CN105293953A - 一种紫外防护镜片及制备方法 - Google Patents

一种紫外防护镜片及制备方法 Download PDF

Info

Publication number
CN105293953A
CN105293953A CN201510813567.5A CN201510813567A CN105293953A CN 105293953 A CN105293953 A CN 105293953A CN 201510813567 A CN201510813567 A CN 201510813567A CN 105293953 A CN105293953 A CN 105293953A
Authority
CN
China
Prior art keywords
film
glass substrate
refractive index
low refractive
index film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510813567.5A
Other languages
English (en)
Inventor
訾云海
杨勇
鞠云祥
訾云旭
李莉
句红兵
荀涛
张宝福
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
YUNNAN HUIHENG OPTOELECTRONIC TECHNOLOGY CO LTD
Original Assignee
YUNNAN HUIHENG OPTOELECTRONIC TECHNOLOGY CO LTD
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by YUNNAN HUIHENG OPTOELECTRONIC TECHNOLOGY CO LTD filed Critical YUNNAN HUIHENG OPTOELECTRONIC TECHNOLOGY CO LTD
Priority to CN201510813567.5A priority Critical patent/CN105293953A/zh
Publication of CN105293953A publication Critical patent/CN105293953A/zh
Pending legal-status Critical Current

Abstract

本发明公开了<b>一</b>种紫外防护镜片及其制备方法，该紫外防护镜片包括玻璃基片，其特征在于玻璃基片上交替镀有高折射率膜及低折射率膜，高折射膜层厚为10～30nm、低折射率膜层厚为25～50nm，高折射率膜及低折射率膜交替10～25次。本发明制备的紫外防护镜片可见光透过高、紫外线防护效果好，实现紫外线防护与正常观察的完美统一，解决了佩戴太阳镜阻隔紫外线防治白内障时，可见光透过率低影响人眼观察的问题。

