CN105326697B - A kind of 3D printing method for nursing film - Google Patents
A kind of 3D printing method for nursing film Download PDFInfo
- Publication number
- CN105326697B CN105326697B CN201510807745.3A CN201510807745A CN105326697B CN 105326697 B CN105326697 B CN 105326697B CN 201510807745 A CN201510807745 A CN 201510807745A CN 105326697 B CN105326697 B CN 105326697B
- Authority
- CN
- China
- Prior art keywords
- nursing
- film
- silk
- powder
- printing method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention discloses a kind of preparation method for the 3D printing method and membrane material for nursing film, including, A. scanning nursing position；B. data processing；C. the counterdie consistent with nursing feature is made；D. membrane material is sent into 3D printer, thin film is printed on counterdie；E. basic nursing composition is sprayed to film general duty nursing position to film surface, and vacates film special care region；F. the special care region sequentially vacated respectively to film sequentially sprays corresponding nursing composition respectively；G. individual nursing film finished product.Beneficial effect is：Nursing film can be bonded completely with personal characteristics completely, and need to add different compositions according to different parts, the defects of overcoming single film single effect, meet the individual character needs of people；Other membrane material selects most light most soft most thin natural fiber silk in nature, but changes the form of existing silk braiding film forming, is changed to pulpous state printed matter, individual nursing film is met multi-party demand.
Description
Technical field
The present invention relates to a kind of preparation method for nursing film, and 3D printing technique printing nursing film is utilized more particularly to one kind
Method.
Background technology
1st, facial mask is to compare the product liked and used in numerous women's skin care item, and its important purpose is to make up makeup removing
With the still insufficient cleaning that washes one's face, while other essential ingredients are coordinated to realize other maintenance functions, such as replenishing water and preserving moisture,
Whitening and anti-aging, Sage Extract etc..
However, current all facial masks on the market, although there is a variety of effects in terms of maintenance function, it has 2
The shortcomings that individual general character.
First shortcoming is every kind of（Every）The overall efficacy of facial mask is single.Such as：P＆G SK-II facial treatment mask masters
It is that NMF gos deep into cuticula, skin care to want effect；The tall and erect effect brilliant white moisturizing silk face of Fei Nameng legend emperors court of a feudal ruler orchid
Film, primary anti-ageing nursing and plant attain extraction nursing；White U.S. flesh concentrates cleawhite pack to Shiseido thoroughly, and white elite rests on skin cutin
Infiltrating cells in layer；The intensive moisturizing elite facial mask of Lancome, catch, pin skin moisture to administer water shortage microgroove；Neutrogena deep layer
Moisture saver mask, absorb, discharge moisturizing molecule to be continuously skin moisturizing；U.S. is the lubricious face film of milk hundred, with protein, amino
Sour and flexible calcareous improvement face skin is dim, matt phenomenon；Olay talent for swimming white Whitening, spot facial mask thoroughly, increase for skin
Bai Weizhu；Refined of Elizabethan, supplement required lipid and the resistance that skin can be strengthened for skin, the Slow that relaxes dries inflammation
Phenomenon；Avene is releived moisture saver mask, is releived, moisturizing, alleviates skin sensitivity phenomenon；The no added nti-freckle brilliant white Face-protecting masks of FANCL,
With net white light spot for purport, etc..These facial masks, although effect is fine, the characteristics of unification based on type, womankind makes
Used time tends not to take into account itself nursing of several needs.Citing, eye nearby may need to administer water shortage microgroove, and main body face can
It can need to brighten nursing, lip may nearby need to releive, moisturizing, and alleviation skin tender subject, this is the facial mask institute of single effect
It is indeterminable.
Second shortcoming of the facial mask sold on the market is every（Kind）Facial mask is all unified production, and production process can not
In view of everyone facial geometric feature.We everyone, the size of the organ such as nose, face, lip, chin, geometric form
Shape, relative position are all different, and each species diversity for being exactly everyone facial geometric feature just causes everyone face in the world
Vary.Difference based on this geometric properties, people often have many to be brought by unified production during facial mask is used
Inconvenience.Such as：Facial mask size is inadequate, it is impossible to covers all face；The reason for face is because of profile, facial mask can not be sturdy, liquid
The suitable seam trickling of meeting and facial mask need to cut out many knives, and (facial mask having can cut 12 knives）To ensure to apply in consolidation on the face, using extremely
Inconvenience, etc..In addition, some facial masks to solve the problems, such as facial geometric feature, face paper is made it is extremely thin, using
Come highly inconvenient.
