CN105272099A - Environmental protection coating and preparation method thereof - Google Patents

Abstract

The invention relates to an environmental protection coating and a preparation method thereof. The environmental protection coating comprises, by weight, 85 parts of pulverized limestone, 22 parts of heavy calcium carbonate, 20 parts of light calcium carbonate, 5.5 parts of 8DEG animal gelatin, 75 parts of water, 0.3 parts of edible salt, 0.003 parts of an essence, 0.6 parts of a color paste and 0.6 parts of phosphor. The environmental protection coating can be used in decoration of interior and exterior walls of guesthouses, hotels, beauty parlors, apartments, dwelling houses and other buildings, has the characteristics of antibiosis, deodorization, air purification, breathing humidification, no toxicity, no smell, flame retardation, waterproof property and no pollution, and also has the advantages of scrub resistance, durability, crack resistance, strong adhesion, and realization of no fading, no shedding, strong waterproof property, no peeling and ageing resistance of wall surfaces.

Description

A kind of environmental protection coating material and preparation method

Technical field

The present invention relates to paint field, be specifically related to a kind of building coating, can be used for the environmental protection coating material of the building inner, external wall decorations such as hotel, hotel, beauty salon, apartment, house, there is antibacterial, deodorizing, purify air, breathe damping, nontoxic, tasteless, fire-retardant, waterproof, the feature such as pollution-free, and there is scrubbing resistance, durability degree, cracking resistance, strong adhesion, metope does not fade, do not come off, water tolerance by force, does not roll up skin, the advantage such as anti-aging.

Background technology

Healthy functions environmental protection coating material refers to that coating is except pollution-free, has as antibacterial, deodorizing, purifies air, breathes damping etc. to environmental improvement, the coating useful to HUMAN HEALTH.Wood wax oil is a kind of novel environment friendly wood coatings, it is domestic being commonly called as of vegetables oil Wax coatings, a kind of similar paint and the natural woodwork coating being different from paint, it is completely different with that paint produced based on petrochemical industry class synthetic resins, raw material mainly with the crude vegetals such as concise oleum lini, palm wax with vegetable wax and coordinate some other natural component merge form, pigment used of mixing colours also reaches food grade.Therefore it is not containing toxic ingredients such as triphen, formaldehyde and heavy metals, does not have pungent smell, and alternative paint is used for house decoration and outdoor garden woodenware.No pollution: 1, containing Toxic, carcinogens and to HUMAN HEALTH, breed and heredity produce dysgenic material; 2, special stipulation: formaldehyde content must not more than 10mg/L; Lead, chromium, cadmium and associated materials must not be used as pigment or siccative in paint making processes; 3, the product indices of natural environmental protection coating material must meet german standard din; 4, to the environmental protection test (living body biological test) of natural diatom ooze environmental protection coating material; Energy-saving effect: for diatom ooze: 1, diatom ooze product possesses unique " molecular sieve " structure, there is extremely strong physical adsorbability and ion exchanging function, the smell effectively can removed the objectionable impurities such as free formaldehyde, benzene, ammonia in air and produce because of pet, smoking, rubbish, purifies the air of a room.2, fire protection flame retarding.Diatom ooze is made up of inorganic materials, does not therefore burn, even if presence of fire, and any harmful smog of also can not emerging.3, damping is breathed.Along with the change of Various Seasonal and sooner or later ambient air temp, diatom ooze can absorb or discharge moisture, automatically regulates indoor air humidity, makes it to reach relative equilibrium.4, absorbing sound and lowering noise.Due to the molecular porous structure of diatom ooze self, therefore there is very strong reduction noise function, effectively can absorb harmful high frequency segment, the function and attenuate low frequency is made an uproar.5, sustain its quality through age.Diatom ooze can reach more than 30 years work-ing life, sustains its quality through age.For gac walling: the objectionable impurities such as free formaldehyde, benzene, ammonia, radon TVOC that 1, environmental protection coating material energy adsorption-decomposition function distributes does not worry secondary pollution completely, peculiar smell is eliminated in sterilization simultaneously.2, environmental protection coating material is from efficiency, possesses thermal and insulating performance, has saved electric energy and heating cost greatly.Be 65% energy conservation standard provide superior condition.3, materials consumption time length, environmental protection coating material has stability.Product attribute has stronger splitting resistance and sticking power, metope does not fade, not skull patch, do not come off.Through its life-span of performance test more than 30 years, reduce consuming excessively of product.

