CN105289533A - 一种用于处理含汞、铅废水的环保吸附材料及其制备方法 - Google Patents
一种用于处理含汞、铅废水的环保吸附材料及其制备方法 Download PDFInfo
- Publication number
- CN105289533A CN105289533A CN201510689057.1A CN201510689057A CN105289533A CN 105289533 A CN105289533 A CN 105289533A CN 201510689057 A CN201510689057 A CN 201510689057A CN 105289533 A CN105289533 A CN 105289533A
- Authority
- CN
- China
- Prior art keywords
- parts
- environmental
- adsorption material
- mercurous
- treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种用于处理含汞、铅废水的环保吸附材料及其制备方法,所述的制备方法步骤如下:(1)按重量分别取羟基磷灰石、硅藻土、氧化镁、氧化锆,将以上材料放入高速粉碎机中,对其进行粉碎;(2)按重量分别取羟丙基壳聚糖4-10份、木质纤维素3-8份、粉碎后的羟基磷灰石3-6份、硅藻土4-9份、氧化镁2-6份、氧化锆3-6份,将上述的成分在室温下搅拌均匀;(3)再向步骤(2)的混合材料中加入海藻纤维3-7份、聚乙烯醇2-5份,搅拌至均匀,制备得到用于处理含汞、铅废水的环保吸附材料。制备得到的环保吸附材料对含有汞、铅的废水具有非常好的处理效果。
Description
技术领域
本发明属于环保材料领域,具体涉及一种用于处理含汞、铅废水的环保吸附材料及其制备方法。
背景技术
重金属废水的处理方法较多,包括物理吸附法、还原沉淀法、离子交换法、电解法等。其中,物理吸附法也是其中一种比较重要的处理方法。通过添加絮凝剂使得重金属废水中的小胶体颗粒稳定性变差,聚集形成大颗粒胶体物质,最终通过重力作用沉淀下来。为增大胶体颗粒的尺寸,采用浮选的办法,用于将不稳定的胶体粒子变为固相絮凝物。这一浮选过程一般包括两个重要的步骤,一是调节pH值,二是加入含铁或铝盐的絮凝剂,以克服离子间静电排斥导致的稳定作用。重金属废水中的汞和铅的污染较大,因此,需要开发有效的处理方法来降低重金属废水中的汞和铅的含量。
发明内容
要解决的技术问题:常规的用于重金属废水处理的环保材料的处理效率较低,本发明的目的是提供一种对重金属废水处理具有较高效率的环保型吸附材料及其制备方法,可用于重金属废水尤其是含汞、铅废水的处理应用。
技术方案
本发明是通过下述技术方案实现的:
一种用于处理含汞、铅废水的环保吸附材料,所述的环保吸附材料包括下述重量份的成分:
羟丙基壳聚糖4-10份、
木质纤维素3-8份、
羟基磷灰石3-6份、
硅藻土4-9份、
氧化镁2-6份、
氧化锆3-6份、
海藻纤维3-7份、
聚乙烯醇2-5份。
优选的,所述的一种用于处理含汞、铅废水的环保吸附材料,包括下述重量份的成分:
羟丙基壳聚糖5-9份、
木质纤维素4-7份、
羟基磷灰石4-5份、
硅藻土5-8份、
氧化镁3-5份、
氧化锆4-5份、
海藻纤维4-6份、
聚乙烯醇3-4份。
所述的一种用于处理含汞、铅废水的环保吸附材料的制备方法,所述的制备方法步骤如下:
(1)按重量分别取羟基磷灰石、硅藻土、氧化镁、氧化锆,将以上材料放入高速粉碎机中,对其进行粉碎,粉碎时间为10-15min,粉碎至目数为200目以上;
(2)按重量分别取羟丙基壳聚糖4-10份、木质纤维素3-8份、粉碎后的羟基磷灰石3-6份、硅藻土4-9份、氧化镁2-6份、氧化锆3-6份,将上述的成分在室温下搅拌,搅拌转速为50-90r/min,搅拌至均匀;
