CN105282282A - Mobile phone screen glass processing technology - Google Patents
Mobile phone screen glass processing technology Download PDFInfo
- Publication number
- CN105282282A CN105282282A CN201510729516.4A CN201510729516A CN105282282A CN 105282282 A CN105282282 A CN 105282282A CN 201510729516 A CN201510729516 A CN 201510729516A CN 105282282 A CN105282282 A CN 105282282A
- Authority
- CN
- China
- Prior art keywords
- glass
- mobile phone
- phone screen
- screen glass
- heating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a mobile phone screen glass processing technology, which comprises the steps of: S1, weighing and taking raw materials according to the following weight ratio; S2, uniformly mixing components, and then heating the mixed components at 350 DEG C for 1.5 hour; carrying out tableting and stretching by using a tablet machine to obtain a mobile phone screen material with a diameter ranging from 0.004 to 0.01mm; S3, cutting a whole piece of glass into the required machining size; S4, groove machining and edge chamfering are conducted on the cut glass; S5, placing the glass into a pure water cleaning tank, and cleaning the surfaces in an ultrasonic vibration mode; S6, heating the glass close to a softening temperature, and cooling the glass with air or a salt solution rapidly; S7, and packaging the machined glass by using a film laminating machine. The mobile phone screen glass processing technology has the beneficial effects of being simple and practical in technology, ensuring that surfaces of the screen glass are smooth and scratch-free, promoting mechanical strength and hardness of the screen glass, being capable of producing the perfectly-fitting screen glass, and being efficient in production and stable in product quality.
Description
Technical field
The present invention relates to mobile phone screen technical field, particularly a kind of mobile phone screen glass machining technique.Background technology
Clear glass refers to the plate glass without deep processing, also referred to as white glass.Clear glass has good perspective, light transmission.Flat screen can be produced by different technology, and wherein main technology is PDP (plasma display panel) and LCD (liquid crystal display) technology.These two technology all need to use glass substrate.In view of the scales of flat screen increases, minimizing of substrate weight is also important, for glass used, is presented as the demand to low density glass, also will prevent large-size substrate from bending simultaneously.
Summary of the invention
The object of the invention is to the shortcoming overcoming prior art, a kind of mechanical strength and the high mobile phone screen glass machining technique of hardness are provided.
Object of the present invention is achieved through the following technical solutions: mobile phone screen glass machining technique, comprises the following steps:
S1: take raw material by following weight ratio:
Silicon dioxide 60-80,
Sodium hydrogen phosphate 3-6,
Sodium pyrophosphate 4-6,
Titanium dioxide 0.8-3,
Boron oxide 2-15,
Sodium oxalate 4-6,
Aluminium oxide 10-25;
S2: each component is mixed, then heats, heating-up temperature is 300 ~ 400 DEG C, and heating time is 1 ~ 2h; Carry out compressing tablet stretching with tablet press machine, obtain the mobile phone screen material that diameter is 0.004 ~ 0.01mm;
S3: monolithic glass is cut into required processing dimension;
S4: the glass processing of well cutting goes out groove and edge chamfer;
S5: pure water rinse bath put into by glass, in addition vibration of ultrasonic wave clean surface;
S6: by glass heats close to softening temperature, with air or salting liquid, it is cooled rapidly;
S7: use laminating machine to pack the glass processed.
The present invention has the following advantages:
Features simple and practical process, ensures screen glass smooth surface, without scratch; Promote mechanical strength and the hardness of screen glass, the screen glass that energy output is fitted entirely, produce efficient, constant product quality.
Embodiment
Below in conjunction with embodiment, the present invention will be further described:
Embodiment 1:
Mobile phone screen glass machining technique, comprises the following steps:
S1: take raw material by following weight ratio:
Silicon dioxide 70,
Sodium hydrogen phosphate 5,
Sodium pyrophosphate 5,
Titanium dioxide 2,
Boron oxide 8,
Sodium oxalate 5,
Aluminium oxide 15;
S2: each component is mixed, then heats, heating-up temperature is 350 DEG C, and heating time is 1.5h; Carry out compressing tablet stretching with tablet press machine, obtain the mobile phone screen material that diameter is 0.004 ~ 0.01mm;
S3: monolithic glass is cut into required processing dimension;
S4: the glass processing of well cutting goes out groove and edge chamfer;
S5: pure water rinse bath put into by glass, in addition vibration of ultrasonic wave clean surface;
S6: by glass heats close to softening temperature, with air or salting liquid, it is cooled rapidly;
S7: use laminating machine to pack the glass processed.
Embodiment 2:
Mobile phone screen glass machining technique, comprises the following steps:
S1: take raw material by following weight ratio:
Silicon dioxide 60,
Sodium hydrogen phosphate 3,
Sodium pyrophosphate 4,
Titanium dioxide 0.8,
Boron oxide 2,
Sodium oxalate 4,
Aluminium oxide 10;
S2: each component is mixed, then heats, heating-up temperature is 300 DEG C, and heating time is 2h; Carry out compressing tablet stretching with tablet press machine, obtain the mobile phone screen material that diameter is 0.004 ~ 0.01mm;
S3: monolithic glass is cut into required processing dimension;
S4: the glass processing of well cutting goes out groove and edge chamfer;
S5: pure water rinse bath put into by glass, in addition vibration of ultrasonic wave clean surface;
S6: by glass heats close to softening temperature, with air or salting liquid, it is cooled rapidly;
S7: use laminating machine to pack the glass processed.
Embodiment 3:
Mobile phone screen glass machining technique, comprises the following steps:
S1: take raw material by following weight ratio:
Silicon dioxide 80,
Sodium hydrogen phosphate 6,
Sodium pyrophosphate 6,
Titanium dioxide 3,
Boron oxide 15,
Sodium oxalate 6,
Aluminium oxide 25;
S2: each component is mixed, then heats, heating-up temperature is 400 DEG C, and heating time is 1h; Carry out compressing tablet stretching with tablet press machine, obtain the mobile phone screen material that diameter is 0.004 ~ 0.01mm;
S3: monolithic glass is cut into required processing dimension;
S4: the glass processing of well cutting goes out groove and edge chamfer;
S5: pure water rinse bath put into by glass, in addition vibration of ultrasonic wave clean surface;
S6: by glass heats close to softening temperature, with air or salting liquid, it is cooled rapidly;
S7: use laminating machine to pack the glass processed.
Claims (1)
1. mobile phone screen glass machining technique, is characterized in that: comprise the following steps:
S1: take raw material by following weight ratio:
Silicon dioxide 60-80,
Sodium hydrogen phosphate 3-6,
Sodium pyrophosphate 4-6,
Titanium dioxide 0.8-3,
Boron oxide 2-15,
Sodium oxalate 4-6,
Aluminium oxide 10-25;
S2: each component is mixed, then heats, heating-up temperature is 300 ~ 400 DEG C, and heating time is 1 ~ 2h; Carry out compressing tablet stretching with tablet press machine, obtain the mobile phone screen material that diameter is 0.004 ~ 0.01mm;
S3: monolithic glass is cut into required processing dimension;
S4: the glass processing of well cutting goes out groove and edge chamfer;
S5: pure water rinse bath put into by glass, in addition vibration of ultrasonic wave clean surface;
S6: by glass heats close to softening temperature, with air or salting liquid, it is cooled rapidly;
S7: use laminating machine to pack the glass processed.