CN105291535B - A kind of preparation system of carbon crystalline substance extrusion coating paper - Google Patents
A kind of preparation system of carbon crystalline substance extrusion coating paper Download PDFInfo
- Publication number
- CN105291535B CN105291535B CN201510701883.3A CN201510701883A CN105291535B CN 105291535 B CN105291535 B CN 105291535B CN 201510701883 A CN201510701883 A CN 201510701883A CN 105291535 B CN105291535 B CN 105291535B
- Authority
- CN
- China
- Prior art keywords
- paper
- carbon
- base material
- extrusion coating
- crystalline substance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of preparation system of carbon crystalline substance extrusion coating paper, with the first base material, carbon crystal electrothermo paper and the second base material for overlapping successively from top to bottom, which includes printing drying system, splitting system and hot pressing hybrid system the carbon crystalline substance extrusion coating paper.The present invention is the preparation system for new product carbon crystalline substance extrusion coating paper Aided design, carbon with some strength and thickness crystalline substance extrusion coating paper is formed directly Jing after " print twice and dry, hot pressing is compound, cutting " operation, the complicated manufacturing procedures such as follow-up assembling frame are reduced, thus has the advantages that low cost, production efficiency are high.And first and second base material due to carbon crystal electrothermo paper with upper and lower both sides is commaterial, with the good compatibility, therefore its structure is relatively reliable.In sum, the streamlined batch production of carbon crystalline substance extrusion coating paper is capable of achieving by above-mentioned preparation system, production efficiency is greatly improved, with the extremely strong market competitiveness.
Description
Technical field
The invention belongs to the manufacturing field of carbon crystalline substance product, more particularly to it is a kind of for production with breathability paper to carry
The preparation system of the carbon crystalline substance extrusion coating paper of body.
Background technology
With the continuous improvement of people's living standard, the living environment of urban and rural residents has great improvement.It is traditional with
Heating wire or electrothermal tube become basically universal in urban and rural households for the heating equipment of heat generating components, such heat generating components
Defect is that energy consumption is larger, and in the not high occasion of living environment these temperature increase requirements, the efficiency of electric heating energy conversion is not high enough, safety
Property is also bad.In recent years, the visual field of people has gradually been come into carbon crystalline substance product of the material as core, as the core in carbon crystalline substance product
Heart heater element, its common form have two kinds of carbon material electrical hotting mask and carbon fiber electric heating paper.
However, for existing carbon material electrical hotting mask, which is remained in following some problems：1. the outside of Electric radiant Heating Film protects
Sheath is to be got on by adhering to processing in the later stage, as the material of protective layer is different from electrothermal film material, is susceptible to pressure multiple
The unreal, situation of dislocation, causes leakage of current, increases fault rate；2. can be too high because of local temperature when Electric radiant Heating Film diaphragm is superimposed
And break down, there is great potential safety hazard；3. metal current-carrying bar and the position of carbon crystal heat body handing-over in Electric radiant Heating Film holds
It is also easy to produce electric spark；4. electric energy conversion ratio need further to improve.
For existing carbon fiber electric heating paper, such as Chinese Patent Application No. discloses a kind of carbon fibre for 201310312273.5
Dimension composite electro-thermal paper and preparation method thereof, which is prepared by the raw materials in：Carbon fiber 30-40, wood pulp 100-120, second
Thiazolinyl triethoxysilane 3-4, nanometer iron powder 3-4, polyvinyl acetate emulsion 2-3, sodium carbonate 1-2, sepiolite powder 3-4, Vermiculitum
Powder 2-3, zinc chloride 1-2, boric acid 1-2, sodium peroxydisulfate 1-2, Oleum Brassicae campestriss 1-2, peanut shell powder 1-2, modified micaceous powder 3-4.Although
Above-mentioned patent compared with traditional carbon fiber composite electro-thermal paper, by adding nanometer iron powder, increases its electric conductivity and stability, changes
The resistance for being apt to existing carbon fiber paper generally existing is uneven, and carbon fiber disperses uneven in paper, causes heating uneven
Problem, but its research and development focuses on paper pulp raw material is thoroughly improved, thus have that manufacturing cost is too high, production efficiency
Low problem.