2nd, gestational period load-bearing that twilight is rung, and the collagenous fibres of skin and elastic fibrous tissue are destroyed, and make thinning of skin
Attenuate as the speckle i.e. striae of pregnancy of reddish violet, after termination of pregnancy（Postpartum）It is difficult to disappear, influences figure and the physical and mental health of women.
Therefore, numerous womankinds are after termination of pregnancy（Postpartum）, the removal as early as possible to belly wrinkle, reply original perfect belly and make
Type, there is strong requirement.
Postpartum belly wrinkle-care（Remove）Though the methods of used can massaging, perform the operation, taking exercise, it can also use slim light line
Film removes.
3rd, other positions of body, when need to nurse, often using modes such as wrappings, for example, treatment of wounds.For another example bone
After folding, either traditional Chinese medical science bag medicine or planter cast, highly inconvenient.
The content of the invention
The technical problem to be solved by the invention is to provide a kind of body is measured for personal nursing need and geometric properties
The nursing film of customization and the preparation method of membrane material.
The technical solution adopted in the present invention is：A kind of 3D printing method for nursing film, including,
Step A. scanning nursing position；
Step B. data processings；
Step C. makes the counterdie consistent with nursing feature；
Membrane material is sent into 3D printer by step D., and thin film is printed on counterdie；
Step E. receive data processed result, to film general duty nursing position by printer head spray basic nursing into
Divide to film surface, and vacate film special care region；
Step F. receives data processed result, and the special care region sequentially vacated respectively to film passes through printer head
Corresponding nursing composition is sequentially sprayed respectively；
Step G. individual nursing film finished products.
The 3D printer includes the streamline printer that multiple shower nozzles are formed, and different nursing products is placed in Storage Box
Film surface is delivered to by shower nozzle.
Forming processes are carried out between above-mentioned steps D and step E, slight drying and moulding is carried out to printed film, or
Cooling shaping, form the nursing film of network structure.
The nursing film includes facial mask, and abdominal pregnancy nurses film, other position special requirements of body such as sun-proof, wound
The film of the needs such as reason, fracture nursing.
A kind of preparation method of membrane material, including tussah powder, Silk Powder, the string for itself having network structure
On powder and to skin fanout free region or have skin-protecting function and can in the drying process with above-mentioned powder-stuck crosslinking agent；It is above-mentioned
Powder uniformly mixes with crosslinking agent, forms pulpous state printed matter.
The Silk Powder includes mulberry silk, tussah silk, ricinus silk, cassava silkwormsilk etc.；Crosslinking agent is medical gelatin liquid
Body or thermoplastic plastic.
The preparation of the powder comprises the following steps：
（1）：Silk cocoon is poured into sodium carbonate liquor, boils 20-30 minutes；Sodium carbonate liquor concentration is 0.3-0.7%；
The weight of silk cocoon and sodium carbonate ratio is 1：20-200；
（2）Silk cocoon is pulled out, is put into the solution of sulfuric acid, boils 40-80 minutes；The concentration of sulfuric acid solution is 2-5%；
The weight of silk cocoon and sulfuric acid solution ratio is 1：20-200；
（3）Silk cocoon is pulled out, is put into clear water, stirs, adds a small amount of sodium hydroxide, while detects the pH value of solution, is controlled
System is in 6-7, stable 10-15 minutes；
（4）Silk cocoon is pulled out, rinsed again with clear water, is dried after pulling out, grinds powdering.
The medical gelatin liquid is that gelatin and water form, and the weight ratio of gelatin and water is 1：100；Powder and medical gelatin
The weight ratio of liquid is 1：20-50.
