CN101250832A - Composite natural micropore energy-saving base paper - Google Patents
Composite natural micropore energy-saving base paper Download PDFInfo
- Publication number
- CN101250832A CN101250832A CNA2008100686754A CN200810068675A CN101250832A CN 101250832 A CN101250832 A CN 101250832A CN A2008100686754 A CNA2008100686754 A CN A2008100686754A CN 200810068675 A CN200810068675 A CN 200810068675A CN 101250832 A CN101250832 A CN 101250832A
- Authority
- CN
- China
- Prior art keywords
- paper
- mixed
- pulp
- energy
- diatomite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a compound natural microporous energy-saving base stock belonging to the wall paper production technique. The invention provides an inner wall decoration base stock which is provided with energy saving and environment protection, which comprises the following parts by weight: bamboo fiber 35-40, cotton fiber 10-15, diatomite 20-25, sepiolite 10-15, zeolite 2-4, polypropylene amide epoxy hexapropane 0.5-0.7 and pH adjuster 0.1-0.2, wherein the bamboo fiber and the cotton fiber are charged in water to pulp, the diatomite, the sepiolite and the zeolite are mixed to charge water and fret, the fiber pulp and the filler pulp are mixed to charge polypropylene amide epoxy hexapropane, pH adjuster to stir, the mixed pulp is dehydrated, modeled, squeezed and dehydrated to obtain the paper, the paper is dried and modeled by heat to obtain the base stock which is tailored and modeled. The compound natural microporous energy-saving base stock has advantages of separating heat, insulating, adsorbing abnormal taste and harmful gas and the maintenance of the filler material is about 97%, which is a new-typed energy-saving, environment-protection wall paper.
Description
Technical field:
The present invention relates to a kind of paper, relate in particular to a kind of indoor wall facing paper.
Background technology:
Along with improving constantly of people's lives, people are also more and more higher to the requirement of interior decoration; Except require wall leveling, attractive in appearance and, people have also proposed new requirement to thermal and insulating performance of indoor air quality and body of wall etc.Yet present widely used interior decoration wallpaper is to add a cover the film embossing by body paper to form mostly, perhaps adds a cover PVC by body paper and forms through the coarse whiting coating then; Main purpose is to beautify indoor environment, does not have energy-conservation and adsorption function.
Summary of the invention:
At the above-mentioned defective that exists in the prior art, the present invention aims to provide a kind of indoor wall that is used for and decorates, and has the composite natural micropore energy-saving base paper of heat insulation, insulation and adsorption function.
To achieve these goals, method of the present invention is by the following technical solutions: it is made by the raw material of following weight portion: bamboo fibre 35～40, cotton fiber 10～15, diatomite 20～25, sepiolite 10～15, zeolite 2～4, polyacrylamide epoxy six bright alkane 0.5～0.7, pH regulator agent 0.1～0.2, wherein, the percent opening of diatomite micropore＞90%, bulk density are 0.2～0.25g/cm
3Its preparation method is:
1) bamboo fibre, cotton fiber being mixed the back, to add weight be 200 times water, with beater smash fiber pulp, beating degree is controlled at 40～60 degree;
2) diatomite, sepiolite and zeolite being mixed the back, to add weight be 120 times water, gets extender paste with the vibrating ball-mill vibration, and particle diameter is controlled at 0.1～6 micron;
3) described fiber pulp, extender paste are mixed, add polyacrylamide epoxy six bright alkane, pH regulator agent then, stir mixed pulp;
4) described mixed pulp is poured into dehydration, moulding in the cylinder-type former, walked vehicle speed and be controlled at 10～15 meter per seconds;
5) push, dewater paper;
6) with the paper oven dry, the moisture content of paper is controlled at 4～5%;
7) hot press finalize the design body paper;
8) cutting moulding.
Described pH regulator agent is sodium sulphate or NaOH.
