CN105297416A - Preparation method of cotton fabric with formaldehyde removing function - Google Patents
Preparation method of cotton fabric with formaldehyde removing function Download PDFInfo
- Publication number
- CN105297416A CN105297416A CN201510858405.3A CN201510858405A CN105297416A CN 105297416 A CN105297416 A CN 105297416A CN 201510858405 A CN201510858405 A CN 201510858405A CN 105297416 A CN105297416 A CN 105297416A
- Authority
- CN
- China
- Prior art keywords
- cotton fabric
- carried out
- minutes
- fabric
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A preparation method of cotton fabric with a formaldehyde removing function comprises the steps of preprocessing the cotton fabric; modifying the cotton fabric; performing formaldehyde removing function finishing on the cotton fabric; printing the cotton fabric; adopting a circular screen printer, selecting a simple pattern to describe and draw a pattern, preparing a screen, adopting an active dye as printing paste, wherein the printing paste comprises the following components according to the weight of the cotton fabric: 2% of active dye, and 30% of thickener consisting of sodium alginate and guar gum, 4% of urea, 1% of reserve salt and 1% of sodium bicarbonate, and deionized water is used for filling to 100%, a steaming temperature is 105-110 DEG C after overprinting and the time is 10-20min.
Description
The application is application number is 2014107032836, and the applying date is on November 29th, 2014, and denomination of invention is the divisional application of the application for a patent for invention of " a kind of preparation method with the COTTON FABRIC of function of removing formaldehyde ".
Technical field
The present invention relates to a kind of preparation method of COTTON FABRIC, particularly relate to a kind of preparation method with the COTTON FABRIC of function of removing formaldehyde.
Background technology
Along with widely using of building material and ornament materials, living environment pollutant increases increasingly, and environment worsens increasingly.Indoor common are harmful substances nearly thousands of kinds, and wherein formaldehyde with the popularity in the generality existed, source, factor become one of the most dangerous pollution sources such as large to the harmfulness of human body, deenergized period is long.
Formaldehyde is volatile organic compounds VOEs(VolatileOrganicCompounds) in topmost one, in China's toxic chemical priority acccess control list, be in second.Modern scientific research shows: when indoor formaldehyde content is 0.1mg/m
3time just have peculiar smell and sense of discomfort; 0.5mg/m
3in time, can stimulate eyes to cause to shed tears; 0.6mg/m
3shi Yinqi throat discomfort or pain; Concentration is high again to cause nausea, vomit, cough, uncomfortable in chest, even pulmonary emphysema of panting; When reaching 30mg/m in air
3time can cause death at once.
There is formaldehyde problem in the newly-decorated residential households in current Chinese cities and towns 80%; these formaldehyde source are in wood-based plate, furniture, wallpaper and coating; under certain environment condition; formaldehyde will evaporate from these materials; and Form aldehyde release slowly; often reach more than 10 years, therefore, the mankind will be among the threat of formaldehyde for a long time.The time of the mankind about 90% is spent in indoor, and the quality of IAQ directly affects the physical condition of people.Reduce indoor formaldehyde concentration, improve IAQ, be improve human lives quality, improve level of human health, reduce disease important channel.Therefore, the development tool of function of removing formaldehyde textiles is of great significance.
Summary of the invention
The object of the present invention is to provide a kind of simple COTTON FABRIC preparation method, by providing cotton fabric function of removing formaldehyde, and reduce indoor content of formaldehyde.The present invention specifically provides a kind of preparation method with the COTTON FABRIC of function of removing formaldehyde.
The technical solution adopted for the present invention to solve the technical problems is:
There is a preparation method for the COTTON FABRIC of function of removing formaldehyde, it is characterized in that comprising the following steps:
Step one: pre-treatment is carried out to COTTON FABRIC;
Step 2: modification is carried out to COTTON FABRIC;
Step 3: function of removing formaldehyde arrangement is carried out to COTTON FABRIC;
Step 4: stamp is carried out to COTTON FABRIC.
