CN105298081A - Ceramic floor tile with diatom mud and method for manufacturing ceramic floor tile - Google Patents
Ceramic floor tile with diatom mud and method for manufacturing ceramic floor tile Download PDFInfo
- Publication number
- CN105298081A CN105298081A CN201510629205.0A CN201510629205A CN105298081A CN 105298081 A CN105298081 A CN 105298081A CN 201510629205 A CN201510629205 A CN 201510629205A CN 105298081 A CN105298081 A CN 105298081A
- Authority
- CN
- China
- Prior art keywords
- diatom ooze
- ceramic floor
- temperature
- stone
- floor tile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a ceramic floor tile with diatom mud and a method for manufacturing the ceramic floor tile. The ceramic floor tile comprises a base layer, a surface layer and an adhesion layer. The adhesion layer is arranged between the base layer and the surface layer, and the base layer is made of the diatom mud, feldspar, kaolin, quartz, clay, porcelain clay, moire stone, marble, broken iron, polystyrene and polyacrylate; the surface layer is made of the diatom mud, Kunshan stone, carborundum disc stone, colorants, pebble, glass cloth, plastic particles, polyurethane, ethylene-ethylic acid ethylene copolymers, silicon dioxide and aluminum oxide. The ceramic floor tile and the method have the advantages that the ceramic floor tile is made of nontoxic and pollution-free raw materials, and the diatom mud which is a main material is easy to obtain, is natural and pollution-free and has diversified sterilization, disinfection and waterproof merits; the ceramic floor tile is made of the easily available materials, processing and manufacturing processes are simple, and the ceramic floor tile manufactured by the aid of the method is high in smoothness and quality.
Description
Technical field
The invention belongs to manufactured construction materials preparing technical field, specifically, is a kind of ceramic floor brick containing diatom ooze and preparation method thereof.
Background technology
Along with expanding economy, growth in the living standard, people more and more pay attention to the requirement to quality of the life aspect.Ceramic floor brick, because have the features such as attractive in appearance, clean and tidy, comfortable and diversified, has been come into huge numbers of families gradually, has been become the requisite building product of house decoration, thus also promoted the fast development of ceramic manufacturing.With nearly Experience in Development during the last ten years, pottery mainly by exploitation clay and the clay work in mountain, can produce a large amount of toxic gases and dust in manufacturing process, directly jeopardizes the health of the mankind and cause great injury to environment for human survival; More there is part producer in order to the maximization of profit-push, use low grade, raw material inferior produces, the destruction of aggravation to environment, also cause that the Ceramic Tiles produced is not durable, hardness is poor simultaneously, not environmentally and color and luster dim, directly have influence on the lifting of people's quality of life.Therefore, it is possible to provide the also practical ceramic floor brick of a kind of environmental protection to become building trade and the current urgent demand of people.
Summary of the invention
Instant invention overcomes shortcoming of the prior art, a kind of ceramic floor brick containing diatom ooze and preparation method thereof is provided, the making raw material of this ceramic floor brick is nontoxic, pollution-free raw material, major ingredient diatom ooze obtains simple, natural pollution-free, there is virus killing, multiple advantage such as disappear bacterium and fire prevention etc., and it is simple to draw materials, processing and fabricating flow process is uncomplicated, produces that ceramic floor brick smoothness is high, quality is better.
In order to solve the problems of the technologies described above, the present invention is achieved by the following technical solutions:
A ceramic floor brick containing diatom ooze, comprises basalis and surface course, and is arranged on the adhesive layer between described basalis and surface course,
The constitutive material of described basalis comprises: diatom ooze, feldspar, kaolin, quartz, clay, china clay, moire stone, Wu Bishi, bushel iron block, polystyrene and polyacrylate;
The constitutive material of described surface course comprises: diatom ooze, Kunshan stone, sand slabstone, colorant, cobble, glass fabric, particles, as polyurethane, ethene-acetate ethylene copolymer, silica and alumina;
The constitutive material of described adhesive layer comprises: epoxide-resin glue, latex, cyanoacrylate, high-temperature repairing agent and neoprene adhesive.
