CN105369620A - Method for preparing environment-friendly waterproof full-cotton colored quadrille cloth with polishing coating - Google Patents
Method for preparing environment-friendly waterproof full-cotton colored quadrille cloth with polishing coating Download PDFInfo
- Publication number
- CN105369620A CN105369620A CN201510645951.9A CN201510645951A CN105369620A CN 105369620 A CN105369620 A CN 105369620A CN 201510645951 A CN201510645951 A CN 201510645951A CN 105369620 A CN105369620 A CN 105369620A
- Authority
- CN
- China
- Prior art keywords
- plaids
- coating
- environment
- cloth
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a method for preparing environment-friendly waterproof full-cotton colored quadrille cloth with a polishing coating and belongs to the technical field of cloth preparation. The method comprises the steps that firstly, full combed cotton and ring spinning yarn are woven into quadrille cloth, and the quadrille cloth is dyed through long-turning active/intellectual circle; the quadrille cloth is coated with acrylic acid resin clear glue at least once, press polishing is carried out after drying, and the quadrille cloth is coated with polishing colored slurry at least twice after press polishing; the quadrille cloth is pre-washed through conventional industrial water, and drying is carried out after prewashing; finally, after penetrant is added to a C6 water-proofing agent or fluoride-free water-proofing agent, waterproof treatment is carried out, and the environment-friendly waterproof full-cotton colored quadrille cloth with the polishing coating can be obtained. According to the preparation method, the prewashing procedure after coating is added, cloth cover oil spots generated by the reaction of anions and the weak cation C6 waterproofing agent or fluoride-free water-proofing agent, in the next step can be reduced, and the cloth cover quality is improved. The C6/fluoride-free environment-friendly water-proofing agent is adopted, and the blank of the high waterproof requirement of current cotton polishing colored coating fabric is filled in.
Description
Technical field
The invention belongs to cloth preparing technical field, particularly a kind of cotton band look polishes the preparation method of coating plaids.
Background technology
Plaids are a kind of common fabrics, have that silk quality is frivolous, the feature of good springiness, are applicable to all kinds of textile product.Outdoor trip, based on light packs, also need fabric to have certain function while of not only requiring that fabric is frivolous, light fabric high-quality becomes the first-selection of outdoor trip.
Carry out in the process of coating in preparation plaids, need to embrocate bright band mill base material, polishing band mill base material is anion, the C6/ fluorine-free and environment-friendly waterproofing agent of general use is CATION or weak cation, so in the process of WATER REPELLENT TREATMENT, anion/cation will react, cause plaids cloth cover to occur oil drop spot after upper waterproof 5-10 minute, and oil drop spot cannot be peeled off/wash off, has a strong impact on the quality of coating plaids.
At present, on market, conventional coating fabric waterproofing agent used is that C8, C8 and C6/ compare without fluoro water proofing agent, its good water-proof effect but not environmentally, and in order to reach good water-proof effect and the object of environmental protection again, technique and waterproof agent all need to upgrade adjustment.
Summary of the invention
The object of the invention is to solve above-mentioned the deficiencies in the prior art, a kind of cotton band look of environment-friendly waterproof is provided to polish the preparation method of coating plaids, first full combed cotton is selected to produce by warp-wise 40S, broadwise 21S and 12S selects the anti-yarn of ring to produce, multi-arm jacquard is adopted to be woven into plaids, cloth cover is made to present lattice effect, add the pre-water-washing step after coating, this pre-water-washing step can be washed off because pasting the anion coating paste pollutant floating over cloth cover, the cloth cover oil drop spot decreasing anion and next step weak cation C6 waterproofing agent or produce without fluoro water proofing agent reacts, improve plaids fabric quality, adopt C6/ fluorine-free and environment-friendly waterproofing agent, fill up the blank that current cotton class polishes color coating fabric height waterproof requirement.
