CN105368354A - Phenolic aldehyde resin derivative glue composition - Google Patents
Phenolic aldehyde resin derivative glue composition Download PDFInfo
- Publication number
- CN105368354A CN105368354A CN201510829632.3A CN201510829632A CN105368354A CN 105368354 A CN105368354 A CN 105368354A CN 201510829632 A CN201510829632 A CN 201510829632A CN 105368354 A CN105368354 A CN 105368354A
- Authority
- CN
- China
- Prior art keywords
- resin derivative
- formaldehyde
- phenol resin
- powder
- glue composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A phenolic aldehyde resin derivative glue composition is prepared from the following raw materials in proportion: a phenolic aldehyde resin derivative, heparin, a metal powder, chondroitin sulfate, and an Mg(OH)2 powder. The bonding performance of the phenolic aldehyde resin derivative is larger, so the heparin and the metal powder are added in the formula to be used as fillers, and the prepared glue composition has higher bonding performance.
Description
Technical field
The present invention relates to a kind of Tackifier materials, particularly a kind of formaldehyde-phenol resin derivative glue composition.
Background technology
Adhesive composition is widely used in various industry, in prior art, formaldehyde-phenol resin derivative glue composition is usually used in the various material that bonds, because the bonding strength of formaldehyde-phenol resin derivative is relatively not high, loosening appears in the formaldehyde-phenol resin derivative bonding often making those duration of service longer.Add heparin and metal-powder as filler, then can change this present situation.
Summary of the invention
The technical problem to be solved in the present invention is for the deficiencies in the prior art, proposes a kind of formaldehyde-phenol resin derivative glue composition of resistance to adhesive-type.
A kind of formaldehyde-phenol resin derivative glue composition, it is made up of the raw material of following weight part,
Formaldehyde-phenol resin derivative 100
Heparin 3 ~ 8
Metal-powder 2 ~ 5
Chondroitin sulfate 0.1 ~ 0.3
Mg (OH) 2 powder 0.1 ~ 0.3.
The tackiness of formaldehyde-phenol resin derivative is also comparatively large, so add heparin and metal-powder in formula of the present invention as filler, and the formaldehyde-phenol resin derivative glue composition made has higher cement properties.
Embodiment
Record see following specific embodiment:
Embodiment 1
A kind of formaldehyde-phenol resin derivative glue composition, it is made up of the raw material of following weight part,
Formaldehyde-phenol resin derivative 100
Heparin 3
Metal-powder 2
Chondroitin sulfate 0.1
Mg (OH) 2 powder 0.1.
Embodiment 2
A kind of formaldehyde-phenol resin derivative glue composition, it is made up of the raw material of following weight part,
Formaldehyde-phenol resin derivative 100
Heparin 4
Metal-powder 3
Chondroitin sulfate 0.2
Mg (OH) 2 powder 0.2.
Embodiment 3
A kind of formaldehyde-phenol resin derivative glue composition, it is made up of the raw material of following weight part,
Formaldehyde-phenol resin derivative 100
Heparin 4
Metal-powder 3
Chondroitin sulfate 0.2
Mg (OH) 2 powder 0.2.
Embodiment 4
A kind of formaldehyde-phenol resin derivative glue composition, it is made up of the raw material of following weight part,
Formaldehyde-phenol resin derivative 100
Heparin 8
Metal-powder 5
Chondroitin sulfate 0.3
Mg (OH) 2 powder 0.3.
Claims (5)
1. a formaldehyde-phenol resin derivative glue composition, is made up of the raw material of following weight part,
Formaldehyde-phenol resin derivative 100
Heparin 3 ~ 8
Metal-powder 2 ~ 5
Chondroitin sulfate 0.1 ~ 0.3
Mg (OH) 2 powder 0.1 ~ 0.3.
2. a formaldehyde-phenol resin derivative glue composition, is made up of the raw material of following weight part,
Formaldehyde-phenol resin derivative 100
Heparin 3
Metal-powder 2
Chondroitin sulfate 0.1
Mg (OH) 2 powder 0.1.
3. a formaldehyde-phenol resin derivative glue composition, is made up of the raw material of following weight part,
Formaldehyde-phenol resin derivative 100
Heparin 4
Metal-powder 3
Chondroitin sulfate 0.2
Mg (OH) 2 powder 0.2.
4. a formaldehyde-phenol resin derivative glue composition, is made up of the raw material of following weight part,
Formaldehyde-phenol resin derivative 100
Heparin 6
Metal-powder 4
Chondroitin sulfate 0.2
Mg (OH) 2 powder 0.2.
5. a formaldehyde-phenol resin derivative glue composition, is made up of the raw material of following weight part,
Formaldehyde-phenol resin derivative 100
Heparin 8
Metal-powder 5
Chondroitin sulfate 0.3
Mg (OH) 2 powder 0.3.