CN1053488A - 高铬稀土钢锅炉喷燃器火嘴 - Google Patents
高铬稀土钢锅炉喷燃器火嘴 Download PDFInfo
- Publication number
- CN1053488A CN1053488A CN 90104566 CN90104566A CN1053488A CN 1053488 A CN1053488 A CN 1053488A CN 90104566 CN90104566 CN 90104566 CN 90104566 A CN90104566 A CN 90104566A CN 1053488 A CN1053488 A CN 1053488A
- Authority
- CN
- China
- Prior art keywords
- rare earth
- burner fire
- good
- fire nozzle
- resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
高铬稀土钢锅炉喷燃器火嘴，是利用中、高碳、高
铬、低镍、含微量钼、钒、稀土的配方，获得铸态下为奥
氏体基体并含有部分碳化物的金相组织。本发明适
用于火力发电厂(国外引进的及国产的)大型燃煤锅
炉喷燃器火嘴。其材质具有四个主要性能：(1)耐高
温性能好(1100～1300℃)；(2)高温耐磨性能好，在
高温(1100～1300℃)状态下，能承受热风——煤粉
混合气流的高速冲刷恶劣的工作环境与对该零件耐
热、抗氧化、抗变形，而磨性能的苛刻要求；(3)冷热疲
劳性能好。
Description
本发明涉及改进的锅炉喷燃器火咀，尤其是用于火力发电厂国产大型锅炉喷燃器火咀。
至今，火力发电厂国产大型锅炉喷燃器火咀，其随炉配件大都采用lCr18Ni9Ti钢板组焊。一般寿命仅能达3000小时左右，达不到一个小修期5000小时。因此，国产锅炉喷燃器火咀的随炉配件，寿命仍然没有得到解决。近年来，国内一些科研院、所及厂家，对国产锅炉喷燃器火咀的随炉配件的研究、制造有所进展。中国专利申请号85102472公开的高温耐热铁基合金，但由于碳、锰、镍含量配比不佳，导致材质的韧性低、可焊性能、耐高温性能差或经不起冷、热疲劳、短时间内不是被烧损，就是断裂变形而被更换，经过有的使用厂家实际使用寿命为5000～6000小时，满足不了使用要求。
火力发电厂从国外引进的大型锅炉喷燃器火咀，它的高温耐热性能、耐磨性能、冶铸工艺比国产锅炉喷燃器火咀要求更苛刻。这项研究制造工作，在国内一些厂家，曾做过几次装炉试验，由于材质的耐高温性能差，几十小时就熔化在炉膛内。
鉴于这种情况，本发明的目的是克服现有技术的不足之处，提供一种改进的、耐高温、长寿命的铁基高铬稀土铸钢喷燃火咀。
这个任务按本发明可以这样解决，它是利用中、高碳、高铬、低镍、含钼、钒、稀土的配方，获得铸态下为奥氏体基体并含有部分碳化物的金相组织，其组成重量的百分比是：
C：0.4～1.3 Cr：26～28 Ni：1～5.5
Si：0.4～1.05 Mo：0.4～0.6 Mn：0.4～1.6
V：0.15～0.35 S≤0.030 P≤0.035
出炉时钢包中外加0.2%包头1＃稀土硅铁合金处理，其余为铁。
本发明最佳配比的重量百分比是：
C：0.4～0.5 Cr：26～28 Nl：4～5.5
Sl：0.4～0.8 Mo：0.4～0.6 Mn：0.4～0.6
S≤0.030 P≤0.035
外加0.2%包头1＃稀土硅铁合金处理。
本发明适用于火力发电厂（国产的及国外引进的）大型燃煤锅炉用的喷燃器火咀。其材质具有四个主要性能：（1）耐高温性能好（1100～1300℃）;（2）高温耐磨性能好，在高温（1100～1300℃）状态下，能承受热风-煤粉混合气流的高速冲刷恶劣的工作环境与对该另件耐热、抗氧化、抗变形、耐磨性能的苛刻要求;（3）冷热疲劳性能好。能适应电厂调峰、调频及各种原因的停炉检修，火咀能承受反复多次急冷、急热冲击，不碎、不裂、不变形;（4）可焊性能好。能适应锅炉检修中火咀更换，组焊前火咀不予热，焊后不作任何热处理。并在铸态下具有良好的机加工性能，同时其冶铸工艺简便。
实施例：
为唐山发电总厂研制成功了国外引进的850T/H锅炉喷燃器火咀新材质及制造工艺。经装炉考核，不但能满足使用要求，其寿命比引进件提高一倍。至此，该厂850T/H锅炉喷燃器火咀备件全部国产化。因为此材质自身的可焊性能、冷热疲劳性能差，不能满足国内锅炉的检修、使用要求。又经过多次研究试验，终于全面突破各项技术关键。由于材质成份设计的合理匹配，从而获得了具备上述良好综合性能的铸态奥氏体组织。满足了国内、外大型燃煤锅炉喷燃器火咀的使用要求。经在包头第二热电厂410T/H、乌拉山发电厂410T/H等国产锅炉上考核运行，已运行8000小时，其间经受了11次停炉，反复升降温、冷热疲劳考核，检测喷燃器火咀无变形、无裂纹，磨损甚微。从实际使用效果观察，使用寿命可达到20000小时，比随炉配备件lCr18Ni9Ti板材组焊件或整体耐热钢铸件寿命可提高近10倍。从而满足了火力发电厂锅炉喷燃器火咀的检修、使用要求，保证锅炉正常运行，根本上解决了国产火咀能保证一个大修期、装炉两年内不更换，国外引进火咀国产化，为我国高温耐磨材料系列增加了新的品种。
Claims (2)
1、一种铁基高铬稀土钢，制成的火电厂锅炉喷燃器火咀，其特征在于它的成份为(重量%)：
C：0.4～1.3 Cr：26～28 Ni：1～5.5
Si：0.4～1.05 Mo：0.4～0.6 Mn：0.4～1.6
V：0.15～0.35 S≤0.035 P≤0.035
出炉时钢水包中外加0.2%包头1#稀土硅铁合金处理。其余为铁质。
2、按权力要求1所说的铁基高铬稀土铸钢，其最佳配比重量百分比是：
C：0.4～0.5 Cr：26～28 Nl：4～5.5
Si 0.4～0.8 Mo：0.4～0.6 Mn：0.4～0.6
S≤0.030 P≤0.035
外加0.2%包头1＃稀土硅铁合金处理，其余为铁质。