The technical scheme that the present invention is adopted for achieving the above object is: a kind of cotton band look of environment-friendly waterproof polishes the preparation method of coating plaids, it is characterized in that: first full combed cotton and ring spinning are woven into plaids, adopts long vehicle activity/intellectual circle's dyeing; Then described plaids are coated with acrylic resin transparent adhesive tape at least one times, press polish after drying, embrocates bright band mill base material at least twice after press polish; Adopt regular industrial water to wash in advance these plaids subsequently, wash post-drying in advance; Finally adopt C6 waterproofing agent or carry out WATER REPELLENT TREATMENT without fluoro water proofing agent after adding bleeding agent, the cotton band look that can obtain environment-friendly waterproof polishes coating plaids.
The cotton band look of environment-friendly waterproof polishes a preparation method for coating plaids, it is characterized in that: comprise following concrete technology step:
(1) plaids are woven:
Select at warp-wise 40S that full combed cotton is produced, broadwise 21S and 12S selects the anti-yarn of ring to produce, be woven into plaids;
(2) dye:
The plaids (1) step be woven into adopt long vehicle activity/intellectual circle to carry out dyeing process;
(3) coating:
Plaids after (2) step process are first coated with acrylic resin transparent adhesive tape at least one times, then carry out press polish process, to plaids being embrocated bright band mill base material at least twice after press polish;
(4) wash in advance:
Adopt regular industrial water to wash in advance the plaids after (3) step coating process, wash post-drying in advance;
(5) WATER REPELLENT TREATMENT:
Plaids after (4) step being washed in advance import and fill C6 waterproofing agent or add the tank of bleeding agent without fluoro water proofing agent, after folder rod, then dry in an oven, finally go out the cotton band look that cloth clot obtains environment-friendly waterproof and polish coating plaids.
Its thread count of plaids be woven in described (1) step is 135-155 piece/inch of * 65-85 piece/inch.
In described (3) step, plaids are coated with the speed of a motor vehicle of acrylic resin transparent adhesive tape is 35-45 m/min, and then dry, the temperature of plaids fabric oven dry is in an oven 140 DEG C-160 DEG C, and the time is 30-45 second; In described (3) step, in press polish processing procedure, temperature is 160 DEG C-180 DEG C, pressure is 40-70 ton.
The water temperature of washing in advance in described (4) step is 40 DEG C-60 DEG C, speed is 15-25 m/min, and wash post-drying in advance, bake out temperature is 120 DEG C-150 DEG C, and drying time is 30-50 second.
In described (5) step, the concrete technology of WATER REPELLENT TREATMENT is:
A) first by C6 waterproofing agent or without fluoro water proofing agent and bleeding agent is deployed pours in tank;
B) baking oven is warming up to 150 DEG C-180 DEG C;
C) the folder rod of machine is wrapped calico;
D) then plaids imported tank, after folder rod, then enter baking oven, the speed of a motor vehicle entering baking oven is 7-10 m/min;
E) finally go out the cotton band look that cloth clot obtains environment-friendly waterproof and polish coating plaids.
The composition of described C6 waterproofing agent is the water of mass fraction 30%-40% alkyl combined polymerization product and mass fraction 60%-70%, and the consumption of described C6 waterproofing agent is 60-100 grams per liter.
Described is the mixture of mass fraction 20%-30% modified fat compound and wax dispersions and the water of mass fraction 70%-80% without fluoro water proofing agent composition, and the described consumption without fluoro water proofing agent is 70-110 grams per liter.
The composition of described bleeding agent is the aliphatic ethanol of mass fraction 5%-15% and the water of mass fraction 85%-95%, and the consumption of described bleeding agent is 5-20 grams per liter.
In described d) step plaids import tank, after folder rod plaids with the mass fraction of waterproofing agent be 50%-80%.
