CN105365291A - Polymer functional nonwoven fabric - Google Patents
Polymer functional nonwoven fabric Download PDFInfo
- Publication number
- CN105365291A CN105365291A CN201510841948.4A CN201510841948A CN105365291A CN 105365291 A CN105365291 A CN 105365291A CN 201510841948 A CN201510841948 A CN 201510841948A CN 105365291 A CN105365291 A CN 105365291A
- Authority
- CN
- China
- Prior art keywords
- layer
- woven fabrics
- magnetic fibre
- bamboo carbon
- conveyer belt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention provides a polymer functional nonwoven fabric. The nonwoven fabric comprises a flax fiber layer, an upper polypropylene layer, and a bamboo charcoal magnetic fiber layer, wherein the flax fiber layer is located between the upper polypropylene layer and the bamboo charcoal magnetic fiber layer, a lower polypropylene layer is arranged below the bamboo charcoal magnetic fiber layer, and a nanometer titania photocatalyst layer is arranged above the upper polypropylene layer. The nonwoven fabric provided by the present invention uses the function of magnetic fiber that far-infrared rays can be released, so that microcirculation of the human body can be effectively improved, the pH value of the human body can be adjusted, electrostatic discharge of the human body can be released, and a healthcare effect is achieved to a certain extent. The structure of novel bamboo charcoal magnetic fiber layer has the advantages of high strength, light weight and the like, the microcirculation is improved, and the small blood vessels are opened. The nonwoven fabric has the functions of beautifying the skin, reducing the fat, preventing the skin pruritus of the elder, sterilizing and protecting the skin, and has air permeability and moisture retainability.
Description
Technical field
The present invention relates to a kind of non-woven fabrics, particularly a kind of high molecular functional non-woven fabrics.
Background technology
Non-woven fabrics is at medical supplies, and large-scale application has been carried out in the fields such as medicine equipment.But the easy balling-up of non-woven fabrics common in the market, in use procedure, antistatic effect is not enough.Fibrage in general non-woven fabrics does not possess yet and effectively improves microcirculation in human body, regulates human body acid-base value, guides the Electro-static Driven Comb of human body, does not possess obvious sterilizing skin beautifying health-care effect; And common non-woven fabric due to its insufficient strength, easily balling-up, gas permeability not, fast and efficient absorbent, can not can not be used for the high-end fields such as medical as desirable cloth.
Summary of the invention
The object of the invention is to provide a kind of high molecular functional non-woven fabrics, to solve, non-woven fabrics antistatic effect in prior art is poor, easily balling-up, poor air permeability, can not fast and the problem such as efficient absorbent, insufficient strength, and realize sterilizing skin beautifying effect and prevent the health-care effect of pruitus.
For solving the problem, the invention provides following technical scheme:
A kind of high molecular functional non-woven fabrics, it is characterized in that this non-woven fabrics comprises flax fiber layer, upper polypropylene layer, bamboo carbon magnetic fibre layer, described flax fiber layer is between upper polypropylene layer and bamboo carbon magnetic fibre layer, be provided with lower polypropylene layer below described bamboo carbon magnetic fibre layer, above described upper polypropylene layer, be also provided with nano-titania photocatalyst layer.
As preferably, described bamboo carbon magnetic fibre layer is interweaved is formed by red polyster fibre far away, bamboo charcoal polyester fiber, magnetic fibre, wherein red polyster fibre far away is warp, and after bamboo charcoal polyester fiber, magnetic fibre plying, formation parallel and warp knitting form bamboo carbon magnetic fibre layer.
As preferably, between described flax fiber layer and bamboo carbon magnetic fibre layer, be provided with open-work aluminum film layer.
As preferably, under described lower polypropylene layer, be compounded with the skin-friendly layer of mulberry silk and silver-colored fiber blend.
Present invention utilizes the function that magnetic fibre can be releasing far infrared, effectively can improve microcirculation in human body, regulate human body acid-base value, guide the Electro-static Driven Comb of human body, play the function of health care to a certain extent.Novel bamboo carbon magnetic fibre Rotating fields has the advantages such as intensity is large, lightweight, can improve microcirculation, dredge the function of thin vessels.Skin makeup, fat reducing, prevention the elderly skin itching, sterilizing skin-protective, air permeable humidity retaining.Nano-titania photocatalyst layer can prevent bacterium, viral invasion and grow; The powerful adsorption capacity of bamboo carbon fibre, can play the effect of effective sterilization, deodorizing.The present invention's application speciality polymer material makes, and not easily balling-up, can be widely used in the making of high-grade medical accessory, medical garment or high-grade household articles.
