CN105349221A - Energy-saving and emission-reduction synergist for coal - Google Patents
Energy-saving and emission-reduction synergist for coal Download PDFInfo
- Publication number
- CN105349221A CN105349221A CN201510798959.9A CN201510798959A CN105349221A CN 105349221 A CN105349221 A CN 105349221A CN 201510798959 A CN201510798959 A CN 201510798959A CN 105349221 A CN105349221 A CN 105349221A
- Authority
- CN
- China
- Prior art keywords
- parts
- coal
- energy
- emission
- saving
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an energy-saving and emission-reduction synergist for coal. The synergist comprises the following materials by weight: 6-8 parts of yttrium oxide, 8-10 parts of manganese dioxide, 10-15 parts of ferrum dioxide, 10-15 parts of ferrous oxide, 3-5 parts of sodium carbonate, 3-5 parts of potassium nitrate, 2-6 parts of lignosulfonate, 4-10 parts of ammonium bicarbonate, 5-10 parts of potassium carbonate, 6-10 parts of urea, 3-5 parts of active carbons, 2-8 parts of diatomite, and 2-3 parts of activated alumina. The energy-saving and emission-reduction synergist for coal has a good desulfurization effect and a stable desulfurization product, and largely reduces pollutant emission.
Description
Technical field
The invention belongs to coal additive technical field, be specifically related to a kind of fire coal energy-saving emission-reducing synergistic agent.
Background technology
Coal resources occupy an important position in Chinese society Economic development, but continually developing and utilizing along with coal resources, and many new problems progressively highlight.Coal resources are Nonrenewable resources, and this just means that the exploitation along with coal is excavated, and coal resources also can reduce day by day.And on the other hand, because the utilization ratio of fire coal is relatively low, discharge pollutants, welding.Therefore, how to improve coal-fired utilization ratio, realizing energy-saving and emission-reduction is global problems, is also the topic that the whole world is paid close attention to jointly.In recent years, the problems such as in China's rapid development of economy process, Coal Energy Source utilization ratio is low, serious environment pollution became increasingly conspicuous, and the aggravation of contradictions of the deterioration of the ecological environment and Economic development, constrains China's sustain economic rapid and healthy to a great extent.
The interpolation of synergistic agent makes utilization ratio coal-fired at present be improved, and existing fire coal synergist majority adopts limestone desulfurization, but fire coal is in high-temp combustion, and desulfurization efficiency is low, and sulfur retention products easily decomposes, and effect is not very good.
Summary of the invention
The object of the invention is, in order to solve prior art Problems existing, to provide a kind of captured sulfur result good, the fire coal energy-saving emission-reducing synergistic agent that sulfur retention products is stable.
In order to achieve the above object, the invention provides following technical scheme:
A kind of fire coal energy-saving emission-reducing synergistic agent, comprises the raw material of following weight part: yttrium oxide 6-8 part, Manganse Dioxide 8-10 part, ferrous oxide 10-15 part, iron protoxide 10-15 part, sodium carbonate 3-5 part, saltpetre 3-5 part, sulfonated lignin 2-6 part, bicarbonate of ammonia 4-10 part, salt of wormwood 5-10 part, urea 6-10 part, gac 3-5 part, diatomite 2-8 part, activated alumina 2-3 part.
Preferably, described fire coal energy-saving emission-reducing synergistic agent, comprises the raw material of following weight part: yttrium oxide 7 parts, Manganse Dioxide 9 parts, ferrous oxide 11 parts, iron protoxide 13 parts, 4 parts, sodium carbonate, 5 parts, saltpetre, sulfonated lignin 5 parts, 6 parts, bicarbonate of ammonia, 8 parts, salt of wormwood, 8 parts, urea, gac 5 parts, 5 parts, diatomite, activated alumina 2 parts.
In such scheme, yttrium oxide, Manganse Dioxide are properties-correcting agent, and ferric oxide, iron protoxide are catalyzer, sodium carbonate, saltpetre are ignition dope, sulfonated lignin, bicarbonate of ammonia are solid sulphur auxiliary agent, and salt of wormwood, urea are denitrfying agent, and activated carbon, diatomite, activated alumina are sorbent material.During reaction, properties-correcting agent changes the coal-fired proterties when burning, and improves temperature of combustion, makes burning more abundant, completely; Provide the burning situation of hypoxemia in combustion processes, improve the volume parts of carbonic acid gas, the calcium sulfate product high temperature of generation is not easily decomposed; Sulfonated lignin and bicarbonate of ammonia improve the microtexture of synergistic agent, promote the carrying out of desulfurization reaction.
The present invention also provides a kind of preparation method of fire coal energy-saving emission-reducing synergistic agent, comprises the following steps:
S1: the raw material taking following weight part respectively: yttrium oxide 6-8 part, Manganse Dioxide 8-10 part, ferrous oxide 10-15 part, iron protoxide 10-15 part, sodium carbonate 3-5 part, saltpetre 3-5 part, sulfonated lignin 2-6 part, bicarbonate of ammonia 4-10 part, salt of wormwood 5-10 part, urea 6-10 part, gac 3-5 part, diatomite 2-8 part, activated alumina 2-3 part;
S2: yttrium oxide, Manganse Dioxide, ferrous oxide, iron protoxide, sodium carbonate, saltpetre are mixed, then add after sulfonated lignin and bicarbonate of ammonia mixes 20 minutes, add salt of wormwood, urea, gac, diatomite, activated alumina again, after mixing, grinding and processing is to 90-100 order, metering packing, obtains fire coal energy-saving emission-reducing synergistic agent.