Additionally, applicant is one specializes in facing paper research and development and manufacturing enterprise, carbon crystal heat body is introduced in research and development
Find to when facing paper and decorative panel：Relative to carbon fiber electric heating paper, carbon material electrical hotting mask is high with low cost, production efficiency
Advantage is favored by lots of manufacturers, thus it is exactly with film as carrier that on Vehicles Collected from Market, the carbon crystal heat body of generally existing is mostly upper
Carbon crystal electric hotting mask, but when Electric radiant Heating Film is combined to form wallboard or floor with facing paper research staff find, due to
Electric radiant Heating Film is different from the material of facing paper, and both easily occur to depart from high temperature, not only affect the normal use of consumer, and
And leave very big potential safety hazard.Applicant constantly explores on this basis, and has succeeded in developing one kind and with breathability paper be
The carbon crystalline substance extrusion coating paper of carrier, carbon crystalline substance extrusion coating paper have high low cost, production efficiency, simple structure and it is firm the characteristics of.
A preparation system matched with the crystalline substance extrusion coating paper production of above-mentioned carbon how is designed so, it has also become pendulum is in this area
The technical problem of urgent solution is needed in face of technical staff.
The content of the invention
To overcome the problems referred to above, the invention provides a kind of preparation system of carbon crystalline substance extrusion coating paper, has filled up existing manufacture and has set
Lack the blank of corresponding carbon crystalline substance extrusion coating paper process units, automatization strong advantage high with production efficiency in standby.
The technical solution adopted for the present invention to solve the technical problems is：A kind of preparation system of carbon crystalline substance extrusion coating paper, the carbon
Brilliant extrusion coating paper has the first base material, carbon crystal electrothermo paper and the second base material for overlapping successively from top to bottom, and above-mentioned the first base material, carbon are brilliant
Electrothermal paper and the second base material are made by melamine material.Above-mentioned preparation system include print drying system, splitting system and
Hot pressing hybrid system.
Wherein, printing drying system is used to print carbon crystal electrothermo paper, and which includes that the first printer for connecting successively, first are dried
Dry machine, the second printer and the second dehydrator.Above-mentioned first printer is printed on for the compound by carbon crystalline flour material with ink
On paper, carbon ink heating layer is made.During work, at the roller of paper horizontal transmission to the first printer, then transport vertically upward
It is dynamic.First dehydrator left and right in the vertical direction of paper is disposed with two, it is preferred that paper is located at two the first dehydrators
Centre position, above-mentioned first dehydrator are hot air type drier, and carbon ink heating layer is quickly dried by the way of left and right is to blowing by which
Dry, its hot blast wind direction is perpendicular with the direction of motion of paper.When paper pass through the first dehydrator after, mono- group of slewing rollers of Jing run to
Second printer.Second printer makes metal current-carrying bar for metal slurries are printed on paper.During work, paper exists
Under the roller of the second printer drives, the paper for being printed with metal slurries is lifted vertically upward.Second dehydrator and first dries
The structure of dry machine is similar to, and equally in the vertical direction of paper, left and right is disposed with two, it is preferred that paper is dried positioned at two second
The centre position of dry machine.Above-mentioned second dehydrator is hot air type drier, and which is by the way of left and right is to blowing by metal current-carrying bar
Flash baking, its hot blast wind direction are perpendicular with the direction of motion of paper.
Splitting system, including carbon crystal electrothermo paper is cut according to default size for the first cutting machine to facilitate hot pressing compound,
And the second cutting machine of carbon crystalline substance extrusion coating paper is cut into for the brilliant compound imposite of the carbon by hot pressing after compound.First cutting machine
Between the second dehydrator and heat-pressing compound machine, the second cutting machine is located at the port of export of heat-pressing compound machine.
Hot pressing hybrid system, it is brilliant compound whole for the first base material, carbon crystal electrothermo paper, the second base material hot pressing are combined into carbon
Plate, which includes heat-pressing compound machine, cup measurer and pallet.Wherein, cup measurer is for according to default thickness the first base of statistics
The number of material and the second base material, pallet are used to carry the first base material, carbon crystal electrothermo paper and the second base material, and heat-pressing compound machine is used for multiple
Synthesis type.