Wherein, step a pair COTTON FABRIC is carried out pre-treatment and mainly COTTON FABRIC is carried out destarch, bleaching, described destarch is the α-amylase of employing 2 ~ 3g/L, 1 ~ 2g/L Surfactant OP-10, the agent of 1 ~ 2g/L strong osmotic, desizing temperature is 95 DEG C, the destarch time is 30 minutes, and adopts 90 DEG C of hot water wash four roads; Bleaching adopts cellulase treatment liquid; bath raio 1:10; described cellulase treatment liquid comprises alkaline pectase, neutral cellulase, neutral-alkaline protease and zytase; the weight ratio of four is 3:2:1:1; at 20 DEG C ~ 60 DEG C temperature; in above-mentioned cellulase treatment liquid, fabric treating 30-40 minute, then uses 90 DEG C of hot water wash four roads.
Step 2 carries out modification to COTTON FABRIC: be COTTON FABRIC at room temperature soaked 10 ~ 20 minutes in the sodium hydroxide solution of 15 ~ 20wt%, bath raio is 1:10, then fabric is passed through evenness calender, liquid carrying rate is below 50%, then fabric is put into sodium chloroacetate, NaOH, in the solution of water and ethanol composition, wherein the concentration of sodium chloroacetate is 15g/L, the concentration of NaOH is 2g/L, the concentration of ethanol is 3g/L, bath raio 1:10, after fabric adds, solution starts to be warming up to 50 ~ 60 DEG C, react 30 minutes, then 80 DEG C of hot washes 10 minutes are used, then cold water washing is to neutral, dry.
Step 3 is carried out function of removing formaldehyde arrangement to COTTON FABRIC and is comprised four steps:
(1) be dissolved in 1-ethyl-3-methyl-imidazolium chloride ionic liquid by the OPC of the 5-7% being equivalent to COTTON FABRIC weight, form OPC ionic liquid, the weight ratio of OPC and ionic liquid is 2-10:45-60;
(2) COTTON FABRIC is at room temperature padded the sodium hydroxide solution of 2g/L, two leachings two are rolled, each dipping 10 minutes, and pick-up is 90%;
(3) COTTON FABRIC be immersed in the OPC ionic liquid of (1), room temperature, dip time is 30-50 minute, and by evenness calender, pick-up is 80 ~ 90%;
(4) by COTTON FABRIC in drying baker, temperature 80 ~ 100 DEG C, dries 5 ~ 10 minutes, and then in baking oven, temperature 140-160 DEG C, dries 30 ~ 60 seconds.
It is adopt rotary screen printing machines that step 4 carries out stamp to COTTON FABRIC, select simple pattern to retouch original text to draw, prepare silk screen, adopt reactive dye printing slurry, printing paste comprises the REACTIVE DYES being equivalent to COTTON FABRIC weight 2%, and the thickener 30% of sodium alginate and guar gum formation, urea 4%, reserve salt s1%, sodium bicarbonate 1%, steam temperature 105 ~ 110 DEG C after over print, 10 ~ 20 minutes time.
The beneficial effect that the present invention has is:
The pretreatment process of COTTON FABRIC adopts cellulase treatment, reduce the use of chemical assistant, especially in bleaching process, the present inventor have selected alkaline pectase, neutral cellulase, neutral-alkaline protease and zytase, the weight ratio of four is 3:2:1:1, bleaching effect is clearly, low to the loss of fabric;
Sodium chloroacetate carries out modification to COTTON FABRIC, improves OPC to the absorption of COTTON FABRIC, combination, improves its Percentage bound;
Adopt ionic liquid as reaction medium, improve the binding ability of OPC and COTTON FABRIC further, effectively improve its adsorption rate, Percentage bound and washing fastness;
And inventor finds in actual production, if what COTTON FABRIC was taked after carrying out function of removing formaldehyde arrangement is dyeing, the combination of OPC and COTTON FABRIC can be destroyed, if carried out dyeing or stamp before function of removing formaldehyde arranges, then affect the combination of OPC and COTTON FABRIC, have the color adopting printing with reactive dye providing cotton fabric certain only, affect minimum on the combination of OPC and COTTON FABRIC, expand the scope of application of COTTON FABRIC.
Adopt GB50325-2001(2006 version) detect, formaldehyde clearance reaches more than 90%.