(3)再向步骤(2)的混合材料中加入海藻纤维3-7份、聚乙烯醇2-5份,再保持转速不变再进行搅拌,搅拌至均匀,制备得到用于处理含汞、铅废水的环保吸附材料。
优选的,所述的一种用于处理含汞、铅废水的环保吸附材料的制备方法,所述的步骤(1)中粉碎至目数至250目以上。
优选的,所述的一种用于处理含汞、铅废水的环保吸附材料的制备方法,所述的步骤(2)中转速为70r/min。
有益效果:本发明制备得到的用于处理含汞、铅废水的环保吸附材料在处理含有汞和铅的重金属废水后,重金属废水中的汞和铅含量得到了有效的显著下降,具有非常好的处理效率,其中本发明的环保吸附材料中的多孔成分、无机成分及高分子成分都发挥了非常好的协同作用,共同的降低了汞和铅的含量。
具体实施例
下面结合具体实施例对本发明进行进一步说明。
实施例1
(1)按重量分别取羟基磷灰石、硅藻土、氧化镁、氧化锆,将以上材料放入高速粉碎机中,对其进行粉碎,粉碎时间为15min,粉碎至目数为200目以上;
(2)按重量分别取羟丙基壳聚糖10份、木质纤维素3份、粉碎后的羟基磷灰石6份、硅藻土9份、氧化镁2份、氧化锆6份,将上述的成分在室温下搅拌,搅拌转速为90r/min,搅拌至均匀;
(3)再向步骤(2)的混合材料中加入海藻纤维7份、聚乙烯醇2份,再保持转速不变再进行搅拌,搅拌至均匀,制备得到用于处理含汞、铅废水的环保吸附材料。
实施例2
(1)按重量分别取羟基磷灰石、硅藻土、氧化镁、氧化锆,将以上材料放入高速粉碎机中,对其进行粉碎,粉碎时间为10min,粉碎至目数为200目以上;
(2)按重量分别取羟丙基壳聚糖4份、木质纤维素8份、粉碎后的羟基磷灰石3份、硅藻土4份、氧化镁6份、氧化锆3份,将上述的成分在室温下搅拌,搅拌转速为50r/min,搅拌至均匀;
(3)再向步骤(2)的混合材料中加入海藻纤维3份、聚乙烯醇5份,再保持转速不变再进行搅拌,搅拌至均匀,制备得到用于处理含汞、铅废水的环保吸附材料。
实施例3
(1)按重量分别取羟基磷灰石、硅藻土、氧化镁、氧化锆,将以上材料放入高速粉碎机中,对其进行粉碎,粉碎时间为15min,粉碎至目数为300目以上;
(2)按重量分别取羟丙基壳聚糖9份、木质纤维素7份、粉碎后的羟基磷灰石4份、硅藻土8份、氧化镁5份、氧化锆4份,将上述的成分在室温下搅拌,搅拌转速为90r/min,搅拌至均匀;
(3)再向步骤(2)的混合材料中加入海藻纤维6份、聚乙烯醇4份,再保持转速不变再进行搅拌,搅拌至均匀,制备得到用于处理含汞、铅废水的环保吸附材料。
实施例4
(1)按重量分别取羟基磷灰石、硅藻土、氧化镁、氧化锆,将以上材料放入高速粉碎机中,对其进行粉碎,粉碎时间为10min,粉碎至目数为300目以上;
(2)按重量分别取羟丙基壳聚糖5份、木质纤维素4份、粉碎后的羟基磷灰石5份、硅藻土5份、氧化镁3份、氧化锆5份,将上述的成分在室温下搅拌,搅拌转速为50r/min,搅拌至均匀;
(3)再向步骤(2)的混合材料中加入海藻纤维4份、聚乙烯醇3份,再保持转速不变再进行搅拌,搅拌至均匀,制备得到用于处理含汞、铅废水的环保吸附材料。
实施例5
(1)按重量分别取羟基磷灰石、硅藻土、氧化镁、氧化锆,将以上材料放入高速粉碎机中,对其进行粉碎,粉碎时间为10min,粉碎至目数为300目以上;
(2)按重量分别取羟丙基壳聚糖7份、木质纤维素6份、粉碎后的羟基磷灰石4份、硅藻土7份、氧化镁4份、氧化锆5份,将上述的成分在室温下搅拌,搅拌转速为50r/min,搅拌至均匀;
(3)再向步骤(2)的混合材料中加入海藻纤维5份、聚乙烯醇3份,再保持转速不变再进行搅拌,搅拌至均匀,制备得到用于处理含汞、铅废水的环保吸附材料。
对比例1
(1)按重量分别取硅藻土、氧化镁,将以上材料放入高速粉碎机中,对其进行粉碎,粉碎时间为15min,粉碎至目数为200目以上;
(2)按重量分别取羟丙基壳聚糖10份、木质纤维素3份、粉碎后的硅藻土9份、氧化镁2份,将上述的成分在室温下搅拌,搅拌转速为90r/min,搅拌至均匀;