As a further improvement on the present invention, also including impregnation drying system before hot pressing hybrid system.The impregnation dries
Dry systems include the first cement dipping machine, the first hot air drier, the second cement dipping machine and the second hot air drier being sequentially connected.Its
In, the first cement dipping machine is used to glue is fully permeated in paper order that both fully to combine, and first cement dipping machine is built with by three
Poly cyanamid glue, firming agent, the mixed solution of penetrating agent composition.First hot air drier is for by the moisture on the paper after impregnation
Rapid evaporation, in case occur the defect bubbled after hot pressing is compound, first hot air drier on sheet movement direction, upper and lower cloth
Be equipped with two groups, by hot blast up and down to blowing, the moisture of the upper and lower both sides of preliminary drying carbon crystal electrothermo paper.The structure of the second cement dipping machine
Similar with the first cement dipping machine, except for the difference that the second cement dipping machine is built with the mixing being made up of melamine glue, firming agent, releasing agent
Solution, its role is to beneficial to the glue demoulding, prevent in compound tense the first base material, carbon crystal electrothermo paper, the second substrate bonding in steel
On plate.The structure of the second hot air drier is similar with the first hot air drier, and its effect is further dried on carbon crystal electrothermo paper
The moisture of lower both sides, which is equally disposed with two groups on sheet movement direction up and down, by hot blast up and down to blowing away except paper
On moisture.In addition, the first hot air drier of ratio that the length of the second hot air drier can be arranged is slightly longer.
The carbon crystalline substance extrusion coating paper mentioned in the present invention is that I takes charge of the brand-new heat-emitting products of original creation, and which includes folding successively from top to bottom
The first base material of conjunction, carbon crystal electrothermo paper and the second base material.Above-mentioned carbon crystal electrothermo paper with breathability paper as carrier, in gas-permeable paper
The side opened is printed with the carbon ink heating layer being mixed by carbon crystal material and ink, is additionally provided with carbon ink heating layer
For forming the metal current-carrying bar of electric heating paper electrode.The cementing layer being adapted with carbon ink heating layer is additionally provided with breathability paper.
Above-mentioned the first base material, breathability paper and the second base material are made by commaterial.Additionally, by the area and carbon ink of cementing layer
The area of heating layer is set to equal, Jing repetition tests, and the area ratio is adapted to, guarantor fully glued with the base material up and down of extrusion coating paper
Card gluing portion is not separated after heating.Even if in preparation process not impregnation and only Jing hot presses be combined, it is also ensured that
Combination between electrothermal paper and upper and lower base material.Preferably, cementing layer and carbon ink heating layer are elongated, and in breathability paper
Upper arranged for interval has multigroup.
The the first gluing portion combined with the cementing layer, carbon crystal electrothermo are provided between the first base material and carbon crystal electrothermo paper
The the second gluing portion combined with the cementing layer is provided between paper and the second base material.As a further improvement on the present invention,
One gluing portion and the second gluing portion are generated by melamine glue Jing hot pressing.As the further improvement of the present invention, the first base material
It is composited by hot press by one or several sheets melamine paper with the second base material.The purpose being arranged such is to pass through
The size of required extrusion coating paper selectes the first base material and the corresponding number of the second base material.
Further, above-mentioned the first base material, breathability paper and the second base material are made by melamine material, certainly its
Other high temperature resistant type materials can also be selected, is not limited by above-mentioned concrete material.Above-mentioned metal current-carrying bar is starched by copper or silver paste
It is obtained.
As breathability paper, the first base material and the second base material are paper material, with the good compatibility, greatly
Avoid the defect that traditional Electric radiant Heating Film is easily separated with the first base material, the second base material under hot environment.Wherein, breathability paper
Preferably melamine paper, can further improve the heat-resisting quantity and fire resistance of carbon crystal electrothermo paper, while tripolycyanamide is also
A kind of good binding agent.It is compound by the hot pressing of the first base material, carbon crystal electrothermo paper, the second base material, can disposably be formed and be had
The carbon crystalline substance extrusion coating paper of very high strength, and without the need for the assembling frame process in later stage, greatly save the activity duration.In sum, on
State carbon crystalline substance extrusion coating paper and there is simple structure, high temperature resistant property is good, and high-temperature heating is indeformable repeatedly, the spy of stable physical property
Point, and sound construction, it is safe and reliable, do not occur to depart from even if can guarantee that good adhesion in high temperature environments yet, it is raw
Produce ultrahigh in efficiency.