The beneficial effect that the present invention obtains is:
(1) method of the present invention overcomes the problem being first coated with and polishing the anion/cation that can produce after then coating paste carries out C6/ fluorine-free and environment-friendly WATER REPELLENT TREATMENT and react, thus makes plaids cloth cover there will not be the phenomenons such as oil drop spot.
(2) the pre-water-washing step in the present invention plays removing because being attached to the anionic impurity of coating cloth cover after polishing coating, and improve rear road waterproof operation, simultaneously sandwich rod and dilute because have employed cloth the zwitterion pollutant floated on waterproofing agent, allow the plaids cloth cover after strong waterproof there is no oil drop spot.
(3) in the present invention, cation impurity is removed in pre-washing, folder rod infantees mode is adopted during WATER REPELLENT TREATMENT, the strong waterproof coating fabric of any environmental protection of producing like this, can solve because the cloth cover caused that mutually reacts of zwitterion between waterproofing agent and coating paste plays oil drop spot problem.
(4) plaids obtained after method process of the present invention, its waterproof effect can reach spray test 100 points of high standards.
(5) because the environmental requirement of the mankind to fabric is more and more higher, obvious C8 waterproofing agent in the past can not meet the environment-friendlyfashionable fashionable requirement of domestic and international top brand, use described technological process of the present invention and the floride-free waterproof agent of relevant environment-friendly type C6/, not only can accomplish or exceed conventional C8 waterproof effect, also comparatively C8 environmental protection more; On cost, differ 0.5 yuan/meter simultaneously, divide every part ready-made clothes roughly expense only improve 0.9 yuan-1.5 yuan/part, but fabric and ready-made clothes added value can improve 25%-50%, for later textile garment coating class fabric opens new chapter at the strong waterproofing industry of environmental protection.
Detailed description of the invention
Describe the present invention in detail below in conjunction with specific embodiment, but the present invention is not limited to specific embodiment.
Embodiment 1
The cotton band look of environment-friendly waterproof polishes a preparation method for coating plaids, it is characterized in that: comprise following concrete technology step:
(1) plaids are woven:
Select at warp-wise 40S that full combed cotton is produced, broadwise 21S and 12S selects the anti-yarn of ring to produce, be woven into plaids, its thread count is 135 pieces/inch * 65 pieces/inch.
(2) dye:
The plaids (1) step be woven into adopt long vehicle activity/intellectual circle to carry out dyeing process;
(3) coating:
Plaids after (2) step process are first coated with acrylic resin transparent adhesive tape once, the speed of a motor vehicle that plaids are coated with acrylic resin transparent adhesive tape is 35 ms/min, then dry, the temperature of plaids fabric oven dry is in an oven 140 DEG C, and the time is 30 seconds; Then carry out press polish process, in press polish processing procedure, temperature is 160 DEG C, pressure is 40 tons.To plaids being embrocated bright band mill base material twice after press polish;
(4) wash in advance:
Washed in advance by plaids employing regular industrial water after (3) step coating process, the water temperature of pre-washing is 40 DEG C, speed is 15 ms/min, and wash post-drying in advance, bake out temperature is 120 DEG C, and drying time is 30 seconds.
(5) WATER REPELLENT TREATMENT:
A) first by C6 waterproofing agent and bleeding agent is deployed pours in tank;
The composition of C6 waterproofing agent is the water of mass fraction 30% alkyl combined polymerization product and mass fraction 70%, and the consumption of C6 waterproofing agent is 60 grams per liters.
The composition of bleeding agent is the aliphatic ethanol of mass fraction 5% and the water of mass fraction 95%, and the consumption of bleeding agent is 5 grams per liters.
B) baking oven is warming up to 150 DEG C;
C) the folder rod of machine is wrapped calico;
D) plaids after then (4) step being washed in advance import tank, after folder rod, then enter baking oven, and the speed of a motor vehicle entering baking oven is 7 ms/min; Plaids import tank, after folder rod plaids with the mass fraction of waterproofing agent be 50%.
