CN105272044A - Novel stamper floor material - Google Patents
Novel stamper floor material Download PDFInfo
- Publication number
- CN105272044A CN105272044A CN201510743342.7A CN201510743342A CN105272044A CN 105272044 A CN105272044 A CN 105272044A CN 201510743342 A CN201510743342 A CN 201510743342A CN 105272044 A CN105272044 A CN 105272044A
- Authority
- CN
- China
- Prior art keywords
- parts
- floor material
- terrace
- spill
- quartz sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a novel stamper floor material, which comprises the following components in parts by weight: 400 parts of portland cement (42.5), 500 parts of quartz sand (10-20 meshes), 2 parts of cellulose ether, 20 parts of redispersible adhesive powder, 35 parts of iron oxide pigment, and 150 parts of coal ash. During construction, the redispersible adhesive powder, the cellulose ether and the iron oxide pigment are poured into a stirrer and are stirred at a high speed for 10-15min so as to be fully mixed; the mixture is poured into the portland cement, the quartz sand and the coal ash so as to be mixed and stirred for 30-40min, and finally the mixture is carried to a construction site for construction. The technical scheme provided by the invention effectively solves the problems of unattractive color and short weather resistance of the stamper floor material; meanwhile, the color preservation duration is greatly enhanced; the coal ash is adopted, so that the cost is greatly reduced, and meanwhile, environment protection is realized since waste materials are utilized.
Description
Technical field
The present invention relates to terrace to make, refer in particular to a kind of novel pressing mold floor material.
Background technology
Terrace is the part that bottom room contacts with soil layer, and it bears the load in bottom room, requires to have certain strength and stiffness, and has protection against the tide, waterproof, warming, wear-resisting performance.There is close relationship in stratum and outdoor buildings place, handle terrace and platform, step and the buildings relation along place, limit well, Building And Grounds are joined clear and definite, whole harmonious.Terrace is applicable to some for the higher place of health conditions requiring such as hospital ground, food factory's mill floor, pharmaceutical factory's mill floor, laboratory building ground, machine room ground etc.; Require the anti-impact anticorrosive wear-resisting ground of pressure such as underground parking, factory's storehouse (crossing fork truck region) etc.Existing for trail, outdoor gardens, walkway, street, its weathering resistance is poor after manufacturing for the terrace of non-slip ramp etc., and easily variable color after colouring, greatly affects the result of use of terrace.
Summary of the invention
The object of the invention is to overcome the deficiencies in the prior art, a kind of good weatherability, brightly painted novel pressing mold floor material are provided.
For achieving the above object, technical scheme provided by the present invention is: a kind of novel pressing mold floor material, and the weight part of described floor material each component is:
Silicate cement (42.5) 400 ~ 450 parts
Quartz sand (10-20 order) 500 ~ 600 parts
Ether of cellulose 1 ~ 3 part
Re-dispersible glue powder 10 ~ 40 parts
Iron oxide pigment 30 ~ 50 parts
100 ~ 200 parts, flyash
The construction technology of above-mentioned materials is:
1), by re-dispersible glue powder, ether of cellulose, iron oxide pigment pour agitator high-speed stirring into 10 ~ 15 minutes, make it fully mix;
2), by compound to pour in silicate cement, quartz sand, flyash mix and blend into 30 ~ 40 minutes, be pulled to working-yard for subsequent use;
3), the complete pea gravel concreten of ground construction of working-yard, and floatingly leave standstill 2 ~ 2.5 hours afterwards, after concrete surface occurs without bleeding, the homogenize material mixed be sprinkled upon the surface of pea gravel concreten, spill material proportion by 2 ~ 2.5 kilograms every square;
4), spilt rear scraper plate smooth out surface, left standstill 0.5 ~ 1 hour, itself and concrete are stained with and are combined formation entirety;
5), more evenly spill second time material by different directions, spill material proportion by 2 ~ 2.5 kilograms every square, after having spilt, use scraper plate smooth out surface again;
6) coloured separating powder is spilt at surface uniform again after, floating;
7), with the rubber mold with marble striped covering has spilt on the terrace of separating powder, utilizes iron plate or iron hammer to beat mould a little, makes it on terrace, extrude various marble grain shape;
8), pressed after remove mould and leave standstill again 45 ~ 52 hours, the separating powder of terrace surface is cleaned up, after natural airing, then with roller brush brush one deck protective agent.
