CN105344930A - 一种用于形成发动机缸套表面毛刺的涂料及其制备方法 - Google Patents
一种用于形成发动机缸套表面毛刺的涂料及其制备方法 Download PDFInfo
- Publication number
- CN105344930A CN105344930A CN201510788386.1A CN201510788386A CN105344930A CN 105344930 A CN105344930 A CN 105344930A CN 201510788386 A CN201510788386 A CN 201510788386A CN 105344930 A CN105344930 A CN 105344930A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- coating
- cylinder sleeve
- parts
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供的一种用于形成发动机缸套表面毛刺的涂料及其制备方法,由下述重量份数的原料制成:宝珠砂40-50重量份、石英砂8-10重量份、硅藻土1.6-1.8重量份、羧甲基纤维素钠1.3-1.6重量份、膨润土3.5-4重量份、石墨粉0.45-1重量份、十二烷基硫酸钠0.13-0.15重量份、胶水3-5重量份、水120-140重量份。一种用于形成发动机缸套表面毛刺的涂料及其制备方法及制备方法的制备方法包括泡发、混碾、搅拌等步骤。本发明所采用的涂料配合离心铸造工艺来形成毛刺状的发动机缸套,具有配方简单、制造方便、成本低廉的优势。
Description
技术领域
本发明涉及缸套制造技术领域,具体涉及一种用于形成发动机缸套表面毛刺的涂料及其制备方法。
背景技术
目前,由于石油资源紧缺和环境污染,提高汽车发动机燃油效率、减少尾气排放已显得日益重要。汽车发动机的两大组件为活塞和缸套,其中,缸套要求其材料具有耐高温、耐磨、耐压以及质轻等性能。发动机性能的改善,势必对缸套在选材及加工方面提出更高的要求。目前,出现了一种外表面呈毛刺状的发动机缸套,比表面光滑的发动机缸套的热稳定性及牢固安装度均有大幅度的提高,其毛刺状的外表面,是通过涂料来实现成型,但现有技术中的涂料存在配方复杂、加工昂贵的缺陷,从而大幅度的提高了缸套的制造成本。
发明内容
本发明的目的在于克服上述现有技术的不足,提供一种配方简单、制造方便、成本低廉的用于形成发动机缸套表面毛刺的涂料。
一种用于形成发动机缸套表面毛刺的涂料及其制备方法,由下述重量份数的原料制成:宝珠砂40-50重量份、石英砂8-10重量份、硅藻土1.6-1.8重量份、羧甲基纤维素钠1.3-1.6重量份、膨润土3.5-4重量份、石墨粉0.45-1重量份、十二烷基硫酸钠0.13-0.15重量份、胶水3-5重量份、水120-140重量份。
一种用于形成发动机缸套表面毛刺的涂料及其制备方法,包括以下步骤:
(1)、泡发:用60-70重量份的水用于对羧甲基纤维素钠进行泡发;
(2)、混碾:将40-50重量份的宝珠砂、8-10重量份的石英砂、1.6-1.8重量份的硅藻土、3.5-4重量份的膨润土、0.45-1重量份的石墨粉加入碾轮式混砂机中混碾;
(3)、第一次搅拌:将混碾好的物料放入搅拌桶中,加入60-70重量份的水,以120-180RP/MIN的转速搅拌5-6个小时;
(4)、第二次搅拌:往搅拌桶中加入1.3-1.6重量份的羧甲基纤维素钠、0.13-0.15重量份的十二烷基硫酸钠,以及3-5重量份的胶水,以120-180RP/MIN的转速,再搅拌20-30分钟即可。
本发明所采用的涂料配合离心铸造工艺来形成毛刺状的发动机缸套,具有配方简单、制造方便、成本低廉的优势。
具体实施方式
以下结合具体实施例对发明作进一步详细的描述。
一种用于形成发动机缸套表面毛刺的涂料及其制备方法,由下述重量份数的原料制成:宝珠砂40-50重量份、石英砂8-10重量份、硅藻土1.6-1.8重量份、羧甲基纤维素钠1.3-1.6重量份、膨润土3.5-4重量份、石墨粉0.45-1重量份、十二烷基硫酸钠0.13-0.15重量份、胶水3-5重量份、水120-140重量份。