Further, the constitutive material of described surface course also comprises refractory material, and described refractory material comprises bauxite, graphite, silicate of soda and tungsten.
Further, in described basalis constitutive material, the quality of diatom ooze, feldspar, kaolin, quartz, clay, china clay, moire stone, Wu Bishi, bushel iron block, polystyrene and polyacrylate is equipped with than being 4:3:3:2:1:1:3:1:1:0.5:0.3;
Diatom ooze in described surface course constitutive material, Kunshan stone, sand slabstone, colorant, cobble, glass fabric, particles, quality as polyurethane, ethene-acetate ethylene copolymer, silica, alumina, bauxite, graphite, silicate of soda and tungsten are equipped with than being 3:2:1:2:2.5:0.5:2:0.8:1:0.8:1:0.2:0.2:0.2:0.2;
The quality of described adhesive layer constitutive material epoxy resin glue, latex, cyanoacrylate, high-temperature repairing agent and neoprene adhesive is equipped with than being 3:3:2:1:1.
Further, the triangular shape iron block that described bushel iron block is thickness is 0.2 ~ 0.3mm, the length of side is 1.0 ~ 1.2mm, described bushel iron block first puts into concentration before using be soak 0.5 ~ 1 hour in the hydrochloric acid solution of 10%, picks up to put into immediately in lubricating grease after draining to soak 5 ~ 10 minutes.
Further, the rectangular shape glass fabric that described glass fabric is lines mode length is 0.5mm, vertical ridge orientation length is 0.2mm, described glass fabric is brushed with one deck anticorrisive agent.
Further, the preparation method of described a kind of ceramic floor brick containing diatom ooze, comprises the following steps:
(1) constitutive material than weighing described basalis and surface course is equipped with by formula, separated;
(2) feldspar, quartz, moire stone and Wu Bishi are put in grater be processed into powder, join in the mixture be made up of diatom ooze, kaolin, clay, china clay, bushel iron block, polystyrene and polyacrylate, add water, the mass ratio of material and water is 4:1, put in mixer together and stir, stirring duration is 1.5 ~ 2.5 hours, stir and complete material to be poured out, draw substrate material, be placed on that temperature is 15 ~ 22 DEG C, humidity is under the condition of 70 ~ 80%, for subsequent use;
(3) first by Kunshan stone, sand slabstone, cobble and graphite are put in grater and are processed into powder, join again by diatom ooze, glass fabric, particles, as polyurethane, silica, alumina, in the composition mixture of bauxite and tungsten, add water, the mass ratio of material and water is 6:1, put into together in mixer and stir 2 ~ 3 hours, add colorant, ethene-acetate ethylene copolymer and silicate of soda, stir 1.5 ~ 2 hours again, pour out, show that top layer is expected, being placed on temperature is 20 ~ 25 DEG C, humidity is under the condition of 65 ~ 70%, for subsequent use,
(4) first step (2) described underlying material is poured in mould, floating; Then described adhesive layer is poured on above initial bed gently, floating; After 4 ~ 6 minutes, then step (3) described top layer material is poured on above described adhesive layer gently, floating;
(5) the described mould after step (4) stone is moved to the space that pressure is 2.2 ~ 2.5MPa, temperature is 22 ~ 28 DEG C, humidity is 75 ~ 78% to leave standstill, after 6 ~ 8 hours, carry out the demoulding;
(6) after the demoulding, effects on surface is polished, and then put in kiln and fire 10 ~ 12 hours, after coming out of the stove, normal temperature cools, and can obtain described a kind of ceramic floor brick containing diatom ooze.
Further, the design temperature of step (6) described kiln is 1100 ~ 1200 DEG C.
Further, the preparation method of described adhesive layer is:
(1) rear more separated than epoxide-resin glue, latex, cyanoacrylate, high-temperature repairing agent and neoprene adhesive are weighed by prescription quality;
(2) first latex is poured in pot and heats, when temperature rises to 80 DEG C, successively epoxide-resin glue, cyanoacrylate, high-temperature repairing agent and neoprene adhesive are poured into, pour into while stir, continuous heating 3 ~ 5 minutes again after interpolation;
(3) pour out in clean container, be positioned over that temperature is 18 ~ 21 DEG C, humidity is cool under the condition of 77 ~ 82%.
