CN105386200B - Double-side raised bleached resin lining and production method thereof - Google Patents

Double-side raised bleached resin lining and production method thereof Download PDF

Info

Publication number
CN105386200B
CN105386200B CN201510660283.7A CN201510660283A CN105386200B CN 105386200 B CN105386200 B CN 105386200B CN 201510660283 A CN201510660283 A CN 201510660283A CN 105386200 B CN105386200 B CN 105386200B
Authority
CN
China
Prior art keywords
fabric
blueing
sided
adjusts
porcupine roller
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201510660283.7A
Other languages
Chinese (zh)
Other versions
CN105386200A (en
Inventor
曹平
朱红耀
曾燕
黄新华
黄�俊
姜伟
吴亮亮
王婷
张鹏飞
刘丽华
王春梅
杨静新
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NANTONG HAIHUI GARMENT ACCESSORIES Co Ltd
Original Assignee
NANTONG HAIHUI GARMENT ACCESSORIES Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NANTONG HAIHUI GARMENT ACCESSORIES Co Ltd filed Critical NANTONG HAIHUI GARMENT ACCESSORIES Co Ltd
Priority to CN201510660283.7A priority Critical patent/CN105386200B/en
Publication of CN105386200A publication Critical patent/CN105386200A/en
Application granted granted Critical
Publication of CN105386200B publication Critical patent/CN105386200B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a double-side raised bleached resin lining and a production method thereof. The production procedure includes the steps of seam turning, refining, bleaching, double-side galling, blueing whitening anti-shrinkage one-bath dyeing and finishing and mechanical pre-shrinking. The process is convenient to operate, the product is excellent in performance, double sides are each provided with a layer of loose fluff, and the content of free and hydrolyzed formaldehyde is smaller than or equal to 35 mg/kg; the warp and weft washing dimensional stability is -0.6% to +0.5%. After the resin lining and clothes fabric are compounded, the hand feeling of the fabric is quite soft and plump.

Description

Resin interlining and its production method are bleached in two-sided raising
Technical field
The present invention relates to a kind of two-sided raising bleaching resin interlining and its production method.
Background technology
Existing resin interlining surface is smooth, after being combined with garment material, typically all compares consolidation, does not have fluffy soft hand Sense.It is big through broadwise washing shrinkage that usual resins are served as a contrast, and dissociates and hydrolysis formaldehyde amount is big, influence performance and using effect.
The content of the invention
Two-sided there is one layer of pluffy hair it is an object of the invention to provide one kind；Free and hydrolysis formaldehyde≤35mg/kg； Resin interlining and its production method are bleached through the two-sided raising that broadwise washing size changing rate is -0.6%~+0.5%.
Technical solution of the invention is：
A kind of two-sided raising bleaching resin interlining and its production method, it is characterized in that：Resin interlining is two-sided one layer of fluffy suede Hair；Free and hydrolysis formaldehyde≤35mg/kg；It is -0.6%~+0.5% through broadwise washing size changing rate.
The fabric of lining cloth is pure cotton fabric or polyester-cotton fabric；Wherein described pure cotton fabric is in following two kinds of specifications Kind：The first is plain weave, and door width is 48.5 inches, yarn count is 20s×20s, density be 60 × 60 pieces/inch, second It is twill-weave, door width is 48.5 inches, yarn count is 20/2 s×20/2s, density be 52 × 68 pieces/inch；The polyester-cotton blend is knitted Thing is the one kind in following two kinds of plain weave specifications：The door width of the first is 48.5 inches, yarn count is 21 s×21s, density It it is 60 × 58 pieces/inch, second of door width is 48.5 inches, yarn count is 16s×16s, density be 50 × 50 pieces/inch.
A kind of production method of two-sided raising resin interlining, brightens including turning over seam, concise, bleaching, two-sided napping, blueing successively Shrinkproof one-bath finishing, machine shrunk step；Brushing process is two-sided each drawing two~tetra- times, and the rpm of cylinder rotating speed 75 turns along porcupine roller Fast 700rpm, along porcupine roller cylinder pressure 0.20Mpa, inverse porcupine roller 0.25~0.40Mpa of cylinder pressure, inverse porcupine roller rotating speed 800~ 850rpm；Upper fabric guide roll tension force 1.8%, preceding fabric guide roll tension force 2.8%, rear fabric guide roll tension force 1.9% enters 14~16m/ of cloth speed min.After plucking, fabric two sides all covers one layer of uniform fine hair.After resin interlining is compound with garment material so that the feel of fabric is special It is not soft and full.
