CN105397299B - A kind of processing method and processing device of tantalum electric capacity tantalum wire surface film oxide - Google Patents
A kind of processing method and processing device of tantalum electric capacity tantalum wire surface film oxide Download PDFInfo
- Publication number
- CN105397299B CN105397299B CN201510947082.5A CN201510947082A CN105397299B CN 105397299 B CN105397299 B CN 105397299B CN 201510947082 A CN201510947082 A CN 201510947082A CN 105397299 B CN105397299 B CN 105397299B
- Authority
- CN
- China
- Prior art keywords
- tantalum
- laser
- tantalum wire
- electric capacity
- demoulding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of processing method and processing device of tantalum electric capacity tantalum wire surface film oxide, periphery for the two or more tantalum wire to being welded on tantalum electric capacity carries out surface oxidation film process, the tantalum electric capacity is welded on steel bar, the treating method comprises following steps:S1:The steel bar is fixed on stepping platform;S2:Tantalum wire periphery is divided into first area, second area, the 3rd region and the 4th region;S3:The method scanned using laser fixed fire successively carries out demoulding to the first area, second area;S4:The steel bar is overturn and is fixed on the stepping platform together with tantalum wire thereon;S5:The method scanned using laser fixed fire successively carries out demoulding to the 3rd region, the 4th region.The invention enables the frock clamp highly versatile of tantalum wire demoulding, demoulding effect are good, the product quality of following process is improved.
Description
Technical field
The present invention relates to technical field of electronic components, more particularly to a kind of processing of tantalum electric capacity tantalum wire surface film oxide
Method and device.
Background technology
Tantalum wire is the anode tap of tantalum electric capacity, on smooth piece, it is necessary to tantalum electricity in the fabrication processing of tantalum electric capacity
Smooth piece held carries out infiltration manganese nitrate solution (or other materials, such as high polymer material), in order to prevent manganese nitrate solution (or high score
Sub- solution) swashed along tantalum wire, it can be thrown in advance into Teflon pad when being welded to technique steel bar, it is to avoid during thermal decomposition on tantalum wire
Forming oxide-film (manganese dioxide or polymeric oxide) causes anode and cathode short circuit.
But in actual production, although throwing into Teflon pad, also can not preferably it avoid on tantalum wire without generation oxide-film
Phenomenon, the tantalum electric capacity of especially big shell number, because the size of itself just it is big, oxide-film produce possibility it is bigger.
Cut off for this in tantalum block from steel bar and be welded to moulding again and go forward, one of removal tantalum wire oxide-film can be increased in technique
Treatment measures, traditional way scrapes film process to be mechanical, i.e., the oxide-film on tantalum electric capacity tantalum wire periphery scraped
Film process.Various sizes of tantalum electric capacity, the frock clamp of knifing will also do corresponding matching, it is difficult to general, and demoulding effect
It is not good enough, it is impossible to realize that demoulding is clean, it is impossible to effectively to prevent anode and cathode short circuit and tantalum wire to be welded to problem of faulty soldering when on moulding.
The disclosure of background above technology contents is only used for inventive concept and the technical scheme that auxiliary understands the present invention, and it is not
The prior art of present patent application is necessarily belonged to, the applying date of the above in present patent application is being shown without tangible proof
In the case of disclosed, above-mentioned background technology should not be taken to evaluate the novelty and creativeness of the application.
The content of the invention
It is above-mentioned to solve present invention aims at a kind of processing method and processing device of tantalum electric capacity tantalum wire surface film oxide is proposed
It is bad and have a strong impact on product that what prior art was present is difficult to general, demoulding effect to various sizes of tantalum electric capacity frock clamp
The technical problem of quality.
Therefore, the present invention proposes a kind of processing method of tantalum electric capacity tantalum wire surface film oxide, for being welded on tantalum electric capacity
On the periphery of two or more tantalum wire carry out surface oxidation film process, the tantalum electric capacity is welded on steel bar, including following step
Suddenly:
S1:The steel bar is fixed on stepping platform;
S2:Tantalum wire periphery is divided into first area, second area, the 3rd region and the 4th region;
S3:The method scanned using laser fixed fire successively carries out demoulding to the first area, second area;
S4:The steel bar is overturn and is fixed on the stepping platform together with tantalum wire thereon;
S5:The method scanned using laser fixed fire successively carries out demoulding to the 3rd region, the 4th region.
