CN105055182A - Method for manufacturing nursing membrane through 3D printing - Google Patents
Method for manufacturing nursing membrane through 3D printing Download PDFInfo
- Publication number
- CN105055182A CN105055182A CN201510550014.5A CN201510550014A CN105055182A CN 105055182 A CN105055182 A CN 105055182A CN 201510550014 A CN201510550014 A CN 201510550014A CN 105055182 A CN105055182 A CN 105055182A
- Authority
- CN
- China
- Prior art keywords
- film
- nursing
- powder
- printing
- membrane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for manufacturing a nursing membrane through 3D printing. The method includes the steps that A, a nursed part is scanned; B, data processing is conducted; C, membrane materials are prepared; D, the fully-mixed membrane materials are fed into a 3D printer, and accordingly a membrane which is completely matched with the geometrical characteristic of the nursed part is printed out; E, the printed membrane is subjected to slight laser sintering, and a nanocrystal nursing membrane of the net-shaped structure is formed; F, nursing components are sprayed onto the surface, making contact with skin, of the laser-sintered membrane according to requirements. The method has the advantages that the nursing membrane can be completely matched with the personal characteristic; moreover, different components can be added according to the needs of different parts, the defect that one single membrane is single in effect is overcome, and the individual needs of people are met.
Description
Technical field
The present invention relates to a kind of manufacture method of nursing film, particularly relate to a kind of method utilizing 3D printer to print nursing film.
Background technology
1, facial film compares the product liked and use in numerous women's skin care item, its important object makes up makeup removing and the still not enough cleaning that washes one's face, coordinate other essential ingredient to realize other maintenance function, such as replenishing water and preserving moisture, whitening, defying age, Sage Extract etc. simultaneously.
But all facial films on the market at present, although there is various different effect in maintenance function, it has the shortcoming of 2 general character.
First shortcoming is the overall efficacy of often kind of (often opening) facial film is single.Such as: P&G SK-II facial treatment mask primary efficacy is that nature moisturizing factor gos deep into horny layer, skin care; Fei Nameng legend emperor court of a feudal ruler Cymbidium ensifolium (L.) Sw. Zhuo effect brilliant white moisturizing silk mask, primary anti-ageing nursing and plant attain extraction nursing; The saturating white U.S. flesh of Shiseido concentrates cleawhite pack, and white elite rests on infiltrating cells in skin horny layer; Lancome intensive moisturizing elite facial film, hydropenia microgroove is administered in seizure, pinning skin moisture; Neutrogena deep moisturizing facial film, absorption, release moisturizing molecule are continuously skin moisturizing; U.S. and the lubricious face film of milk hundred, with protein, aminoacid with pliable and toughly calcareously improve face skin dimness, matt phenomenon; Olay talent for swimming is white Whitening, spot facial film thoroughly, is main for skin whitening; Elizabethan. Ya Dun, for skin supplements required lipid and the phenomenon can strengthening the resistance of skin, the dry inflammation of the Slow that relaxes; Avene is releived moisture saver mask, releives, moisturizing, alleviates skin sensitivity phenomenon; FANCL without interpolation speckle dispelling brilliant white Face-protecting mask, with clean white light speckle for purport, etc.These facial films, although effect is fine, based on the feature that type is unified, womankind often can not take into account self nursing of several needs in use.Citing, may need near eye to administer hydropenia microgroove, main body face may need to brighten nursing, may need to releive, moisturizing near lip, alleviates skin tender subject, and this is that the facial film of single effect cann't be solved.
Second shortcoming of the facial film sold on the market is that often to open (kind) facial film be all unified production, and production process cannot consider everyone facial geometric feature.We everyone, the size of the organs such as nose, face, lip, chin, geometry, relative position are all different, and each species diversity of everyone facial geometric feature just makes everyone face in the world vary just.Based on the difference of this geometric properties, people often have the much inconvenience brought by unified production in the process using facial film.Such as: facial film size is inadequate, can not cover face completely; Face is because of the reason of profile, and facial film can not be sturdy, and liquid can along seam trickling and facial film need cut out many cuttves (facial film had can cutting 12 cutter) to ensure to apply at consolidation on the face, use extremely inconvenient, etc.In addition, some facial film is the problem solving facial geometric feature, and what made by face paper is thin especially, uses extremely inconvenient.