When pure cotton fabric blueing brightens shrinkproof one-bath finishing, the composition of replenisher is：
The g/L of crease-shedding finishing agent RESIN KH-1 85 ~ 100
Arkofix NDF liqc 35~50 g/L
MgCl2·6H2O 12~ 15 g/L
The g/L of ethylene urea 1.8
The g/L of NON IONIC SOFTNER FTT 3.5
The g/L of azogeramine 0B 0.00450 ~ 0.00564
The g/L of acid blue A2R 0.01020 ~ 0.01282
The g/L of brightening agent MST-B 2.74 ~ 3.67
Remaining is water, and adjusts pH to 4.2 with citric acid；
It is new when driving, pad blueing in groove and brighten the composition of shiinkproof finish working solution and be：
The g/L of crease-shedding finishing agent RESIN KH-1 85 ~ 100
Arkofix NDF liqc 35~50 g/L
MgCl2·6H2O 12~ 15 g/L
The g/L of ethylene urea 1.8
The g/L of NON IONIC SOFTNER FTT 3.5
Azogeramine 0B（0.00450~0.00564）×1.25×80% g/L
Acid blue A2R（0.01020~0.01282）×80% g/L
Brightening agent MST-B（2.74~3.67）×80% g/L
Remaining is water, and adjusts pH to 4.2 with citric acid；
When polyester cotton fabric blueing brightens shrinkproof one-bath finishing, the composition of replenisher is：
The g/L of crease-shedding finishing agent RESIN KH-1 50 ~ 60
Arkofix NDF liqc 30~40 g/L
MgCl2·6H2O 8~10 g/L
The g/L of ethylene urea 1.0
The g/L of NON IONIC SOFTNER FTT 2.5
The g/L of azogeramine 0B 0.00450
The g/L of acid blue A2R 0.01020
The g/L of brightening agent MST-B 2.74
Remaining is water, and adjusts pH to 3.8 with citric acid；
It is new when driving, pad blueing in groove and brighten the composition of shiinkproof finish working solution and be：
The g/L of crease-shedding finishing agent RESIN KH-1 50 ~ 60
Arkofix NDF liqc 30~40 g/L
MgCl2·6H2O 8~10 g/L
The g/L of ethylene urea 1.0
The g/L of NON IONIC SOFTNER FTT 2.5
The g/L of azogeramine 0B 0.00450 × 1.25 × 80%
The g/L of acid blue A2R 0.01020 × 80%
The g/L of brightening agent MST-B 2.74 × 80%
Remaining is water, and adjusts pH to 3.8 with citric acid.
Present invention process is easy to operate, excellent product performance, dissociates and hydrolysis formaldehyde≤35mg/kg；Chi is washed through broadwise Very little rate of change is -0.6%~+0.5%, and resin interlining is two-sided one layer of pluffy hair, after resin interlining is compound with garment material so that The feel particularly soft of fabric is plentiful.
With reference to embodiment, the invention will be further described.
Specific embodiment
Embodiment 1：
Lining cloth fabric is pure cotton plain weave, and door width is 48.5 inches, yarn count is 20s×20s, density be 60 × 60/ Inch,
A kind of production method of two-sided raising resin interlining, brightens including turning over seam, concise, bleaching, two-sided napping, blueing successively Shrinkproof one-bath finishing, machine shrunk step.
Brushing process is two-sided each drawing three times, the rpm of cylinder rotating speed 75, along porcupine roller rotating speed 700rpm, along porcupine roller cylinder pressure 0.20Mpa, inverse porcupine roller cylinder pressure 0.35Mpa, inverse porcupine roller rotating speed 850rpm；Upper fabric guide roll tension force 1.8%, preceding fabric guide roll tension force 2.8%, rear fabric guide roll tension force 1.9% enters 14~16m/min of cloth speed.After plucking, fabric two sides all covers one layer of uniform fine hair. After resin interlining is compound with garment material so that the feel particularly soft of fabric is plentiful.