E) finally go out the cotton band look that cloth clot obtains environment-friendly waterproof and polish coating plaids.
Embodiment 2
The cotton band look of environment-friendly waterproof polishes a preparation method for coating plaids, it is characterized in that: comprise following concrete technology step:
(1) plaids are woven:
Select at warp-wise 40S that full combed cotton is produced, broadwise 21S and 12S selects the anti-yarn of ring to produce, be woven into plaids, its thread count is 145 pieces/inch * 75 pieces/inch.
(2) dye:
The plaids (1) step be woven into adopt long vehicle activity/intellectual circle to carry out dyeing process;
(3) coating:
Plaids after (2) step process are first coated with acrylic resin transparent adhesive tape three times, the speed of a motor vehicle that plaids are coated with acrylic resin transparent adhesive tape is 40 ms/min, then dry, the temperature of plaids fabric oven dry is in an oven 150 DEG C, and the time is 40 seconds; Then carry out press polish process, in press polish processing procedure, temperature is 170 DEG C, pressure is 55 tons.To plaids being embrocated bright band mill base material five times after press polish;
(4) wash in advance:
Washed in advance by plaids employing regular industrial water after (3) step coating process, the water temperature of pre-washing is 50 DEG C, speed is 20 ms/min, and wash post-drying in advance, bake out temperature is 130 DEG C, and drying time is 40 seconds.
(5) WATER REPELLENT TREATMENT:
A) first will without fluoro water proofing agent and bleeding agent be deployed pours in tank;
Be the mixture of mass fraction 25% modified fat compound and wax dispersions and the water of mass fraction 75% without fluoro water proofing agent composition, the consumption without fluoro water proofing agent is 90 grams per liters.
The composition of bleeding agent is the aliphatic ethanol of mass fraction 10% and the water of mass fraction 90%, and the consumption of bleeding agent is 16 grams per liters.
B) baking oven is warming up to 165 DEG C;
C) the folder rod of machine is wrapped calico;
D) plaids after then (4) step being washed in advance import tank, after folder rod, then enter baking oven, and the speed of a motor vehicle entering baking oven is 8 ms/min; Plaids import tank, after folder rod plaids with the mass fraction of waterproofing agent be 65%.
E) finally go out the cotton band look that cloth clot obtains environment-friendly waterproof and polish coating plaids.
Embodiment 3
The cotton band look of environment-friendly waterproof polishes a preparation method for coating plaids, it is characterized in that: comprise following concrete technology step:
(1) plaids are woven:
Select at warp-wise 40S that full combed cotton is produced, broadwise 21S and 12S selects the anti-yarn of ring to produce, be woven into plaids, its thread count is 155 pieces/inch * 85 pieces/inch.
(2) dye:
The plaids (1) step be woven into adopt long vehicle activity/intellectual circle to carry out dyeing process;
(3) coating:
Plaids after (2) step process are first coated with acrylic resin transparent adhesive tape five times, the speed of a motor vehicle that plaids are coated with acrylic resin transparent adhesive tape is 45 ms/min, then dry, the temperature of plaids fabric oven dry is in an oven 160 DEG C, and the time is 45 seconds; Then carry out press polish process, in press polish processing procedure, temperature is 180 DEG C, pressure is 70 tons.To plaids being embrocated bright band mill base material nine times after press polish;
(4) wash in advance:
Washed in advance by plaids employing regular industrial water after (3) step coating process, the water temperature of pre-washing is 60 DEG C, speed is 25 ms/min, and wash post-drying in advance, bake out temperature is 150 DEG C, and drying time is 50 seconds.
(5) WATER REPELLENT TREATMENT:
A) first by C6 waterproofing agent and bleeding agent is deployed pours in tank;
The composition of C6 waterproofing agent is the water of mass fraction 40% alkyl combined polymerization product and mass fraction 60%, and the consumption of C6 waterproofing agent is 100 grams per liters.
