CN105348940A - High-strength IBC (intermediate bulk container) - Google Patents
High-strength IBC (intermediate bulk container) Download PDFInfo
- Publication number
- CN105348940A CN105348940A CN201510978726.7A CN201510978726A CN105348940A CN 105348940 A CN105348940 A CN 105348940A CN 201510978726 A CN201510978726 A CN 201510978726A CN 105348940 A CN105348940 A CN 105348940A
- Authority
- CN
- China
- Prior art keywords
- parts
- protective paint
- metal frame
- ibc
- strength
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-strength IBC (intermediate bulk container). The high-strength IBC comprises an inner container and a metal framework which are combined, wherein the metal framework is coated with protective paint; the protective paint comprises components in parts by weight as follows: 1-2 parts of coco trimethyl ammonium chloride, 1.3 parts of precipitated barium sulphate, 0.8 parts of silicon nitride, 0.9 parts of aluminium paste, 1.1 parts of ammonium persulfate, 0.8 parts of sodium tripolyphosphate, 0.4 parts of aluminum dihydrogen tripolyphosphate and 15.6 parts of a styrene-acrylic emulsion. According to the high-strength IBC, the metal framework is coated with the protective paint, and the high-strength IBC has excellent wear resistance, ageing resistance, oxidation resistance, corrosion resistance and weather fastness.
Description
Technical field
The present invention relates to high strength ton bucket.
Background technology
The environment for use of high strength ton bucket is severe, higher to the performance requriements of metal frame.
Summary of the invention
The object of the present invention is to provide a kind of high strength ton bucket, its metal frame Tu is covered with protective paint, has excellent wear-resisting, anti-aging, anti-oxidant, corrosion-resistant, weather resistance.
For achieving the above object, technical scheme of the present invention is a kind of high strength ton bucket of design, and combined by inner jar and metal frame, this metal frame Tu is covered with protective paint, and by weight, described protective paint is composed of the following components:
1 ~ 2 part of chlorination cocotrimonium ammonium,
1.3 parts of process whites,
0.8 part of silicon nitride,
0.9 part of aluminium-silver slurry,
1.1 parts of ammonium persulphates,
0.8 part of tripoly phosphate sodium STPP,
0.4 part of aluminium dihydrogen tripolyphosphate,
15.6 part benzene emulsion.
Preferably, high strength ton bucket, is combined by inner jar and metal frame, and this metal frame Tu is covered with protective paint, and by weight, described protective paint is composed of the following components:
1 part of chlorination cocotrimonium ammonium,
1.3 parts of process whites,
0.8 part of silicon nitride,
0.9 part of aluminium-silver slurry,
1.1 parts of ammonium persulphates,
0.8 part of tripoly phosphate sodium STPP,
0.4 part of aluminium dihydrogen tripolyphosphate,
15.6 part benzene emulsion.
Preferably, high strength ton bucket, is combined by inner jar and metal frame, and this metal frame Tu is covered with protective paint, and by weight, described protective paint is composed of the following components:
2 parts of chlorination cocotrimonium ammoniums,
1.3 parts of process whites,
0.8 part of silicon nitride,
0.9 part of aluminium-silver slurry,
1.1 parts of ammonium persulphates,
0.8 part of tripoly phosphate sodium STPP,
0.4 part of aluminium dihydrogen tripolyphosphate,
15.6 part benzene emulsion.
Advantage of the present invention and beneficial effect are: provide a kind of high strength ton bucket, its metal frame Tu is covered with protective paint, have excellent wear-resisting, anti-aging, anti-oxidant, corrosion-resistant, weather resistance.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A kind of high strength ton bucket, combined by inner jar and metal frame, this metal frame Tu is covered with protective paint, and by weight, described protective paint is composed of the following components:
1 ~ 2 part of chlorination cocotrimonium ammonium,
1.3 parts of process whites,
0.8 part of silicon nitride,
0.9 part of aluminium-silver slurry,
1.1 parts of ammonium persulphates,
0.8 part of tripoly phosphate sodium STPP,
0.4 part of aluminium dihydrogen tripolyphosphate,
15.6 part benzene emulsion.
Embodiment 2
High strength ton bucket, is combined by inner jar and metal frame, and this metal frame Tu is covered with protective paint, and by weight, described protective paint is composed of the following components:
1 part of chlorination cocotrimonium ammonium,
1.3 parts of process whites,
0.8 part of silicon nitride,
0.9 part of aluminium-silver slurry,
1.1 parts of ammonium persulphates,
0.8 part of tripoly phosphate sodium STPP,
0.4 part of aluminium dihydrogen tripolyphosphate,
15.6 part benzene emulsion.
Embodiment 3
High strength ton bucket, is combined by inner jar and metal frame, and this metal frame Tu is covered with protective paint, and by weight, described protective paint is composed of the following components:
2 parts of chlorination cocotrimonium ammoniums,
1.3 parts of process whites,
0.8 part of silicon nitride,
0.9 part of aluminium-silver slurry,
1.1 parts of ammonium persulphates,
0.8 part of tripoly phosphate sodium STPP,
0.4 part of aluminium dihydrogen tripolyphosphate,
15.6 part benzene emulsion.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (3)
1. high strength ton bucket, is characterized in that, is combined by inner jar and metal frame, and this metal frame Tu is covered with protective paint, and by weight, described protective paint is composed of the following components:
1 ~ 2 part of chlorination cocotrimonium ammonium,
1.3 parts of process whites,
0.8 part of silicon nitride,
0.9 part of aluminium-silver slurry,
1.1 parts of ammonium persulphates,
0.8 part of tripoly phosphate sodium STPP,
0.4 part of aluminium dihydrogen tripolyphosphate,
15.6 part benzene emulsion.
2. high strength ton bucket according to claim 1, is characterized in that, combined by inner jar and metal frame, and this metal frame Tu is covered with protective paint, and by weight, described protective paint is composed of the following components:
1 part of chlorination cocotrimonium ammonium,
1.3 parts of process whites,
0.8 part of silicon nitride,
0.9 part of aluminium-silver slurry,
1.1 parts of ammonium persulphates,
0.8 part of tripoly phosphate sodium STPP,
0.4 part of aluminium dihydrogen tripolyphosphate,
15.6 part benzene emulsion.
3. high strength ton bucket according to claim 1, is characterized in that, combined by inner jar and metal frame, and this metal frame Tu is covered with protective paint, and by weight, described protective paint is composed of the following components:
2 parts of chlorination cocotrimonium ammoniums,
1.3 parts of process whites,
0.8 part of silicon nitride,
0.9 part of aluminium-silver slurry,
1.1 parts of ammonium persulphates,
0.8 part of tripoly phosphate sodium STPP,
0.4 part of aluminium dihydrogen tripolyphosphate,
15.6 part benzene emulsion.