CN105314217A - Production method of high-air permeability corrugated paper packing box - Google Patents
Production method of high-air permeability corrugated paper packing box Download PDFInfo
- Publication number
- CN105314217A CN105314217A CN201510860710.6A CN201510860710A CN105314217A CN 105314217 A CN105314217 A CN 105314217A CN 201510860710 A CN201510860710 A CN 201510860710A CN 105314217 A CN105314217 A CN 105314217A
- Authority
- CN
- China
- Prior art keywords
- dry powder
- packing chest
- wrapper
- packing box
- zeolite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a production method of a high-air permeability corrugated paper packing box. The production method comprises the following steps: step 1, producing a corrugated board from such raw materials as zeolite dry powder, corrugated paper pulp, KH550, heavy calcium carbonate, polyvinyl chloride and tributyl phosphate; step 2, performing film laminating; and step 3, preparing the packing box: performing a nailing operation or a gluing operation on the film-laminated packing paper according to output parameters to form the high-air permeability corrugated paper packing box.
Description
Technical field
The invention belongs to corrugated board packing box preparing technical field, be specifically related to a kind of method preparing highly-breathable corrugated board packing box.
Background technology
Along with economic development, the in-depth day by day of economic globalization, the kinds such as long-distance transport flowers, fresh fruit, vegetables, seafood and quantity increase day by day.When packing chest is Commodity Transportation must article, usually, in order to keeping and the transport various article such as agriculture, aquatic products, often all utilize packing chest to enter packaging.Existing packing chest great majority are made by fluting board, and also some is made by resin.Low according to cost, lightweight, easy to use, the feature such as recycling, fluting board also just becomes the main separation making packing chest.In the long-distance transport process of agriculture, aquatic products commodity, the permeability to air problem of packing chest must be considered for some commodity.
In the transportation of the agriculture and forestry products such as fruit, in order to keep the fresh of products such as fruit, need the air in packing chest can to circulate renewal, existing packing chest cannot accomplish this point.The fruit packaging box circulated in market is short of mostly because considering fruit ventilating problem during cabinet design in long-distance transport process, and causes fruit poor air permeability, and fresh-keeping effect is bad, to such an extent as to fruit goes bad in transit, degenerates, and affects economic benefit.
In the transporting procedures of cut-flower, vital movement and the aging of flowers not yet stop, and cause flowers that some changes occur in transporting procedures.As dehydration wilting, rotten leaf, flower fade, come off, petal can not open, the series of problems such as the fast development of disease and propagation.Therefore the conditions such as suitable temperature, humidity and a gas must be provided to the cut-flower of transportation.Owing to being the environment being in a relative closure in cut-flower transportation, easily causing the accumulation of especially gas particularly ethene, cause ethylene-sensitive cut-flower petal, flower abscission, old and feeble in advance; Because cut-flower can cause the decline of oxygen concentration and the rising of gas concentration lwevel in the breathing of transportation, if do not regulated, easily cause high concentration carbon dioxide and low concentration oxygen impairment of qi evil.
In order to the consideration of permeability to air, prior art generally can offer hole on packing chest.After the Box Cover of the surrounding of casing closes, centre reserves space, form ventilation mouth, the ventilation mouth design of above-mentioned packing chest, is not easy to disposable joint sealing, needs to carry out at twice when joint sealing, first seal the side of ventilation mouth, and then seal the opposite side of ventilation mouth, otherwise sealing tape easily blocks ventilation mouth, makes ventilation mouth lose ventilative effect.Therefore this design is also not easy to carry out automatic joint sealing by machinery, makes troubles to the joint sealing of packing chest, reduces joint sealing efficiency, and ventilation mouth can affect the intensity of packing chest simultaneously, reduces the service life of packing chest.
Therefore, current casing is to its packaging out of reach corresponding requirements.
Summary of the invention
In order to overcome, existing corrugated-paper packaging box can not effectively be breathed freely, joint sealing inconvenience etc. deficiency, the object of the invention is to provide a kind of method preparing highly-breathable corrugated board packing box, solve corrugated board packing box production process in prior art loaded down with trivial details, be not easy to carry out automatic joint sealing by machinery, ventilation mouth can affect the intensity of packing chest simultaneously, reduces the problems such as the service life of packing chest.
