CN105295467A - Metal component - Google Patents
Metal component Download PDFInfo
- Publication number
- CN105295467A CN105295467A CN201510821396.0A CN201510821396A CN105295467A CN 105295467 A CN105295467 A CN 105295467A CN 201510821396 A CN201510821396 A CN 201510821396A CN 105295467 A CN105295467 A CN 105295467A
- Authority
- CN
- China
- Prior art keywords
- parts
- protective coating
- polycarbonate
- calcium sulfate
- metallic element
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a metal component. The metal component is coated with a protection coating. The protection coating comprises, by weight, 26 parts of amino resin, 1 to 2 parts of aluminum powder, 5 to 6 parts of methyl methacrylate, 3 to 4 parts of polycarbonate, 1 to 2 parts of organic bentonite and 2 to 3 parts of calcium sulfate. The metal component provided by the invention has the advantages of high strength, wear resistance and corrosion resistance.
Description
Technical field
The present invention relates to metallic element.
Background technology
Existing metallic element, its intensity, abrasion-resistant, corrosion resistance nature all have much room for improvement.
Summary of the invention
The object of the present invention is to provide a kind of metallic element, its intensity be high, abrasion-resistant, corrosion-resistant.
For achieving the above object, technical scheme of the present invention is a kind of metallic element of design, and it is coated with protective coating, and by weight percentage, described protective coating is composed of the following components:
26 parts of aminoresin,
1 ~ 2 part of aluminium powder,
5 ~ 6 parts of methyl methacrylates,
3 ~ 4 parts of polycarbonate,
1 ~ 2 part of organobentonite,
2 ~ 3 parts of calcium sulfate.
Preferably, by weight percentage, described protective coating is composed of the following components:
26 parts of aminoresin,
1 ~ 2 part of aluminium powder,
5 ~ 6 parts of methyl methacrylates,
3 ~ 4 parts of polycarbonate,
1 ~ 2 part of organobentonite,
2 ~ 3 parts of calcium sulfate.
Preferably, by weight percentage, described protective coating is composed of the following components:
26 parts of aminoresin,
1 ~ 2 part of aluminium powder,
5 ~ 6 parts of methyl methacrylates,
3 ~ 4 parts of polycarbonate,
1 ~ 2 part of organobentonite,
2 ~ 3 parts of calcium sulfate.
Preferably, by weight percentage, described protective coating is composed of the following components:
26 parts of aminoresin,
1.2 parts of aluminium powders,
5.6 parts of methyl methacrylates,
3.4 parts of polycarbonate,
1.2 parts of organobentonites,
2.3 parts of calcium sulfate.
Advantage of the present invention and beneficial effect are: provide a kind of metallic element, and its intensity is high, abrasion-resistant, corrosion-resistant.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A kind of metallic element, it is coated with protective coating, and by weight percentage, described protective coating is composed of the following components:
26 parts of aminoresin,
1 ~ 2 part of aluminium powder,
5 ~ 6 parts of methyl methacrylates,
3 ~ 4 parts of polycarbonate,
1 ~ 2 part of organobentonite,
2 ~ 3 parts of calcium sulfate.
Embodiment 2
A kind of metallic element, it is coated with protective coating, and by weight percentage, described protective coating is composed of the following components:
26 parts of aminoresin,
1 ~ 2 part of aluminium powder,
5 ~ 6 parts of methyl methacrylates,
3 ~ 4 parts of polycarbonate,
1 ~ 2 part of organobentonite,
2 ~ 3 parts of calcium sulfate.
Embodiment 3
A kind of metallic element, it is coated with protective coating, and by weight percentage, described protective coating is composed of the following components:
26 parts of aminoresin,
1.2 parts of aluminium powders,
5.6 parts of methyl methacrylates,
3.4 parts of polycarbonate,
1.2 parts of organobentonites,
2.3 parts of calcium sulfate.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (4)
1. metallic element, is characterized in that, it is coated with protective coating, and by weight percentage, described protective coating is composed of the following components:
26 parts of aminoresin,
1 ~ 2 part of aluminium powder,
5 ~ 6 parts of methyl methacrylates,
3 ~ 4 parts of polycarbonate,
1 ~ 2 part of organobentonite,
2 ~ 3 parts of calcium sulfate.
2. metallic element according to claim 1, is characterized in that, by weight percentage, described protective coating is composed of the following components:
26 parts of aminoresin,
1 ~ 2 part of aluminium powder,
5 ~ 6 parts of methyl methacrylates,
3 ~ 4 parts of polycarbonate,
1 ~ 2 part of organobentonite,
2 ~ 3 parts of calcium sulfate.
3. metallic element according to claim 1, is characterized in that, by weight percentage, described protective coating is composed of the following components:
26 parts of aminoresin,
1 ~ 2 part of aluminium powder,
5 ~ 6 parts of methyl methacrylates,
3 ~ 4 parts of polycarbonate,
1 ~ 2 part of organobentonite,
2 ~ 3 parts of calcium sulfate.
4. metallic element according to claim 1, is characterized in that, by weight percentage, described protective coating is composed of the following components:
26 parts of aminoresin,
1.2 parts of aluminium powders,
5.6 parts of methyl methacrylates,
3.4 parts of polycarbonate,
1.2 parts of organobentonites,
2.3 parts of calcium sulfate.