CN105400247A - Environment-friendly anticorrosive paint - Google Patents
Environment-friendly anticorrosive paint Download PDFInfo
- Publication number
- CN105400247A CN105400247A CN201510894018.5A CN201510894018A CN105400247A CN 105400247 A CN105400247 A CN 105400247A CN 201510894018 A CN201510894018 A CN 201510894018A CN 105400247 A CN105400247 A CN 105400247A
- Authority
- CN
- China
- Prior art keywords
- environment
- corrosive
- filler
- friendlyanti
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to environment-friendly anticorrosive paint. The environment-friendly anticorrosive paint is prepared from, by weight, potassium metasilicate, acrylate resin, polyvinyl alcohol, silicon dioxide, kaolin, feldspar, cerium oxide, potassium hydroxide, distilled water, stabilizer, a dispersing agent, a deformaing agent and a thickening agent. The formula is reasonable. Inorganic filler appropriate in melting point is selected and can be subjected to a complex physicochemical reaction in the high-temperature melting process. The filler can make eutectic mixtures and melt which have been generated dissolved in one another when the filler is molten. Part of raw materials are volatilized, the filler starts to be sintered and molten and form a smooth glaze on a green body. In the process, the green body is porcelainized, the inorganic filler is vitrified at the same time, the surface performance of a base body is improved, the mechanical property of the base body is enhanced, and therefore a protection effect is achieved for metal.
Description
Technical field
The invention belongs to paint field, especially a kind of Environment-friendlyanti-corrosive anti-corrosive paint.
Background technology
Protective system, is generally divided into conventional protective system and heavy-duty coating, is requisite a kind of coating in paint.Conventional protective system is under general condition, plays etch-proof effect to metal etc.
Summary of the invention
The object of the invention is to overcome the deficiencies in the prior art, provide a kind of Environment-friendlyanti-corrosive anti-corrosive paint, this stopper-adding machine structure is simple, and design science is reasonable, efficiency is high, equipment is little, power consumption is little, can meet high-speed canning requirement.
The present invention solves its technical problem and is achieved through the following technical solutions:
A kind of Environment-friendlyanti-corrosive anti-corrosive paint, component and the ratio of weight and number thereof of its Environment-friendlyanti-corrosive anti-corrosive paint are respectively: potassium silicate 20-50 part, acrylic resin 0.5-2 part, polyvinyl alcohol 0.1-0.6 part, silicon-dioxide 2-8 part, kaolin 5-11 part, feldspar 2-9 part, cerium oxide 17-34 part, potassium hydroxide 1-2 part, distilled water 35-70 part, stablizer 0.2-0.5 part, dispersion agent 0.4-0.7 part, defoamer 0.2-0.5 part, thickening material 0.4-0.8 part.
And component and the optimum ratio of weight and number thereof of described Environment-friendlyanti-corrosive anti-corrosive paint are respectively: potassium silicate 30 parts, acrylic resin 1 part, polyvinyl alcohol 0.3 part, silicon-dioxide 4 parts, kaolin 8 parts, feldspar 4 parts, cerium oxide 18 parts, 1.5 parts, potassium hydroxide, distilled water 45 parts, stablizer 0.3 part, dispersion agent 0.5 part, defoamer 0.3 part, thickening material 0.6 part.
And described stablizer is silicate coating stablizer.
Advantage of the present invention and beneficial effect are:
This Environment-friendlyanti-corrosive anti-corrosive paint, component and the ratio of weight and number thereof of its Environment-friendlyanti-corrosive anti-corrosive paint are respectively: potassium silicate 20-50 part, acrylic resin 0.5-2 part, polyvinyl alcohol 0.1-0.6 part, silicon-dioxide 2-8 part, kaolin 5-11 part, feldspar 2-9 part, cerium oxide 17-34 part, potassium hydroxide 1-2 part, distilled water 35-70 part, stablizer 0.2-0.5 part, dispersion agent 0.4-0.7 part, defoamer 0.2-0.5 part, thickening material 0.4-0.8 part, this formula is reasonable, have selected the mineral filler that fusing point is suitable, complicated physical reaction can be there is in it in high-temperature fusion process, and filler can make when melting the eutectic that generated, melts dissolves mutually, part material volatilization color stuffing starts sintering, fusing also forms smooth glaze paint on base substrate.In this course, base substrate is by porcelain, and mineral filler, simultaneously by vitrifying, improves the surface property of matrix, strengthens the mechanical property of matrix, thus plays a protective role to metal.