The present invention is after employing such scheme, and adopt ether of cellulose to have thermoplasticity, it can play fresh-keeping for a long time after mixing with pigment, strengthen the effect of weathering resistance simultaneously.It is not bright-coloured that this programme effectively solves die floor material color, the problem that weathering resistance is short, and greatly strengthen the fresh-keeping duration of color, by being compression molded into line, reach a surface strength firm, bright-colored have again imitative various marmorean artistic effect simultaneously; Namely employing flyash can make cost greatly reduce, waste wood utilization simultaneously, environmental protection more; This programme is especially suitable for trail, outdoor gardens, walkway, street, non-slip ramp etc.
Embodiment
The invention will be further described below, and preferred embodiment of the present invention is the novel pressing mold floor material described in the present embodiment: the weight part of described floor material each component is:
Silicate cement (42.5) 400 parts
Quartz sand (10-20 order) 500 parts
Ether of cellulose 2 parts
Re-dispersible glue powder 20 parts
Iron oxide pigment 35 parts
150 parts, flyash
By adding water reducer and retardant season during construction, add-on is 1 ~ 5 part
The construction technology of above-mentioned materials is:
1), by re-dispersible glue powder, ether of cellulose, iron oxide pigment pour agitator high-speed stirring into 10 minutes, make it fully mix, add retardant when hot weather construction, winter then adds water reducer; The rhodia of 3 ~ 10 parts can also be added, to increase bright-colored property when stirring;
2), by compound to pour in silicate cement, quartz sand, flyash mix and blend into 30 minutes, be pulled to working-yard for subsequent use;
3), the complete pea gravel concreten of ground construction of working-yard, and floatingly leave standstill 2 hours afterwards, after concrete surface occurs without bleeding, the homogenize material mixed be sprinkled upon the surface of pea gravel concreten, spill material proportion by 2 kilograms every square;
4), spill rear scraper plate smooth out surface, leave standstill 0.5 hour;
5), more evenly spill second time material by different directions, spill material proportion by 2 kilograms every square, after having spilt, use scraper plate smooth out surface again;
6) coloured separating powder is spilt at surface uniform again after, floating;
7), with the rubber mold with marble striped covering has spilt on the terrace of separating powder, utilizes iron plate or iron hammer to beat mould a little, makes it on terrace, extrude various marble grain shape;
8), pressed after remove mould and leave standstill again 48 hours, the separating powder of terrace surface is cleaned up, after natural airing, then with roller brush brush one deck protective agent.
Adopt ether of cellulose to have thermoplasticity, it can play fresh-keeping for a long time after mixing with pigment, strengthen the effect of weathering resistance simultaneously.It is not bright-coloured that this programme effectively solves die floor material color, the problem that weathering resistance is short, greatly strengthens the fresh-keeping duration of color simultaneously, and namely employing flyash can make cost greatly reduce, waste wood utilization simultaneously, environmental protection more.
Claims (1)
1. a novel pressing mold floor material: it is characterized in that, the weight part of described floor material each component is:
Silicate cement (42.5) 400 ~ 450 parts
Quartz sand (10-20 order) 500 ~ 600 parts
Ether of cellulose 1 ~ 3 part
Re-dispersible glue powder 10 ~ 40 parts
Iron oxide pigment 30 ~ 50 parts
100 ~ 200 parts, flyash
The construction technology of above-mentioned materials is:
1), by re-dispersible glue powder, ether of cellulose, iron oxide pigment pour agitator high-speed stirring into 10 ~ 15 minutes, make it fully mix;
2), by compound to pour in silicate cement, quartz sand, flyash mix and blend into 30 ~ 40 minutes, be pulled to working-yard for subsequent use;
3), the complete pea gravel concreten of ground construction of working-yard, and floatingly leave standstill 2 ~ 2.5 hours afterwards, after concrete surface occurs without bleeding, the homogenize material mixed be sprinkled upon the surface of pea gravel concreten, spill material proportion by 2 ~ 2.5 kilograms every square;
4), spill rear scraper plate smooth out surface, leave standstill 0.5 ~ 1 hour;
5), more evenly spill second time material by different directions, spill material proportion by 2 ~ 2.5 kilograms every square, after having spilt, use scraper plate smooth out surface again;
6) coloured separating powder is spilt at surface uniform again after, floating;
7), with the rubber mold with marble striped covering has spilt on the terrace of separating powder, utilizes iron plate or iron hammer to beat mould a little, makes it on terrace, extrude various marble grain shape;
8), pressed after remove mould and leave standstill again 45 ~ 52 hours, the separating powder of terrace surface is cleaned up, after natural airing, then with roller brush brush one deck protective agent.