The thermoplastic plastic is sufficiently stirred with Silk Powder, mixed, and being warming up to thermoplastic plastic's raw material has good fluidity
Required temperature；The weight of thermoplastic plastic and powder ratio is 1：0.1-2.
The beneficial effects of the invention are as follows：Nursing film can be bonded completely with personal characteristics completely, and according to different parts
Need to add different compositions, the defects of overcoming single film single effect, meet the individual character needs of people；Other membrane material choosing
With most gently most soft most thin natural fiber silk, but change the form of existing silk braiding film forming in nature, pulpous state is changed to
Printed matter, individual nursing film is set to meet multi-party demand.
Brief description of the drawings
Fig. 1 is the block diagram for nursing film 3D printing method.
Embodiment
The present invention is described in further detail with reference to embodiment：
Step A. nurses the scanning at position；The nursing position of individual is scanned using commercial ripe scanner,
Obtain corresponding information；
By taking face as an example, the face recognizing system for such as Visionics companies of can be selected is scanned；Lau Tech. companies
Face recognizing/confirmation system；The system of Miros companies；The system of C-VIS companies；Banque-Tech. the system of company；
Visage Gallery system；The system of Plettac Electronic companies；The BioID systems in Taiwan, and other skills
Relatively low system of art content, etc.；The size of the accurate facial geometric feature such as facial contour for obtaining facial mask user, eye
The organs such as eyeball, nose, face, lip, chin（Including eyebrow, beard）Geometry, the master data such as size, relative position
Most basic foundation is printed as facial mask.
Again by taking face as an example, when being scanned using commercial ripe facial scanner to the face of individual, simultaneously
Some trickle physical features and its ad-hoc location of face are obtained, as whether canthus has whether microgroove, forehead have wrinkle, skin spy
Positioning put it is whether coarse, dim, have a spot, and some physiological characteristics are as on the face with whelk, the size of mole, particular location
Deng.
Or by taking face as an example, when being scanned using commercial ripe facial scanner to the face of individual, also
The mass-type foundation of human body face need to be obtained.Such as：Whether face skin is dim, matt；Whether face skin is in dry shape
State, whether face skin, which needs, brightens.
Step B. data processings；After nursing dept.'s bit scan, all data enter computer and carried out at data
Reason.
Step C. makes the counterdie consistent with nursing feature；
Step D. nurses the preparation of membrane material；The present invention is used for the nursing membrane material of 3D printing, and main body is wild silkworm silk powder
End, Silk Powder（Including mulberry silk, tussah silk, ricinus silk, cassava silkwormsilk etc.）, or itself have network structure, Ke Yiyong
The method production of the present invention, other various string powder.
Silk is most light most soft most thin natural fiber in nature, can easily be restored to the original state after cancelling external force, its is main
It is made up of animal protein, rich in amino acid necessary to 18 kinds of human bodies, Skin Cell vigor, anti-vascular sclerosis, length can be promoted
Phase use can anti-skin senescence, have special antipruritic effect to some skin diseases.Structure and human skin pole because of natural silk
Similar, silk beauty has long history in China, and early in the Ming Dynasty of China, silk is because of its important medical value, by imperial palace
Highest-ranking imperial concubines are used for daily beauty and health care.According to《Compendium of Materia Medica》Record：Silk fibroin powder can eliminate skin blackspot, and treatment is suppurative
Dermatitis.In addition, there is substantial amounts of longitude and latitude network structure in silk, skin care ingredient can be made effectively to be accommodated in the inner.Fibroin fiber
It is enriched many amidos（-CHNH）, amino（-NH2）Deng hydrophilic radical, and due to its porous, it is easy to water diffusion, institute
It can effectively be absorbed with it and discharge moisture.Therefore beauty circle is even more to have started one silk beauty agitation, using silk as raw material development
The fibroin cosmetics formed, the skin care for becoming the countless women that like to be beautiful are preferred.
But the facial mask using silk as raw material at present, still employ weaving method and form film, then add and add skin care raw material to exist
Above, it is impossible to for carrying out the production of personalized facial mask.
The preparation of membrane material has two methods.