Embodiment
Below by specific embodiment, the invention will be further described, and following examples are descriptive, is not determinate, can not limit protection scope of the present invention with this.
Embodiment 1
A kind of Environment-friendlyanti-corrosive anti-corrosive paint, component and the weight thereof of its Environment-friendlyanti-corrosive anti-corrosive paint are respectively: potassium silicate 20Kg, acrylic resin 0.5Kg, polyvinyl alcohol 0.1Kg, silicon-dioxide 2Kg, kaolin 5Kg, feldspar 2Kg, cerium oxide 17Kg, potassium hydroxide 1Kg, distilled water 35Kg, stablizer 0.2Kg, dispersion agent 0.4Kg, defoamer 0.2Kg, thickening material 0.4Kg.
Embodiment 2
A kind of Environment-friendlyanti-corrosive anti-corrosive paint, component and the weight thereof of its Environment-friendlyanti-corrosive anti-corrosive paint are respectively: potassium silicate 50Kg, acrylic resin 2Kg, polyvinyl alcohol 0.6Kg, silicon-dioxide 8Kg, kaolin 11Kg, feldspar 9Kg, cerium oxide 34Kg, potassium hydroxide 2Kg, distilled water 70Kg, stablizer 0.5Kg, dispersion agent 0.7Kg, defoamer 0.5Kg, thickening material 0.8Kg.
Embodiment 3
A kind of Environment-friendlyanti-corrosive anti-corrosive paint, component and the weight thereof of its Environment-friendlyanti-corrosive anti-corrosive paint are respectively: potassium silicate 30Kg, acrylic resin 1Kg, polyvinyl alcohol 0.3Kg, silicon-dioxide 4Kg, kaolin 8Kg, feldspar 4Kg, cerium oxide 18Kg, potassium hydroxide 1.5Kg, distilled water 45Kg, stablizer 0.3Kg, dispersion agent 0.5Kg, defoamer 0.3Kg, thickening material 0.6Kg.
Claims (3)
1. an Environment-friendlyanti-corrosive anti-corrosive paint, is characterized in that: component and the ratio of weight and number thereof of this Environment-friendlyanti-corrosive anti-corrosive paint are respectively: potassium silicate 20-50 part, acrylic resin 0.5-2 part, polyvinyl alcohol 0.1-0.6 part, silicon-dioxide 2-8 part, kaolin 5-11 part, feldspar 2-9 part, cerium oxide 17-34 part, potassium hydroxide 1-2 part, distilled water 35-70 part, stablizer 0.2-0.5 part, dispersion agent 0.4-0.7 part, defoamer 0.2-0.5 part, thickening material 0.4-0.8 part.
2. Environment-friendlyanti-corrosive anti-corrosive paint according to claim 1, is characterized in that: component and the optimum ratio of weight and number thereof of described Environment-friendlyanti-corrosive anti-corrosive paint are respectively: potassium silicate 30 parts, acrylic resin 1 part, polyvinyl alcohol 0.3 part, silicon-dioxide 4 parts, kaolin 8 parts, feldspar 4 parts, cerium oxide 18 parts, 1.5 parts, potassium hydroxide, distilled water 45 parts, stablizer 0.3 part, dispersion agent 0.5 part, defoamer 0.3 part, thickening material 0.6 part.
3. Environment-friendlyanti-corrosive anti-corrosive paint according to claim 1, is characterized in that: described stablizer is silicate coating stablizer.