When blueing brightens shrinkproof one-bath finishing, the composition of replenisher is：
The g/L of crease-shedding finishing agent RESIN KH-1 85
Arkofix NDF liqc 35 g/L
MgCl2·6H2O 12 g/L
The g/L of ethylene urea 1.8
The g/L of NON IONIC SOFTNER FTT 3.5
Azogeramine 0B 0.00450g/L
The g/L of acid blue A2R 0.01020
The g/L of brightening agent MST-B 2.74
Remaining is water, and adjusts pH to 4.2 with citric acid；
It is new when driving, pad blueing in groove and brighten the composition of shiinkproof finish working solution and be：
Crease-shedding finishing agent RESIN KH-1 85g/L
Arkofix NDF liqc 35 g/L
MgCl2·6H2O 12 g/L
The g/L of ethylene urea 1.8
The g/L of NON IONIC SOFTNER FTT 3.5
The g/L of azogeramine 0B 0.00450 × 1.25 × 80%
The g/L of acid blue A2R 0.01020 × 80%
The g/L of brightening agent MST-B 2.74 × 80%
Remaining is water, and adjusts pH to 4.2 with citric acid；
When blueing brightens shiinkproof finish, cloth is entered by open width, shiinkproof finish liquid is rolled in two leachings two, working liquid ph 4.2-4.4, 90~130 DEG C of loose formula dryings, needle plate on overfeeding 1.5%~3.0%, eight lattice hot blasts are baked, wherein 160 DEG C of the first lattice temperature, second 165 DEG C of lattice temperature, the three ~ eight 175 DEG C of lattice temperature, speed is 28m/min when baking, and two cylinders cool down cropping step.
Embodiment 2
Lining cloth fabric is that pure cotton is twill-weave, and door width is 48.5 inches, yarn count is 20/2 s×20/2s, density be 52 × 68 pieces/inch；
A kind of production method of two-sided raising resin interlining, brightens including turning over seam, concise, bleaching, two-sided napping, blueing successively Shrinkproof one-bath finishing, machine shrunk step.
Brushing process is two-sided each drawing four times, the rpm of cylinder rotating speed 75, along porcupine roller rotating speed 700rpm, along porcupine roller cylinder pressure 0.20Mpa, inverse porcupine roller cylinder pressure 0.40Mpa, inverse porcupine roller rotating speed 850rpm；Upper fabric guide roll tension force 1.8%, preceding fabric guide roll tension force 2.8%, rear fabric guide roll tension force 1.9% enters 14~16m/min of cloth speed.After plucking, fabric two sides all covers one layer of uniform fine hair. After resin interlining is compound with garment material so that the feel particularly soft of fabric is plentiful.
When blueing brightens shrinkproof one-bath finishing, the composition of replenisher is：
The g/L of crease-shedding finishing agent RESIN KH-1 100
Arkofix NDF liqc 50 g/L
MgCl2·6H2O 15 g/L
The g/L of ethylene urea 1.8
The g/L of NON IONIC SOFTNER FTT 3.5
The g/L of azogeramine 0B 0.00564
The g/L of acid blue A2R 0.01282
The g/L of brightening agent MST-B 3.67
Remaining is water, and adjusts pH to 4.2 with citric acid；
It is new when driving, pad blueing in groove and brighten the composition of shiinkproof finish working solution and be：
The g/L of crease-shedding finishing agent RESIN KH-1 100
Arkofix NDF liqc 50 g/L
MgCl2·6H2O 15 g/L
The g/L of ethylene urea 1.8
The g/L of NON IONIC SOFTNER FTT 3.5
The g/L of azogeramine 0B 0.00564 × 1.25 × 80%
The g/L of acid blue A2R 0.01282 × 80%
The g/L of brightening agent MST-B 3.67 × 80%
Remaining is water, and adjusts pH to 4.2 with citric acid；
When blueing brightens shiinkproof finish, cloth is entered by open width, shiinkproof finish liquid is rolled in two leachings two, working liquid ph 4.2-4.4, 90~130 DEG C of loose formula dryings, needle plate on overfeeding 1.5%~3.0%, eight lattice hot blasts are baked, wherein 160 DEG C of the first lattice temperature, second 165 DEG C of lattice temperature, the three ~ eight 175 DEG C of lattice temperature, speed is 28m/min when baking, and two cylinders cool down cropping step.