First method：
a:（1）：Silk cocoon is poured into sodium carbonate liquor, boils 20-30 minutes.The concentration of sodium carbonate is in sodium carbonate liquor
0.3-0.7%；Silk cocoon：Na2CO3 solution is 1 kilogram：20 kilograms to 1 kilogram：200 kilograms；（2）Silk cocoon is pulled out, is put into sulfuric acid
Solution in, boil 40-80 minutes.The concentration of sulfuric acid is 2-5% in sulfuric acid solution；Silk cocoon：Sulfuric acid solution is 1 kilogram：20 kilograms are arrived
1 kilogram：200 kilograms；（3）3rd step, silk cocoon is pulled out, is put into clear water, stirring, adds a small amount of NaOH, while detect solution
PH value, control to 6-7, stable 10-15 minutes；（4）4th step, silk cocoon is pulled out, is rinsed again with clear water, is done after pulling out
It is dry, powdering is ground, claims substance A.
b:The pharmagel that will be made using fresh ox-hide, by 1 kilogram of gelatin：The ratio of double centner clear water, heat, endure
Change, referred to as substance B.
Gelatin is all made up of as other oroteins a variety of α-amino acid, substantially by 18 kinds of amino acid
Composition.The characteristics of gelatin amino acid forms：1）Containing substantial amounts of glycine, alanine, proline and hydroxyproline, 70% is accounted for.
Proline and hydroxyproline are then more rare in other oroteins, and the hydroxyproline content in gelatin is generally 14.4%；2）Contain
The content of sulphur amino acid is very low, is free of cystine and cysteine mostly.Therefore gelatin is also a kind of skincare material.
c：AB materials are sufficiently mixed, are incubated, moisturizing, are conveyed into 3D printer, mixed proportion A：B=1 kilogram：20000
Gram to 1 kilogram：50 kilograms.
Second method：
a:（1）：Silk cocoon is poured into Na2CO3 solution, boils 20-30 minutes.Na2CO3 concentration is in N a2CO3 solution
0.3-0.7%；Silk cocoon：Na2CO3 solution is 1 kilogram：20 kilograms to 1 kilogram：200 kilograms；（2）Silk cocoon is pulled out, is put into sulfuric acid
Solution in, boil 40-80 minutes.The concentration of sulfuric acid is 2-5% in sulfuric acid solution；Silk cocoon：Sulfuric acid solution is 1 kilogram：20 kilograms are arrived
1 kilogram：200 kilograms；（3）3rd step, silk cocoon is pulled out, is put into clear water, stirring, adds a small amount of NaOH, while detect solution
PH value, control to 6-7, stable 10-15 minutes；（4）4th step, silk cocoon is pulled out, is rinsed again with clear water, is done after pulling out
It is dry, powdering is ground, claims substance A.
b：By thermoplastic plastic's raw material grind powdering, claim substance C.
c：AC materials are sufficiently stirred, mixed, there is needed for good fluidity thermoplastic plastic's raw material used by being warming up to
Temperature, be conveyed into 3D printer, mixed proportion A：B=1 kilogram：0.1 kilogram to 1 kilogram：2 kilograms.
Notice that thermoplastic plastic's raw material there are many kinds, have the temperature needed for good fluidity also different.
Silk Powder recited above, including tussah powder, silk (including mulberry silk, tussah silk, ricinus silk, cassava
Silk etc.）Powder, or itself have network structure, can use this patent methods described production other various plant fiber powders
End.
Nursing membrane material after being sufficiently mixed is sent into 3D printer, is printed and is matched completely with nursing dept. geometric properties
Individual nursing film.
By taking face as an example, it is ensured that nostril, eyes, eyebrow, beard, lip etc. are on the facial mask printed accurately by shape
Reserve.In addition, coming downwards to chin along the basal part of the ear and the face wheel for all sites at edge of being gained fame and fortune behind canthus, on the upside of ear to forehead
Exterior feature can completely be covered by facial mask.The facial mask so printed plays the size by facial contour and the facial geometric feature of people
The characteristics of complete covering.
To the 3D printing with AB materials, printed nursing film carries out slight drying process shaping, to the 3D with AC materials
Print, it is i.e. plastic after printed nursing film progress cooling down.
