CN105350335A - Dyeing and finishing process for compound material - Google Patents
Dyeing and finishing process for compound material Download PDFInfo
- Publication number
- CN105350335A CN105350335A CN201510936370.0A CN201510936370A CN105350335A CN 105350335 A CN105350335 A CN 105350335A CN 201510936370 A CN201510936370 A CN 201510936370A CN 105350335 A CN105350335 A CN 105350335A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- parts
- weight
- dyeing
- dressing liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a dyeing and finishing process for a compound material. The process comprises the following steps: 1) preprocessing; 2) dyeing; 3) finishing: sequentially putting 1 to 2 parts by weight of vinyltrimethoxysilane, 1.4 parts by weight of 2-octyl-3(2H)-isothiazolone, 0.5 parts by weight of tebuconazole and 1.3 parts by weight of tetrabutyl titanate into 25 parts by mass of deionized water, and uniformly stirring; simultaneously putting 0.2 parts by weight of angelica dahurica, 0.9 parts by weight of 1,3,5-trihydroxyethyl isocyanurate, 1.1 parts by weight of sodium alcohol ether sulphate and 2.2 parts by weight of amino-modified silicone oil into the mixture, continuously stirring, till being fully uniformly mixed, so that finishing liquor is prepared; then enabling the compound material to be subjected to padding treatment in the finishing liquor, taking the compound material out, and drying at a constant temperature. By adopting the dyeing and finishing process for the compound material, the dyed and finished compound material has the excellent performances of being antibacterial, mildew-proof, mothproof, flame retardant and antistatic, and is strong in washability and soft in hand feel.
Description
Technical field
The present invention relates to the dyeing and finishing technology of composite material.
Background technology
Antibacterial, the mildew-resistant of existing fabric, mothproof, fire-retardant, antistatic, washing fastness all have much room for improvement, and feel is soft not.
Summary of the invention
The object of the present invention is to provide a kind of dyeing and finishing technology of composite material, the fabric after its dyeing and finishing has excellent antibacterial, mildew-resistant, mothproof, fire-retardant, antistatic property, and washability is strong, soft.
For achieving the above object, technical scheme of the present invention designs a kind of dyeing and finishing technology of composite material, comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 1 ~ 2 parts by weight of ethylene base trimethoxy silane, 1.4 weight portion 2-n-octyl-isothiazolin ketone, 0.5 weight portion Tebuconazole, 1.3 weight portion metatitanic acid four fourths are dropped in 25 parts by mass deionized waters successively, stirs; Drop into the 0.2 weight portion root of Dahurain angelica, 0.9 weight portion isocyanuric acid 1,3,5-tri-hydroxyl ethyl ester, 1.1 parts by weight of fatty alcohol polyethenoxy ether sodium sulfates, 2.2 weight portion amido silicon oils more simultaneously, continue to stir, to fully mixing, obtained dressing liquid; Again fabric is padded process in dressing liquid, constant temperature drying after taking out.
Preferably, the dyeing and finishing technology of composite material, comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 1 parts by weight of ethylene base trimethoxy silane, 1.4 weight portion 2-n-octyl-isothiazolin ketone, 0.5 weight portion Tebuconazole, 1.3 weight portion metatitanic acid four fourths are dropped in 25 parts by mass deionized waters successively, stirs; Drop into the 0.2 weight portion root of Dahurain angelica, 0.9 weight portion isocyanuric acid 1,3,5-tri-hydroxyl ethyl ester, 1.1 parts by weight of fatty alcohol polyethenoxy ether sodium sulfates, 2.2 weight portion amido silicon oils more simultaneously, continue to stir, to fully mixing, obtained dressing liquid; Again fabric is padded process in dressing liquid, constant temperature drying after taking out.
Preferably, the dyeing and finishing technology of composite material, comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 2 parts by weight of ethylene base trimethoxy silanes, 1.4 weight portion 2-n-octyl-isothiazolin ketone, 0.5 weight portion Tebuconazole, 1.3 weight portion metatitanic acid four fourths are dropped in 25 parts by mass deionized waters successively, stirs; Drop into the 0.2 weight portion root of Dahurain angelica, 0.9 weight portion isocyanuric acid 1,3,5-tri-hydroxyl ethyl ester, 1.1 parts by weight of fatty alcohol polyethenoxy ether sodium sulfates, 2.2 weight portion amido silicon oils more simultaneously, continue to stir, to fully mixing, obtained dressing liquid; Again fabric is padded process in dressing liquid, constant temperature drying after taking out.
Advantage of the present invention and beneficial effect are: the dyeing and finishing technology providing a kind of composite material, and the fabric after its dyeing and finishing has excellent antibacterial, mildew-resistant, mothproof, fire-retardant, antistatic property, and washability is strong, soft.