Embodiment 3
Lining cloth fabric is polyester-cotton blend plain weave, and door width is 48.5 inches, yarn count is 21 s×21s, density be 60 × 58 Piece/inch,
A kind of production method of two-sided raising resin interlining, brightens including turning over seam, concise, bleaching, two-sided napping, blueing successively Shrinkproof one-bath finishing, machine shrunk step.
Brushing process respectively draws secondary for two-sided, the rpm of cylinder rotating speed 75, along porcupine roller rotating speed 700rpm, along porcupine roller cylinder pressure 0.20Mpa, inverse porcupine roller cylinder pressure 0.25Mpa, inverse porcupine roller rotating speed 800rpm；Upper fabric guide roll tension force 1.8%, preceding fabric guide roll tension force 2.8%, rear fabric guide roll tension force 1.9% enters 14~16m/min of cloth speed.After plucking, fabric two sides all covers one layer of uniform fine hair. After resin interlining is compound with garment material so that the feel particularly soft of fabric is plentiful.
When blueing brightens shrinkproof one-bath finishing, the composition of replenisher is：
The g/L of crease-shedding finishing agent RESIN KH-1 50
Arkofix NDF liqc 30 g/L
MgCl2·6H2O 8 g/L
The g/L of ethylene urea 1.0
The g/L of NON IONIC SOFTNER FTT 2.5
The g/L of azogeramine 0B 0.00450
The g/L of acid blue A2R 0.01020
The g/L of brightening agent MST-B 2.74
Remaining is water, and adjusts pH to 3.8 with citric acid；
It is new when driving, pad blueing in groove and brighten the composition of shiinkproof finish working solution and be：
Crease-shedding finishing agent RESIN KH-1 50g/L
Arkofix NDF liqc 30g/L
MgCl2·6H2O 8g/L
The g/L of ethylene urea 1.0
The g/L of NON IONIC SOFTNER FTT 2.5
The g/L of azogeramine 0B 0.00450 × 1.25 × 80%
The g/L of acid blue A2R 0.01020 × 80%
The g/L of brightening agent MST-B 2.74 × 80%
Remaining is water, and adjusts pH to 3.8 with citric acid.
When blueing brightens shiinkproof finish, cloth is entered by open width, shiinkproof finish liquid is rolled in two leachings two, working liquid ph 3.8-4.0, 90~130 DEG C of loose formula dryings, needle plate on overfeeding 1.0%~2.0%, eight lattice hot blasts are baked, wherein 160 DEG C of the first lattice temperature, second 165 DEG C of lattice temperature, the three ~ eight 175 DEG C of lattice temperature, speed is 30m/min when baking, and two cylinders cool down cropping step.
Embodiment 4
Lining cloth fabric is polyester-cotton blend plain weave, and door width is 48.5 inches, yarn count is 16s×16s, density be 50 × 50/ Inch.
A kind of production method of two-sided raising resin interlining, brightens including turning over seam, concise, bleaching, two-sided napping, blueing successively Shrinkproof one-bath finishing, machine shrunk step.
Brushing process is two-sided each drawing two~tetra- times, the rpm of cylinder rotating speed 75, along porcupine roller rotating speed 700rpm, along porcupine roller cylinder Pressure 0.20Mpa, inverse porcupine roller cylinder pressure 0.30Mpa, inverse porcupine roller rotating speed 800rpm；Upper fabric guide roll tension force 1.8%, preceding fabric guide roll Tension force 2.8%, rear fabric guide roll tension force 1.9% enters 14~16m/min of cloth speed.After plucking, fabric two sides all covers one layer uniformly Fine hair.After resin interlining is compound with garment material so that the feel particularly soft of fabric is plentiful.