During use, add synergistic agent of the present invention according to the 0.8-1.2% of Coal-fired capacity, also can add appropriate water in synergistic agent, be prepared into liquor and add to again in fire coal.
The invention has the beneficial effects as follows:
1. fire coal energy-saving emission-reducing synergistic agent of the present invention is in use when desulfurization reaction, the volume parts of oxygen can be reduced, improve the volume parts of carbonic acid gas simultaneously, effectively inhibit the decomposition of calcium sulfate, improve the high-temperature stability of calcium sulfate, substantially increase captured sulfur result, sulfur-fixing rate is more than 90%.
2. fire coal energy-saving emission-reducing synergistic agent of the present invention is under the effect of solid sulphur auxiliary agent, effectively can improve the microtexture of synergistic agent, promote desulfurization reaction, make reaction more fully, completely, realize energy-saving and emission-reduction, and the burning situation of hypoxemia also substantially increases denitration rate, the discharge of further decreasing pollution thing, NOx, SO2 quantity discharged reduces more than 80%.
3. fire coal energy-saving emission-reducing synergistic agent of the present invention is under the effect of properties-correcting agent, and changing the coal-fired proterties when burning, improving temperature of combustion, thus improve coal-fired utilization ratio, coal combustion thermo-efficiency is more than 85%.
Embodiment
Below in conjunction with specific embodiment, the invention will be further described, but do not limit the scope of the invention and range of application.
One, the preparation of fire coal energy-saving emission-reducing synergistic agent
Embodiment 1
A kind of fire coal energy-saving emission-reducing synergistic agent, comprises the raw material of following weight part: yttrium oxide 6kg, Manganse Dioxide 8kg, ferrous oxide 10kg, iron protoxide 10kg, sodium carbonate 3kg, saltpetre 3kg, sulfonated lignin 2kg, bicarbonate of ammonia 10kg, salt of wormwood 10kg, urea 10kg, gac 5kg, diatomite 8kg, activated alumina 3kg.
Embodiment 2
A kind of fire coal energy-saving emission-reducing synergistic agent, comprises the raw material of following weight part: yttrium oxide 8kg, Manganse Dioxide 10kg, ferrous oxide 15kg, iron protoxide 15kg, sodium carbonate 3kg, saltpetre 3kg, sulfonated lignin 2kg, bicarbonate of ammonia 4kg, salt of wormwood 5kg, urea 6kg, gac 3kg, diatomite 2kg, activated alumina 2kg.
Embodiment 3
A kind of fire coal energy-saving emission-reducing synergistic agent, comprises the raw material of following weight part: yttrium oxide 7kg, Manganse Dioxide 9kg, ferrous oxide 11kg, iron protoxide 13kg, sodium carbonate 4kg, saltpetre 5kg, sulfonated lignin 5kg, bicarbonate of ammonia 6kg, salt of wormwood 8kg, urea 8kg, gac 5kg, diatomite 5kg, activated alumina 2kg.
The method preparing embodiment 1-3 synergistic agent sample is: yttrium oxide, Manganse Dioxide, ferrous oxide, iron protoxide, sodium carbonate, saltpetre are mixed, then add after sulfonated lignin and bicarbonate of ammonia mixes 20 minutes, add salt of wormwood, urea, gac, diatomite, activated alumina again, after mixing, grinding and processing is to 90-100 order, metering packing, obtains fire coal energy-saving emission-reducing synergistic agent.
Two, application test
Fire coal energy-saving emission-reducing synergistic agent sample prepared by the present invention, once tested in needing the actual production of coal combustion to use.In the fire coal of same batch, the synergistic agent sample that with the addition of commercially available fire coal synergist and the interpolation embodiment of the present invention carries out simultaneous test.Be below the sample of embodiment 1-3 and the effect comparison of commercially available fire coal synergist:
As seen from the above table: fire coal energy-saving emission-reducing synergistic agent sample of the present invention, captured sulfur result is better than commercially available fire coal synergist product far away, and sulfur-fixing rate, more than 90%, discharges pollutants and also greatly reduces, and NOx, SO2 quantity discharged reduces more than 80%.
Above content can not assert that specific embodiment of the invention is confined to these explanations; for general technical staff of the technical field of the invention; without departing from the inventive concept of the premise; some simple deduction or replace can also be made, all should be considered as belonging to the scope of patent protection that the present invention is determined by submitted to claims.
Claims (2)
1. a fire coal energy-saving emission-reducing synergistic agent, it is characterized in that, comprise the raw material of following weight part: yttrium oxide 6-8 part, Manganse Dioxide 8-10 part, ferrous oxide 10-15 part, iron protoxide 10-15 part, sodium carbonate 3-5 part, saltpetre 3-5 part, sulfonated lignin 2-6 part, bicarbonate of ammonia 4-10 part, salt of wormwood 5-10 part, urea 6-10 part, gac 3-5 part, diatomite 2-8 part, activated alumina 2-3 part.
2. fire coal energy-saving emission-reducing synergistic agent according to claim 1, it is characterized in that, comprise the raw material of following weight part: yttrium oxide 7 parts, Manganse Dioxide 9 parts, ferrous oxide 11 parts, iron protoxide 13 parts, 4 parts, sodium carbonate, 5 parts, saltpetre, sulfonated lignin 5 parts, 6 parts, bicarbonate of ammonia, 8 parts, salt of wormwood, 8 parts, urea, gac 5 parts, 5 parts, diatomite, activated alumina 2 parts.