The preparation method of above-mentioned carbon crystalline substance extrusion coating paper, which comprises the steps：
1. debugging prepares：First breathability paper is arranged in frame roller, it is then that carbon crystalline flour material is mixed with ink
Close material, metal slurries to be respectively installed in the specified ink groove of the first printer, the second printer.Wherein, the first printer is used for
Printed carbon ink heating layer, the second printer are used for type metal current-carrying bar.The starting up speed of two groups of printer is arranged to 200m/
First dehydrator and the second dehydrator are then warming up to 150～200 DEG C by min, then by the first cement dipping machine, the second cement dipping machine
Starting up speed be set as 40～50m/min, finally the temperature of drying baker in impregnation link is set, complete debugging.
2. one-step print dry：By the first printer on breathability paper printed carbon ink heating layer, then Jing
One dehydrator carries out drying and processing to carbon ink, to remove the moisture in ink as early as possible.Preferably, first dehydrator or so is disposed with
Two, the breathability paper for printing carbon ink heating layer is located between two the first dehydrators, breathability paper leading in roller
Moved under drawing from bottom to top, above-mentioned first dehydrator be heated air drier, its using left and right to blowing by the way of, its hot blast wind direction
It is perpendicular with the direction of motion of breathability paper.
3. secondary printing dry：By the second printer on breathability paper type metal current-carrying bar, then with
Two drying machine drying metal current-carrying bars, equally remove the moisture on metal current-carrying bar as early as possible, obtain final product carbon crystal electrothermo paper.Preferably,
Second dehydrator or so is disposed with two, and the breathability paper for printing metal current-carrying bar is located between two the second dehydrators,
Breathability paper is moved under the traction of roller from bottom to top, and above-mentioned second dehydrator is heated air drier, and which adopts left and right
To the mode blown, its hot blast wind direction is perpendicular with the direction of motion of breathability paper, and specifically, second dehydrator in left side is to the right
Blowout hot blast, second dehydrator on right side blow out hot blast to the left.
4. impregnation dry：The operation can be carried out in four steps, the first step by step 3. in the immersion of carbon crystal electrothermo paper by three
In poly cyanamid glue, firming agent, the mixed solution of penetrating agent composition so that melamine glue can be sufficiently impregnated with very short time
In carbon crystal electrothermo paper.Second step Jing hot air driers, by hot blast up and down to blowing, the upper and lower both sides of preliminary drying carbon crystal electrothermo paper
Moisture.The mixed solution that carbon crystal electrothermo paper immersion after drying is made up of by the 3rd step melamine glue, firming agent, releasing agent
In, prevent melamine glue to be bonded on the pressing plate of hot press in follow-up hot pressing is compound.4th step Jing hot air drier, passes through
Hot blast up and down to blowing, further dry the moisture of the upper and lower both sides of carbon crystal electrothermo paper.
Above-mentioned second step, the hot air drier of the 4th step are in upper and lower arranged for interval, during the carbon crystal electrothermo paper after impregnation is located at
Between position, and travel forward under roller traction, the hot air drier on top blows out downwards hot blast, the hot air drier of bottom to
Upper blowout hot blast, the carbon crystal electrothermo paper after impregnation is in two strands of hot blast effect low suspensions in centre position, specifically, heat in second step
Wind drying baker is provided with three groups, and in the 4th step, hot air drier is provided with five groups.
5. once cut：Set color marker according to staying at electrothermal paper edge in printing process carries out precision and cuts, and can have
Effect prevents from damaging electrothermal paper Shang Tan roads and circuit because cutting not in place.As, in immersing glue process, carbon crystal electrothermo paper is unavoidable
Can there is a certain degree of stretching, it is therefore desirable to electrothermal paper is once cut before hot pressing is compound.