Accompanying drawing explanation
Fig. 1 is the structural representation of the embodiment of the present invention 1;
Fig. 2 is the structural representation of the embodiment of the present invention 2;
Fig. 3 is the structural representation of the embodiment of the present invention 3;
Fig. 4 is bamboo carbon magnetic fibre Rotating fields schematic diagram of the present invention;
Fig. 5 is production line schematic diagram of the present invention.
Detailed description of the invention
Below in conjunction with the drawings and specific embodiments, the invention will be further described:
Embodiment 1: shown in composition graphs 1, this high molecular functional non-woven fabrics, comprise flax fiber layer 2 and upper polypropylene layer 3 and lower polypropylene layer 6, flax fiber layer 2 is between upper polypropylene layer 3 and lower polypropylene layer 6, bamboo carbon magnetic fibre layer 5 is set between flax fiber layer 2 and lower polypropylene layer 6, upper polypropylene layer 3 is also provided with nano-titania photocatalyst layer 1.
As shown in Figure 4, bamboo carbon magnetic fibre layer 5 is interweaved is formed by red polyster fibre 51 far away, bamboo charcoal polyester fiber 52, magnetic fibre 52.Wherein red polyster fibre 51 far away is warp, and bamboo charcoal polyester fiber 52, magnetic fibre 53 form parallel after pooling capital and warp knitting forms bamboo carbon magnetic fibre layer 5.
Manufacture method: 1. weave bamboo carbon magnetic fibre layer 5 in advance, then flax fiber layer 2 and bamboo carbon magnetic fibre layer 5 are compounded to form grey cloth, then first level that is placed on by grey cloth is held on net conveyer belt 28, makes bamboo carbon magnetic fibre layer 5 down;
2. adopt polypropylene (PP) particulate material to be raw material, extrude through screw extruder high-temperature fusion, by melt spraying non-woven fabrics shower nozzle 10 die head spray silk, be sprayed on flax fiber layer 2, polypropylene layer 3 in formation;
3. grey cloth holds net conveyer belt 12 coiling through the second level, makes bamboo carbon magnetic fibre layer 5 upward, and another screw extruder sprays silk, air drawing by spun-bonded non-woven fabrics shower nozzle 25, is sprayed on the lower polypropylene layer 6 of formation on bamboo carbon magnetic fibre layer 5;
4. grey cloth is after vertically holding net conveyer belt 11 and the 3rd level and holding net conveyer belt 22 coiling, upper polypropylene layer 3 upward, through nano titanium oxide shower nozzle 23, be sprayed on the upper polypropylene layer 3 of grey cloth containing nano titanium oxide liquid, then form photocatalyst layer 1 after baker 210;
Manufacturing equipment: the device making above-mentioned cloth comprises the first level and holds net conveyer belt 28, described holding above net conveyer belt 28 is provided with melt spraying non-woven fabrics shower nozzle 10, be provided with the second level above the end holding net conveyer belt 28 in the first level and hold net conveyer belt 12, be provided with in the left side that the second level holds net conveyer belt 12 and vertically hold net conveyer belt 11, hold on net conveyer belt 12 in the second level and be provided with spun-bonded non-woven fabrics shower nozzle 25, vertically hold and be provided with the 3rd level on the right side of net conveyer belt 11 upper end and hold net conveyer belt 22, hold on net conveyer belt 22 in the 3rd level and be respectively equipped with nano titanium oxide shower nozzle 23 and baker 210.
Described first level is held bottom net conveyer belt 28 and is provided with first negative pressure trough 31 corresponding with melt spraying non-woven fabrics shower nozzle 10, hold bottom net conveyer belt 12 in the second level and be provided with second negative pressure trough corresponding with spun-bonded non-woven fabrics shower nozzle 25, described first negative pressure trough, the second negative pressure trough are connected with air exhauster 29 respectively.
In order to verify effect of the present invention, the compound nonwoven cloth prepare above-mentioned detailed description of the invention and existing non-woven fabrics carry out contrast test, and its result is as shown in table 1.
