CN105382241A - 一种分油器箱体的浇铸工艺 - Google Patents
一种分油器箱体的浇铸工艺 Download PDFInfo
- Publication number
- CN105382241A CN105382241A CN201511019589.0A CN201511019589A CN105382241A CN 105382241 A CN105382241 A CN 105382241A CN 201511019589 A CN201511019589 A CN 201511019589A CN 105382241 A CN105382241 A CN 105382241A
- Authority
- CN
- China
- Prior art keywords
- casting
- platform body
- rising head
- die
- metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明的一种分油器箱体的浇铸工艺，包括制备型腔砂芯工序、制备铝液工序、预热金属浇铸模具工序、下芯合模工序、浇铸成型工序、冷却开模工序和铸件清理工序。本发明的一种分油器箱体的浇铸工艺，易于实现，使得铸件组织致密度高，铸件质量好。
Description
技术领域
本发明涉及金属型低压铸造技术领域，尤其是大型箱体铸件低压铸造领域,具体涉及一种分油器箱体的浇铸工艺。
背景技术
请参阅图1，德国普旭605分油器的分油器箱体1'是真空泵体关键部件，分油器箱体1'的外轮廓为约为253mm*405mm*626mm。客户对铸件尺寸要求精度高、外观平整、轮廓清晰完整；铸件内部组织致密，无气孔、缩松等铸造缺陷；要求铸件材质为铝硅合金，材料对应的抗拉强度≥235Mpa，延伸≥1，并且要求在2bar空气压力下无泄漏；又由于铸件均匀壁厚在6-8mm区间，但存在多处孤立厚大的形状结构；最大一处孤立厚大区域轮廓形状为123mm*71mm*80mm由于铸件外形尺寸大，无法进行补缩产生气孔和缩松缺陷。
发明内容
本发明的目的是为了克服现有技术的不足，提供一种分油器箱体的浇铸工艺，它易于实现，解决壁厚变化较大远离浇口无法补缩的厚大部位缩松问题，使得铸件组织致密度高，铸件质量好，满足设计要求。
一种分油器箱体的浇铸工艺，包括下述工序：
S1，制备型腔砂芯工序：准备型腔砂芯模具，型腔砂芯模具的冒口采用保温冒口，用50-100目的覆膜砂，通过加热到220℃-400℃的内腔砂芯模具制成型腔砂芯；
S2，制备铝液工序，将铝合金熔料投入熔炉中熔化成液体，熔炉内的温度为700℃-750℃，再通过铝液处理工序得到铝液待用；
S3，预热金属浇铸模具工序：先将金属浇铸模具安装在浇铸机上，并用天然气加热装置预热金属浇铸模具，金属浇铸模具的预热温度为200℃-350℃，用喷砂工具清除掉金属浇铸模具表面上的锈迹和杂物，然后喷涂上一层防粘铝金属模型腔涂料；
S4，下芯合模工序：将S1中制备好的型腔砂芯按金属浇铸模具上的砂芯定位座位置放入预热后的金属浇铸模具内，然后合上金属外模；
S5，浇铸成型工序：将S2中制备好的铝液经过浇铸机上的升液管压入金属浇铸模具内，其浇铸温度为700℃-730℃；
S6，冷却开模工序：浇铸完成后，铸件在金属浇铸模具的浇、冒口的持续补缩作用下经过350s的冷却凝固成固态的分油器箱体铸件产品，之后打开金属浇铸模具取出分油器箱体铸件产品；
S7，铸件清理工序：去除S6中得到的分油器箱体铸件产品的浇、冒口，去除分油器箱体铸件产品的内腔的芯砂，将分油器箱体铸件产品进行打磨修整和表面抛丸处理得到成品的分油器箱体铸件。
