CN105484038A - Composite fabric dyeing and finishing process - Google Patents
Composite fabric dyeing and finishing process Download PDFInfo
- Publication number
- CN105484038A CN105484038A CN201510945076.6A CN201510945076A CN105484038A CN 105484038 A CN105484038 A CN 105484038A CN 201510945076 A CN201510945076 A CN 201510945076A CN 105484038 A CN105484038 A CN 105484038A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- parts
- weight
- dyeing
- dressing liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a composite fabric dyeing and finishing process. The process comprises the steps of 1, pretreatment; 2, dyeing; 3, finishing, wherein 1-2 parts by weight of Gumacabic powder, 0.9 part by weight of fatty alcohol-polyoxyethylene ether sodium sulfate, 1.1 parts by weight of lavender essence and 1.4 parts by weight of olive oil macrogol ester are placed in 24 parts by mass of deionized water in sequence and evenly stirred, 0.7 part by weight of camphor powder, 0.9 part by weight of zinc hydroxystannate, 1.2 parts by weight of zinc acetate and 2.3 parts by weight of triethanolamine esterquats are added at the same time for continuous stirring till the substances are fully and evenly mixed, so that finishing liquid is obtained, then pad-rolling is conducted on fabric in the finishing liquid, and finally the fabric is taken out to be dried at a constant temperature. The fabric dyed and finished by means of the process has excellent mothproof performance, moldproof performance, anti-microbial performance, inflaming retarding performance and anti-static performance, and has high washability and soft handfeel.
Description
Technical field
The present invention relates to the dyeing and finishing technology of composite material-feeding.
Background technology
Mothproof, the mildew-resistant of existing cloth, antibacterial, fire-retardant, antistatic, washing fastness all have much room for improvement, and feel is soft not.
Summary of the invention
The object of the present invention is to provide a kind of dyeing and finishing technology of composite material-feeding, the cloth after its dyeing and finishing has excellent mothproof, mildew-resistant, antibacterial, fire-retardant, antistatic property, and washability is strong, soft.
For achieving the above object, technical scheme of the present invention designs a kind of dyeing and finishing technology of composite material-feeding, comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 1 ~ 2 weight portion gum arabic powder, 0.9 parts by weight of fatty alcohol polyethenoxy ether sodium sulfate, 1.1 weight portion lavender Essences, 1.4 wt parts of olive oil macrogol esters are dropped in 24 parts by mass deionized waters successively, stirs; Drop into 0.7 weight portion camphor powder, 0.9 weight portion zinc hydroxyl stannate, 1.2 weight portion zinc acetates, 2.3 weight portion triethanolamine ester based quaternary ammonium salts more simultaneously, continue to stir, to fully mixing, obtained dressing liquid; Again cloth is padded process in dressing liquid, constant temperature drying after taking out.
Preferably, the dyeing and finishing technology of composite material-feeding, comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 1 weight portion gum arabic powder, 0.9 parts by weight of fatty alcohol polyethenoxy ether sodium sulfate, 1.1 weight portion lavender Essences, 1.4 wt parts of olive oil macrogol esters are dropped in 24 parts by mass deionized waters successively, stirs; Drop into 0.7 weight portion camphor powder, 0.9 weight portion zinc hydroxyl stannate, 1.2 weight portion zinc acetates, 2.3 weight portion triethanolamine ester based quaternary ammonium salts more simultaneously, continue to stir, to fully mixing, obtained dressing liquid; Again cloth is padded process in dressing liquid, constant temperature drying after taking out.
Preferably, the dyeing and finishing technology of composite material-feeding, comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 2 weight portion gum arabic powder, 0.9 parts by weight of fatty alcohol polyethenoxy ether sodium sulfate, 1.1 weight portion lavender Essences, 1.4 wt parts of olive oil macrogol esters are dropped in 24 parts by mass deionized waters successively, stirs; Drop into 0.7 weight portion camphor powder, 0.9 weight portion zinc hydroxyl stannate, 1.2 weight portion zinc acetates, 2.3 weight portion triethanolamine ester based quaternary ammonium salts more simultaneously, continue to stir, to fully mixing, obtained dressing liquid; Again cloth is padded process in dressing liquid, constant temperature drying after taking out.
Advantage of the present invention and beneficial effect are: the dyeing and finishing technology providing a kind of composite material-feeding, and the cloth after its dyeing and finishing has excellent mothproof, mildew-resistant, antibacterial, fire-retardant, antistatic property, and washability is strong, soft.