In technique scheme, bamboo fibre and cotton fiber form the paper skeleton jointly, and fine-grained diatomite, sepiolite, zeolite are filled in therebetween as packing material; Polyacrylamide epoxy six bright alkane mainly play adhesive effect, and the pH regulator agent works to regulate pH value.Wherein, bamboo fibre forms thick skeleton, and cotton fiber forms the thin skeleton of branch-like; Diatomite has the fine holes structure, is a kind of good heat insulation heat preservation energy-saving material; The layer structure of sepiolite had both had function of heat insulation, again adsorption function selectively; Zeolite has the effect of molecular sieve, and the different assorted function of odor of absorption is arranged.
Compared with the prior art, the present invention is because on the basis of conventional paper film forming process, diatomite, sepiolite and the zeolite of energy-conservation to have, heat insulation, insulation, selective absorption function replaces kaolin or talcum powder in the conventional paper technology as packing material, adhesive effect by polyacrylamide epoxy six bright alkane fills, attached between the skeleton that forms jointly by bamboo fibre and cotton fiber, so have the function of heat insulation, insulation, selective absorption peculiar smell or pernicious gas.
Below be the contrast test that the present invention and traditional wallpaper are done under the same conditions:
Table 1: heat-insulation and heat-preservation test
Table 2: peculiar smell adsorption test
From above-mentioned result of the test as can be seen, the present invention has function heat insulation, that be incubated, adsorb peculiar smell or pernicious gas.According to test, the retention of packing material of the present invention is about 97%.
The specific embodiment:
The invention will be further described below in conjunction with specific embodiment:
Embodiments of the invention see the following form:
Table 3: embodiment tabulation (unit: kilogram)
In the above-described embodiments, the pH regulator agent can be sodium sulphate, also can be NaOH.Preparation method of the present invention is as follows:
1) finished product bamboo fibre, cotton fiber being mixed the back, to add weight ratio be 1: 200 water, with beater smash fiber pulp, beating degree is controlled at 40～60 degree;
2) diatomite, sepiolite and zeolite being mixed the back, to add weight ratio be 1: 120 water, gets extender paste with the vibrating ball-mill vibration, and particle diameter is controlled at 0.1～6 micron;
3) described fiber pulp, extender paste are mixed, add polyacrylamide epoxy six bright alkane, pH regulator agent then, stir mixed pulp;
4) described mixed pulp is poured into dehydration, moulding in the cylinder-type former, walked vehicle speed and be controlled at 10～15 meter per seconds;
5) push, dewater paper;
6) with the paper oven dry, the moisture content of paper is controlled at 4～5%;
7) hot press finalize the design body paper;
8) cutting moulding.
Claims (3)
1. composite natural micropore energy-saving base paper, it is characterized in that making: bamboo fibre 35～40, cotton fiber 10～15, diatomite 20～25, sepiolite 10～15, zeolite 2～4, polyacrylamide epoxy six bright alkane 0.5～0.7, pH regulator agent 0.1～0.2 by the raw material of following weight portion, wherein, the percent opening of diatomite micropore＞90%, bulk density are 0.2～0.25g/cm
3Its preparation method is:
1) bamboo fibre, cotton fiber being mixed the back, to add weight be 200 times water, with beater smash fiber pulp, beating degree is controlled at 40～60 degree;
2) diatomite, sepiolite and zeolite being mixed the back, to add weight be 120 times water, gets extender paste with the vibrating ball-mill vibration, and particle diameter is controlled at 0.1～6 micron;
3) described fiber pulp, extender paste are mixed, add polyacrylamide epoxy six bright alkane, pH regulator agent then, stir mixed pulp;
4) described mixed pulp is poured into dehydration, moulding in the cylinder-type former, walked vehicle speed and be controlled at 10～15 meter per seconds;
5) push, dewater paper;
6) with the paper oven dry, the moisture content of paper is controlled at 4～5%;
7) hot press finalize the design body paper;
8) cutting moulding.
2. composite natural micropore energy-saving base paper according to claim 1 is characterized in that: described pH regulator agent is a sodium sulphate.
3. composite natural micropore energy-saving base paper according to claim 1 is characterized in that: described pH regulator agent is a NaOH.