Embodiment 2: shown in composition graphs 2, as different from Example 1: this is antibacterial, antistatic high-performance non-woven fabrics, is provided with open-work aluminum film layer 4 between flax fiber layer 2 and bamboo carbon magnetic fibre layer 5.
Manufacture method: 1. weave bamboo carbon magnetic fibre layer 5 in advance, putting into vacuum aluminum-plating machine carries out vacuum aluminum-coated to bamboo carbon magnetic fibre layer, by adding express delivery aluminium speed, reducing evaporation boat electric current, form the open-work aluminum film layer 4 of band hole, then flax fiber layer 2 and open-work aluminum film layer 4, bamboo carbon magnetic fibre layer 5 are compounded to form grey cloth, first level that is placed on by grey cloth is again held on net conveyer belt 28, makes bamboo carbon magnetic fibre layer 5 down;
2. adopt polypropylene (PP) particulate material to be raw material, extrude through screw extruder high-temperature fusion, by melt spraying non-woven fabrics shower nozzle 10 die head spray silk, be sprayed on flax fiber layer 2, polypropylene layer 3 in formation;
3. grey cloth holds net conveyer belt 12 coiling through the second level, makes bamboo carbon magnetic fibre layer 2 upward, and another screw extruder sprays silk, air drawing by spun-bonded non-woven fabrics shower nozzle 25, is sprayed on the lower polypropylene layer 6 of formation on bamboo carbon magnetic fibre layer 5;
4. grey cloth is after vertically holding net conveyer belt 11 and the 3rd level and holding net conveyer belt 22 coiling, upper polypropylene layer 3 upward, through nano titanium oxide shower nozzle 23, be sprayed on the upper polypropylene layer 3 of grey cloth containing nano titanium oxide liquid, then form photocatalyst layer 1 after baker 210.
Manufacturing equipment: the device making above-mentioned cloth comprises the first level and holds net conveyer belt 28, described holding above net conveyer belt 28 is provided with melt spraying non-woven fabrics shower nozzle 10, be provided with the second level above the end holding net conveyer belt 28 in the first level and hold net conveyer belt 12, be provided with in the left side that the second level holds net conveyer belt 12 and vertically hold net conveyer belt 11, hold on net conveyer belt 12 in the second level and be provided with spun-bonded non-woven fabrics shower nozzle 25, vertically hold and be provided with the 3rd level on the right side of net conveyer belt 11 upper end and hold net conveyer belt 22, hold on net conveyer belt 22 in the 3rd level and be respectively equipped with nano titanium oxide shower nozzle 23 and baker 210.
Described first level is held bottom net conveyer belt 28 and is provided with first negative pressure trough 31 corresponding with melt spraying non-woven fabrics shower nozzle 10, hold bottom net conveyer belt 12 in the second level and be provided with second negative pressure trough corresponding with spun-bonded non-woven fabrics shower nozzle 25, described first negative pressure trough, the second negative pressure trough are connected with air exhauster 29 respectively.
In order to verify effect of the present invention, the compound nonwoven cloth prepare above-mentioned detailed description of the invention and existing non-woven fabrics carry out contrast test, and its result is as shown in table 1.
Table 2 non-woven fabrics contrast test data:
Can be found by contrast experiment's data of table 2, by the non-woven fabrics after this manufacture method compound, its hot strength is obtained for and significantly improves.Bamboo carbon magnetic fibre layer 5 can be releasing far infrared function, effectively can improve microcirculation in human body, regulate human body acid-base value, guide the Electro-static Driven Comb of human body, create the health-care effect of significant sterilizing skin beautifying effect and prevention pruitus.Magnetic fibre not only has that anti-inflammatory is anti-swollen, step-down, improve the curative effect such as blood viscosity and microcirculation, and comfortable and easy to wear.
Embodiment 3: shown in composition graphs 3, as different from Example 1: lower polypropylene layer is compounded with the skin-friendly layer of mulberry silk and silver-colored fiber blend for 6 times.