2, your twilight of load-bearing is rung trimester of pregnancy, and collagen fiber and the elastic fibrous tissue of skin are destroyed, and make thinning of skin attenuate as purpureal speckle and striae gravidarum, after termination of pregnancy (puerperal) be difficult to disappear, affect figure and the physical and mental health of women.Therefore, numerous womankinds are (puerperal) after termination of pregnancy, to the removal as early as possible of abdominal part wrinkle, replys original perfectly abdominal part moulding, have strong requirement.
In abdominal part wrinkle-care in puerperal (removal), cross the methods such as massage, operation, exercise though available, also can remove with slim light stricture of vagina film.
3, other positions of health, when need nurse, often adopt the modes such as wrapping, such as, and treatment of wounds.Again such as, after fracture, traditional Chinese medical science bag medicine or planter cast, extremely inconvenient.
Summary of the invention
Technical problem to be solved by this invention is, provides a kind of personal nursing need and geometric properties and customized 3D printer to print the method for nursing film.
The technical solution adopted in the present invention is: a kind of method of 3D printing and making nursing film, comprises,
Steps A. scanning nursing position;
Step B. date processing;
The preparation of step C. membrane material;
Abundant mixed membrane material is sent in 3D printer by step D., prints and the film of nursing position geometric properties and mating completely;
Step e. printed film is carried out slightly laser sintered, form the cancellated nursing film of nanocrystal;
Step F. to laser sintered good film, on the surface with contact skin, spray nursing composition on demand.
Described steps A, obtains and obtains relevant information by nursing dept.'s scanner.
Described 3D prints and includes many nozzle printings machine, places different nursing products and be delivered to nursing film surface by shower nozzle in Storage Box;
Described nursing membrane material comprises organic titanium and nano titanium oxide, by organic titanium powder and nano titanium dioxide powder Homogeneous phase mixing, forms powdery printed matter; Described organic titanium powder is butyl titanate powder, titanium propanolate powder, isopropyl titanate powder, titanium ethanolate powder, methoxyl group titanium powder or titanium alcohol fourth vinegar powder etc.
Described nursing membrane material comprises organic titanium powder, anhydrous alcohol and nano titanium oxide; First, organic titanium powder and anhydrous alcohol are mixed to form liquid, and the weight ratio of liquid mixing is 1g:3-100ml; Then joined by hydrochloric acid in the liquid state of organic titanium powder and anhydrous alcohol, liquid viscosity improves, but does not form jelly, and the pH value of the mixture liquid of organic titanium powder and anhydrous alcohol is 3-5, is not less than 3; And then nano titanium dioxide powder is joined in liquid, form pulpous state printed matter; The ratio of nano titanium dioxide powder and liquid is 1g:2-10ml.
The printed nursing film of described flour 3D carries out slightly laser sintered, forms the cancellated facial film of nanocrystal; Laser sintered film surface and inner (entirety) temperature, between 300-600 degree Celsius, are no more than 600 degrees Celsius; The printed nursing film of described slurry like material 3D is slightly sintered by laser, but laser sintered film surface temperature is between 300-600 degree Celsius, is no more than 600 degrees Celsius.Film internal temperature control, between 150-250 degree Celsius, is no more than 250 degrees Celsius.
Described 3D printer print thickness is 0.1-0.5mm, laser sintered; Print on sintered membrane again, again laser sintered, to required nursing thickness.
Described 3D printer is disposable be printed to desired thickness after, disposable sintering completes.
After described 3D prints nursing film is laser sintered and completes, on the surface that nursing film contacts with skin of face, spray on demand nurse composition enter film body for.
Described 3D prints nursing film and comprises facial film, abdominal pregnancy nursing film, other position special requirements of health as sun-proof, treatment of wounds, fracture nursing etc. need film, laser sintered complete after, on the surface that contacts with skin of face of nursing film, spray on demand required composition enter film body for.
The invention has the beneficial effects as follows: nursing film can be fitted with individual characteristics completely completely, and according to the composition needing interpolation different of different parts, overcome the defect that single film effect is single, meet the individual sexual needs of people.
