CN105342066B - A kind of preparation method of charcoal shoe-pad - Google Patents
A kind of preparation method of charcoal shoe-pad Download PDFInfo
- Publication number
- CN105342066B CN105342066B CN201510736544.9A CN201510736544A CN105342066B CN 105342066 B CN105342066 B CN 105342066B CN 201510736544 A CN201510736544 A CN 201510736544A CN 105342066 B CN105342066 B CN 105342066B
- Authority
- CN
- China
- Prior art keywords
- parts
- shoe
- pad
- charcoal
- sandwich layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention provides a kind of preparation method of charcoal shoe-pad, and step is as follows：From seat straw plaited, braiding, which is flattened, is made sandwich layer；It is placed in closed container and softens, softening process is that water vapour is passed through into closed container, keep 180 DEG C of temperature in closed container, pressure 0.2MPa, heat-insulation pressure keeping 2 hours then takes out, dries dehydration 18 30 hours, it is stand-by；In the lower surface bonds lower floor of sandwich layer, upper strata is bonded in the upper surface of sandwich layer, lower floor is made of soft plastic；Lower floor upper surface is provided with medicament hole, and the spacing in the medicament hole is 1.5cm；Chinese medicine rod is inserted in medicament hole；Upper strata uses cotton；The shoe-pad of different specification size is cut out by mould size, and in shoe-pad edge bound edge；The bound edge is to sew or be bonded wrapped belt at shoe-pad edge.Shoe-pad produced by the present invention, with good gas permeability, hydrofuge absorbing sweat effect is good, with antibacterial effect, can reach the effect for the treatment of tinea pedis, prepare it is with low cost, it is with health role.
Description
Technical field
The present invention relates to shoe-pad production technical field, more particularly to a kind of preparation method of charcoal shoe-pad.
Background technology
Shoe-pad is the most frequently used daily necessities in daily production, and its effect is to make the smooth cleaning of inner sole, excludes pin
Sweat and moisture absorption, make inner sole flat smooth comfortable and easy to wear.
The insole products species of existing market is various, and quality and performance are also uneven.There is most mainly by changing
Learn material to be made, poor air permeability, foot's sweat is difficult to quick volatilization, foot is moist for a long time, and easy breed bacteria and fungi cause
The diseases such as foot's infection tinea pedis.The main shoe-pad being made up of chemical material, usage cycles are short, after discarding, it is difficult to degrade, not ring
Protect.
The content of the invention
It is an object of the invention to provide a kind of preparation method of charcoal shoe-pad, to solve above-mentioned technical problem.
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of preparation method of charcoal shoe-pad, it is characterised in that step is as follows：
(a) sandwich layer is made：From seat straw plaited, remove seat toothed burclover portion and heel, take center section, then braiding flattens system
Obtain sandwich layer；Sandwich layer is placed in closed container and softened, softening process is that water vapour is passed through into closed container after pressing, protects
180 DEG C of temperature in closed container are held, pressure 0.2MPa, heat-insulation pressure keeping 2 hours then takes out, dry dehydration 18-30 hours, treat
With；
(b) in the lower surface bonds lower floor of sandwich layer, upper strata is bonded in the upper surface of sandwich layer, lower floor uses soft plastic system
Into；Lower floor upper surface is provided with medicament hole, and the spacing in the medicament hole is 1.5cm；Chinese medicine rod is inserted in medicament hole；The Chinese medicine
Rod is made up of the raw material of following weight part ratio：55 parts of charcoal, 15 parts of borneol, 12 parts of potassium permanganate, nano silicon 15
Part, 6 parts of wormwood powder；Upper strata uses cotton；
(c) shoe-pad of different specification size is cut out by mould size, and in shoe-pad edge bound edge；The bound edge be
Sew or bonding wrapped belt at shoe-pad edge；
The preparation method of the charcoal is：
1) respectively by sawdust, the leaf of bamboo, Shell of Water Chestnut, peanut shell, granatum, selfheal, wormwood, caulis clematidis armandii, green tea powder, wild jujube
Branch, the seedpod of the lotus, Radix Astragali crushed after being dried are stand-by to particle diameter 0.3mm；
2) 65 parts of sawdust, 25 parts of the leaf of bamboo, 5 parts of Shell of Water Chestnut, 15 parts of peanut shell, granatum 18 after crushing are taken by weight
Part, 15 parts of selfheal, 25 parts of wormwood, 8 parts of caulis clematidis armandii, 5 parts of green tea powder, 9 parts of Ramulus Ziziphi Spinosae, 5 parts of the seedpod of the lotus, 6 parts of mixtures of the Radix Astragali, and stir
Mix uniform, obtain processing powder；
3) above-mentioned processing powder is placed in closed container, is passed through water vapour, 180 DEG C of keeping temperature, pressure 0.2MPa is protected
Warm pressurize 2 hours, then processing powder is taken out and is dried through 260 DEG C of high temperature, gained processes the moisture content of powder 15%,
In order to the machine-shaping of next procedure；
4) it is the processing powder after above-mentioned drying and 45 parts of mixtures of diatomite is uniform, add and charcoal lump base is carried out in forming machine
Heating-up temperature in processing and forming, forming machine is not less than 220 DEG C, obtains charcoal lump base stand-by；
5) charcoal lump base obtained above is piled up, airing it is stand-by；
6) the charcoal lump base after above-mentioned airing is loaded into retort, the temperature carried out in charing process, retort is maintained at
465 DEG C, the duration is 3 days, charcoal lump base is occurred half and carbonizes, it is 65-72% to control carbonization degree.