Compared with prior art, the invention has the beneficial effects as follows:
(1) to draw materials environmental protection: ceramic floor brick of the present invention makes raw material and is environment friendly and pollution-free, major ingredient diatom ooze is natural material, and not containing any hazardous substances and harmful additive, material is originally as pure Green Product, derive from the diatom mineral of ocean seaweed plant, aboundresources; (2) Making programme is simple: ceramic floor brick Making programme of the present invention is uncomplicated, and technology difficulty is lower, and the art personnel can grasp left-hand seat easily, and does not need extra main equipment to assist; (3) quality is good; The ceramic floor brick using preparation method of the present invention to produce has the multiple advantages such as large, the wear-resistant and tack-free mark of good looking appearance, bearing capacity.
Detailed description of the invention
Below the preferred embodiments of the present invention are described, should be appreciated that preferred embodiment described herein is only for instruction and explanation of the present invention, is not intended to limit the present invention.
In order to solve the problems of the technologies described above, the present invention is achieved by the following technical solutions:
Embodiment 1
A ceramic floor brick containing diatom ooze, comprises basalis and surface course, and is arranged on the adhesive layer between basalis and surface course,
The constitutive material of basalis comprises: diatom ooze, feldspar, kaolin, quartz, clay, china clay, moire stone, Wu Bishi, bushel iron block, polystyrene and polyacrylate;
The constitutive material of surface course comprises: diatom ooze, Kunshan stone, sand slabstone, colorant, cobble, glass fabric, particles, as polyurethane, ethene-acetate ethylene copolymer, silica and alumina;
The constitutive material of adhesive layer comprises: epoxide-resin glue, latex, cyanoacrylate, high-temperature repairing agent and neoprene adhesive.
Further, the constitutive material of surface course also comprises refractory material, and refractory material comprises bauxite, graphite, silicate of soda and tungsten.
Further, in basalis constitutive material, the quality of diatom ooze, feldspar, kaolin, quartz, clay, china clay, moire stone, Wu Bishi, bushel iron block, polystyrene and polyacrylate is equipped with than being 4:3:3:2:1:1:3:1:1:0.5:0.3;
Diatom ooze in surface course constitutive material, Kunshan stone, sand slabstone, colorant, cobble, glass fabric, particles, quality as polyurethane, ethene-acetate ethylene copolymer, silica, alumina, bauxite, graphite, silicate of soda and tungsten are equipped with than being 3:2:1:2:2.5:0.5:2:0.8:1:0.8:1:0.2:0.2:0.2:0.2;
The quality of adhesive layer constitutive material epoxy resin glue, latex, cyanoacrylate, high-temperature repairing agent and neoprene adhesive is equipped with than being 3:3:2:1:1.
Further, the triangular shape iron block that bushel iron block is thickness is 0.2mm, the length of side is 1.0mm, bushel iron block first puts into concentration before using be soak 0.5 hour in the hydrochloric acid solution of 10%, picks up to put into immediately after draining in lubricating grease and soak 5 minutes.
Further, the rectangular shape glass fabric that glass fabric is lines mode length is 0.5mm, vertical ridge orientation length is 0.2mm, glass fabric is brushed with one deck anticorrisive agent.
Further, a kind of preparation method of the ceramic floor brick containing diatom ooze, comprises the following steps:
(1) constitutive material than weighing basalis and surface course is equipped with by formula, separated;
(2) feldspar, quartz, moire stone and Wu Bishi are put in grater be processed into powder, join in the mixture be made up of diatom ooze, kaolin, clay, china clay, bushel iron block, polystyrene and polyacrylate, add water, the mass ratio of material and water is 4:1, puts in mixer together and stirs, and stirring duration is 1.5 hours, stir and complete material to be poured out, draw substrate material, be placed on that temperature is 15 DEG C, humidity is under the condition of 70%, for subsequent use;
(3) first Kunshan stone, sand slabstone, cobble and graphite are put in grater and be processed into powder, join by diatom ooze, glass fabric, particles, composition mixture as polyurethane, silica, alumina, bauxite and tungsten again, add water, the mass ratio of material and water is 6:1, put into together in mixer and stir 2 hours, add colorant, ethene-acetate ethylene copolymer and silicate of soda, stir 1.5 hours again, pour out, show that top layer is expected, be placed on that temperature is 20 DEG C, humidity is under the condition of 65%, for subsequent use;
(4) first step (2) underlying material is poured in mould, floating; Then adhesive layer is poured on above initial bed gently, floating; After 4 minutes, then step (3) top layer material is poured on above adhesive layer gently, floating;
(5) mould after step (4) stone is moved to the space that pressure is 2.2MPa, temperature is 22 DEG C, humidity is 75% to leave standstill, after 6 hours, carry out the demoulding;
(6) after the demoulding, effects on surface is polished, and then put in kiln and fire 10 hours, after coming out of the stove, normal temperature cools, and can obtain a kind of ceramic floor brick containing diatom ooze.