Detailed description of the invention
Below in conjunction with detailed description of the invention, the present invention is described in further detail:
Steps A. the scanning at nursing position; Use the nursing position of the scanner of commercial maturation to individual to scan, obtain corresponding information;
For face, scan the face recognizing system of optional use such as Visionics company; LauTech. face recognizing/confirmation the system of company; The system of Miros company; The system of C-VIS company; Banque-Tech. the system of company; The system of VisageGallery; The system of PlettacElectronic company; The BioID system in Taiwan, and the system that other technologies content is lower, etc.; The organ such as size, eyes, nose, face, lip, chin of the facial geometric feature such as facial contour of Obtaining Accurate facial film end user (comprises eyebrow, beard) geometry, size, the master datas such as relative position print the most basic foundation as facial film.
Again for face, when using the face of facial scanner to individual of commercial maturation to scan, obtain some trickle physical features extremely ad-hoc location of face simultaneously, as whether canthus has microgroove, forehead whether to have wrinkle, whether skin ad-hoc location coarse, dim, have spot, and some physiological features such as length on the face has the size, particular location etc. of comedo, nevus.
Or for face, when using the face of facial scanner to individual of commercial maturation to scan, also need the mass-type foundation obtaining human body face.Such as: whether face skin is dim, matt; Whether face skin is in drying regime, and face skin is the need of brightening.
Step B. date processing; After nursing dept.'s bit scan, all data enter computer and carry out date processing.
Step C. nurses the preparation of membrane material; The present invention is used for the nursing membrane material that 3D prints, and is the mixture of organic titanium and nano titanium oxide.
Far away from 1972, people just find, n-type semiconductor TiO2 is subject to light (ultraviolet light) that wavelength is less than or equal to 387.5nm when irradiating, and the electronics of valence band will obtain the energy of photon and more front to conduction band, forms light induced electron (e-) and photohole (h+).
The Organic substance on the oxidable TiO2 of the being adsorbed in surface of photohole h+ or OH-and the H2O molecular oxygen being adsorbed on TiO2 surface is changed into OH free radical, the oxidability of OH free radical is the strongest in the oxidant existed in water body, its mineralising is the innocuous substance such as inorganic molecules, CO2 and H2O by most Organic substances and inorganic pollution in energy oxidize water.Such nursing film, effect is multi-functional.For facial film, the facial film that method described in this patent is produced, after skin care ingredient uses, facial film itself, if use by day, still have the oils and fats on skin, Lao Pi cleaned, decompose, effect that mineralising is the innocuous substances such as CO2 and H2O of inorganic molecules, play nature whitening, brighten, the effect of tenderization skin.Why Here it is nurses the material of film, the reason of first-selected organic titanium and nano titanium oxide.
Ultra-fine titanium dioxide has excellent ultravioletlight screening and the transparency, and Chang Zuowei sunscreen mixes in textile fabric.Again due to its avirulence, harmless feature, ultra-fine titania powder is also added into makes sun care preparations in sun-proof cream.Traditional sunscreen mostly is the organic compound such as benzophenone, o-amino benzoyl ketone, salicylic acid esters, para-amino benzoic acid class, cinnamate derivative, thus unstable, the life-span is short, and side effect is larger, there is certain toxicity and zest, if it is excessive to add, chemical allergy can be produced, even may cause skin carcinoma.And nano titanium oxide is inorganic constituents, there is excellent chemical stability, heat stability and non-migratory and stronger reducing power, covering power, lower corrosivity, good easily disperse, and nontoxic, tasteless, nonirritant, use safety, also has the effect of deodorization and sterilization concurrently.Just because of this, nano titanium oxide is extensively paid attention to and is progressively replaced some organic anti ultraviolet agents very soon, becomes a kind of physical shielding type of superior performance anti ultraviolet agent in current sun care preparations.
But the application of titanium dioxide in skin protection, is still in the application using powder.That is: ultra-fine titania powder is added in sun-proof cream, make sun care preparations.
The preparation of nursing membrane material has two kinds of methods.
First method:
A: by the organic titanium of powder, such as butyl titanate powder (chemical molecular formula Ti (OC
4h
9)
4) (being called for short composition A) and nano titanium dioxide powder (being called for short composition B) Homogeneous phase mixing, form the 3D printed matter of powdery.In mixture ratio, the percentage by weight of composition A can from 10% to 100%, and alleged organic titanium can comprise titanium propanolate, isopropyl titanate, titanium ethanolate, methoxyl group titanium, titanium alcohol fourth vinegar;
B: AB material is fully mixed.