Contain lily essential oil in plants essential oil containing atomization in the water vapour being passed through in step (a), every 100g water vapours
0.1g, Lavender 0.1g.
Contain diatomite in charcoal component, the viscosity of raw material can be increased, beneficial to shaping, be not easy out charcoal
Broken, the charing of charcoal half is split, i.e., with preferable adsorption capacity, effective components of Chinese medicinal can be contained again wherein, final system
Into Chinese medicine rod, resistivity of the human body to disease can be strengthened, Wen Jing, rationale blood, by cold-dampness.Pass through vapor in production method
Heat-insulation pressure keeping, makes steam and plants essential oil well into seat grass, the shoe-pad processed is had special fragrance.
Common carbon rod molding machine machine-shaping can be used in Chinese medicine rod, by each material component mixture in proportion, and the stirring that adds water is equal
It is even, add and barred body is processed into forming machine, Chinese medicine rod is produced after drying.
The beneficial effects of the invention are as follows：
Shoe-pad produced by the present invention, with good gas permeability, hydrofuge absorbing sweat effect is good, with antibacterial effect, can be with
Reach treatment tinea pedis effect, prepare it is with low cost, it is with health role.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Specific embodiment is closed, the present invention, but following embodiments only the preferred embodiments of the present invention, and not all are expanded on further.
Based on the embodiment in embodiment, those skilled in the art obtain other realities on the premise of creative work is not made
Example is applied, protection scope of the present invention is belonged to.
A kind of preparation method of charcoal shoe-pad, step is as follows：
(a) sandwich layer is made：From seat straw plaited, remove seat toothed burclover portion and heel, take center section, then braiding flattens system
Obtain sandwich layer；Sandwich layer is placed in closed container and softened, softening process is that water vapour is passed through into closed container, water after pressing
Contain lily essential oil 0.1g, Lavender 0.1g in plants essential oil containing atomization in steam, every 100g water vapours, keep close
180 DEG C of temperature in container are closed, pressure 0.2MPa, heat-insulation pressure keeping 2 hours then takes out, dry dehydration 18-30 hours, it is stand-by；
(b) in the lower surface bonds lower floor of sandwich layer, upper strata is bonded in the upper surface of sandwich layer, lower floor uses soft plastic system
Into；Lower floor upper surface is provided with medicament hole, and the spacing in the medicament hole is 1.5cm；Chinese medicine rod is inserted in medicament hole；The Chinese medicine
Rod is made up of the raw material of following weight part ratio：55 parts of charcoal, 15 parts of borneol, 12 parts of potassium permanganate, nano silicon 15
Part, 6 parts of wormwood powder；Upper strata uses cotton；
(c) shoe-pad of different specification size is cut out by mould size, and in shoe-pad edge bound edge；The bound edge be
Sew or bonding wrapped belt at shoe-pad edge；
The preparation method of charcoal is：
1) respectively by sawdust, the leaf of bamboo, Shell of Water Chestnut, peanut shell, granatum, selfheal, wormwood, caulis clematidis armandii, green tea powder, wild jujube
Branch, the seedpod of the lotus, Radix Astragali crushed after being dried are stand-by to particle diameter 0.3mm；
2) 65 parts of sawdust, 25 parts of the leaf of bamboo, 5 parts of Shell of Water Chestnut, 15 parts of peanut shell, granatum 18 after crushing are taken by weight
Part, 15 parts of selfheal, 25 parts of wormwood, 8 parts of caulis clematidis armandii, 5 parts of green tea powder, 9 parts of Ramulus Ziziphi Spinosae, 5 parts of the seedpod of the lotus, 6 parts of mixtures of the Radix Astragali, and stir
Mix uniform, obtain processing powder；
3) above-mentioned processing powder is placed in closed container, is passed through water vapour, 180 DEG C of keeping temperature, pressure 0.2MPa is protected
Warm pressurize 2 hours, then processing powder is taken out and is dried through 260 DEG C of high temperature, gained processes the moisture content of powder 15%,
In order to the machine-shaping of next procedure；
4) it is the processing powder after above-mentioned drying and 45 parts of mixtures of diatomite is uniform, add and charcoal lump base is carried out in forming machine
Heating-up temperature in processing and forming, forming machine is not less than 220 DEG C, obtains charcoal lump base stand-by；
5) charcoal lump base obtained above is piled up, airing it is stand-by；
6) the charcoal lump base after above-mentioned airing is loaded into retort, the temperature carried out in charing process, retort is maintained at
465 DEG C, the duration is 3 days, charcoal lump base is occurred half and carbonizes, it is 65-72% to control carbonization degree.