In order to solve these problems of the prior art, technical scheme provided by the invention is:
Prepare a method for highly-breathable corrugated board packing box, it is characterized in that comprising the following steps:
Step 1, production corrugated board:
1.1 select zeolite dry powder feeding roller mill to be crushed to 20-50 micron obtains zeolite dry powder;
1.2 get described zeolite dry powder, fluting board paper pulp, KH550, ground calcium carbonate, polyvinylchloride, tributyl phosphate mix, each raw material weight consumption is zeolite dry powder 10-20 part, fluting board paper pulp 500-800 part, KH55012-20 part, ground calcium carbonate 5-12 part, polyethylene 1-3 part, tributyl phosphate 1-3 part; The paper making raw material mixed is sent into corrugated paper making processing line;
1.3 dry and add and be pressed into fluting board, become wrapper through polishing;
Step 2, overlay film:
Be that spray film liquid sprays film on the wrapper with water paint, coating thickness 5 microns-0.5 millimeter, then rolls operation firmly;
The preparation of step 3, packing chest:
To be designed a package box structure by packing chest computer aided design (CAD), comprise empty size (length) in packing chest, cardboard materials calculate, the type selecting of standard box-shaped, carry out packing chest printout;
According to output parameter to the wrapper of overlay film carry out stitching operation or laminating operation make highly-breathable corrugated board packing box.
Further, the wrapper after described polishing has the Bendtsen permeability to air of the 200-500ml/min according to ISO5636-3:1992.
Further, ZSM-5, X, Y, L, A, SAPO type zeolite molecular sieve selected by described zeolite dry powder.
Further, the weight average molecular weight of described polyvinylchloride is 10-15 ten thousand.
Further, each raw material weight consumption is zeolite dry powder 12-15 part, fluting board paper pulp 550-700 part, KH55015-18 part, ground calcium carbonate 6-9 part, polyethylene 1-2 part, tributyl phosphate 2-3 part; 14 parts, preferred zeolite dry powder, fluting board paper pulp 600 parts, KH55016 part, ground calcium carbonate 8 parts, polyethylene 2 parts, tributyl phosphate 2 parts.
Further, step 2 uses hard milling train firmly to roll, hard milling train comprises frame, paper advance mechanism, coating and printing mechanism, preliminary pre-press nips, the shaping wheels of line ball and grooving mechanism, described frame is provided with the Membrane jetter structure between described coating and printing mechanism and precompressed mechanism.
Relative to scheme of the prior art, advantage of the present invention is:
Highly-breathable corrugated board packing box of the present invention compared with prior art, namely casing having excellent permeability without the need to arranging ventilation mouth, can meet the demand of agricultural aquatic products long-distance transport.Owing to not adopting ventilation mouth, packing chest of the present invention can facilitate disposable joint sealing and machine automatization joint sealing, improves joint sealing efficiency, ensures intensity and the service life of packing chest simultaneously.
Meanwhile, by using zeolite dry powder, KH550, ground calcium carbonate, polyvinylchloride, tributyl phosphate in the present invention, coordinating with paper pulp and selecting its weight consumption, products obtained therefrom has excellent permeability, cushion characteristic is good, firmly light, can be widely used in transport package.
Adopt water-based coating to carry out watermark spray film in technical solution of the present invention, water-based coating is environmental protection coating material, and leftover bits and pieces carton reclaims papermaking process easily, can not cause the wasting of resources.
Detailed description of the invention
Below in conjunction with specific embodiment, such scheme is described further.Should be understood that these embodiments are not limited to for illustration of the present invention limit the scope of the invention.The implementation condition adopted in embodiment can do further adjustment according to the condition of concrete producer, and not marked implementation condition is generally the condition in normal experiment.