When blueing brightens shrinkproof one-bath finishing, the composition of replenisher is：
The g/L of crease-shedding finishing agent RESIN KH-1 60
Arkofix NDF liqc 40 g/L
MgCl2·6H2O 10 g/L
The g/L of ethylene urea 1.0
The g/L of NON IONIC SOFTNER FTT 2.5
The g/L of azogeramine 0B 0.00450
The g/L of acid blue A2R 0.01020
The g/L of brightening agent MST-B 2.74
Remaining is water, and adjusts pH to 3.8 with citric acid；
It is new when driving, pad blueing in groove and brighten the composition of shiinkproof finish working solution and be：
The g/L of crease-shedding finishing agent RESIN KH-1 60
Arkofix NDF liqc 40 g/L
MgCl2·6H2O 10 g/L
The g/L of ethylene urea 1.0
The g/L of NON IONIC SOFTNER FTT 2.5
The g/L of azogeramine 0B 0.00450 × 1.25 × 80%
The g/L of acid blue A2R 0.01020 × 80%
The g/L of brightening agent MST-B 2.74 × 80%
Remaining is water, and adjusts pH to 3.8 with citric acid.
When blueing brightens shiinkproof finish, cloth is entered by open width, shiinkproof finish liquid is rolled in two leachings two, working liquid ph 3.8-4.0, 90~130 DEG C of loose formula dryings, needle plate on overfeeding 1.0%~2.0%, eight lattice hot blasts are baked, wherein 160 DEG C of the first lattice temperature, second 165 DEG C of lattice temperature, the three ~ eight 175 DEG C of lattice temperature, speed is 30m/min when baking, and two cylinders cool down cropping step.

Claims (2)

1. the production method of resin interlining is bleached in a kind of two-sided raising, it is characterized in that：Resin interlining is two-sided one layer of pluffy hair；Trip From with hydrolysis formaldehyde≤35mg/kg；It is -0.6%~+0.5% through broadwise washing size changing rate；Successively include turn over seam, it is concise, Bleaching, two-sided napping, blueing brighten shrinkproof one-bath finishing, machine shrunk step；Brushing process is two-sided each drawing two~tetra- times, tin Woods rotating speed 75rpm, along porcupine roller rotating speed 700rpm, along porcupine roller cylinder pressure 0.20Mpa, inverse porcupine roller cylinder pressure 0.25~ 0.40Mpa, 800~850rpm of inverse porcupine roller rotating speed；Upper fabric guide roll tension force 1.8%, preceding fabric guide roll tension force 2.8%, rear fabric guide roll Power 1.9%, enters cloth 14~16m/min of speed, and after plucking, fabric two sides all covers one layer of uniform fine hair；
When pure cotton fabric blueing brightens shrinkproof one-bath finishing, the composition of replenisher is：
Remaining is water, and adjusts pH to 4.2 with citric acid；
It is new when driving, pad blueing in groove and brighten the composition of shiinkproof finish working solution and be：
Remaining is water, and adjusts pH to 4.2 with citric acid；
When polyester cotton fabric blueing brightens shrinkproof one-bath finishing, the composition of replenisher is：
Remaining is water, and adjusts pH to 3.8 with citric acid；
It is new when driving, pad blueing in groove and brighten the composition of shiinkproof finish working solution and be：
Remaining is water, and adjusts pH to 3.8 with citric acid.
2. the production method of resin interlining is bleached in two-sided raising according to claim 1, it is characterized in that：The fabric of lining cloth is pure Bafta or polyester-cotton fabric；Wherein described pure cotton fabric is the one kind in following two kinds of specifications：The first is plain weave, door width For 48.5 inches, yarn count are 20s×20s, density be 60 × 60 pieces/inch, be for second twill-weave, door width is 48.5 English Very little, yarn count is 20/2s×20/2s, density be 52 × 68 pieces/inch；The polyester-cotton fabric is following two kinds of plain weave specifications In one kind：The door width of the first is 48.5 inches, yarn count is 21s×21s, density be 60 × 58 pieces/inch, second Door width is 48.5 inches, yarn count is 16s×16s, density be 50 × 50 pieces/inch.
CN201510660283.7A 2015-10-13 2015-10-13 Double-side raised bleached resin lining and production method thereof Active CN105386200B (en)