Step E and step F, for nursing demand, on the surface that film contacts with skin of face, by other shower nozzles of printer
Order addition nurses raw material to film surface.Method is：By inversion membrane, in film and the surface of skin contact, first by overall shield
Basic material needed for reason is sprayed to film surface by printer head.During this spraying, to needing other special shields
The part of reason, shower nozzle are not spray basic material, are vacated.Then, when film is transported to next shower nozzle along production line
During position, the part of other special cares is being needed, the shower nozzle containing its composition again sprays the raw material for needing special care
Beat the demand for the film position for needing special care, reaching individual nursing.
Illustrate below by taking facial mask as an example.
By taking facial mask as an example, first, after scanner is scanned to the face of individual, facial-care is basic by their entirety, if
Conclusion is that mass-type foundation needs facial mask based on whitening, and mass-type foundation composition is added based on whitening elite by the shower nozzle of printer
Skin care raw material is to facial mask and the surface of skin contact；If conclusion, which is mass-type foundation, to be needed to alleviate the facial mask based on drying regime,
Connect by skin care raw material of the shower nozzle addition mass-type foundation composition of printer based on amino acid and hyaluronic acid to facial mask and skin
Tactile surface；Etc..
Further, in addition to skin care raw material is added in mass-type foundation, the physical features and its ad-hoc location that are obtained in facial scan
Facial mask part, skin care raw material is added using subtraction/Shift Method method.That is, the privileged site is in print procedure, addition
The printing head of mass-type foundation composition does not operate in the part（Subtraction）, but by other charging shower nozzles addition targetedly other
Special care composition is to facial mask surface（Replace）.Such as：Determine that the skin of particular location and size is coarse, dark for facial scan
The positions such as light, spot, in facial mask by the surface with skin contact, mass-type foundation composition is replaced by spraying with collagen, reed
Skin care raw material based on luxuriant growth extract solution, amino acid or hyaluronic acid etc. is in this privileged site；The spy of whelk is being grown on the face
Determine position, mass-type foundation composition be replaced by spraying containing anti-acne, anti-inflammatory, calmness skin care raw material；In the lineolate portion in canthus
Position, mass-type foundation composition, which is replaced by, sprays the skin care raw material for pinning skin moisture to administer water shortage microgroove, etc..
It is described above to be carried out using streamline spraying, for example, after scanner is scanned to the face of individual, if knot
It is first that the basis of whitening is former in film and the surface of skin contact by being that mass-type foundation needs based on whitening, locally to need anti-inflammatory anti-acne
Material is sprayed to film surface by printer head.During this spraying, position is needed to topical anti-inflammatory anti-acne, shower nozzle is not
Whitening raw material is sprayed, is vacated.Then, when film is transported to next nozzle position along production line, anti-inflammatory anti-acne is being needed
Part, shower nozzle sprays the raw material for needing anti-inflammatory anti-acne to film part.
The business model that the present invention considers is to establish facial-care consulting shop throughout the country, by training qualified face
Nurse consultant and facial scan is carried out to client, scan data is straight after the printing of the production center by network delivery to the production center
Sending and receiving goods is to user.
Nurse film it is therein another be belly wrinkle-care, belly wrinkle-care is to be directed to postpartum belly wrinkle-care,
You are rung at twilight gestational period load-bearing, and the collagenous fibres of skin and elastic fibrous tissue are destroyed, and thinning of skin is attenuated for purple
The speckle of color is striae of pregnancy, after termination of pregnancy（Postpartum）It is difficult to disappear, influences figure and the physical and mental health of women.Therefore, it is vast
Womankind is after termination of pregnancy（Postpartum）, the removal as early as possible to belly wrinkle, original perfect belly moulding is replied, is had strong
It is required that.
Postpartum belly wrinkle-care（Remove）, can by massage, perform the operation, take exercise the methods of, produced with it with slim light line
Product remove.
Personalized postpartum belly wrinkle-care（Remove）The 3D printing method of film, it is exactly personal using matching completely is printed
The belly wrinkle-care of stature feature（Remove）Film, the method for slim light line product is printed with film to remove belly wrinkle.
