CN105271920A - 一种墙面装饰涂料的制造工艺及其应用工艺 - Google Patents
一种墙面装饰涂料的制造工艺及其应用工艺 Download PDFInfo
- Publication number
- CN105271920A CN105271920A CN201410241582.2A CN201410241582A CN105271920A CN 105271920 A CN105271920 A CN 105271920A CN 201410241582 A CN201410241582 A CN 201410241582A CN 105271920 A CN105271920 A CN 105271920A
- Authority
- CN
- China
- Prior art keywords
- mixed
- coating
- water
- mixing
- mixed liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种墙面装饰涂料的制造工艺及其应用工艺,将水3.3kg、纤维素HPMC50g、苯丙乳液125g、增白液体10ml一起混合后制得混合液A备用;将水550g、玉米淀粉150g两者混合后制得混合液P,将水260g、火碱30g混合后制得混合液Q,将混合液P和混合液Q一起混合后制得混合液B备用;将灰钙2.3kg、重钙6kg、膨润土125g一起混合后制得混合粉末C备用;将混合液A、混合液B、混合粉末C一起混合均匀后即可获得涂料基体。本发明制造流程简便,成本稳定可靠,能够通过涂料的涂覆实现瓷砖的效果,有效降低了墙面装饰的成本,能够达到水洗上千次,按茬压光更容易更快捷,是一种理想的墙面装饰涂料。
Description
技术领域
本发明涉及墙面涂料的技术领域,尤其是一种墙面装饰涂料的制造工艺及其应用工艺。
背景技术
在公知的技术领域,墙面涂料是指用於建筑墙面起装饰和保护,使建筑墙面美观整洁,同时也能够起到保护建筑墙面,延长其使用寿命的作用。在目前现有的涂料产品中,长时间的使用后,容易发生爆皮、发花、起碱等不足的现象,所以一般人们在墙面上还会结合各类瓷砖制品进行装饰,如仿瓷玉瓷、水晶瓷等,这样就增加了装修的成本,同时施工繁复,也增加了人工成本。
发明内容
本发明要解决的技术问题是:克服上述问题,提供一种墙面装饰涂料的制造工艺,能够结合常规墙面涂料和瓷砖制品两者的优点,具备节约成本、美观大方的优点。
本发明解决其技术问题所采用的技术方案是:一种墙面装饰涂料的制造工艺,包括如下步骤:
(a)将水3.3kg、纤维素HPMC50g、苯丙乳液125g、增白液体10ml一起混合后制得混合液A备用;
(b)将水550g、玉米淀粉150g两者混合后制得混合液P,将水260g、火碱30g混合后制得混合液Q,将混合液P和混合液Q一起混合后制得混合液B备用;
(c)将灰钙2.3kg、重钙6kg、膨润土125g一起混合后制得混合粉末C备用;
(d)将混合液A、混合液B、混合粉末C一起混合均匀后即可获得涂料基体。
作为一种具体的施工方式,一种墙面装饰涂料的应用工艺,包括如下步骤:
(ⅰ)将上述步骤(d)中所获得涂料基体与水按照重量比2:1的比例配制并混合均匀,放置5~10min,再次充分搅拌均匀获得涂料体;
(ⅱ)用钢刮板或抹刀按常规进行批刮,刮涂次数不可过多,控制在三次以内,刮图平面需均匀平整,在交接处不能留痕迹,刮涂厚度为1~3mm,用量在1~3kg/㎡之间。
本发明的有益效果是:本发明制造流程简便,成本稳定可靠,能够通过涂料的涂覆实现瓷砖的效果,从而结合了两者的优点,达到一种“墙面瓷”的外观效果,具有细腻结合、覆盖力强、耐潮湿、耐擦洗、耐碱性、保色性强、施工方便、干燥快等特点,有效降低了墙面装饰的成本,能够达到水洗上千次,硬度5H~8H以上,不发花、不起碱、不脱落,手感细腻结白,施工方便流畅,按茬压光比一般涂料更容易更快捷,是一种理想的墙面装饰涂料。
具体实施方式
本发明一种墙面装饰涂料的制造工艺的优选实施例,包括如下步骤:
(a)将水3.3kg、纤维素HPMC50g、苯丙乳液125g、增白液体10ml一起混合后制得混合液A备用;
(b)将水550g、玉米淀粉150g两者混合后制得混合液P,将水260g、火碱30g混合后制得混合液Q,将混合液P和混合液Q一起混合后制得混合液B备用;
(c)将灰钙2.3kg、重钙6kg、膨润土125g一起混合后制得混合粉末C备用;
(d)将混合液A、混合液B、混合粉末C一起混合均匀后即可获得涂料基体。
在实际的施工时,上述实施例的应用工艺,包括如下步骤:
(ⅰ)将上述步骤(d)中所获得涂料基体与水按照重量比2:1的比例配制并混合均匀,放置5~10min,再次充分搅拌均匀获得涂料体;
(ⅱ)用钢刮板或抹刀按常规进行批刮,刮涂次数不可过多,控制在三次以内,刮图平面需均匀平整,在交接处不能留痕迹,刮涂厚度为1~3mm,用量在1~3kg/㎡之间。
同时在施工时,需要注意:(1)基层应坚实、干净,基层强度应大于刮墙宝强度;(2)非潮湿基层应在刮涂刮墙宝前先用清水或者稀释后的刮墙宝胶水进行封底处理;(3)吸水性较大的基层、强度较低的基层(如各种轻体隔墙板)必须用稀释后的刮墙宝胶水进行封底处理。
以上述依据本发明的理想实施例为启示,通过上述的说明内容,相关工作人员完全可以在不偏离本项发明技术思想的范围内,进行多样的变更以及修改。本项发明的技术性范围并不局限于说明书上的内容,必须要根据权利要求范围来确定其技术性范围。
Claims (2)
1.一种墙面装饰涂料的制造工艺,其特征在于:包括如下步骤:
(a)将水3.3kg、羟丙基甲基纤维素HPMC50g、苯丙乳液125g、增白液体10ml一起混合后制得混合液A备用;
(b)将水550g、玉米淀粉150g两者混合后制得混合液P,将水260g、火碱30g混合后制得混合液Q,将混合液P和混合液Q一起混合后制得混合液B备用;
(c)将灰钙2.3kg、重钙6kg、膨润土125g一起混合后制得混合粉末C备用;
(d)将混合液A、混合液B、混合粉末C一起混合均匀后即可获得涂料基体。
2.一种墙面装饰涂料的应用工艺,其特征在于:包括如下步骤:
(ⅰ)将上述步骤(d)中所获得涂料基体与水按照重量比2:1的比例配制并混合均匀,放置5~10min,再次充分搅拌均匀获得涂料体;
(ⅱ)用钢刮板或抹刀按常规进行批刮,刮涂次数不可过多,控制在三次以内,刮图平面需均匀平整,在交接处不能留痕迹,刮涂厚度为1~3mm,用量在1~3kg/㎡之间。