According to embodiment, processing method proposed by the present invention can also have following technical characteristic:
In the step S3, journey is gone to carry out contraposition demoulding to the first area in the stepping platform, backhaul is to institute
State second area and carry out contraposition demoulding;In the step S5, journey is gone to the 3rd region progress pair in the stepping platform
Position demoulding, backhaul carries out contraposition demoulding to the 4th region.
The method of the laser fixed fire scanning is to carry out demoulding, institute to the tantalum wire for stepping to fixed fire position by laser head
State the projected position that fixed fire position is the laser head.
The laser head is more than the radius of the tantalum wire in the distance of the radial scan of the tantalum wire.
The laser head treats the length of demoulding in the length of the axial scan of the tantalum wire for the tantalum wire.
The laser is that the solid-state laser of micro Process ablation can be done to oxide on surface.
The invention also provides a kind of tantalum electric capacity tantalum wire surface oxidation membrane treatment appts, including stepping platform, and with step
Enter the laser fixed fire scanning element that platform matches, the laser head of the laser fixed fire scanning element can adjust the side of fixed fire scanning
To and angle.
According to embodiment, processing unit proposed by the present invention can also have following technical characteristic:
The stepping platform is provided with the magnetic fixture for being used for fixing the steel bar.
The stepping platform for straight line stepping module.
The angle of the laser head can arbitrarily be adjusted between 0-180 °.
The beneficial effect that the present invention is compared with the prior art includes:The present invention uses machinery to be to scrape compared in the prior art
Film process is compared, and the oxide-film on tantalum wire circumferential surface is etched with laser, substantially increases grasping for demoulding
The property made, it is adaptable to which demouldings are carried out to various various sizes of tantalum electric capacity, it is to avoid due to the frock folder existed using mechanical demoulding
Has uncurrent problem;Further, in order to reach good membrane removal effect, the present invention uses subregion method for demoulding, reachable
It is clean and thorough to 360 ° of comprehensive demoulding effects.
In preferred scheme, during demoulding is carried out using laser subregion, using on stepping platform courses steel bar
All tantalum wires are stepped through the fixed fire position of laser demoulding one by one, effectively complete the membrane removal to all tantalum wires, go journey complete
Into the membrane removal in first area and the 3rd region, backhaul can complete the membrane removal in second area and the 3rd region, adopt rotatable sharp
Shaven head so that the scanning pattern of laser is adjustable, and demoulding effect is more preferable.
Brief description of the drawings
Fig. 1 is the process flow figure of the specific embodiment of the invention one;
Fig. 2 is the structural representation of the processing unit of the specific embodiment of the invention one.
Fig. 3 is the structural representation of the stepping platform of the specific embodiment of the invention one.
Fig. 4 is the Fig. 2 of the specific embodiment of the invention one close-up schematic view.
Fig. 5 is the tantalum wire subregion schematic diagram of the specific embodiment of the invention one.
Fig. 6 is the working state figure of the specific embodiment of the invention one.
1 stepping platform
2 laser fixed fire scanning elements
3 steel bars
4 tantalum wires
5 smooth pieces
6th, 7 fixed fire position
41 first areas
42 second areas
43 the 3rd regions
44 the 4th regions
Embodiment
With reference to embodiment and compare accompanying drawing the present invention is described in further detail.It is emphasized that
What the description below was merely exemplary, the scope being not intended to be limiting of the invention and its application.
With reference to figure 1 below -6, the embodiment of non-limiting and nonexcludability, wherein identical reference table will be described
Show identical part, unless stated otherwise.