Second method:
A: by powder organic titanium, such as butyl titanate (chemical molecular formula Ti (OC
4h
9)
4) mix with anhydrous alcohol, mixed proportion can from 1 gram of powder organic titanium to 3 milliliters of anhydrous alcohols to 1 gram powder organic titanium to 100 milliliters of anhydrous alcohols, alleged organic titanium can comprise titanium propanolate, isopropyl titanate, titanium ethanolate, methoxyl group titanium, titanium alcohol fourth vinegar, alleged anhydrous alcohol can comprise ethanol, methanol, butanols, propanol, isopropyl alcohol, mixed like this material is called liquid parts A.
B: nano titanium dioxide powder (being called for short composition B) is joined in liquid parts A, fully stirs, mix, form the printed matter of pulpous state.Mixed proportion can from 2 milliliters of liquid parts A to 1 gram of nano titanium dioxide powder (composition B) to 10 milliliters of liquid parts A to 1 gram of nano titanium dioxide powder (composition B);
C: AB mixture is fully stirred;
D: hydrochloric acid is joined in the liquid state of organic titanium powder and anhydrous alcohol, liquid viscosity improves, but does not form jelly, and the pH value of the mixture liquid of organic titanium powder and anhydrous alcohol is 3-5, is not less than 3;
E: joined by nano titanium dioxide powder in liquid, forms pulpous state printed matter; The ratio of nano titanium dioxide powder and liquid is 1g:2-10ml.
Mixed nursing membrane material abundant in above-mentioned steps is sent in 3D printer by step D., prints the individual nursing film mated completely with nursing dept. geometric properties.
For face, guarantee nostril, eyes, eyebrow, beard, lip etc. reserve by shape accurately on the facial film printed.In addition, chin and can by the complete covering of facial film from gaining fame and fortune the facial contour of all sites at edge to forehead behind canthus, on the upside of ear is come downwards to along the basal part of the ear.The facial film printed like this plays the feature by the size of facial contour and the complete covering of the facial geometric feature of people.
Step e. print with the 3D of flour, printed nursing film carries out slightly laser sintered, forms the cancellated nursing film of nanocrystal.Laser sintered film surface and inner (entirety) temperature, between 300-600 degree Celsius, are no more than 600 degrees Celsius.Print with the 3D of slurry like material, printed nursing film is slightly sintered by laser, but laser sintered film surface temperature is between 300-600 degree Celsius, is no more than 600 degrees Celsius.Film internal temperature control, between 150-250 degree Celsius, is no more than 250 degrees Celsius.Laser sinteredly play two effects, one is by powder material sinter molding, and two is in sintering process, and the C-H material in organic titanium is all removed by sintering, C-H material forms cavity after being removed by sintering, and nursing film is actually like this and is made up of thin film nanometer level microporous in a large number.Its effect has two: a) ventilative; B) store skin protection raw material to use for skin protection in hole.
Printing wherein, sintering can divide again two kinds of modes to carry out.Method A): print one deck, control print thickness is 0.1-0.5mm, laser sintered afterwards, then prints on sintered membrane, again laser sintered, so repeatedly, till required facial film thickness (0.5-5mm); Method B): be once printed to desired thickness, disposable sintering.
For facial film, utilize organic titanium and nano titanium dioxide powder Homogeneous phase mixing and the facial film printed, its internal structure is multi-level nanostructure-containing and the thin film of nano-pore.The existing certain pliability of this facial film, facial film intensity is good again, and facial film after a procedure, can be collected, return the production center by individual, after sterilization, cleaning, by data on file data, facial film sprays skin care ingredient again, recycles.
Secondly, 3D prints and includes many nozzle printings machine, and what in Storage Box, placement was different protects nursing product by shower nozzle to nursing film surface,
Step F. after laser sintered completing, for nursing demand, on the surface that film contacts with skin of face, add nursing raw material on the surface by other shower nozzles of printer.
Illustrate for facial film below.