(3)再向步骤(2)的混合材料中加入海藻纤维7份、聚乙烯醇2份,再保持转速不变再进行搅拌,搅拌至均匀,制备得到用于处理含汞、铅废水的环保吸附材料。
对比例2
(1)按重量分别取羟基磷灰石、硅藻土、氧化镁、氧化锆,将以上材料放入高速粉碎机中,对其进行粉碎,粉碎时间为15min,粉碎至目数为200目以上;
(2)按重量分别取羟丙基壳聚糖10份、木质纤维素3份、粉碎后的羟基磷灰石6份、硅藻土9份、氧化镁2份、氧化锆6份,将上述的成分在室温下搅拌,搅拌转速为90r/min,搅拌至均匀;制备得到用于处理含汞、铅废水的环保吸附材料。
对比例3
(1)按重量分别取羟基磷灰石、硅藻土、氧化镁,将以上材料放入高速粉碎机中,对其进行粉碎,粉碎时间为15min,粉碎至目数为200目以上;
(2)按重量分别取羟丙基壳聚糖10份、木质纤维素3份、粉碎后的羟基磷灰石6份、硅藻土9份、氧化镁2份,将上述的成分在室温下搅拌,搅拌转速为90r/min,搅拌至均匀;
(3)再向步骤(2)的混合材料中加入聚乙烯醇2份,再保持转速不变再进行搅拌,搅拌至均匀,制备得到用于处理含汞、铅废水的环保吸附材料。
含有汞、铅的重金属废水中汞含量为154mg/L,铅含量为135mg/L,向重金属废水中分别加入实施例1至5和对比例1至3的环保吸附材料,加入量为1wt%,再搅拌30-60min,离心分离后,测定废水中汞和铅的含量,结果如下:
汞含量(mg/L) | 铅含量(mg/L) | |
实施例1 | 42 | 39 |
实施例2 | 45 | 44 |
实施例3 | 30 | 29 |
实施例4 | 33 | 31 |
实施例5 | 19 | 22 |
对比例的环保吸附材料处理结果如下:
汞含量(mg/L) | 铅含量(mg/L) | |
对比例1 | 79 | 64 |
对比例2 | 82 | 71 |
对比例3 | 74 | 68 |
以上是对本发明进行了阐述,用于帮助理解本发明,但本发明的实施方式并不受上述实施例的限制,任何未背离本发明原理下所作的改变、修饰、替代、组合、简化,均应为等效的置换方式,都包含在本发明的保护范围之内。
Claims (5)
1.一种用于处理含汞、铅废水的环保吸附材料,其特征在于,所述的环保吸附材料包括下述重量份的成分:
羟丙基壳聚糖4-10份、
木质纤维素3-8份、
羟基磷灰石3-6份、
硅藻土4-9份、
氧化镁2-6份、
氧化锆3-6份、
海藻纤维3-7份、
聚乙烯醇2-5份。
2.根据权利要求1所述的一种用于处理含汞、铅废水的环保吸附材料,其特征在于,所述的环保吸附材料包括下述重量份的成分:
羟丙基壳聚糖5-9份、
木质纤维素4-7份、
羟基磷灰石4-5份、
硅藻土5-8份、
氧化镁3-5份、
氧化锆4-5份、
海藻纤维4-6份、
聚乙烯醇3-4份。
3.根据权利要求1所述的一种用于处理含汞、铅废水的环保吸附材料的制备方法,其特征在于,所述的制备方法步骤如下:
(1)按重量分别取羟基磷灰石、硅藻土、氧化镁、氧化锆,将以上材料放入高速粉碎机中,对其进行粉碎,粉碎时间为10-15min,粉碎至目数为200目以上;
(2)按重量分别取羟丙基壳聚糖4-10份、木质纤维素3-8份、粉碎后的羟基磷灰石3-6份、硅藻土4-9份、氧化镁2-6份、氧化锆3-6份,将上述的成分在室温下搅拌,搅拌转速为50-90r/min,搅拌至均匀;
(3)再向步骤(2)的混合材料中加入海藻纤维3-7份、聚乙烯醇2-5份,再保持转速不变再进行搅拌,搅拌至均匀,制备得到用于处理含汞、铅废水的环保吸附材料。
4.根据权利要求3所述的一种用于处理含汞、铅废水的环保吸附材料的制备方法,其特征在于,所述的步骤(1)中粉碎至目数至250目以上。
5.根据权利要求3所述的一种用于处理含汞、铅废水的环保吸附材料的制备方法,其特征在于,所述的步骤(2)中转速为70r/min。