一种用于形成发动机缸套表面毛刺的涂料及其制备方法的制备方法,包括以下步骤:
(1)、泡发:用60-70重量份的水用于对羧甲基纤维素钠进行泡发;
(2)、混碾:将40-50重量份的宝珠砂、8-10重量份的石英砂、1.6-1.8重量份的硅藻土、3.5-4重量份的膨润土、0.45-1重量份的石墨粉加入碾轮式混砂机中混碾;
(3)、第一次搅拌:将混碾好的物料放入搅拌桶中,加入60-70重量份的水,以120-180RP/MIN的转速搅拌5-6个小时;
(4)、第二次搅拌:往搅拌桶中加入1.3-1.6重量份的羧甲基纤维素钠、0.13-0.15重量份的十二烷基硫酸钠,以及3-5重量份的胶水,以120-180RP/MIN的转速,再搅拌20-30分钟即可。
实施例1
一种用于形成发动机缸套表面毛刺的涂料及其制备方法,由下述重量份数的原料制成:宝珠砂40重量份、石英砂8重量份、硅藻土1.6重量份、羧甲基纤维素钠1.3重量份、膨润土3.5重量份、石墨粉0.45重量份、十二烷基硫酸钠0.13重量份、胶水3重量份、水120重量份。
一种用于形成发动机缸套表面毛刺的涂料及其制备方法的制备方法,包括以下步骤:
(1)、泡发:用60重量份的水用于对羧甲基纤维素钠进行泡发;
(2)、混碾:将40重量份的宝珠砂、8重量份的石英砂、1.6重量份的硅藻土、3.5重量份的膨润土、0.45重量份的石墨粉加入碾轮式混砂机中混碾;
(3)、第一次搅拌:将混碾好的物料放入搅拌桶中,加入60重量份的水,以120RP/MIN的转速搅拌5个小时;
(4)、第二次搅拌:往搅拌桶中加入1.3重量份的羧甲基纤维素钠、0.13重量份的十二烷基硫酸钠,以及3重量份的胶水,以120RP/MIN的转速,再搅拌20分钟即可。
实施例2
一种用于形成发动机缸套表面毛刺的涂料及其制备方法,由下述重量份数的原料制成:宝珠砂50重量份、石英砂10重量份、硅藻土1.8重量份、羧甲基纤维素钠1.6重量份、膨润土4重量份、石墨粉1重量份、十二烷基硫酸钠0.15重量份、胶水5重量份、水140重量份。
一种用于形成发动机缸套表面毛刺的涂料及其制备方法的制备方法,包括以下步骤:
(1)、泡发:用70重量份的水用于对羧甲基纤维素钠进行泡发;
(2)、混碾:将50重量份的宝珠砂、10重量份的石英砂、1.8重量份的硅藻土、4重量份的膨润土、1重量份的石墨粉加入碾轮式混砂机中混碾;
(3)、第一次搅拌:将混碾好的物料放入搅拌桶中,加入70重量份的水,以180RP/MIN的转速搅拌6个小时;
(4)、第二次搅拌:往搅拌桶中加入1.6重量份的羧甲基纤维素钠、0.15重量份的十二烷基硫酸钠,以及5重量份的胶水,以180RP/MIN的转速,再搅拌30分钟即可。
以上所述仅是本发明的优选实施方式,本发明的保护范围并不仅局限于上述实施例,凡属于本发明思路下的技术方案均属于本发明的保护范围。应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明原理前提下的若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (2)
1.一种用于形成发动机缸套表面毛刺的涂料及其制备方法,其特征在于:由下述重量份数的原料制成:宝珠砂40-50重量份、石英砂8-10重量份、硅藻土1.6-1.8重量份、羧甲基纤维素钠1.3-1.6重量份、膨润土3.5-4重量份、石墨粉0.45-1重量份、十二烷基硫酸钠0.13-0.15重量份、胶水3-5重量份、水120-140重量份。
2.制备权利要求1所述的一种用于形成发动机缸套表面毛刺的涂料及其制备方法,其特征在于:包括以下步骤:
(1)、泡发:用60-70重量份的水用于对羧甲基纤维素钠进行泡发;
(2)、混碾:将40-50重量份的宝珠砂、8-10重量份的石英砂、1.6-1.8重量份的硅藻土、3.5-4重量份的膨润土、0.45-1重量份的石墨粉加入碾轮式混砂机中混碾;
(3)、第一次搅拌:将混碾好的物料放入搅拌桶中,加入60-70重量份的水,以120-180RP/MIN的转速搅拌5-6个小时;
(4)、第二次搅拌:往搅拌桶中加入1.3-1.6重量份的羧甲基纤维素钠、0.13-0.15重量份的十二烷基硫酸钠,以及3-5重量份的胶水,以120-180RP/MIN的转速,再搅拌20-30分钟即可。