Personalized postpartum belly wrinkle-care（Remove）The 3D printing method of film, it is consistent with the printing production method of facial mask,
Therefore will not be repeated here, difference is：
1st, facial scan is changed to belly, waist swept-volume：
2nd, by skincare material on demand, position be changed to slim light line product.Such as：For tangerine hull constitution, desalination striae of pregnancy
And fat line position, grape candy factoring and Lu Ding compositions can be used；The positions such as waist, stern to easily producing fat accumulation
It is local, plant body shaping composition etc. can be equipped with using natural mineral elite.
Nursing film another item therein is the nursing of other positions, and its method is consistent with the printing production method of facial mask, herein
Repeat no more, difference is：
1st, facial scan is changed to need position to scan：
2nd, skincare material on demand, position be changed to customized as required material, such as skin care, sun-proof, wound care, medicine
Administer, fracture nursing etc..
Claims (7)
- A kind of 1. 3D printing method for nursing film, it is characterised in that including,Step A. scanning nursing position；Step B. data processings；Step C. makes the counterdie consistent with nursing feature；Membrane material is sent into 3D printer by step D., and thin film is printed on counterdie；Membrane material include Silk Powder, from Body have on the string powder of network structure and to skin fanout free region or have skin-protecting function and can in the drying process with it is above-mentioned The crosslinking agent of powder-stuck；Above-mentioned powder uniformly mixes with crosslinking agent, forms pulpous state printed matter；The Silk Powder includes mulberry Silk, tussah silk, ricinus silk, cassava silkwormsilk, tussah；Crosslinking agent is medical gelatin liquid or thermoplastic plastic；Step E. receives data processed result, and basic nursing composition is sprayed extremely by printer head to film general duty nursing position Film surface, and vacate film special care region；Step F. receives data processed result, and the special care region sequentially vacated respectively to film is distinguished by printer head Sequentially spray corresponding nursing composition；Step G. individual nursing film finished products.
- 2. the 3D printing method of nursing film according to claim 1, it is characterised in that the 3D printer includes multiple The streamline printer that shower nozzle is formed, the different nursing product of the interior placement of Storage Box are delivered to film surface by shower nozzle.
- 3. the 3D printing method of nursing film according to claim 1, it is characterised in that between above-mentioned steps D and step E Forming processes are carried out, slight drying and moulding, or cooling shaping are carried out to printed film, form the nursing film of network structure.
- 4. the 3D printing method of nursing film according to claim 1, it is characterised in that the nursing film includes facial mask, abdomen Portion's gestation nursing film, the film that the sun-proof of other position special requirements of body, treatment of wounds, fracture nursing need.
- 5. the 3D printing method of nursing film according to claim 1, it is characterised in that the preparation of the powder includes following Step：（1）：Silk cocoon is poured into sodium carbonate liquor, boils 20-30 minutes；Sodium carbonate liquor concentration is 0.3-0.7%；The weight of silk cocoon and sodium carbonate ratio is 1：20-200；（2）Silk cocoon is pulled out, is put into the solution of sulfuric acid, boils 40-80 minutes；The concentration of sulfuric acid solution is 2-5%；The weight of silk cocoon and sulfuric acid solution ratio is 1：20-200；（3）Silk cocoon is pulled out, is put into clear water, stirs, adds a small amount of sodium hydroxide, while detects the pH value of solution, is controlled 6-7, stable 10-15 minutes；（4）Silk cocoon is pulled out, rinsed again with clear water, is dried after pulling out, grinds powdering.
- 6. the 3D printing method of nursing film according to claim 1, it is characterised in that the medical gelatin liquid is gelatin Formed with water, the weight ratio of gelatin and water is 1：100；The weight ratio of powder and medical gelatin liquid is 1：20-50.
- 7. the 3D printing method of nursing film according to claim 1, it is characterised in that the thermoplastic plastic and Silk Powder End is sufficiently stirred, mixed, and being warming up to thermoplastic plastic's raw material has temperature needed for good fluidity；Thermoplastic plastic and powder Weight ratio is 1：0.1-2.