Description

一种紫外防护镜片及制备方法
技术领域
本发明涉及光学镜片领域，尤其是一种紫外防护镜片及其制备方法。
背景技术
长期的慢性紫外线辐射是导致白内障发生最为重要的诱因，佩戴防紫外线眼镜是防治白内障发生的最佳手段。太阳镜通过遮挡或吸收一部分光线达到防止阻挡紫外线的目的，是最为常见的防紫外线眼镜。但太阳镜在阻隔紫外线的同时，也阻隔了可见光的透过，降低了人眼的观察效果。
发明内容
本发明的目的在于，解决了佩戴太阳镜阻隔紫外线防治白内障的时，可见光透过率低，影响人眼观察的问题。提供一种可见光透过高、紫外线防护效果好，实现紫外线防护与正常观察完美统一的紫外防护镜片及其制备方法。
本发明公开了一种紫外防护镜片，包括玻璃基片，其特征在于玻璃基片上由玻璃基片向外交替镀有高折射率膜及低折射率膜，高折射膜层厚为10～30nm、低折射率膜层厚为25～50nm，高折射率膜及低折射率膜交替10～25次玻璃基片交替镀有高折射率膜及低折射率膜，高折射膜层厚为10～30nm、低折射率膜层厚为25～50nm，高折射率膜及低折射率膜交替8～25次。
所述高折射率膜为二氧化钛膜、二氧化锆膜、二氧化铈膜中的一种或几种。
所述低折射率膜为氟化镁膜、二氧化硅膜、三氧化二铝膜中的一种或几种。
本发明所述的紫外防护镜片制备方法包含以下步骤:
(1)待镀膜玻璃基片通过超声波清洗除去污渍并烘干；
(2)将待镀膜玻璃基片置于真空镀膜机真空舱内，在2.8×10-3～3.2×10-3Pa真空度下用离子枪轰击玻璃基片,对玻璃基片进行处理；
(3)在2.8×10-3～3.2×10-3Pa真空度、玻璃基片温度280～320℃下，用离子枪依次轰击镀膜材料，镀膜材料蒸发，由玻璃基片向外交替镀制高折射率膜及低折射率膜，用真空镀膜机中的膜厚控制仪控制高折射膜层厚为10～30nm、低折射率膜层厚为25～50nm，交替镀膜8～25次。
本发明制备的紫外防护镜片可见光透过高、紫外线防护效果好，实现紫外线防护与正常观察的完美统一，解决了佩戴太阳镜阻隔紫外线防治白内障时，可见光透过率低影响人眼观察的问题。
具体实施方式
下面结合具体实施事例，进一步阐述本发明。
实例1:
紫外防护镜片的制备方法，包括如下步骤:
(1)待镀膜玻璃基片通过超声波清洗除去污渍并烘干；
(2)将待镀膜玻璃基片置于真空镀膜机真空舱内，在3×10-3Pa真空度下用离子枪轰击玻璃基片；
(3)在3×10-3Pa真空度、玻璃基片温度300℃下，用离子枪依次轰击镀膜材料，，由玻璃基片向外交替镀制二氧钛膜及二氧化硅膜，用真空镀膜机中的膜厚控制仪控制二氧钛膜膜层厚为20nm、二氧化硅膜膜层厚为30nm，交替镀膜10次。
紫外防护镜片镀膜前可见光透过率为91%、380nm以下波长紫外线透过率为50%，镀膜后可见光透过率为93%、380nm以下波长紫外线透过率为20%、镜片呈无色透明。
实例2:
紫外防护镜片的制备方法，包括如下步骤:
(1)待镀膜玻璃基片通过超声波清洗除去污渍并烘干；
(2)将待镀膜玻璃基片置于真空镀膜机真空舱内，在2.9×10-3Pa真空度下用离子枪轰击玻璃基片；
(3)在2.9×10-3Pa真空度、玻璃基片温度310℃下，用离子枪依次轰击镀膜材料，，由玻璃基片向外交替镀制二氧化锆膜及二氧化硅膜，用真空镀膜机中的膜厚控制仪控制二氧钛膜膜层厚为15nm、二氧化硅膜膜层厚为35nm，交替镀膜15次。
紫外防护镜片镀膜前可见光透过率为91%、380nm以下波长紫外线透过率为50%，镀膜后可见光透过率为94%、380nm以下波长紫外线透过率为18%、镜片呈无色透明。
实例3:
紫外防护镜片的制备方法，包括如下步骤:
(1)待镀膜玻璃基片通过超声波清洗除去污渍并烘干；
(2)将待镀膜玻璃基片置于真空镀膜机真空舱内，在3.1×10-3Pa真空度下用离子枪轰击玻璃基片；
(3)在3.1×10-3Pa真空度、玻璃基片温度290℃下，用离子枪依次轰击镀膜材料，，由玻璃基片向外交替镀制二氧锆膜及氟化镁膜，用真空镀膜机中的膜厚控制仪控制二氧钛膜膜层厚为25nm、二氧化硅膜膜层厚为40nm，交替镀膜20次。
紫外防护镜片镀膜前可见光透过率为91%、380nm以下波长紫外线透过率为50%，镀膜后可见光透过率为95%、380nm以下波长紫外线透过率为15%、镜片呈无色透明。

Claims (4)

1.一种紫外防护镜片，包括玻璃基片，其特征在于玻璃基片上由玻璃基片向外交替镀有高折射率膜及低折射率膜，高折射膜层厚为10～30nm、低折射率膜层厚为25～50nm，高折射率膜及低折射率膜交替10～25次。
2.如权利要求1所述一种紫外防护镜片，其特征在于所述高折射率膜为二氧化钛膜、二氧化锆膜、二氧化铈膜中的一种或几种。
3.如权利要求1所述一种紫外防护镜片，其特征在于所述低折射率膜为氟化镁膜、二氧化硅膜、三氧化二铝膜中的一种或几种。
4.如权利要求1所述的一种紫外防护镜片，其特征在于制备方法包括如下步骤:
(1)待镀膜玻璃基片通过超声波清洗除去污渍并烘干；
(2)将待镀膜玻璃基片置于真空镀膜机真空舱内，在2.8×10-3～3.2×10-3Pa真空度下用离子枪轰击玻璃基片；
(3)在2.8×10-3～3.2×10-3Pa真空度、玻璃基片温度280～320℃下，用离子枪依次轰击镀膜材料，由玻璃基片向外交替镀制高折射率膜及低折射率膜，用真空镀膜机中的膜厚控制仪控制高折射膜层厚为10～30nm、低折射率膜层厚为25～50nm，交替镀膜8～25次。
CN201510813567.5A 2015-11-23 2015-11-23 一种紫外防护镜片及制备方法 Pending CN105293953A (zh)