Embodiment one:
As shown in figures 1 to 6, present embodiment discloses a kind of processing method of tantalum electric capacity tantalum wire surface film oxide, for butt welding
The periphery for the multiple tantalum wires 4 being connected on tantalum electric capacity carries out surface oxidation film process, and the tantalum electric capacity is welded on steel bar 3, tantalum
Electric capacity can be divided into smooth piece 5 and the tantalum wire 4 on smooth piece 5, and tantalum wire 4 is the anode tap of tantalum electric capacity, and one end of tantalum wire 4 is welded on
On steel bar 3, the other end is connected with exposed smooth piece 5, and the processing method of the surface film oxide of tantalum wire 4 of the present embodiment is just using sharp
Light carries out demoulding processing to the tantalum wire 4 between steel bar 3 and smooth piece 5, comprises the following steps:
S1:The steel bar 3 is fixed on stepping platform 1;
S2:The periphery of tantalum wire 4 is divided into first area 41, second area 42, the 3rd region 43 and the 4th region 44;
S3:The method scanned using laser fixed fire successively carries out demoulding to the first area 41, second area 42;
S4:The steel bar 3 is overturn and is fixed on the stepping platform 1 together with tantalum wire 4 thereon;
S5:The method scanned using laser fixed fire successively carries out demoulding to the 3rd region 43, the 4th region 44.
More specifically:
In step sl, steel bar 3 is placed on stepping platform 1, all tantalum wires 4 on the good steel bar 3 of precheck
Whether level is neat, that is, allows the circumferential section of all tantalum wires 4 to be highly in unanimously, if it not, first by whole levels pair of tantalum wire 4
Together, it is to avoid indivedual warpages of tantalum wire 4, cause demoulding effect bad.
Meanwhile, the method for the laser fixed fire scanning is that the tantalum wire 4 for stepping to fixed fire position 6,7 is entered by laser head
Row demoulding, the fixed fire position 6,7 is the projected position of the laser head.Fixed fire position 6,7 can be determined in advance, general, point
The position penetrated is positioned as close to smooth piece of 5 end faces, but laser facula can not be allowed to be irradiated to smooth piece 5, it is to avoid made during laser-induced thermal etching
Smooth piece 5 of etching in pairs.
In step s 2, it is that subregion demoulding is carried out to the circumferential surface of tantalum wire 4 during laser-induced thermal etching demoulding,
As shown in figure 5, the periphery of tantalum wire 4 is divided into four equal cambered surface regions of correspondence angle altogether, be respectively first area 41,
Second area 42, the 3rd region 43 and the 4th region 44, wherein, it is 90 ° that the region angle of each periphery, which is preferably,.
In the step S3, journey is gone to carry out contraposition demoulding, backhaul pair to the first area 41 in the stepping platform 1
The second area 42 carries out contraposition demoulding;Laser is set to carry out fixed point fixed fire in fixed fire position 6,7 using the control of laser software
Scanning, laser head is more than the radius of (or at least equal to) described tantalum wire 4, laser head in the distance of the radial scan of the tantalum wire 4
The length of demoulding is treated for the tantalum wire 4 in the length of the axial scan of the tantalum wire 4;Before laser fixed fire scanning is carried out, in advance
The focal length of laser-induced thermal etching is adjusted, it is ensured that the energy of laser can meet the effect for etching away the oxide-film of tantalum wire 4 just, then by steel
Bar 3 is fixed on can be on the workbench of stepping, the movement of stepping from left to right of the driving steel bar 3 of stepping platform 1, and tantalum wire 4 is one by one through too drastic
The fixed fire position 6 of light, laser triggering etching completes to scan etching to the first area 41 of the periphery of tantalum wire 4;Wait stepping platform
1 driving steel bar 3 is moved to limit on the right-right-hand limit, after being etched to all tantalum wires 4, then runs from right to left automatically again, is working as
Tantalum wire 4 one by one step motion to laser fixed fire position 7 when, laser now again fixed fire position 7 triggering etching, complete to tantalum wire 4
The laser fixed fire scanning etching of the second area 42 of periphery.
In step s 4, after completing to first area 41 and the demoulding of second area 42, steel bar 3 is overturn into fixation, is
Step S5 prepares.
