CN1052839A - Making method for inorganic glass steel - Google Patents
Making method for inorganic glass steel Download PDFInfo
- Publication number
- CN1052839A CN1052839A CN 89106888 CN89106888A CN1052839A CN 1052839 A CN1052839 A CN 1052839A CN 89106888 CN89106888 CN 89106888 CN 89106888 A CN89106888 A CN 89106888A CN 1052839 A CN1052839 A CN 1052839A
- Authority
- CN
- China
- Prior art keywords
- frim
- making method
- hydrochloric acid
- dilute hydrochloric
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The making method of FRIM, main raw has: light calcined magnesia, dilute hydrochloric acid, bittern, the Yellow River sand, water-proofing powder, resin, promotor, solidifying agent, floor wax, woven fiber glass.Its feature is that the adding quick solidifying of dilute hydrochloric acid, the adding of the Yellow River sand strengthen intensity.Add water-proofing powder, FRIM is not seeped water.
The FRIM cost of utilizing this formed material to make is low, intensity big, flexible is easy to produce in enormous quantities, applies.
Description
The invention belongs to a kind of compound method of industrial chemicals.
Molding material, the kind of present domestic use are a lot.Unsaturated polyester resin, resol, modified phenolic resins, Resins, epoxy, furane resin etc. are arranged, add vinylbenzene and solidifying agent etc., coat on glass fibre or the woven fiber glass, again through curing molding.Cost is promoted than the higher big area that is difficult for.What also have forms with magnesia, bittern modulation, coats on the woven fiber glass.The glass reinforced plastic that this method is made, fragility is big, set time is long, intensity is low, can not widespread use.
Task of the present invention is: provide that a kind of cost is low, intensity is high, the compound method of the FRIM molding material of quick solidifying, easy-formation.
The method that the present invention solves is:
Compound method:
1, batching:
(1) proportioning: light calcined magnesia (80-100 order): 2.1
Dilute hydrochloric acid (16%): 1.25
Bittern (halogen sheet or bulk): 1
The Yellow River sand (100-150 order): 0.4
Water-proofing powder (200 order): 0.1
Resin: 0.05
Promotor: a little
Solidifying agent: a little
Floor wax is an amount of
Woven fiber glass is an amount of
(2) modulation:
A, bittern is dissolved in dilute hydrochloric acid.
B, light calcined magnesia is slowly added in the acidic solution limit edged stir.
C, with resin, promotor, solidifying agent, prepare the back in proportion and add and stir evenly.
D, will water-resisting agent, the Yellow River husky mix to add in the cylinder stir.(whole blending process need not heat.Envrionment temperature is not less than 0 ℃.)
2, paste:
Pasty state slip with preparing spreads upon on the woven fiber glass, promptly is FRIM after the curing.
Make in this way, the FRIM of making, characteristics are that cost is low, fire prevention, waterproof, antifreeze, corrosion-resistant, highly polished, intensity big, flexible, be easy to promote.
Embodiment one:
The making of solar cooker shell:
(1) batching:
1, the bittern of 2380 grams is put into the Porcelain Jar that fills 2975 grams, 16% dilute hydrochloric acid, stirring and dissolving.
2,5000 gram light calcined magnesias are slowly added in the cylinder, the limit edged stirs.
3, stir evenly in the unsaturated polyester that will temporarily prepare (methylethyl ketone peroxide 2.38 grams are prepared in glass cylinder for unsaturated polyester 119 grams, cobalt naphthenate 3.55 grams) the adding cylinder.
4, husky 950 grams in the Yellow River and water-proofing powder 238 grams are mixed well after, add in the cylinder and stir evenly.
(2) making of housing:
1, floor wax is spread upon on the solar cooker cement mold, spread woven fiber glass then, slip is spread upon on the woven fiber glass, the continuous like this four-layer glass cloth of smearing.
2, the demoulding: will paste the FRIM demoulding on mould more than 10 hours.
3, carriage is reinforced: the housing after the demoulding is placed on the mould, and the Steel Fabric Reinforcement carriage that will make in advance again sticks on the unorganic glass Steel Sheel.Solar cooker shell like this.
Embodiment two:
The making of bathtub:
(1) batching:
1,3333 gram bittern is put into the Porcelain Jar that fills 4167 grams, 16% dilute hydrochloric acid, stirring and dissolving.
2,7000 gram light calcined magnesias are slowly added in the cylinder, the limit edged stirs.
3, the unsaturated polyester resin that will temporarily prepare (resin 167 grams, cobalt naphthenate 5 grams, methylethyl ketone peroxide 3 grams) adds in the cylinder and mixes thoroughly.
4, with husky 1333 grams in the Yellow River and water-proofing powder 334 grams, stir in the adding cylinder after mixing well.
(2) pasting of bathtub:
1, floor wax is spread upon on the bathtub mould, spread woven fiber glass then, the slip for preparing in advance is put on the woven fiber glass, smear 10 layers of woven fiber glass continuously like this.
2, the demoulding: more than 10 hours, with the FRIM demoulding that pastes on mould.
3, the demoulding is after trimming is a finished product.
Claims (5)
1, the making method of FRIM is characterized in that having added dilute hydrochloric acid, makes this molding material quick solidifying.
2, the making method of FRIM according to claim 1 is characterized in that having added resin, has increased toughness.
3, according to the making method of claim 1,2 described FRIM, it is characterized in that having added the Yellow River sand, increased intensity.
4, according to claim 1,2,3 described making methods, it is characterized in that having added woven fiber glass, increased tensile strength.
5, according to claim 1,2,3,4 described making methods, it is characterized in that having added water-proofing powder.