CN105400308A - Fireproof coating and preparing method thereof - Google Patents

Fireproof coating and preparing method thereof Download PDF

Info

Publication number
CN105400308A
CN105400308A CN201510909624.XA CN201510909624A CN105400308A CN 105400308 A CN105400308 A CN 105400308A CN 201510909624 A CN201510909624 A CN 201510909624A CN 105400308 A CN105400308 A CN 105400308A
Authority
CN
China
Prior art keywords
parts
water
agent
stirring
retardant coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510909624.XA
Other languages
Chinese (zh)
Inventor
康明哲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510909624.XA priority Critical patent/CN105400308A/en
Publication of CN105400308A publication Critical patent/CN105400308A/en
Pending legal-status Critical Current

Abstract

Fireproof coating and a preparing method thereof are provided. The coating comprises following raw materials by weight: 42 parts of styrene-acrylic emulsion, 11 parts of melamine, 5 parts of zinc oxide, 4.5 parts of a film coalescing aid, 8 parts of water, 13 parts of combined water-borne resin, 31 parts of a water-borne expanding auxiliary agent, 7 parts of dipentaerythritol, 21 parts of ammonium polyphosphate, 5 parts of an expanding adjusting agent, 5 parts of titanium dioxide, 0.6 part of a dispersing agent, 0.3 part of a defoaming agent, 0.7 part of a thickening agent and 3 parts of a leveling agent. The coating can be used for fireproof coating of building structures, is advantaged by convenient transportation and construction, no toxicity, no odor, no pollution, flame retardance, and the like, and is characterized by beautiful coatings, corrosion resistance, good ageing resistance, weather resistance, good water proofness, and the like.

Description

A kind of frie retardant coating and preparation method
Technical field
The present invention relates to paint field, be specifically related to a kind of frie retardant coating, can be used for fabric structure fp frie retardant coating, there is transport, easy construction, nontoxic, free from extraneous odour, the advantage such as pollution-free, fire-retardant, and there is attractive coat, the feature such as corrosion-resistant, resistance to deterioration good, weather-proof, water resisting property is good.
Background technology
Frie retardant coating is for flammable substrates surface, can reduce by the rapid spread of the combustibility of painting material surface, retardance fire, in order to improve by a kind of speciality coating being coated with material fire endurance.Be applied to flammable substrates surface, in order to change material surface combustioncharacteristics, retardance fire rapid spread; Or be applied on building slab, in order to improve the speciality coating of the fire endurance of component, claim frie retardant coating.Frie retardant coating is exactly by by the surface of paint brush at those inflammable materials, can improve the refractory ability of material, slow down propagation of flame velocity of propagation, or can stop burning within a certain period of time, and this class coating is called frie retardant coating, or is called anti-flaming dope.The fire prevention principle of frie retardant coating roughly can be summarized as following 5 points: (1), frie retardant coating itself have flame retardancy or uninflammability, and protected base material is not directly contacted with air, postpones the speed that object catches fire and reduces burning.(2), frie retardant coating except itself there is flame retardancy or uninflammability, it also has lower thermal conductivity, can postpone the transmission of flame temperature to protected base material.(3), frie retardant coating decomposes goes out and do not fire rare gas element, waters down the inflammable gas that protected object decomposes goes out, and makes it nonflammable or combustionvelocity slows down.(4), nitrogenous frie retardant coating decomposes goes out the groups such as NO, NH3, with organic radical chemical combination, interrupts chain reaction, reduces temperature.(5), the foaming of expanding fire-proof paint expanded by heating, form carbonaceous foam thermofin and close protected object, postpone the transmission of heat and base material, stop object ignition or Yin Wendu rising and the strength degradation that causes.
Summary of the invention
The object of the present invention is to provide a kind of frie retardant coating, can be used for fabric structure fp frie retardant coating, there is transport, easy construction, nontoxic, free from extraneous odour, the advantage such as pollution-free, fire-retardant, and there is attractive coat, the feature such as corrosion-resistant, resistance to deterioration good, weather-proof, water resisting property is good.
Present invention employs such technical scheme: the material in described frie retardant coating and weight proportion respectively: benzene emulsion 42 parts, trimeric cyanamide 11 parts, 5 parts, zinc oxide, film coalescence aid 4.5 parts, 8 parts, water, split water-base resin 13 parts, water-based bulking promoter 31 parts, dipentaerythritol 7 parts, ammonium polyphosphate 21 parts, expansion conditioning agent 5 parts, titanium dioxide 5 parts, dispersion agent 0.6 part, defoamer 0.3 part, thickening material 0.7 part, flow agent 3 parts.
The present invention is specifically related to a kind of frie retardant coating, can be used for fabric structure fp frie retardant coating.
This product has transport, easy construction, nontoxic, free from extraneous odour, the advantage such as pollution-free, fire-retardant, and there is attractive coat, the feature such as corrosion-resistant, resistance to deterioration good, weather-proof, water resisting property is good.
Embodiment
Present invention employs such technical scheme: in described frie retardant coating, material and weight proportion are respectively: benzene emulsion 42 parts, trimeric cyanamide 11 parts, 5 parts, zinc oxide, film coalescence aid 4.5 parts, 8 parts, water, split water-base resin 13 parts, water-based bulking promoter 31 parts, dipentaerythritol 7 parts, ammonium polyphosphate 21 parts, expansion conditioning agent 5 parts, titanium dioxide 5 parts, dispersion agent 0.6 part, defoamer 0.3 part, thickening material 0.7 part, flow agent 3 parts.
Its preparation method is following steps:
Step one), in pill tank, add water, film coalescence aid, water-based bulking promoter, stir rear for subsequent use;
Step 2), in step one) institute obtains in material stirring and adds benzene emulsion, trimeric cyanamide, zinc oxide, dipentaerythritol, ammonium polyphosphate, expansion conditioning agent, titanium dioxide, dispersion agent, flow agent successively, for subsequent use after stirring into sticky pasty state;
Step 3) by step 2) material that obtains is for subsequent use after putting into grinding machine for grinding to 130 μm;
Step 4) by step 3) material that obtains adds in pill tank, adds split water-base resin, defoamer, thickening material successively in stirring, after stirring, finished product.

Claims (2)

1. a frie retardant coating, it is characterized in that, material and weight proportion respectively: benzene emulsion 42 parts, trimeric cyanamide 11 parts, 5 parts, zinc oxide, film coalescence aid 4.5 parts, 8 parts, water, split water-base resin 13 parts, water-based bulking promoter 31 parts, dipentaerythritol 7 parts, ammonium polyphosphate 21 parts, expansion conditioning agent 5 parts, titanium dioxide 5 parts, dispersion agent 0.6 part, defoamer 0.3 part, thickening material 0.7 part, flow agent 3 parts.
2. according to frie retardant coating according to claim 1, it is characterized in that, its preparation method, preparation method is following steps: step one), in pill tank, add water, film coalescence aid, water-based bulking promoter, stir rear for subsequent use;
Step 2), in step one) institute obtains in material stirring and adds benzene emulsion, trimeric cyanamide, zinc oxide, dipentaerythritol, ammonium polyphosphate, expansion conditioning agent, titanium dioxide, dispersion agent, flow agent successively, for subsequent use after stirring into sticky pasty state;
Step 3) by step 2) material that obtains is for subsequent use after putting into grinding machine for grinding to 130 μm;
Step 4) by step 3) material that obtains adds in pill tank, adds split water-base resin, defoamer, thickening material successively in stirring, after stirring, finished product.
CN201510909624.XA 2015-12-06 2015-12-06 Fireproof coating and preparing method thereof Pending CN105400308A (en)