In step s 5, journey is gone to carry out contraposition demoulding to the 3rd region 43 in the stepping platform 1, backhaul is to institute
State the 4th region 44 and carry out contraposition demoulding.Stepping platform 1 continues to drive the stepping from left to right of steel bar 3 movement, and tantalum wire 4 passes through one by one
The fixed fire position 6 of laser, laser triggering etching completes to scan etching to the 3rd region 43 of the periphery of tantalum wire 4;Stepping is waited to put down
The driving steel bar 3 of platform 1 is moved to limit on the right-right-hand limit, after being etched to all tantalum wires 4, then runs from right to left automatically again,
When tantalum wire 4 one by one step motion to laser fixed fire position 7 when, laser now again fixed fire position 7 triggering etching, complete to tantalum wire
The laser fixed fire scanning etching in the 4th region 44 of 4 peripheries.Thus by the subregion demoulding in this four regions, 360 ° can be reached
Comprehensive film takes off effect, it is ensured that whole tantalum wire 4 needs in the length and whole circumferential surfaces of demoulding that thoroughly demoulding is done
Only.
In the present embodiment, the speed that stepping platform 1 is moved is controlled by software, is controlled its movement velocity by software
Good (speed can be set on software).
In the present embodiment, the laser is can do the solid-state laser of micro Process ablation to oxide on surface, more specifically,
The laser of selection is low power ultraviolet solid-state laser, and laser facula is small.
The present embodiment also proposed a kind of surface oxidation membrane treatment appts of tantalum electric capacity tantalum wire 4, as shown in figures 2-6, including step
Enter platform 1, and the laser fixed fire scanning element 2 matched with stepping platform 1, the laser of the laser fixed fire scanning element 2
The direction of adjustable fixed fire scanning and angle.
More specifically:
The stepping platform 1 is provided with the magnetic fixture for being used for fixing the steel bar 3, is welded in tantalum wire 4 on the steel bar 3
Be fixed on by magnetic fixture on stepping platform 1, be easy to steel bar 3 overturning commutation, the stepping platform 1 for straight line stepping
Module (is not illustrated) in figure, and the laser head of laser fixed fire scanning element 2 can adjust fixed fire scanning direction and angle, can conveniently control
The scanning pattern of laser.
When carrying out demoulding to all regions, laser head is more than the tantalum wire 4 in the distance of the radial scan of the tantalum wire 4
Radius, laser head for the tantalum wire 4 treats the length of demoulding in the length of the axial scan of the tantalum wire 4, to first area
41 go to second area 42 carry out demoulding when, now the angle of laser head can carry out angle adjustment between 0-180 °, specifically
When stepping platform 1 has etched first area 41, to be moved in the driving steel bar 3 of stepping platform 1 at limit on the right-right-hand limit, completing laser
The conversion of brilliance degree, to adapt to de-filming process of the laser head to second area 42;The 4th is being gone to the 3rd region 43 accordingly
When region 44 carries out demoulding, also need to complete above-mentioned laser angle conversion.
In the present embodiment, it is desirable in the clean surrounding environment processed, specific embodiment, more than 10,000 grades are may be selected
Dust proof workshop, and surrounding in demoulding in the processing unit installs a draft hood additional, can avoid demoulding chip to ring
The influence in border, with avoid fragmentary chip may Electrostatic Absorption on tantalum wire 4.
The beneficial effect that the present embodiment is compared with the prior art includes:
The present embodiment uses machinery to be to scrape film process to compare compared in the prior art, with laser to the circumference table of tantalum wire 4
Oxide-film on face is etched, and substantially increases the operability of demoulding, further, in order to reach good membrane removal
Effect, the present invention uses subregion method for demoulding, can reach 360 ° of comprehensive demoulding effects, clean and thorough.