Detailed description of the invention
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A dyeing and finishing technology for composite material-feeding, comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 1 ~ 2 weight portion gum arabic powder, 0.9 parts by weight of fatty alcohol polyethenoxy ether sodium sulfate, 1.1 weight portion lavender Essences, 1.4 wt parts of olive oil macrogol esters are dropped in 24 parts by mass deionized waters successively, stirs; Drop into 0.7 weight portion camphor powder, 0.9 weight portion zinc hydroxyl stannate, 1.2 weight portion zinc acetates, 2.3 weight portion triethanolamine ester based quaternary ammonium salts more simultaneously, continue to stir, to fully mixing, obtained dressing liquid; Again cloth is padded process in dressing liquid, constant temperature drying after taking out.
Embodiment 2
The dyeing and finishing technology of composite material-feeding, comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 1 weight portion gum arabic powder, 0.9 parts by weight of fatty alcohol polyethenoxy ether sodium sulfate, 1.1 weight portion lavender Essences, 1.4 wt parts of olive oil macrogol esters are dropped in 24 parts by mass deionized waters successively, stirs; Drop into 0.7 weight portion camphor powder, 0.9 weight portion zinc hydroxyl stannate, 1.2 weight portion zinc acetates, 2.3 weight portion triethanolamine ester based quaternary ammonium salts more simultaneously, continue to stir, to fully mixing, obtained dressing liquid; Again cloth is padded process in dressing liquid, constant temperature drying after taking out.
Embodiment 3
The dyeing and finishing technology of composite material-feeding, comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 2 weight portion gum arabic powder, 0.9 parts by weight of fatty alcohol polyethenoxy ether sodium sulfate, 1.1 weight portion lavender Essences, 1.4 wt parts of olive oil macrogol esters are dropped in 24 parts by mass deionized waters successively, stirs; Drop into 0.7 weight portion camphor powder, 0.9 weight portion zinc hydroxyl stannate, 1.2 weight portion zinc acetates, 2.3 weight portion triethanolamine ester based quaternary ammonium salts more simultaneously, continue to stir, to fully mixing, obtained dressing liquid; Again cloth is padded process in dressing liquid, constant temperature drying after taking out.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (3)
1. the dyeing and finishing technology of composite material-feeding, is characterized in that, comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 1 ~ 2 weight portion gum arabic powder, 0.9 parts by weight of fatty alcohol polyethenoxy ether sodium sulfate, 1.1 weight portion lavender Essences, 1.4 wt parts of olive oil macrogol esters are dropped in 24 parts by mass deionized waters successively, stirs; Drop into 0.7 weight portion camphor powder, 0.9 weight portion zinc hydroxyl stannate, 1.2 weight portion zinc acetates, 2.3 weight portion triethanolamine ester based quaternary ammonium salts more simultaneously, continue to stir, to fully mixing, obtained dressing liquid; Again cloth is padded process in dressing liquid, constant temperature drying after taking out.
2. the dyeing and finishing technology of composite material-feeding according to claim 1, is characterized in that, comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 1 weight portion gum arabic powder, 0.9 parts by weight of fatty alcohol polyethenoxy ether sodium sulfate, 1.1 weight portion lavender Essences, 1.4 wt parts of olive oil macrogol esters are dropped in 24 parts by mass deionized waters successively, stirs; Drop into 0.7 weight portion camphor powder, 0.9 weight portion zinc hydroxyl stannate, 1.2 weight portion zinc acetates, 2.3 weight portion triethanolamine ester based quaternary ammonium salts more simultaneously, continue to stir, to fully mixing, obtained dressing liquid; Again cloth is padded process in dressing liquid, constant temperature drying after taking out.
3. the dyeing and finishing technology of composite material-feeding according to claim 1, is characterized in that, comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 2 weight portion gum arabic powder, 0.9 parts by weight of fatty alcohol polyethenoxy ether sodium sulfate, 1.1 weight portion lavender Essences, 1.4 wt parts of olive oil macrogol esters are dropped in 24 parts by mass deionized waters successively, stirs; Drop into 0.7 weight portion camphor powder, 0.9 weight portion zinc hydroxyl stannate, 1.2 weight portion zinc acetates, 2.3 weight portion triethanolamine ester based quaternary ammonium salts more simultaneously, continue to stir, to fully mixing, obtained dressing liquid; Again cloth is padded process in dressing liquid, constant temperature drying after taking out.