6. hot pressing is combined：By the second base material for presetting, the carbon crystal electrothermo paper after cutting, and the first base material are stacked successively
Together, and by conveyer belt the specified location for being transported to hot press carries out hot pressing and is combined, and the pressure requirements of hot press are 1600～
2500t, hot pressing temperature are 100～180 DEG C.
7. secondary cutting：The carbon crystalline substance extrusion coating paper of composite molding is cut according to the size of regulation.
8. assemble, carbon crystalline substance extrusion coating paper is obtained.
The present invention compared with prior art, has an advantage in that：
The present invention is the preparation system for new product carbon crystalline substance extrusion coating paper Aided design, and the preparation system has production efficiency pole
High advantage.Carbon with some strength and thickness is formed directly Jing after " print twice and dry, hot pressing is compound, cutting " operation
Brilliant extrusion coating paper, reduces the complicated manufacturing procedures such as follow-up assembling frame, thus has the advantages that low cost, production efficiency are high.
And first and second base material due to carbon crystal electrothermo paper with upper and lower both sides is commaterial, with the good compatibility, therefore
Its structure is relatively reliable.To sum up, the streamlined batch production of carbon crystalline substance extrusion coating paper is capable of achieving by above-mentioned preparation system, is greatly improved
Production efficiency, in addition it is noted that the carbon crystalline substance extrusion coating paper of the present invention has than any one carbon crystalline substance product on the market
Significant cost advantage, with the extremely strong market competitiveness.
Below with reference to drawings and Examples, the present invention is described in detail.
Description of the drawings
Fig. 1 is the structural representation of preparation system in embodiment 1.
Fig. 2 is the structural representation of preparation system in embodiment 2.
Fig. 3 is the structural representation for printing drying system, and wherein arrow represents hot blast wind direction.
Structural representations of the Fig. 4 for impregnation drying system, wherein arrow represent hot blast wind direction.
Fig. 5 is the sectional view of carbon crystalline substance extrusion coating paper.
Sectional views of the Fig. 6 for carbon crystal electrothermo paper.
Front views of the Fig. 7 for carbon crystal electrothermo paper.
In figure, 101, the first base material；102nd, carbon crystal electrothermo paper；103rd, the second base material；104th, the first gluing portion；105th, second
Glued portion；106th, generate heat extrusion coating paper；1st, paper；2nd, carbon ink heating layer；3rd, metal current-carrying bar；4th, cementing layer；5th, the first printer；
6th, the first dehydrator；7th, the second printer；8th, the second dehydrator；9th, the first cement dipping machine；10th, the first hot air drier；11st, second
Cement dipping machine；12nd, the second hot air drier；13rd, the first cutting machine；14th, the second cutting machine；15th, heat-pressing compound machine.
Specific embodiment
Embodiment 1,
Fig. 5 to 7 is referred to, a kind of carbon crystalline substance extrusion coating paper 106 includes that the first base material 101, carbon for overlapping successively from top to bottom is brilliant
Electrothermal paper 102 and the second base material 103.Wherein, carbon crystal electrothermo paper 102 is with breathability paper 1 as carrier, in breathability paper 1
Side is printed with the carbon ink heating layer 2 being mixed by carbon crystal material and ink, on carbon ink heating layer 2 is additionally provided with use
In the metal current-carrying bar 3 for forming electric heating paper electrode.The cementing layer being adapted with carbon ink heating layer 2 is additionally provided with breathability paper 1
4.The the first gluing portion 104 combined with the cementing layer is provided between the first base material 101 and carbon crystal electrothermo paper 102, carbon is brilliant
The the second gluing portion 105 combined with the cementing layer is provided between electrothermal paper 102 and the second base material 103.Carbon ink heating layer 2
The area equation of area and cementing layer 4.Carbon ink heating layer 2 and cementing layer 4 are elongated, and are spaced on breathability paper 1
It is disposed with multigroup.Breathability paper 1 is made up of melamine material, and metal current-carrying bar 3 is starched by copper or silver paste is obtained.The first base material
101 and second base material 103 made by melamine material.The first base material 101 and the second base material 103 are by one or several sheets
Melamine paper passes through hot press composite molding.First gluing portion 104 and the second gluing portion 105 are given birth to by melamine glue Jing hot pressing
Into.