Further, the design temperature of step (6) kiln is 1100 DEG C.
Further, the preparation method of adhesive layer is:
(1) rear more separated than epoxide-resin glue, latex, cyanoacrylate, high-temperature repairing agent and neoprene adhesive are weighed by prescription quality;
(2) first latex is poured in pot and heats, when temperature rises to 80 DEG C, successively epoxide-resin glue, cyanoacrylate, high-temperature repairing agent and neoprene adhesive are poured into, pour into while stir, continuous heating 3 minutes again after interpolation;
(3) pour out in clean container, be positioned over that temperature is 18 DEG C, humidity is cool under the condition of 77%.
Embodiment 2
A ceramic floor brick containing diatom ooze, comprises basalis and surface course, and is arranged on the adhesive layer between basalis and surface course,
The constitutive material of basalis comprises: diatom ooze, feldspar, kaolin, quartz, clay, china clay, moire stone, Wu Bishi, bushel iron block, polystyrene and polyacrylate;
The constitutive material of surface course comprises: diatom ooze, Kunshan stone, sand slabstone, colorant, cobble, glass fabric, particles, as polyurethane, ethene-acetate ethylene copolymer, silica and alumina;
The constitutive material of adhesive layer comprises: epoxide-resin glue, latex, cyanoacrylate, high-temperature repairing agent and neoprene adhesive.
Further, the constitutive material of surface course also comprises refractory material, and refractory material comprises bauxite, graphite, silicate of soda and tungsten.
Further, in basalis constitutive material, the quality of diatom ooze, feldspar, kaolin, quartz, clay, china clay, moire stone, Wu Bishi, bushel iron block, polystyrene and polyacrylate is equipped with than being 4:3:3:2:1:1:3:1:1:0.5:0.3;
Diatom ooze in surface course constitutive material, Kunshan stone, sand slabstone, colorant, cobble, glass fabric, particles, quality as polyurethane, ethene-acetate ethylene copolymer, silica, alumina, bauxite, graphite, silicate of soda and tungsten are equipped with than being 3:2:1:2:2.5:0.5:2:0.8:1:0.8:1:0.2:0.2:0.2:0.2;
The quality of adhesive layer constitutive material epoxy resin glue, latex, cyanoacrylate, high-temperature repairing agent and neoprene adhesive is equipped with than being 3:3:2:1:1.
Further, the triangular shape iron block that bushel iron block is thickness is 0.3mm, the length of side is 1.2mm, bushel iron block first puts into concentration before using be soak 1 hour in the hydrochloric acid solution of 10%, picks up to put into immediately after draining in lubricating grease and soak 10 minutes.
Further, the rectangular shape glass fabric that glass fabric is lines mode length is 0.5mm, vertical ridge orientation length is 0.2mm, glass fabric is brushed with one deck anticorrisive agent.