For facial film, by overall face nursing basis, need the facial film based on whitening, by other shower nozzles interpolation mass-type foundation composition of printer based on the surface of the skin protection raw material of whitening elite to facial film and contact skin; Need based on the facial film alleviating drying regime, in facial film print procedure, by other shower nozzles interpolation mass-type foundation composition of printer based on the surface of the skin protection raw material of aminoacid and hyaluronic acid to facial film and contact skin; Etc..
Further, except skin protection raw material is added in mass-type foundation, the facial film position of the physical features obtained in facial scan and ad-hoc location thereof, adopts subtraction/Shift Method method to add skin protection raw material.That is, this specific part is in print procedure, adds the printing head of mass-type foundation composition in this local inoperation (subtraction), but by other reinforced shower nozzles add targetedly other special care compositions to facial film surface (replacement).Such as: the position such as the skin for facial scan determination particular location and size is coarse, dim, spot, at facial film by the surface with contact skin, mass-type foundation composition is replaced by and sprays based on the skin protection raw material of collagen protein, Aloe extraction solution, aminoacid or hyaluronic acid etc. at this specific part; Growing the specific part of comedo on the face, mass-type foundation composition is replaced by and sprays containing anti-pox, antiinflammatory, calm skin protection raw material; The lineolate position at canthus, mass-type foundation composition is replaced by the skin protection raw material that sprays and pin skin moisture to administer hydropenia microgroove, etc.
The facial film that the powdery utilizing powdery organic titanium and powdered nanoparticles titanium dioxide to be uniformly mixed to form prints raw material and prints, its internal structure is multi-level nanostructure-containing and the thin film of nano-pore.The existing certain pliability of this facial film, facial film intensity is good again, and facial film after a procedure, can be collected, return the production center by individual, after sterilization, cleaning, by data on file data, facial film sprays skin care ingredient again, recycles.Based on the C-H material can removing part in machine titanium in facial film time laser sintered, facial film contains a large amount of nanoscales, micron order micropore, meets ventilative, storage skin protection raw material effect in hole.
Utilize powdery organic titanium powder to mix the pulpous state be uniformly mixed to form with powdered nanoparticles titanium dioxide again with anhydrous alcohol and print raw material and the facial film printed, based on the C-H material of part in the organic titanium can removing facial film surface time laser sintered and the volatilization of anhydrous alcohol in sintering process of facial film inside, facial film is also have containing a large amount of nanoscales, micron order micropore, also meets ventilative, storage skin protection raw material effect in hole.This facial film pliability is better, but facial film intensity difference, can only single use.But the facial film that the method makes, transparency is higher, and people can be worn over and go on a journey in the daytime on the face, effectively takes precautions against ultraviolet instrument as face.This is because nano titanium oxide all has iris action to medium wave district and long-wavelength region ultraviolet, it is higher at the absworption peak of ultra-violet (UV) band.
The business model that the present invention considers is, set up facial-care consulting shop throughout the country, by training, qualified facial-care consultant carries out facial scan to client, and scan-data is by network delivery to the production center, and the production center prints rear directly delivery to user.
Nursing film wherein another is abdominal part wrinkle-care, abdominal part wrinkle-care is for abdominal part wrinkle-care in puerperal, trimester of pregnancy, your twilight of load-bearing rang, collagen fiber and the elastic fibrous tissue of skin are destroyed, thinning of skin is made to attenuate as purpureal speckle and striae gravidarum, after termination of pregnancy (puerperal) be difficult to disappear, affect figure and the physical and mental health of women.Therefore, numerous womankinds are (puerperal) after termination of pregnancy, to the removal as early as possible of abdominal part wrinkle, replys original perfectly abdominal part moulding, have strong requirement.
Abdominal part wrinkle-care in puerperal (removal), can by methods such as massage, operation, exercises, that joins removes with slim light stricture of vagina product.
The 3D Method of printing of personalization abdominal part wrinkle-care (removal) film in puerperal, adopts exactly and prints abdominal part wrinkle-care (removal) film mating individual stature feature completely, and film prints has the method for slim light stricture of vagina product to remove abdominal part wrinkle.