Refer to Fig. 1,3, a kind of preparation system for preparing above-mentioned carbon crystalline substance extrusion coating paper, it include printing drying system,
Splitting system and hot pressing hybrid system.
Wherein, the first printer 5, the first dehydrator 6,7 and of the second printer that drying system includes connecting successively are printed
Second dehydrator 8.
First printer 5 is printed on paper for the compound by carbon crystalline flour material with ink, makes carbon ink heating layer.Work
When making, at the roller of 1 horizontal transmission of paper to the first printer, then upward vertical movement.
First dehydrator 6 left and right in the vertical direction of paper is disposed with two, and paper 1 is located at two the first dehydrators
Centre position, above-mentioned first dehydrator are hot air type drier, and carbon ink heating layer is quickly dried by the way of left and right is to blowing by which
Dry, its hot blast wind direction is perpendicular with the direction of motion of paper.After paper 1 passes through the first dehydrator 6, mono- group of slewing rollers operation of Jing
To the second printer 7.
Second printer 7 makes metal current-carrying bar for metal slurries are printed on paper.During work, paper 1 is
Under the roller of two printer 7 drives, the paper for being printed with metal slurries is lifted vertically upward.
Second dehydrator 8 left and right in the vertical direction of paper 1 is disposed with two, and paper 1 is located at two the second dehydrators
Centre position.Above-mentioned second dehydrator 8 is hot air type drier, and which will be metal current-carrying bar quick by the way of left and right is to blowing
Drying, its hot blast wind direction are perpendicular with the direction of motion of paper.
Hot pressing hybrid system includes heat-pressing compound machine 15, cup measurer and pallet.Wherein, cup measurer is for according to default
Thickness statistics the first base material and the second base material number, pallet be used for carry the first base material, carbon crystal electrothermo paper and the second base material,
Heat-pressing compound machine is used for composite molding.
Splitting system includes according to default size the first cutting machine 13 by the cutting of carbon crystal electrothermo paper to facilitate hot pressing compound,
And the second cutting machine 14 of carbon crystalline substance extrusion coating paper is cut into for the brilliant compound imposite of the carbon by hot pressing after compound.First cutting machine 13
Between the second dehydrator 8 and heat-pressing compound machine 15, the second cutting machine 14 is located at the port of export of heat-pressing compound machine 15.
Embodiment 2,
Refer to Fig. 2,4, the preparation system of a kind of carbon crystalline substance extrusion coating paper, before which also includes being arranged on hot pressing hybrid system
Impregnation drying system, remaining is identical with embodiment 1.
The first cement dipping machine 9 that the impregnation drying system includes being sequentially connected, the first hot air drier 10, the second cement dipping machine 11
With the second hot air drier 12.
Wherein, the first cement dipping machine 9 is used to make both fully combine in paper so that glue fully permeates, first cement dipping machine
9 built with the mixed solution being made up of melamine glue, firming agent, penetrating agent.
First hot air drier 10 for by the moisture rapid evaporation on the paper after impregnation, in case occurring after hot pressing is compound
The defect of foaming, first hot air drier 10 are disposed with two groups on sheet movement direction up and down, by the right up and down of hot blast
Blow, the moisture of preliminary drying carbon crystal electrothermo paper both sides about 102.
Second cement dipping machine 11 its role is to built with the mixed solution being made up of melamine glue, firming agent, releasing agent
Beneficial to the glue demoulding, prevent compound tense the first base material 101, carbon crystal electrothermo paper 102, the second base material 103 be bonded in hot pressing be combined
On the molding steel plate of machine.
The effect of the second hot air drier 12 is the moisture for further drying carbon crystal electrothermo paper both sides about 102, and which is same
Be disposed with two groups on sheet movement direction up and down, by hot blast up and down to blowing away except the moisture on paper.