上述的一种分油器箱体的浇铸工艺，其中，工序S2中，所述铝液处理工序依次包括铝液精炼工序、铝液除气工序、铝液除渣工序和铝液变质工序。
上述的一种分油器箱体的浇铸工艺，其中，所述金属浇铸模具包括上模和下模，所述上模和下模采用分体设计。
上述的一种分油器箱体的浇铸工艺，其中，工序S1中的所述保温冒口包括壳体、外冒口和内冒口，所述壳体包括上台体和下台体，其中：
所述上台体的上端面的尺寸小于所述上台体的下端面的尺寸，所述下台体的上端面的尺寸大于所述下台体的下端面的尺寸，所述上台体的下端面的尺寸与所述下台体的上端面的尺寸相等；
所述上台体的下端面固定在所述下台体的上端面，且所述上台体与所述下台体为一体成型结构；
所述内冒口和外冒口均设置在所述壳体的内部，且所述外冒口套接在所述内冒口的外部，所述内冒口和外冒口均呈上大下小的喇叭状结构，所述外冒口的上端的一侧具有一向内弯折的折弯部，该折弯部与所述内冒口的一侧固定在一起。
上述的一种分油器箱体的浇铸工艺，其中，工序S1中，所述型腔砂芯模具采用金属材质制成。
本发明的一种分油器箱体的浇铸工艺，包括制备型腔砂芯工序、制备铝液工序、预热金属浇铸模具工序、下芯合模工序、浇铸成型工序、冷却开模工序和铸件清理工序。它易于实现，解决壁厚变化较大远离浇口无法补缩的厚大部位缩松问题，使得铸件组织致密度高，铸件质量好，满足设计要求。
附图说明
图1为德国普旭605分油器的分油器箱体的结构示意图；
图2为本发明的一种分油器箱体的浇铸工艺流程图；
图3为本发明的一种分油器箱体的浇铸工艺的型腔砂芯的结构图；
图4为金属浇铸模具的上模结构图；
图5为金属浇铸模具的下模结构图；
图6为保温冒口的结构图；
图7为图6的侧视图。
具体实施方式
为了能更好地对本发明的技术方案进行理解，下面通过具体地实施例并结合附图进行详细地说明。
请参阅图2，本发明的一种分油器箱体的浇铸工艺，包括制备型腔砂芯工序、制备铝液工序、预热金属浇铸模具工序、下芯合模工序、浇铸成型工序、冷却开模工序和铸件清理工序。
S1，制备型腔砂芯工序：请参阅图3，准备型腔砂芯模具10，型腔砂芯模具10采用金属材质制成，型腔砂芯模具的冒口采用保温冒口，用50-100目的覆膜砂，通过加热到220℃-400℃的内腔砂芯模具制成型腔砂芯；
S2，制备铝液工序，将铝合金熔料投入熔炉中熔化成液体，熔炉内的温度为700℃-750℃，再通过铝液处理工序得到铝液待用，铝液处理工序依次包括铝液精炼工序、铝液除气工序、铝液除渣工序和铝液变质工序；
S3，预热金属浇铸模具工序：先将金属浇铸模具安装在浇铸机上，并用天然气加热装置预热金属浇铸模具，金属浇铸模具的预热温度为200℃-350℃，用喷砂工具清除掉金属浇铸模具表面上的锈迹和杂物，然后喷涂上一层防粘铝金属模型腔涂料；
S4，下芯合模工序：将S1中制备好的型腔砂芯按金属浇铸模具上的砂芯定位座位置放入预热后的金属浇铸模具内，然后合上金属外模；
S5，浇铸成型工序：将S2中制备好的铝液经过浇铸机上的升液管压入金属浇铸模具内，其浇铸温度为700℃-730℃；
S6，冷却开模工序：浇铸完成后，铸件在金属浇铸模具的浇、冒口的持续补缩作用下经过350s的冷却凝固成固态的分油器箱体铸件产品，之后打开金属浇铸模具取出分油器箱体铸件产品；
S7，铸件清理工序：去除S6中得到的分油器箱体铸件产品的浇、冒口，去除分油器箱体铸件产品的内腔的芯砂，将分油器箱体铸件产品进行打磨修整和表面抛丸处理得到成品的分油器箱体铸件。
请参阅图4和图5，金属浇铸模具包括上模20和下模30，上模20和下模30采用分体设计。