General principle, principal character and the advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and that described in above-described embodiment and specification is only the present invention
Preference, be not intended to limit the present invention, without departing from the spirit and scope of the present invention, the present invention also have it is various
Changes and improvements, these changes and improvements all fall within the protetion scope of the claimed invention.The claimed scope of the invention is by institute
Attached claims and its equivalent thereof.
Claims (2)
1. a kind of preparation method of charcoal shoe-pad, it is characterised in that step is as follows：
(a) sandwich layer is made：From seat straw plaited, remove seat toothed burclover portion and heel, take center section, then braiding, which is flattened, is made core
Layer；Sandwich layer is placed in closed container and softened, softening process is that water vapour is passed through into closed container after pressing, keeps close
180 DEG C of temperature in container are closed, pressure 0.2MPa, heat-insulation pressure keeping 2 hours then takes out, dry dehydration 18-30 hours, it is stand-by；
(b) in the lower surface bonds lower floor of sandwich layer, upper strata is bonded in the upper surface of sandwich layer, lower floor is made of soft plastic；Under
Layer upper surface is provided with medicament hole, and the spacing in the medicament hole is 1.5cm；Chinese medicine rod is inserted in medicament hole；The Chinese medicine rod by
The raw material of following weight part ratio is made：55 parts of charcoal, 15 parts of borneol, 12 parts of potassium permanganate, 15 parts of nano silicon, Chinese mugwort
6 parts of grass meal；Upper strata uses cotton；
(c) shoe-pad of different specification size is cut out by mould size, and in shoe-pad edge bound edge；The bound edge is in shoe-pad
Sew or bonding wrapped belt at edge；
The preparation method of the charcoal is：
1) respectively by sawdust, the leaf of bamboo, Shell of Water Chestnut, peanut shell, granatum, selfheal, wormwood, caulis clematidis armandii, green tea powder, Ramulus Ziziphi Spinosae,
The seedpod of the lotus, Radix Astragali crushed after being dried are stand-by to particle diameter 0.3mm；
2) 65 parts of sawdust after crushing, 25 parts of the leaf of bamboo, 5 parts of Shell of Water Chestnut, 15 parts of peanut shell, 18 parts of granatum, summer are taken by weight
15 parts of withered grass, 25 parts of wormwood, 8 parts of caulis clematidis armandii, 5 parts of green tea powder, 9 parts of Ramulus Ziziphi Spinosae, 5 parts of the seedpod of the lotus, 6 parts of mixtures of the Radix Astragali, and stir equal
It is even, obtain processing powder；
3) above-mentioned processing powder is placed in closed container, is passed through water vapour, 180 DEG C of keeping temperature, pressure 0.2MPa, insulation is protected
Pressure 2 hours, then processing powder is taken out and is dried through 260 DEG C of high temperature, gained processes the moisture content of powder 15%, so as to
In the machine-shaping of next procedure；
4) it is the processing powder after above-mentioned drying and 45 parts of mixtures of diatomite is uniform, add and charcoal lump base shaping is carried out in forming machine
Heating-up temperature in processing, forming machine is not less than 220 DEG C, obtains charcoal lump base stand-by；
5) charcoal lump base obtained above is piled up, airing it is stand-by；
6) the charcoal lump base after above-mentioned airing is loaded into retort, the temperature carried out in charing process, retort is maintained at 465
DEG C, the duration is 3 days, charcoal lump base is occurred half and carbonizes, it is 65-72% to control carbonization degree.
2. the preparation method of charcoal shoe-pad according to claim 1, it is characterised in that：The water being passed through in step (a)
Contain lily essential oil 0.1g, Lavender 0.1g in plants essential oil containing atomization in steam, every 100g water vapours.