. environmental-friendly construction material as claimed in claim 1, is characterized in that: described whipping agent is for being that 1:1 configures and forms by gelatin and rosin according to weight ratio.
5. environmental-friendly construction material as claimed in claim 1, is characterized in that: described environmental-friendly construction material is composed of the following components according to parts by weight:
Phosphogypsum 16 parts;
Gesso 6 parts;
Modified grammite 10 parts;
10 parts, trevira;
Magnesium hypophosphite 10 parts;
Carbamate 15 parts
Polyvinyl chloride 5 parts;
Polyvinyl alcohol 1 part;
Talcum powder 7 parts;
5 parts, Wingdale;
Whipping agent 5 parts;
Auxiliary agent 10 parts;
30 parts, water.