请参阅图6和图7，工序S1中的保温冒口包括壳体1、外冒口2和内冒口3，壳体1包括上台体11和下台体12。
上台体11的上端面的尺寸小于上台体11的下端面的尺寸，下台体12的上端面的尺寸大于下台体12的下端面的尺寸，上台体11的下端面的尺寸与下台体12的上端面的尺寸相等；上台体11的下端面固定在下台体12的上端面，且上台体11与下台体12为一体成型结构；内冒口3和外冒口2均设置在壳体1的内部，且外冒口2套接在内冒口3的外部，内冒口3和外冒口2均呈上大下小的喇叭状结构，外冒口2的上端的一侧具有一向内弯折的折弯部，该折弯部与内冒口3的一侧固定在一起。且内冒口3与外冒口2的折弯部相邻的一侧与外冒口2的折弯部固定在一起。
采用本发明的分油器箱体的浇铸工艺，易于实现，可以解决壁厚变化较大远离浇口无法补缩的厚大部位缩松问题，使得铸件组织致密度高，铸件质量好，满足设计要求。
本技术领域中的普通技术人员应当认识到，以上的实施例仅是用来说明本发明，而并非用作为对本发明的限定，只要在本发明的实质精神范围内，对以上所述实施例的变化、变型都将落在本发明的权利要求书范围内。
Claims (5)
1.一种分油器箱体的浇铸工艺，其特征在于，包括下述工序：
S1，制备型腔砂芯工序：准备型腔砂芯模具，型腔砂芯模具的冒口采用保温冒口，用50-100目的覆膜砂，通过加热到220℃-400℃的内腔砂芯模具制成型腔砂芯；
S2，制备铝液工序，将铝合金熔料投入熔炉中熔化成液体，熔炉内的温度为700℃-750℃，再通过铝液处理工序得到铝液待用；
S3，预热金属浇铸模具工序：先将金属浇铸模具安装在浇铸机上，并用天然气加热装置预热金属浇铸模具，金属浇铸模具的预热温度为200℃-350℃，用喷砂工具清除掉金属浇铸模具表面上的锈迹和杂物，然后喷涂上一层防粘铝金属模型腔涂料；
S4，下芯合模工序：将S1中制备好的型腔砂芯按金属浇铸模具上的砂芯定位座位置放入预热后的金属浇铸模具内，然后合上金属外模；
S5，浇铸成型工序：将S2中制备好的铝液经过浇铸机上的升液管压入金属浇铸模具内，其浇铸温度为700℃-730℃；
S6，冷却开模工序：浇铸完成后，铸件在金属浇铸模具的浇、冒口的持续补缩作用下经过350s的冷却凝固成固态的分油器箱体铸件产品，之后打开金属浇铸模具取出分油器箱体铸件产品；
S7，铸件清理工序：去除S6中得到的分油器箱体铸件产品的浇、冒口，去除分油器箱体铸件产品的内腔的芯砂，将分油器箱体铸件产品进行打磨修整和表面抛丸处理得到成品的分油器箱体铸件。
2.根据权利要求1所述的一种分油器箱体的浇铸工艺，其特征在于，工序S2中所述铝液处理工序依次包括铝液精炼工序、铝液除气工序、铝液除渣工序和铝液变质工序。
3.根据权利要求1所述的一种分油器箱体的浇铸工艺，其特征在于，所述金属浇铸模具包括上模和下模，所述上模和下模采用分体设计。
4.根据权利要求1所述的一种分油器箱体的浇铸工艺，其特征在于，工序S1中的所述保温冒口包括壳体、外冒口和内冒口，所述壳体包括上台体和下台体，其中：
所述上台体的上端面的尺寸小于所述上台体的下端面的尺寸，所述下台体的上端面的尺寸大于所述下台体的下端面的尺寸，所述上台体的下端面的尺寸与所述下台体的上端面的尺寸相等；
所述上台体的下端面固定在所述下台体的上端面，且所述上台体与所述下台体为一体成型结构；
所述内冒口和外冒口均设置在所述壳体的内部，且所述外冒口套接在所述内冒口的外部，所述内冒口和外冒口均呈上大下小的喇叭状结构，所述外冒口的上端的一侧具有一向内弯折的折弯部，该折弯部与所述内冒口的一侧固定在一起。
5.根据权利要求1所述的一种分油器箱体的浇铸工艺，其特征在于，工序S1中，所述型腔砂芯模具采用金属材质制成。