Detailed description of the invention
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A dyeing and finishing technology for composite material, comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 1 ~ 2 parts by weight of ethylene base trimethoxy silane, 1.4 weight portion 2-n-octyl-isothiazolin ketone, 0.5 weight portion Tebuconazole, 1.3 weight portion metatitanic acid four fourths are dropped in 25 parts by mass deionized waters successively, stirs; Drop into the 0.2 weight portion root of Dahurain angelica, 0.9 weight portion isocyanuric acid 1,3,5-tri-hydroxyl ethyl ester, 1.1 parts by weight of fatty alcohol polyethenoxy ether sodium sulfates, 2.2 weight portion amido silicon oils more simultaneously, continue to stir, to fully mixing, obtained dressing liquid; Again fabric is padded process in dressing liquid, constant temperature drying after taking out.
Embodiment 2
The dyeing and finishing technology of composite material, comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 1 parts by weight of ethylene base trimethoxy silane, 1.4 weight portion 2-n-octyl-isothiazolin ketone, 0.5 weight portion Tebuconazole, 1.3 weight portion metatitanic acid four fourths are dropped in 25 parts by mass deionized waters successively, stirs; Drop into the 0.2 weight portion root of Dahurain angelica, 0.9 weight portion isocyanuric acid 1,3,5-tri-hydroxyl ethyl ester, 1.1 parts by weight of fatty alcohol polyethenoxy ether sodium sulfates, 2.2 weight portion amido silicon oils more simultaneously, continue to stir, to fully mixing, obtained dressing liquid; Again fabric is padded process in dressing liquid, constant temperature drying after taking out.
Embodiment 3
The dyeing and finishing technology of composite material, comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 2 parts by weight of ethylene base trimethoxy silanes, 1.4 weight portion 2-n-octyl-isothiazolin ketone, 0.5 weight portion Tebuconazole, 1.3 weight portion metatitanic acid four fourths are dropped in 25 parts by mass deionized waters successively, stirs; Drop into the 0.2 weight portion root of Dahurain angelica, 0.9 weight portion isocyanuric acid 1,3,5-tri-hydroxyl ethyl ester, 1.1 parts by weight of fatty alcohol polyethenoxy ether sodium sulfates, 2.2 weight portion amido silicon oils more simultaneously, continue to stir, to fully mixing, obtained dressing liquid; Again fabric is padded process in dressing liquid, constant temperature drying after taking out.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (3)
1. the dyeing and finishing technology of composite material, is characterized in that, comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 1 ~ 2 parts by weight of ethylene base trimethoxy silane, 1.4 weight portion 2-n-octyl-isothiazolin ketone, 0.5 weight portion Tebuconazole, 1.3 weight portion metatitanic acid four fourths are dropped in 25 parts by mass deionized waters successively, stirs; Drop into the 0.2 weight portion root of Dahurain angelica, 0.9 weight portion isocyanuric acid 1,3,5-tri-hydroxyl ethyl ester, 1.1 parts by weight of fatty alcohol polyethenoxy ether sodium sulfates, 2.2 weight portion amido silicon oils more simultaneously, continue to stir, to fully mixing, obtained dressing liquid; Again fabric is padded process in dressing liquid, constant temperature drying after taking out.
2. the dyeing and finishing technology of composite material according to claim 1, is characterized in that, comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 1 parts by weight of ethylene base trimethoxy silane, 1.4 weight portion 2-n-octyl-isothiazolin ketone, 0.5 weight portion Tebuconazole, 1.3 weight portion metatitanic acid four fourths are dropped in 25 parts by mass deionized waters successively, stirs; Drop into the 0.2 weight portion root of Dahurain angelica, 0.9 weight portion isocyanuric acid 1,3,5-tri-hydroxyl ethyl ester, 1.1 parts by weight of fatty alcohol polyethenoxy ether sodium sulfates, 2.2 weight portion amido silicon oils more simultaneously, continue to stir, to fully mixing, obtained dressing liquid; Again fabric is padded process in dressing liquid, constant temperature drying after taking out.
3. the dyeing and finishing technology of composite material according to claim 1, is characterized in that, comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 2 parts by weight of ethylene base trimethoxy silanes, 1.4 weight portion 2-n-octyl-isothiazolin ketone, 0.5 weight portion Tebuconazole, 1.3 weight portion metatitanic acid four fourths are dropped in 25 parts by mass deionized waters successively, stirs; Drop into the 0.2 weight portion root of Dahurain angelica, 0.9 weight portion isocyanuric acid 1,3,5-tri-hydroxyl ethyl ester, 1.1 parts by weight of fatty alcohol polyethenoxy ether sodium sulfates, 2.2 weight portion amido silicon oils more simultaneously, continue to stir, to fully mixing, obtained dressing liquid; Again fabric is padded process in dressing liquid, constant temperature drying after taking out.