CN105350291A - 一种防静电性织物涂层整理用涂层材料 - Google Patents
一种防静电性织物涂层整理用涂层材料 Download PDFInfo
- Publication number
- CN105350291A CN105350291A CN201511013283.4A CN201511013283A CN105350291A CN 105350291 A CN105350291 A CN 105350291A CN 201511013283 A CN201511013283 A CN 201511013283A CN 105350291 A CN105350291 A CN 105350291A
- Authority
- CN
- China
- Prior art keywords
- parts
- calcium carbonate
- coating material
- static
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
一种防静电性织物涂层整理用涂层材料,其由以下重量份数的原料制成:丙烯酸乳液12-25份,天然胶乳6-11份,氧化聚丙烯酯2-4份,PS5-7份,碳酸钙粉体2-4份,钛酸酯偶联剂TMC-TTS0.5-1.2份,粘着力促进剂KH-5600.6-0.9份,石墨粉15-22份,闭孔膨胀珍珠岩15-24份,分散剂3-5份,增塑剂16-22份,紫外线吸收剂2-4份,碳酸钙5-10份,流平剂2-4份,羧基聚醚改性聚二甲基硅氧烷0.2-0.6份,热塑性聚氨酯粒料20-30份。本发明的有益效果是,本发明的防静电性织物涂层整理用涂层材料,具有保温、透气、防静电的功能,改进了防水透湿的效果,手感更好,弹性好。
Description
技术领域
本发明涉及一种防静电性织物涂层整理用涂层材料。
背景技术
纺织品涂层整理剂又称涂层胶,是一种均匀涂布于织物表面的高分子类化合物。它通过粘合作用在织物表面形成一层或多层薄膜,不仅能改善织物的外观和风格,而且能增加织物的功能。涂层整理的主要目的是改善织物的手感、外观和风格,赋予织物保温、抗菌、隔音等特殊功能。在我国,涂层加工技术对于橡胶、造纸等行业并不属新工艺,但在纺织印染工业中应用涂层技术,还只是近几年扩大发展起来的,所以还存在许多不足,涂层织物使用时有闷热感,舒适性差、而且保温效果差,不具有防静电效果,尤其静电给人们的生活带来很多的不便,所以涂层材料有待遇进一步提高,来完善性能满足使用需求。
发明内容
针对现有技术的不足,本发明要解决的问题是,提供一种防静电性织物涂层整理用涂层材料,具有保温、透气、防静电的功能,改进了防水透湿的效果,手感更好,弹性好。
为解决上述技术问题,本发明的技术方案是,一种防静电性织物涂层整理用涂层材料,其由以下重量份数的原料制成:
丙烯酸乳液12-25份,天然胶乳6-11份,氧化聚丙烯酯2-4份,PS5-7份,碳酸钙粉体2-4份,钛酸酯偶联剂TMC-TTS0.5-1.2份,粘着力促进剂KH-5600.6-0.9份,石墨粉15-22份,闭孔膨胀珍珠岩15-24份,分散剂3-5份,增塑剂16-22份,紫外线吸收剂2-4份,碳酸钙5-10份,流平剂2-4份,羧基聚醚改性聚二甲基硅氧烷0.2-0.6份,热塑性聚氨酯粒料20-30份。
优化的,一种防静电性织物涂层整理用涂层材料,其由以下重量份数的原料制成:
丙烯酸乳液18份,天然胶乳8.5份,氧化聚丙烯酯3份,PS6份,碳酸钙粉体3份,钛酸酯偶联剂TMC-TTS0.9份,粘着力促进剂KH-5600.7份,石墨粉19份,闭孔膨胀珍珠岩18份,分散剂4份,增塑剂19份,紫外线吸收剂3份,碳酸钙7.5份,流平剂3份,羧基聚醚改性聚二甲基硅氧烷0.4份,热塑性聚氨酯粒料25份。
本发明的有益效果是,本发明的防静电性织物涂层整理用涂层材料,具有保温、透气、防静电的功能,改进了防水透湿的效果,手感更好,弹性好。
具体实施方式
实施例1
一种防静电性织物涂层整理用涂层材料,其由以下重量份数的原料制成:
丙烯酸乳液12份,天然胶乳6份,氧化聚丙烯酯2份,PS5份,碳酸钙粉体2份,钛酸酯偶联剂TMC-TTS0.5份,粘着力促进剂KH-5600.6份,石墨粉15份,闭孔膨胀珍珠岩15份,分散剂3份,增塑剂16份,紫外线吸收剂2份,碳酸钙5份,流平剂2份,羧基聚醚改性聚二甲基硅氧烷0.2份,热塑性聚氨酯粒料20份。
实施例2
一种防静电性织物涂层整理用涂层材料,其由以下重量份数的原料制成:
丙烯酸乳液25份,天然胶乳11份,氧化聚丙烯酯4份,PS7份,碳酸钙粉体4份,钛酸酯偶联剂TMC-TTS1.2份,粘着力促进剂KH-5600.9份,石墨粉22份,闭孔膨胀珍珠岩24份,分散剂5份,增塑剂22份,紫外线吸收剂4份,碳酸钙10份,流平剂4份,羧基聚醚改性聚二甲基硅氧烷0.6份,热塑性聚氨酯粒料30份。
实施例3
一种防静电性织物涂层整理用涂层材料,其由以下重量份数的原料制成:
丙烯酸乳液18份,天然胶乳8.5份,氧化聚丙烯酯3份,PS6份,碳酸钙粉体3份,钛酸酯偶联剂TMC-TTS0.9份,粘着力促进剂KH-5600.7份,石墨粉19份,闭孔膨胀珍珠岩18份,分散剂4份,增塑剂19份,紫外线吸收剂3份,碳酸钙7.5份,流平剂3份,羧基聚醚改性聚二甲基硅氧烷0.4份,热塑性聚氨酯粒料25份。
Claims (2)
1.一种防静电性织物涂层整理用涂层材料,其特征在于:其由以下重量份数的原料制成:
丙烯酸乳液12-25份,天然胶乳6-11份,氧化聚丙烯酯2-4份,PS5-7份,碳酸钙粉体2-4份,钛酸酯偶联剂TMC-TTS0.5-1.2份,粘着力促进剂KH-5600.6-0.9份,石墨粉15-22份,闭孔膨胀珍珠岩15-24份,分散剂3-5份,增塑剂16-22份,紫外线吸收剂2-4份,碳酸钙5-10份,流平剂2-4份,羧基聚醚改性聚二甲基硅氧烷0.2-0.6份,热塑性聚氨酯粒料20-30份。
2.根据权利要求1所述的防静电性织物涂层整理用涂层材料,其特征在于:其由以下重量份数的原料制成:
丙烯酸乳液18份,天然胶乳8.5份,氧化聚丙烯酯3份,PS6份,碳酸钙粉体3份,钛酸酯偶联剂TMC-TTS0.9份,粘着力促进剂KH-5600.7份,石墨粉19份,闭孔膨胀珍珠岩18份,分散剂4份,增塑剂19份,紫外线吸收剂3份,碳酸钙7.5份,流平剂3份,羧基聚醚改性聚二甲基硅氧烷0.4份,热塑性聚氨酯粒料25份。