Manufacture method: 1. weave bamboo carbon magnetic fibre layer 5 in advance, then flax fiber layer 2 and bamboo carbon magnetic fibre layer 5 are compounded to form grey cloth, then first level that is placed on by grey cloth is held on net conveyer belt 28, makes bamboo carbon magnetic fibre layer 5 down;
2. adopt polypropylene (PP) particulate material to be raw material, extrude through screw extruder high-temperature fusion, by melt spraying non-woven fabrics shower nozzle 10 die head spray silk, be sprayed on flax fiber layer 2, polypropylene layer 3 in formation;
3. grey cloth holds net conveyer belt 30 coiling through the second level, makes bamboo carbon magnetic fibre layer 5 upward, and another screw extruder sprays silk, air drawing by spun-bonded non-woven fabrics shower nozzle 25, is sprayed on the lower polypropylene layer 6 of formation on bamboo carbon magnetic fibre layer 5; Lower polypropylene layer 6, through pro-skin fabric set composite, is provided with the pro-skin fabric composite roll 24 by mulberry silk and silver-colored fiber blend in pro-skin fabric set composite, form skin-friendly layer 7.
4. grey cloth is after vertically holding net conveyer belt 11 and the 3rd level and holding net conveyer belt 22 coiling, upper polypropylene layer 3 upward, through nano titanium oxide shower nozzle 23, be sprayed on the upper polypropylene layer 3 of grey cloth containing nano titanium oxide liquid, then form photocatalyst layer 1 after baker 210;
Manufacturing equipment: the device making above-mentioned cloth comprises the first level and holds net conveyer belt 28, described holding above net conveyer belt 28 is provided with melt spraying non-woven fabrics shower nozzle 10, be provided with the second level above the end holding net conveyer belt 28 in the first level and hold net conveyer belt 12, be provided with in the left side that the second level holds net conveyer belt 12 and vertically hold net conveyer belt 11, hold on net conveyer belt 12 in the second level and be provided with spun-bonded non-woven fabrics shower nozzle 25, pro-skin fabric composite roll 24 is provided with on the left of spun-bonded non-woven fabrics shower nozzle 25, vertically hold and be provided with the 3rd level on the right side of net conveyer belt 11 upper end and hold net conveyer belt 22, hold on net conveyer belt 22 in the 3rd level and be provided with nano titanium oxide shower nozzle 23 and baker 210 successively.
Described first level is held bottom net conveyer belt 28 and is provided with first negative pressure trough 31 corresponding with melt spraying non-woven fabrics shower nozzle 10, hold bottom net conveyer belt 12 in the second level and be provided with second negative pressure trough corresponding with spun-bonded non-woven fabrics shower nozzle 25, described first negative pressure trough, the second negative pressure trough are connected with air exhauster 29 respectively.
In order to verify effect of the present invention, the compound nonwoven cloth prepare above-mentioned detailed description of the invention and existing non-woven fabrics carry out contrast test, and its result is as shown in table 1.
Table 3 non-woven fabrics contrast test data:
By table 1,2, contrast experiment's data of 3 can find, by the non-woven fabrics after this manufacture method compound, its hot strength is obtained for and significantly improves.Bamboo carbon magnetic fibre layer 5 can be releasing far infrared function, effectively can improve microcirculation in human body, regulate human body acid-base value, guide the Electro-static Driven Comb of human body, create the health-care effect of significant sterilizing skin beautifying effect and prevention pruitus.Magnetic fibre not only has that anti-inflammatory is anti-swollen, step-down, improve the curative effect such as blood viscosity and microcirculation, and comfortable and easy to wear.
Claims (4)
1. a high molecular functional non-woven fabrics, it is characterized in that this non-woven fabrics comprises flax fiber layer, upper polypropylene layer, bamboo carbon magnetic fibre layer, described flax fiber layer is between upper polypropylene layer and bamboo carbon magnetic fibre layer, be provided with lower polypropylene layer below described bamboo carbon magnetic fibre layer, above described upper polypropylene layer, be also provided with nano-titania photocatalyst layer.
2. a kind of high molecular functional non-woven fabrics according to claim 1, it is characterized in that described bamboo carbon magnetic fibre layer is interweaved is formed by red polyster fibre far away, bamboo charcoal polyester fiber, magnetic fibre, wherein red polyster fibre far away is warp, and after bamboo charcoal polyester fiber, magnetic fibre plying, formation parallel and warp knitting form bamboo carbon magnetic fibre layer.
3. a kind of high molecular functional non-woven fabrics according to claim 1, is characterized in that being provided with open-work aluminum film layer between described flax fiber layer and bamboo carbon magnetic fibre layer.
4. a kind of high molecular functional non-woven fabrics according to claim 1, is compounded with the skin-friendly layer of mulberry silk and silver-colored fiber blend under it is characterized in that described lower polypropylene layer.