The composition of bleeding agent is the aliphatic ethanol of mass fraction 15% and the water of mass fraction 85%, and the consumption of bleeding agent is 20 grams per liters.
B) baking oven is warming up to 180 DEG C;
C) the folder rod of machine is wrapped calico;
D) plaids after then (4) step being washed in advance import tank, after folder rod, then enter baking oven, and the speed of a motor vehicle entering baking oven is 10 ms/min; Plaids import tank, after folder rod plaids with the mass fraction of waterproofing agent be 80%.
E) finally go out the cotton band look that cloth clot obtains environment-friendly waterproof and polish coating plaids.
Embodiment 4
The cotton band look of environment-friendly waterproof polishes a preparation method for coating plaids, it is characterized in that: comprise following concrete technology step:
(1) plaids are woven:
Select at warp-wise 40S that full combed cotton is produced, broadwise 21S and 12S selects the anti-yarn of ring to produce, be woven into plaids, its thread count is 150 pieces/inch * 80 pieces/inch.
(2) dye:
The plaids (1) step be woven into adopt long vehicle activity/intellectual circle to carry out dyeing process;
(3) coating:
Plaids after (2) step process are first coated with acrylic resin transparent adhesive tape six times, the speed of a motor vehicle that plaids are coated with acrylic resin transparent adhesive tape is 40 ms/min, then dry, the temperature of plaids fabric oven dry is in an oven 145 DEG C, and the time is 35 seconds; Then carry out press polish process, in press polish processing procedure, temperature is 165 DEG C, pressure is 55 tons.To plaids being embrocated bright band mill base material 12 times after press polish;
(4) wash in advance:
Washed in advance by plaids employing regular industrial water after (3) step coating process, the water temperature of pre-washing is 55 DEG C, speed is 20 ms/min, and wash post-drying in advance, bake out temperature is 140 DEG C, and drying time is 45 seconds.
(5) WATER REPELLENT TREATMENT:
A) first will without fluoro water proofing agent and bleeding agent be deployed pours in tank;
Be the mixture of mass fraction 30% modified fat compound and wax dispersions and the water of mass fraction 70% without fluoro water proofing agent composition, the consumption without fluoro water proofing agent is 110 grams per liters.
The composition of bleeding agent is the aliphatic ethanol of mass fraction 15% and the water of mass fraction 85%, and the consumption of bleeding agent is 5 grams per liters.
B) baking oven is warming up to 170 DEG C;
C) the folder rod of machine is wrapped calico;
D) plaids after then (4) step being washed in advance import tank, after folder rod, then enter baking oven, and the speed of a motor vehicle entering baking oven is 7 ms/min; Plaids import tank, after folder rod plaids with the mass fraction of waterproofing agent be 80%.
E) finally go out the cotton band look that cloth clot obtains environment-friendly waterproof and polish coating plaids.
Claims (10)
1. the cotton band look of environment-friendly waterproof polishes a preparation method for coating plaids, it is characterized in that: first full combed cotton and ring spinning are woven into plaids, adopts long vehicle activity/intellectual circle's dyeing; Then described plaids are coated with acrylic resin transparent adhesive tape at least one times, press polish after drying, embrocates bright band mill base material at least twice after press polish; Adopt regular industrial water to wash in advance these plaids subsequently, wash post-drying in advance; Finally adopt C6 waterproofing agent or carry out WATER REPELLENT TREATMENT without fluoro water proofing agent after adding bleeding agent, the cotton band look that can obtain environment-friendly waterproof polishes coating plaids.