The COTTON FABRIC using preparation method of the present invention to obtain can directly and skin contact, and security is good, do not have carcinogenic, teratogenesis or cause allergic reaction; Good with ecological environment compatibility, biodegradable, be a kind of novel green product, its market prospects are very wide, can be applicable to the fields such as family is spun, garment material.
Detailed description of the invention
Illustrate the present invention further below in conjunction with specific embodiment, but protection scope of the present invention is not limited thereto.
embodiment 1:
Embodiment 1: COTTON FABRIC is carried out pre-treatment and mainly COTTON FABRIC carried out destarch, bleaching, described destarch adopts the α-amylase of 2g/L, 1g/L Surfactant OP-10, the agent of 1g/L strong osmotic, desizing temperature is 95 DEG C, the destarch time is 30 minutes, and adopts 90 DEG C of hot water wash four roads; Bleaching adopts cellulase treatment liquid; bath raio 1:10; described cellulase treatment liquid comprises alkaline pectase, neutral cellulase, neutral-alkaline protease and zytase; the weight ratio of four is 3:2:1:1; at 40 DEG C of temperature; in above-mentioned cellulase treatment liquid, fabric treating 30 minutes, then uses 90 DEG C of hot water wash four roads.Modification is carried out to COTTON FABRIC: be COTTON FABRIC at room temperature soaked 20 minutes in the sodium hydroxide solution of 15wt%, bath raio is 1:10, then fabric is passed through evenness calender, liquid carrying rate is below 50%, then fabric is put into sodium chloroacetate, NaOH, in the solution of water and ethanol composition, wherein the concentration of sodium chloroacetate is 15g/L, the concentration of NaOH is 2g/L, the concentration of ethanol is 3g/L, bath raio 1:10, after fabric adds, solution starts to be warming up to 50 DEG C, react 30 minutes, then 80 DEG C of hot washes 10 minutes are used, then cold water washing is to neutral, dry.
Function of removing formaldehyde arrangement is carried out to COTTON FABRIC and comprises four steps: the OPC of be equivalent to COTTON FABRIC weight 5% is dissolved in 1-ethyl-3-methyl-imidazolium chloride ionic liquid by (1), form OPC ionic liquid, the weight ratio of OPC and ionic liquid is 2:45; (2) COTTON FABRIC is at room temperature padded the sodium hydroxide solution of 2g/L, two leachings two are rolled, each dipping 10 minutes, and pick-up is 90%; (3) COTTON FABRIC be immersed in the OPC ionic liquid of (1), room temperature, dip time is 30 minutes, and by evenness calender, pick-up is 80%; (4) by COTTON FABRIC in drying baker, temperature 80 DEG C, dries 6 minutes, and then in baking oven, temperature 140 DEG C, dries 50 seconds.
Carrying out stamp to COTTON FABRIC is adopt rotary screen printing machines, select simple pattern to retouch original text to draw, prepare silk screen, adopt reactive dye printing slurry, printing paste comprises the REACTIVE DYES being equivalent to COTTON FABRIC weight 2%, and the thickener 30% of sodium alginate and guar gum formation, urea 4%, reserve salt s1%, sodium bicarbonate 1%, deionized water is adjusted to 100%, steam temperature 105 DEG C after over print, 20 minutes time.
Record COTTON FABRIC except formaldehyde rate be 91.4%.
Embodiment 2: pre-treatment is carried out to COTTON FABRIC and mainly COTTON FABRIC is carried out destarch, bleaching, described destarch adopts the α-amylase of 3g/L, 2g/L Surfactant OP-10, the agent of 2g/L strong osmotic, desizing temperature is 95 DEG C, the destarch time is 30 minutes, and adopts 90 DEG C of hot water wash four roads; Bleaching adopts cellulase treatment liquid; bath raio 1:10; described cellulase treatment liquid comprises alkaline pectase, neutral cellulase, neutral-alkaline protease and zytase; the weight ratio of four is 3:2:1:1; at 60 DEG C of temperature; in above-mentioned cellulase treatment liquid, fabric treating 40 minutes, then uses 90 DEG C of hot water wash four roads.Modification is carried out to COTTON FABRIC, that COTTON FABRIC is at room temperature soaked 10 minutes in the sodium hydroxide solution of 20wt%, bath raio is 1:10, then fabric is passed through evenness calender, liquid carrying rate is below 50%, then fabric is put into sodium chloroacetate, NaOH, in the solution of water and ethanol composition, wherein the concentration of sodium chloroacetate is 15g/L, the concentration of NaOH is 2g/L, the concentration of ethanol is 3g/L, bath raio 1:10, after fabric adds, solution starts to be warming up to 60 DEG C, react 30 minutes, then 80 DEG C of hot washes 10 minutes are used, then cold water washing is to neutral, dry.