Embodiment 1:
This prepares the method for highly-breathable corrugated board packing box, carries out according to following steps:
Step 1, production corrugated board:
1.1 select ZSM-5 zeolite dry powder feeding roller mill to be crushed to 20-30 micron obtains zeolite dry powder;
1.2 get described ZSM-5 zeolite dry powder, fluting board paper pulp, KH550, ground calcium carbonate, polyvinylchloride, tributyl phosphate mix, each raw material weight consumption is 12 parts, zeolite dry powder, fluting board paper pulp 550 parts, KH55015 part, ground calcium carbonate 6 parts, polyethylene 1 part, tributyl phosphate 2 parts; Polyvinylchloride weight average molecular weight is about 100,000, and the paper making raw material mixed is sent into corrugated paper making processing line;
1.3 dry and add and be pressed into fluting board, become wrapper through polishing;
Step 2, overlay film:
Be that spray film liquid sprays film on the wrapper with water paint, coating thickness 50 microns, then rolls operation firmly;
The preparation of step 3, packing chest:
To be designed a package box structure by packing chest computer aided design (CAD), comprise empty size (length) in packing chest, cardboard materials calculate, the type selecting of standard box-shaped, carry out packing chest printout;
According to output parameter to the wrapper of overlay film carry out stitching operation or laminating operation make highly-breathable corrugated board packing box.
Embodiment 2:
This prepares the method for highly-breathable corrugated board packing box, carries out according to following steps:
Step 1, production corrugated board:
1.1 select X-type zeolite dry powder feeding roller mill to be crushed to 20-40 micron obtains zeolite dry powder;
1.2 get described X-type zeolite dry powder, fluting board paper pulp, KH550, ground calcium carbonate, polyvinylchloride, tributyl phosphate mix, each raw material weight consumption is 18 parts, zeolite dry powder, fluting board paper pulp 750 parts, KH55018 part, ground calcium carbonate 10 parts, polyethylene 3 parts, tributyl phosphate 3 parts; Polyvinylchloride weight average molecular weight is about 140,000, and the paper making raw material mixed is sent into corrugated paper making processing line;
1.3 dry and add and be pressed into fluting board, become wrapper through polishing; Wrapper after described polishing has the Bendtsen permeability to air of the 250ml/min according to ISO5636-3:1992;
Step 2, overlay film:
Be that spray film liquid sprays film on the wrapper with water paint, coating thickness 0.1 millimeter, then rolls operation firmly;
The preparation of step 3, packing chest:
To be designed a package box structure by packing chest computer aided design (CAD), comprise empty size (length) in packing chest, cardboard materials calculate, the type selecting of standard box-shaped, carry out packing chest printout;
According to output parameter to the wrapper of overlay film carry out stitching operation or laminating operation make highly-breathable corrugated board packing box.
Embodiment 3:
This prepares the method for highly-breathable corrugated board packing box, carries out according to following steps:
Step 1, production corrugated board:
1.1 select ZSM-5 zeolite dry powder feeding roller mill to be crushed to 20-40 micron obtains zeolite dry powder;
1.2 get described zeolite dry powder, fluting board paper pulp, KH550, ground calcium carbonate, polyvinylchloride, tributyl phosphate mix, each raw material weight consumption is 13 parts, zeolite dry powder, fluting board paper pulp 650 parts, KH55015 part, ground calcium carbonate 9 parts, polyethylene 2 parts, tributyl phosphate 2 parts; Polyvinylchloride weight average molecular weight is about 150,000, and the paper making raw material mixed is sent into corrugated paper making processing line;
1.3 dry and add and be pressed into fluting board, become wrapper through polishing; Wrapper after described polishing has the Bendtsen permeability to air of the 350ml/min according to ISO5636-3:1992;
Step 2, overlay film:
Be that spray film liquid sprays film on the wrapper with water paint, coating thickness 0.2 millimeter, then rolls operation firmly;
The preparation of step 3, packing chest:
To be designed a package box structure by packing chest computer aided design (CAD), comprise empty size (length) in packing chest, cardboard materials calculate, the type selecting of standard box-shaped, carry out packing chest printout;
According to output parameter to the wrapper of overlay film carry out stitching operation or laminating operation make highly-breathable corrugated board packing box.