Summary of the invention

The object of the present invention is to provide a kind of building coating, can be used for the environmental protection coating material of the building inner, external wall decorations such as hotel, hotel, beauty salon, apartment, house, there is antibacterial, deodorizing, purify air, breathe damping, nontoxic, tasteless, fire-retardant, waterproof, the feature such as pollution-free, and there is scrubbing resistance, durability degree, cracking resistance, strong adhesion, metope does not fade, do not come off, water tolerance by force, does not roll up skin, the advantage such as anti-aging.

Present invention employs such technical scheme: the material in described environmental protection coating material and weight proportion respectively: calcium lime powder 85 parts, water-ground limestone 22 parts, light calcium carbonate 20 parts, 8 degree of animal gelatins 5.5 parts, 75 parts, water, salt 0.3 part, 0.003 part, essence, mill base 0.6 part, 0.6 part, fluorescent material.

The present invention is specifically related to a kind of building coating, can be used for the environmental protection coating material of the building inner, external wall decorations such as hotel, hotel, beauty salon, apartment, house.

This product has antibacterial, deodorizing, purify air, breathe damping, nontoxic, tasteless, fire-retardant, waterproof, the feature such as pollution-free, and there is scrubbing resistance, durability degree, cracking resistance, strong adhesion, metope does not fade, do not come off, water tolerance by force, does not roll up skin, the advantage such as anti-aging.

Embodiment

Present invention employs such technical scheme: in described environmental protection coating material, material and weight proportion are respectively: calcium lime powder 85 parts, water-ground limestone 22 parts, light calcium carbonate 20 parts, 8 degree of animal gelatins 5.5 parts, 75 parts, water, salt 0.3 part, 0.003 part, essence, mill base 0.6 part, 0.6 part, fluorescent material.

Its preparation method is following steps:

Step one), in stirred vessel, add calcium lime powder, water-ground limestone, light calcium carbonate, fully mix, for subsequent use after stirring;

Step 2), add in stirred vessel 11: 1 water and animal gelatin, invade bubble dissolve after for subsequent use;

Step 3), by step 2) add the boiling water that equal quality is 1: 11 in gained material, after stirring, be incubated 35muin in the boiling water of 100 DEG C and stir in temperature, naturally cool to 40 DEG C for subsequent use;

Step 4), by step one), step 3) after gained material mixes, add salt, essence, mill base, fluorescent material in stirring, after paste mill grinding, load in container and seal 20d, finished product.

Claims (2)

1. an environmental protection coating material, it is characterized in that, material and weight proportion respectively: calcium lime powder 85 parts, water-ground limestone 22 parts, light calcium carbonate 20 parts, 8 degree of animal gelatins 5.5 parts, 75 parts, water, salt 0.3 part, 0.003 part, essence, mill base 0.6 part, 0.6 part, fluorescent material.

2. according to environmental protection coating material according to claim 1, it is characterized in that, its preparation method, preparation method is following steps: step one), in stirred vessel, add calcium lime powder, water-ground limestone, light calcium carbonate, fully mix, for subsequent use after stirring;

Step 2), add in stirred vessel 11: 1 water and animal gelatin, invade bubble dissolve after for subsequent use;

Step 3), by step 2) add the boiling water that equal quality is 1: 11 in gained material, after stirring, be incubated 35muin in the boiling water of 100 DEG C and stir in temperature, naturally cool to 40 DEG C for subsequent use;

Step 4), by step one), step 3) after gained material mixes, add salt, essence, mill base, fluorescent material in stirring, after paste mill grinding, load in container and seal 20d, finished product.