Function of removing formaldehyde arrangement is carried out to COTTON FABRIC and comprises four steps:
(1) be dissolved in 1-ethyl-3-methyl-imidazolium chloride ionic liquid by the OPC of be equivalent to COTTON FABRIC weight 7%, form OPC ionic liquid, the weight ratio of OPC and ionic liquid is 2:9; (2) COTTON FABRIC is at room temperature padded the sodium hydroxide solution of 2g/L, two leachings two are rolled, each dipping 10 minutes, and pick-up is 90%; (3) COTTON FABRIC be immersed in the OPC ionic liquid of (1), room temperature, dip time is 50 minutes, and by evenness calender, pick-up is 90%; (4) by COTTON FABRIC in drying baker, temperature 100 DEG C, dries 5 minutes, and then in baking oven, temperature 160 DEG C, dries 30 seconds.
Carrying out stamp to COTTON FABRIC is adopt rotary screen printing machines, select simple pattern to retouch original text to draw, prepare silk screen, adopt reactive dye printing slurry, printing paste comprises the REACTIVE DYES being equivalent to COTTON FABRIC weight 2%, and the thickener 30% of sodium alginate and guar gum formation, urea 4%, reserve salt s1%, sodium bicarbonate 1%, deionized water is adjusted to 100%, steam temperature 110 DEG C after over print, 10 minutes time.
Record COTTON FABRIC except formaldehyde rate be 92.6%.
The specific embodiment described in the invention detailed description of specific implementation process only for violating the law to the preparation with the COTTON FABRIC of function of removing formaldehyde of the present invention, instead of to the restriction with the preparation method of the COTTON FABRIC of function of removing formaldehyde of the present invention.Any modification of carrying out the method and improvement, the substituting and using of similar or close material in the scope of the claims or category, all belongs to scope of patent protection of the present invention.
Claims (2)
1. there is a preparation method for the COTTON FABRIC of function of removing formaldehyde, it is characterized in that comprising the following steps:
Step one: pre-treatment is carried out to COTTON FABRIC;
Step 2: modification is carried out to COTTON FABRIC;
Step 3: function of removing formaldehyde arrangement is carried out to COTTON FABRIC;
Step 4: carry out stamp to COTTON FABRIC, adopts rotary screen printing machines, selects simple pattern to retouch original text and draws, prepare silk screen, adopt reactive dye printing slurry, printing paste comprises the REACTIVE DYES being equivalent to COTTON FABRIC weight 2%, and the thickener 30% of sodium alginate and guar gum composition, urea 4%, reserve salt s1%, sodium bicarbonate 1%, is transferred to 100% with deionized water, steam temperature 105 ~ 110 DEG C after over print, 10 ~ 20 minutes time.
2. there is the preparation method of the COTTON FABRIC of function of removing formaldehyde as claimed in claim 1, it is characterized in that,
Step a pair COTTON FABRIC is carried out pre-treatment and mainly COTTON FABRIC is carried out destarch, bleaching, described destarch is the α-amylase of employing 2 ~ 3g/L, 1 ~ 2g/L Surfactant OP-10, the agent of 1 ~ 2g/L strong osmotic, desizing temperature is 95 DEG C, the destarch time is 30 minutes, and adopts 90 DEG C of hot water wash four roads; Bleaching adopts cellulase treatment liquid; bath raio 1:10; described cellulase treatment liquid comprises alkaline pectase, neutral cellulase, neutral-alkaline protease and zytase; the weight ratio of four is 3:2:1:1; at 20 DEG C ~ 60 DEG C temperature; in above-mentioned cellulase treatment liquid, fabric treating 30 ~ 40 minutes, then uses 90 DEG C of hot water wash four roads.