Embodiment 4:
This prepares the method for highly-breathable corrugated board packing box, carries out according to following steps:
Step 1, production corrugated board:
1.1 select type A zeolite dry powder feeding roller mill to be crushed to 20-50 micron obtains zeolite dry powder;
1.2 get described zeolite dry powder, fluting board paper pulp, KH550, ground calcium carbonate, polyvinylchloride, tributyl phosphate mix, each raw material weight consumption is 14 parts, zeolite dry powder, fluting board paper pulp 600 parts, KH55016 part, ground calcium carbonate 8 parts, polyethylene 2 parts, tributyl phosphate 2 parts; Polyvinylchloride weight average molecular weight is about 150,000, and the paper making raw material mixed is sent into corrugated paper making processing line;
1.3 dry and add and be pressed into fluting board, become wrapper through polishing; Wrapper after described polishing has the Bendtsen permeability to air of the 450ml/min according to ISO5636-3:1992;
Step 2, overlay film:
Be that spray film liquid sprays film on the wrapper with water paint, coating thickness 0.2 millimeter, then rolls operation firmly;
The preparation of step 3, packing chest:
To be designed a package box structure by packing chest computer aided design (CAD), comprise empty size (length) in packing chest, cardboard materials calculate, the type selecting of standard box-shaped, carry out packing chest printout;
According to output parameter to the wrapper of overlay film carry out stitching operation or laminating operation make highly-breathable corrugated board packing box.
Packing chest finished product of the present invention is detected, meets following technical index:
Above-mentioned example, only for technical conceive of the present invention and feature are described, its object is to person skilled in the art can be understood content of the present invention and implement according to this, can not limit the scope of the invention with this.All equivalent transformations of doing according to Spirit Essence of the present invention or modification, all should be encompassed within protection scope of the present invention.
Claims (6)
1. a production method for highly-breathable corrugated board packing box, is characterized in that said method comprising the steps of:
Step 1, production corrugated board:
1.1 select zeolite dry powder feeding roller mill to be crushed to 20-50 micron obtains zeolite dry powder;
1.2 get described zeolite dry powder, fluting board paper pulp, KH550, ground calcium carbonate, polyvinylchloride, tributyl phosphate mix, each raw material weight consumption is zeolite dry powder 10-20 part, fluting board paper pulp 500-800 part, KH55012-20 part, ground calcium carbonate 5-12 part, polyethylene 1-3 part, tributyl phosphate 1-3 part; The paper making raw material mixed is sent into corrugated paper making processing line;
1.3 dry and add and be pressed into fluting board, become wrapper through polishing;
Step 2, overlay film:
Be that spray film liquid sprays film on the wrapper with water paint, coating thickness 5 microns-0.5 millimeter, then rolls operation firmly;
The preparation of step 3, packing chest:
To be designed a package box structure by packing chest computer aided design (CAD), comprise empty size (length) in packing chest, cardboard materials calculate, the type selecting of standard box-shaped, carry out packing chest printout;
According to output parameter to the wrapper of overlay film carry out stitching operation or laminating operation make highly-breathable corrugated board packing box.
2. method according to claim 1, is characterized in that the wrapper after described polishing has the Bendtsen permeability to air of the 200-500ml/min according to ISO5636-3:1992.
3. the method according to claim 1-2, is characterized in that ZSM-5, X, Y, L, A, SAPO type zeolite molecular sieve selected by described zeolite dry powder.
4. the method according to claim 1-3, is characterized in that the weight average molecular weight of described polyvinylchloride is 10-15 ten thousand.
5. the method according to claim 1-4, it is characterized in that described step 2 uses hard milling train firmly to roll, hard milling train comprises frame, paper advance mechanism, coating and printing mechanism, preliminary pre-press nips, the shaping wheels of line ball and grooving mechanism, described frame is provided with the Membrane jetter structure between described coating and printing mechanism and precompressed mechanism.
6. the packing chest that the method according to claim 1-4 is produced.