Further, a kind of preparation method of the ceramic floor brick containing diatom ooze, comprises the following steps:
(1) constitutive material than weighing basalis and surface course is equipped with by formula, separated;
(2) feldspar, quartz, moire stone and Wu Bishi are put in grater be processed into powder, join in the mixture be made up of diatom ooze, kaolin, clay, china clay, bushel iron block, polystyrene and polyacrylate, add water, the mass ratio of material and water is 4:1, puts in mixer together and stirs, and stirring duration is 2.5 hours, stir and complete material to be poured out, draw substrate material, be placed on that temperature is 22 DEG C, humidity is under the condition of 80%, for subsequent use;
(3) first Kunshan stone, sand slabstone, cobble and graphite are put in grater and be processed into powder, join by diatom ooze, glass fabric, particles, composition mixture as polyurethane, silica, alumina, bauxite and tungsten again, add water, the mass ratio of material and water is 6:1, put into together in mixer and stir 3 hours, add colorant, ethene-acetate ethylene copolymer and silicate of soda, stir 2 hours again, pour out, show that top layer is expected, be placed on that temperature is 25 DEG C, humidity is under the condition of 70%, for subsequent use;
(4) first step (2) underlying material is poured in mould, floating; Then adhesive layer is poured on above initial bed gently, floating; After 6 minutes, then step (3) top layer material is poured on above adhesive layer gently, floating;
(5) mould after step (4) stone is moved to the space that pressure is 2.5MPa, temperature is 28 DEG C, humidity is 78% to leave standstill, after 8 hours, carry out the demoulding;
(6) after the demoulding, effects on surface is polished, and then put in kiln and fire 12 hours, after coming out of the stove, normal temperature cools, and can obtain a kind of ceramic floor brick containing diatom ooze.
Further, the design temperature of step (6) kiln is 1200 DEG C.
Further, the preparation method of adhesive layer is:
(1) rear more separated than epoxide-resin glue, latex, cyanoacrylate, high-temperature repairing agent and neoprene adhesive are weighed by prescription quality;
(2) first latex is poured in pot and heats, when temperature rises to 80 DEG C, successively epoxide-resin glue, cyanoacrylate, high-temperature repairing agent and neoprene adhesive are poured into, pour into while stir, continuous heating 5 minutes again after interpolation;
(3) pour out in clean container, be positioned over that temperature is 21 DEG C, humidity is cool under the condition of 82%.
Embodiment 3
A ceramic floor brick containing diatom ooze, comprises basalis and surface course, and is arranged on the adhesive layer between basalis and surface course,
The constitutive material of basalis comprises: diatom ooze, feldspar, kaolin, quartz, clay, china clay, moire stone, Wu Bishi, bushel iron block, polystyrene and polyacrylate;
The constitutive material of surface course comprises: diatom ooze, Kunshan stone, sand slabstone, colorant, cobble, glass fabric, particles, as polyurethane, ethene-acetate ethylene copolymer, silica and alumina;
The constitutive material of adhesive layer comprises: epoxide-resin glue, latex, cyanoacrylate, high-temperature repairing agent and neoprene adhesive.
Further, the constitutive material of surface course also comprises refractory material, and refractory material comprises bauxite, graphite, silicate of soda and tungsten.
Further, in basalis constitutive material, the quality of diatom ooze, feldspar, kaolin, quartz, clay, china clay, moire stone, Wu Bishi, bushel iron block, polystyrene and polyacrylate is equipped with than being 4:3:3:2:1:1:3:1:1:0.5:0.3;
Diatom ooze in surface course constitutive material, Kunshan stone, sand slabstone, colorant, cobble, glass fabric, particles, quality as polyurethane, ethene-acetate ethylene copolymer, silica, alumina, bauxite, graphite, silicate of soda and tungsten are equipped with than being 3:2:1:2:2.5:0.5:2:0.8:1:0.8:1:0.2:0.2:0.2:0.2;
The quality of adhesive layer constitutive material epoxy resin glue, latex, cyanoacrylate, high-temperature repairing agent and neoprene adhesive is equipped with than being 3:3:2:1:1.
Further, the triangular shape iron block that bushel iron block is thickness is 0.25mm, the length of side is 1.1mm, bushel iron block first puts into concentration before using be soak 0.7 hour in the hydrochloric acid solution of 10%, picks up to put into immediately after draining in lubricating grease and soak 8 minutes.
Further, the rectangular shape glass fabric that glass fabric is lines mode length is 0.5mm, vertical ridge orientation length is 0.2mm, glass fabric is brushed with one deck anticorrisive agent.