The 3D Method of printing of personalization abdominal part wrinkle-care (removal) film in puerperal, consistent with the printing production method of facial film, therefore do not repeat them here, difference is:
1, facial scan is changed into abdominal part, waist swept-volume:
2, skincare material is changed into slim light stricture of vagina product by demand, position.Such as: for tangerine hull constitution, desalination striae gravidarum and obesity striae position, Fructus Vitis viniferae candy factoring and rutosids composition can be adopted; To the local, the position such as waist, buttocks easily producing athero, natural mineral elite can be adopted to be equipped with plant body shaping composition.Etc..
Nursing film wherein again one be other positions nursing, its method is consistent with the printing production method of facial film, and do not repeat them here, difference is:
1, facial scan changed into need position to scan:
2, skincare material changes customized as required material into by demand, position, such as skin protection, sun-proof, wound care, medicine improvement, fracture nursing etc.
Claims (10)
1. a method for 3D printing and making nursing film, is characterized in that, comprises,
Steps A. scanning nursing position;
Step B. date processing;
The preparation of step C. membrane material;
Abundant mixed membrane material is sent in 3D printer by step D., prints and the film of nursing position geometric properties and mating completely;
Step e. printed film is carried out slightly laser sintered, form the cancellated nursing film of nanocrystal;
Step F. to laser sintered good film, on the surface with contact skin, spray nursing composition on demand.
2. 3D printing and making nurses the method for film according to claim 1, it is characterized in that, described steps A, obtains and obtains relevant information by nursing dept.'s scanner.
3. 3D printing and making nurses the method for film according to claim 1, it is characterized in that, described 3D prints and includes many nozzle printings machine, and it is surperficial that the nursing product that in Storage Box, placement is different is delivered to nursing film by shower nozzle.
4. 3D printing and making nurses the method for film according to claim 1, and it is characterized in that, described nursing membrane material comprises organic titanium and nano titanium oxide, by organic titanium powder and nano titanium dioxide powder Homogeneous phase mixing, forms powdery printed matter; Described organic titanium powder is butyl titanate powder, titanium propanolate powder, isopropyl titanate powder, titanium ethanolate powder, methoxyl group titanium powder or titanium alcohol fourth vinegar powder etc.
5. 3D printing and making nurses the method for film according to claim 1, and it is characterized in that, described nursing membrane material comprises organic titanium powder, anhydrous alcohol and nano titanium oxide; First, organic titanium powder and anhydrous alcohol are mixed to form liquid, and the weight ratio of liquid mixing is 1g:3-100ml; Then joined by hydrochloric acid in the liquid state of organic titanium powder and anhydrous alcohol, liquid viscosity improves, but does not form jelly, and the pH value of the mixture liquid of organic titanium powder and anhydrous alcohol is 3-5, is not less than 3; And then nano titanium dioxide powder is joined in liquid, form pulpous state printed matter; The ratio of nano titanium dioxide powder and liquid is 1g:2-10ml.
6. the method for 3D printing and making nursing film according to claim 1, it is characterized in that, the printed nursing film of described flour 3D carries out slightly laser sintered, the cancellated facial film of formation nanocrystal; Laser sintered film surface and inner (entirety) temperature, between 300-600 degree Celsius, are no more than 600 degrees Celsius; The printed nursing film of described slurry like material 3D is slightly sintered by laser, but laser sintered film surface temperature is between 300-600 degree Celsius, is no more than 600 degrees Celsius; Film internal temperature control, between 150-250 degree Celsius, is no more than 250 degrees Celsius.
7. 3D printing and making nurses the method for film according to claim 1, and it is characterized in that, described 3D printer print thickness is 0.1-0.5mm, laser sintered; Print on sintered membrane again, again laser sintered, to required nursing thickness.
8. according to claim 1 3D printing and making nursing film method, it is characterized in that, described 3D printer is disposable be printed to desired thickness after, disposable sintering completes.
9. the method for 3D printing and making nursing film according to claim 1, after described 3D prints nursing film is laser sintered and completes, on the surface that nursing film contacts with skin of face, spray on demand nurse composition enter film body for.
10. 3D printing and making nurses the method for film according to claim 1, described 3D prints nursing film and comprises facial film, abdominal pregnancy nursing film, the film as the needs such as sun-proof, treatment of wounds, fracture nursing of other position special requirements of health, laser sintered complete after, on the surface that contacts with skin of face of nursing film, spray on demand required composition enter film body for.