2. the cotton band look of a kind of environment-friendly waterproof according to claim 1 polishes the preparation method of coating plaids, it is characterized in that: comprise following concrete technology step:
(1) plaids are woven:
Select at warp-wise 40S that full combed cotton is produced, broadwise 21S and 12S selects the anti-yarn of ring to produce, be woven into plaids;
(2) dye:
The plaids (1) step be woven into adopt long vehicle activity/intellectual circle to carry out dyeing process;
(3) coating:
Plaids after (2) step process are first coated with acrylic resin transparent adhesive tape at least one times, then carry out press polish process, to plaids being embrocated bright band mill base material at least twice after press polish;
(4) wash in advance:
Adopt regular industrial water to wash in advance the plaids after (3) step coating process, wash post-drying in advance;
(5) WATER REPELLENT TREATMENT:
Plaids after (4) step being washed in advance import and fill C6 waterproofing agent or add the tank of bleeding agent without fluoro water proofing agent, after folder rod, then dry in an oven, finally go out the cotton band look that cloth clot obtains environment-friendly waterproof and polish coating plaids.
3. the cotton band look of a kind of environment-friendly waterproof according to claim 2 polishes the preparation method of coating plaids, it is characterized in that: its thread count of plaids be woven in described (1) step is 135-155 piece/inch of * 65-85 piece/inch.
4. the cotton band look of a kind of environment-friendly waterproof according to claim 2 polishes the preparation method of coating plaids, it is characterized in that: in described (3) step, plaids are coated with the speed of a motor vehicle of acrylic resin transparent adhesive tape is 35-45 m/min, then dry, the temperature of plaids fabric oven dry is in an oven 140 DEG C-160 DEG C, and the time is 30-45 second; In described (3) step, in press polish processing procedure, temperature is 160 DEG C-180 DEG C, pressure is 40-70 ton.
5. the cotton band look of a kind of environment-friendly waterproof according to claim 2 polishes the preparation method of coating plaids, it is characterized in that: the water temperature of washing in advance in described (4) step is 40 DEG C-60 DEG C, speed is 15-25 m/min, pre-washing post-drying, bake out temperature is 120 DEG C-150 DEG C, and drying time is 30-50 second.
6. the cotton band look of a kind of environment-friendly waterproof according to claim 2 polishes the preparation method of coating plaids, it is characterized in that: in described (5) step, the concrete technology of WATER REPELLENT TREATMENT is:
A) first by C6 waterproofing agent or without fluoro water proofing agent and bleeding agent is deployed pours in tank;
B) baking oven is warming up to 150 DEG C-180 DEG C;
C) the folder rod of machine is wrapped calico;
D) then plaids imported tank, after folder rod, then enter baking oven, the speed of a motor vehicle entering baking oven is 7-10 m/min;
E) finally go out the cotton band look that cloth clot obtains environment-friendly waterproof and polish coating plaids.
7. the preparation method of coating plaids is polished according to the cotton band look of the arbitrary described a kind of environment-friendly waterproof of claim 1,2 or 6, it is characterized in that: the composition of described C6 waterproofing agent is the water of mass fraction 30%-40% alkyl combined polymerization product and mass fraction 60%-70%, the consumption of described C6 waterproofing agent is 60-100 grams per liter.
8. the preparation method of coating plaids is polished according to the cotton band look of the arbitrary described a kind of environment-friendly waterproof of claim 1,2 or 6, it is characterized in that: described is the mixture of mass fraction 20%-30% modified fat compound and wax dispersions and the water of mass fraction 70%-80% without fluoro water proofing agent composition, and the described consumption without fluoro water proofing agent is 70-110 grams per liter.
9. the preparation method of coating plaids is polished according to the cotton band look of the arbitrary described a kind of environment-friendly waterproof of claim 1,2 or 6, it is characterized in that: the composition of described bleeding agent is the aliphatic ethanol of mass fraction 5%-15% and the water of mass fraction 85%-95%, and the consumption of described bleeding agent is 5-20 grams per liter.
10. the cotton band look of a kind of environment-friendly waterproof according to claim 6 polishes the preparation method of coating plaids, it is characterized in that: in described d) step plaids import tank, after folder rod plaids with the mass fraction of waterproofing agent be 50%-80%.