Further, a kind of preparation method of the ceramic floor brick containing diatom ooze, comprises the following steps:
(1) constitutive material than weighing basalis and surface course is equipped with by formula, separated;
(2) feldspar, quartz, moire stone and Wu Bishi are put in grater be processed into powder, join in the mixture be made up of diatom ooze, kaolin, clay, china clay, bushel iron block, polystyrene and polyacrylate, add water, the mass ratio of material and water is 4:1, puts in mixer together and stirs, and stirring duration is 2 hours, stir and complete material to be poured out, draw substrate material, be placed on that temperature is 18 DEG C, humidity is under the condition of 75%, for subsequent use;
(3) first Kunshan stone, sand slabstone, cobble and graphite are put in grater and be processed into powder, join by diatom ooze, glass fabric, particles, composition mixture as polyurethane, silica, alumina, bauxite and tungsten again, add water, the mass ratio of material and water is 6:1, put into together in mixer and stir 2.5 hours, add colorant, ethene-acetate ethylene copolymer and silicate of soda, stir 1.8 hours again, pour out, show that top layer is expected, be placed on that temperature is 23 DEG C, humidity is under the condition of 68%, for subsequent use;
(4) first step (2) underlying material is poured in mould, floating; Then adhesive layer is poured on above initial bed gently, floating; After 5 minutes, then step (3) top layer material is poured on above adhesive layer gently, floating;
(5) mould after step (4) stone is moved to the space that pressure is 2.4MPa, temperature is 26 DEG C, humidity is 76% to leave standstill, after 7 hours, carry out the demoulding;
(6) after the demoulding, effects on surface is polished, and then put in kiln and fire 11 hours, after coming out of the stove, normal temperature cools, and can obtain a kind of ceramic floor brick containing diatom ooze.
Further, the design temperature of step (6) kiln is 1150 DEG C.
Further, the preparation method of adhesive layer is:
(1) rear more separated than epoxide-resin glue, latex, cyanoacrylate, high-temperature repairing agent and neoprene adhesive are weighed by prescription quality;
(2) first latex is poured in pot and heats, when temperature rises to 80 DEG C, successively epoxide-resin glue, cyanoacrylate, high-temperature repairing agent and neoprene adhesive are poured into, pour into while stir, continuous heating 4 minutes again after interpolation;
(3) pour out in clean container, be positioned over that temperature is 20 DEG C, humidity is cool under the condition of 80%.
Last it is noted that these are only the preferred embodiments of the present invention; be not limited to the present invention; although with reference to embodiment to invention has been detailed description; for a person skilled in the art; it still can be modified to the technical scheme described in foregoing embodiments; or equivalent replacement is carried out to wherein portion of techniques feature; but it is within the spirit and principles in the present invention all; any amendment of doing, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (8)
1. the ceramic floor brick containing diatom ooze, is characterized in that, comprise basalis and surface course, and be arranged on the adhesive layer between described basalis and surface course,
The constitutive material of described basalis comprises: diatom ooze, feldspar, kaolin, quartz, clay, china clay, moire stone, Wu Bishi, bushel iron block, polystyrene and polyacrylate;
The constitutive material of described surface course comprises: diatom ooze, Kunshan stone, sand slabstone, colorant, cobble, glass fabric, particles, as polyurethane, ethene-acetate ethylene copolymer, silica and alumina;
The constitutive material of described adhesive layer comprises: epoxide-resin glue, latex, cyanoacrylate, high-temperature repairing agent and neoprene adhesive.
2. a kind of ceramic floor brick containing diatom ooze according to claim 1, it is characterized in that, the constitutive material of described surface course also comprises refractory material, and described refractory material comprises bauxite, graphite, silicate of soda and tungsten.