In preferred scheme, during demoulding is carried out using laser subregion, controlled using stepping platform 1 on steel bar 3
All tantalum wires 4 be stepped through the fixed fire position of laser demoulding one by one, effectively complete the membrane removal to all tantalum wires 4, go journey
The membrane removal in the region 43 of first area 41 and the 3rd can be completed, backhaul can complete the membrane removal in the region 43 of second area 42 and the 3rd, adopt
There is rotatable laser head so that the scanning pattern of laser is adjustable, demoulding effect is more preferable.
It would be recognized by those skilled in the art that it is possible that numerous accommodations are made to above description, so embodiment is only
For describing one or more particular implementations.
Although having been described above and describing the example embodiment for being counted as the present invention, it will be apparent to those skilled in the art that
It can be variously modified and replaced, without departing from the spirit of the present invention.Furthermore it is possible to make many modifications with by spy
Condition of pledging love is fitted to the religious doctrine of the present invention, without departing from invention described herein central concept.So, the present invention is unrestricted
In specific embodiment disclosed here, but the present invention all embodiments that may also include belonging to the scope of the invention and its equivalent
Thing.
Claims (8)
1. a kind of processing method of tantalum electric capacity tantalum wire surface film oxide, for the two or more tantalum wire to being welded on tantalum electric capacity
Periphery carries out surface oxidation film process, and the tantalum electric capacity is welded on steel bar, it is characterised in that comprised the following steps:
S1:The steel bar is fixed on stepping platform;
S2:Tantalum wire periphery is divided into first area, second area, the 3rd region and the 4th region;
S3:The stepping platform drives the steel bar stepping movement, and the method scanned using laser fixed fire is successively to described first
Region second area carries out demoulding, goes journey to carry out contraposition demoulding to the first area in the stepping platform, backhaul is to institute
State second area and carry out contraposition demoulding;
S4:The steel bar is overturn and is fixed on the stepping platform together with tantalum wire thereon;
S5:The stepping platform drives the steel bar stepping movement, and the method scanned using laser fixed fire is successively to the described 3rd
Region, the 4th region carry out demoulding, go journey to carry out contraposition demoulding to the 3rd region in the stepping platform, backhaul is to institute
State the 4th region and carry out contraposition demoulding.
2. the processing method of tantalum electric capacity tantalum wire surface film oxide as claimed in claim 1, it is characterised in that:The laser fixed fire
The method of scanning is that demoulding is carried out to the tantalum wire for stepping to fixed fire position by laser head, and the fixed fire position is the laser
The projected position of head.
3. the processing method of tantalum electric capacity tantalum wire surface film oxide as claimed in claim 2, it is characterised in that:The laser head exists
The distance of the radial scan of the tantalum wire is more than the radius of the tantalum wire.
4. the processing method of tantalum electric capacity tantalum wire surface film oxide as claimed in claim 2, it is characterised in that:The laser head exists
The length of the axial scan of the tantalum wire is the length that the tantalum wire treats demoulding.
5. the processing method of tantalum electric capacity tantalum wire surface film oxide as claimed in claim 1, it is characterised in that:The laser is energy
The solid-state laser of micro Process ablation is done to oxide on surface.
6. a kind of tantalum electric capacity tantalum wire surface oxidation membrane treatment appts, the circle for the two or more tantalum wire to being welded on tantalum electric capacity
Side face carries out surface oxidation film process, and the tantalum electric capacity is welded on steel bar, it is characterised in that:Including stepping platform, Yi Jiyu
The laser fixed fire scanning element that stepping platform matches, the laser fixed fire scanning element includes laser head and by the laser head
The fixed fire position of projection, the laser head of the laser fixed fire scanning element can adjust direction and the angle of fixed fire scanning, the step
Enter platform can the two-way step motion in left and right, the stepping platform, which is provided with, to be used to fix the magnetic fixture of the steel bar.
7. tantalum electric capacity tantalum wire surface oxidation membrane treatment appts as claimed in claim 6, it is characterised in that:The stepping platform is
Straight line stepping module.
8. tantalum electric capacity tantalum wire surface oxidation membrane treatment appts as claimed in claim 6, it is characterised in that:The angle of the laser head
Degree can arbitrarily be adjusted between 0-180 °.