The above is only, to presently preferred embodiments of the present invention, not the scope of the present invention to be defined, therefore is not being taken off
On the premise of design spirit of the present invention, those of ordinary skill in the art are done to construction of the present invention, feature and principle
Equivalence changes or decoration, such as change print order of the first printer and the second printer etc., all should fall into the present invention's
In protection domain.
Claims (7)
1. the preparation system of a kind of carbon crystalline substance extrusion coating paper, carbon crystalline substance extrusion coating paper have the first base material, the carbon for overlapping successively from top to bottom
Brilliant electrothermal paper and the second base material, it is characterised in that：The first base material, carbon crystal electrothermo paper and the second base material are by tripolycyanamide material
Material is made；The preparation system includes printing drying system, splitting system and hot pressing hybrid system；
The printing drying system is used to print carbon crystal electrothermo paper, it include connecting successively for by carbon crystalline flour material and ink
Compound is printed on paper the first printer for making carbon ink heating layer, dries for first by carbon ink heating layer flash baking
Dry machine, for metal slurries to be printed on paper the second printer for making metal current-carrying bar, and for by metal current-carrying
Second dehydrator of bar flash baking；
Hot pressing hybrid system includes heat-pressing compound machine, cup measurer and pallet；Wherein, cup measurer is for according to default thickness
The number of statistics the first base material and the second base material, pallet are used to carry the first base material, carbon crystal electrothermo paper and the second base material, and hot pressing is multiple
For the first base material, carbon crystal electrothermo paper, the second base material hot pressing are combined into, carbon is brilliant to be combined imposite to conjunction machine；
Splitting system, including carbon crystal electrothermo paper is cut according to default size for the first cutting machine to facilitate hot pressing compound, and
The second cutting machine of carbon crystalline substance extrusion coating paper is cut into for the brilliant compound imposite of the carbon by hot pressing after compound；First cutting machine is located at
Between second dehydrator and heat-pressing compound machine, the second cutting machine is located at the port of export of heat-pressing compound machine.
2. the preparation system of carbon as claimed in claim 1 crystalline substance extrusion coating paper, it is characterised in that：The version of first printer of paper Jing
Upward vertical movement after roller strap is dynamic, the first dehydrator left and right in the direction of motion of paper are disposed with two, first dehydrator
By carbon ink heating layer flash baking by the way of left and right is to blowing, its hot blast wind direction is perpendicular with the direction of motion of paper.
3. the preparation system of carbon as claimed in claim 1 crystalline substance extrusion coating paper, it is characterised in that：The version of second printer of paper Jing
Upward vertical movement after roller strap is dynamic, the second dehydrator left and right in the direction of motion of paper are disposed with two, second dehydrator
Will be metal current-carrying bar flash baking, its hot blast wind direction perpendicular with the direction of motion of paper by the way of left and right is to blowing.
4. the preparation system of carbon as claimed in claim 1 crystalline substance extrusion coating paper, it is characterised in that：Also included before hot pressing hybrid system
Impregnation drying system.
5. the preparation system of carbon as claimed in claim 4 crystalline substance extrusion coating paper, it is characterised in that：The impregnation drying system is included successively
It is connected for causing glue fully to permeate the first cement dipping machine in paper, for by moisture rapid evaporation on paper after impregnation
First hot air drier, is used to help the second cement dipping machine of the glue demoulding, and upper and lower for further drying carbon crystal electrothermo paper
Second hot air drier of both sides moisture.
6. the preparation system of carbon as claimed in claim 5 crystalline substance extrusion coating paper, it is characterised in that：First cement dipping machine is built with by three
Poly cyanamid glue, firming agent, the mixed solution of penetrating agent composition；Second cement dipping machine is built with by melamine glue, firming agent, the demoulding
The mixed solution of agent composition.
7. the preparation system of carbon as claimed in claim 5 crystalline substance extrusion coating paper, it is characterised in that：First hot air drier is in level
Be disposed with two groups on direction up and down, by hot blast up and down to blowing, the moisture of the upper and lower both sides of preliminary drying carbon crystal electrothermo paper；Second
Hot air drier is disposed with two groups in the horizontal direction up and down, by hot blast up and down to blowing, thoroughly on drying carbon crystal electrothermo paper
The moisture of lower both sides.