3. a kind of ceramic floor brick containing diatom ooze according to claim 1 and 2, is characterized in that,
In described basalis constitutive material, the quality of diatom ooze, feldspar, kaolin, quartz, clay, china clay, moire stone, Wu Bishi, bushel iron block, polystyrene and polyacrylate is equipped with than being 4:3:3:2:1:1:3:1:1:0.5:0.3;
Diatom ooze in described surface course constitutive material, Kunshan stone, sand slabstone, colorant, cobble, glass fabric, particles, quality as polyurethane, ethene-acetate ethylene copolymer, silica, alumina, bauxite, graphite, silicate of soda and tungsten are equipped with than being 3:2:1:2:2.5:0.5:2:0.8:1:0.8:1:0.2:0.2:0.2:0.2;
The quality of described adhesive layer constitutive material epoxy resin glue, latex, cyanoacrylate, high-temperature repairing agent and neoprene adhesive is equipped with than being 3:3:2:1:1.
4. a kind of ceramic floor brick containing diatom ooze according to claim 1, it is characterized in that, the triangular shape iron block that described bushel iron block is thickness is 0.2 ~ 0.3mm, the length of side is 1.0 ~ 1.2mm, described bushel iron block first puts into concentration before using be soak 0.5 ~ 1 hour in the hydrochloric acid solution of 10%, picks up to put into immediately in lubricating grease after draining to soak 5 ~ 10 minutes.
5. a kind of ceramic floor brick containing diatom ooze according to claim 1, is characterized in that, the rectangular shape glass fabric that described glass fabric is lines mode length is 0.5mm, vertical ridge orientation length is 0.2mm, described glass fabric is brushed with one deck anticorrisive agent.
6. the preparation method of a kind of ceramic floor brick containing diatom ooze according to claim 1, is characterized in that, comprise the following steps:
(1) constitutive material than weighing described basalis and surface course is equipped with by formula, separated;
(2) feldspar, quartz, moire stone and Wu Bishi are put in grater be processed into powder, join in the mixture be made up of diatom ooze, kaolin, clay, china clay, bushel iron block, polystyrene and polyacrylate, add water, the mass ratio of material and water is 4:1, put in mixer together and stir, stirring duration is 1.5 ~ 2.5 hours, stir and complete material to be poured out, draw substrate material, be placed on that temperature is 15 ~ 22 DEG C, humidity is under the condition of 70 ~ 80%, for subsequent use;
(3) first by Kunshan stone, sand slabstone, cobble and graphite are put in grater and are processed into powder, join again by diatom ooze, glass fabric, particles, as polyurethane, silica, alumina, in the composition mixture of bauxite and tungsten, add water, the mass ratio of material and water is 6:1, put into together in mixer and stir 2 ~ 3 hours, add colorant, ethene-acetate ethylene copolymer and silicate of soda, stir 1.5 ~ 2 hours again, pour out, show that top layer is expected, being placed on temperature is 20 ~ 25 DEG C, humidity is under the condition of 65 ~ 70%, for subsequent use,
(4) first step (2) described underlying material is poured in mould, floating; Then described adhesive layer is poured on above initial bed gently, floating; After 4 ~ 6 minutes, then step (3) described top layer material is poured on above described adhesive layer gently, floating;
(5) the described mould after step (4) stone is moved to the space that pressure is 2.2 ~ 2.5MPa, temperature is 22 ~ 28 DEG C, humidity is 75 ~ 78% to leave standstill, after 6 ~ 8 hours, carry out the demoulding;
(6) after the demoulding, effects on surface is polished, and then put in kiln and fire 10 ~ 12 hours, after coming out of the stove, normal temperature cools, and can obtain described a kind of ceramic floor brick containing diatom ooze.
7. the preparation method of a kind of ceramic floor brick containing diatom ooze according to claim 6, it is characterized in that, the design temperature of step (6) described kiln is 1100 ~ 1200 DEG C.
8. a kind of ceramic floor brick containing diatom ooze according to claim 1, it is characterized in that, the preparation method of described adhesive layer is:
(1) rear more separated than epoxide-resin glue, latex, cyanoacrylate, high-temperature repairing agent and neoprene adhesive are weighed by prescription quality;
(2) first latex is poured in pot and heats, when temperature rises to 80 DEG C, successively epoxide-resin glue, cyanoacrylate, high-temperature repairing agent and neoprene adhesive are poured into, pour into while stir, continuous heating 3 ~ 5 minutes again after interpolation;
(3) pour out in clean container, be positioned over that temperature is 18 ~ 21 DEG C, humidity is cool under the condition of 77 ~ 82%.