CN105255267A - Internal wall matt latex paint based on ASE thickening agents, and production process thereof - Google Patents
Internal wall matt latex paint based on ASE thickening agents, and production process thereof Download PDFInfo
- Publication number
- CN105255267A CN105255267A CN201410332744.3A CN201410332744A CN105255267A CN 105255267 A CN105255267 A CN 105255267A CN 201410332744 A CN201410332744 A CN 201410332744A CN 105255267 A CN105255267 A CN 105255267A
- Authority
- CN
- China
- Prior art keywords
- parts
- latex paint
- thickening material
- ase
- interior wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a formula and a production process of a middle-high-grade internal wall latex paint, wherein the components comprise, by weight, 320 parts of water, 1 parts of a TritonCo-630 wetting agent, 4 parts of a CPA dispersant, 1 part of a FG-5 defoamer, 355 parts of a white light pigment filler, 10 parts of f a Texanol film-forming auxiliary agent, 180 parts of a styrene-acrylic emulsion, 6 parts of a PH value adjusting agent, 2 parts of a defoamer, 2 parts of an acrylic acid thickening agent, and 7 parts of a association type thickening agent. According to the present invention, the ASE thickening agents such as the acrylic acid thickening agent and the association type thickening agent are used, and the CPA dispersant is used and has excellent thermal storage stability, such that the adverse phenomenon during the storage process due to the increase of the dispersant consumption can not be generated.
Description
Technical field
The present invention relates to a kind of paint, particularly a kind of medium-to-high grade interiro wall latex paint formula and production technique thereof.
Background technology
Along with the quality of life of people improves constantly, people are also more and more higher for the specification of quality of interiro wall latex paint, and existing ASE class thickening material is owing to can directly be adsorbed on without the color stuffing covered on the surface.Because this kind of thickening material and polymeric dispersant are being chemically similar, thus the contention of adsorption site can occur on color stuffing surface between both acid groups, and make coating store so unstable, storage time is short, poor quality.
Summary of the invention
For solving the problem, the object of the present invention is to provide a kind of interior wall matt latex paint based on ASE class thickening material and production technique thereof that effectively can improve ASE class thickening material emulsion paint shelf-time and quality.
The present invention solves the technical scheme that its problem adopts:
Based on an interior wall matt latex paint for ASE class thickening material, the parts by weight of each component are: 320 parts, water, TritonCo-630 wetting agent 1 part, CPA dispersion agent 4 parts, FG-5 suds suppressor 1 part, white light color stuffing 355 parts, Texanol film coalescence aid 10 parts, benzene emulsion 180 parts, PH conditioning agent 6 parts, defoamer 2 parts, acrylic thickener 2 parts, associative thickener 7 parts.
Further, described acrylic thickener is MC-201 acrylic thickener.
Further, described associative thickener is MC-35 associative thickener.
Particularly, described white light color stuffing is made up of sharp titanium white 100 parts, calcined kaolin 100 parts and water-ground limestone 255 parts.
Further, P-123 fungicidal preservative 2 parts is also comprised.
Further, described synthetic emulsion benzene emulsion adopts TL-615 benzene emulsion.
A kind of manufacture craft of the interior wall matt latex paint based on ASE class thickening material, add 180 parts, water, TritonCo-630 wetting agent 1 part, CPA dispersion agent 4 parts, FG-5 suds suppressor 1 part, sharp titanium white 100 parts, calcined kaolin 100 parts, water-ground limestone 255 parts successively, then high speed dispersion is after 20 minutes, slow down stirring velocity, add successively: 140 parts, water, TL-615 benzene emulsion 180 parts, AMP-19 defoamer 2 parts, MC-201 acrylic thickener 2 parts, MC-35 associative thickener 7 parts.
The invention has the beneficial effects as follows: a kind of interior wall matt latex paint based on ASE class thickening material that the present invention adopts and production technique thereof, in order to the stability of emulsion paint, selection and the consumption of dispersion agent have great significance.Poly-acids dispersion agent generally has better effect to stability, acid is then slightly poor in this respect with the multipolymer of hydrophobic or hydrophilic monomer. with ASE and ASE class thickening material with the use of time, dispersant dosage is slightly higher than color stuffing good distribution aequum in high speed dispersion, also higher with the consumption in the emulsion paint of conventional fibre element thickening than general.Therefore, when adopting acrylic thickener, these ASE thickening materials of associative thickener, the present invention adopts CPA dispersion agent, and the hot storage stability of CPA dispersion agent is excellent, can not occur bad phenomenon because of the increase of dispersant dosage in storage process.The emulsion paint that excellent performance, good can opening effect, package stability are fabulous can be made.
Embodiment
A kind of interior wall matt latex paint based on ASE class thickening material of the present invention, the parts by weight of each component are: 320 parts, water, TritonCo-630 wetting agent 1 part, CPA dispersion agent 4 parts, FG-5 suds suppressor 1 part, white light color stuffing 355 parts, Texanol film coalescence aid 10 parts, benzene emulsion 180 parts, PH conditioning agent 6 parts, defoamer 2 parts, acrylic thickener 2 parts, associative thickener 7 parts.
Further, described acrylic thickener is MC-201 acrylic thickener.Described associative thickener is MC-35 associative thickener.MC35 aqueous phase thickening capabilities is strong, and mobility is excellent, cuts viscosity in outstanding, is the substitute products of the best low cost of HEC class thickening material; MC201 provides shear viscosity, increases film fullness ratio, improves the anti-splashing performance of construction.
Particularly, described white light color stuffing is made up of sharp titanium white 100 parts, calcined kaolin 100 parts and water-ground limestone 255 parts.Adopt calcined kaolin to make it have good covering performance, excellent suspension and anti-moisture absorption, shock resistance, adopt water-ground limestone then because its whiteness is high, rheological is good.Having in body of light system latex paint formulation, generally do not adding filler (mainly most of filler all delustrings, but consider from cost angle, we select to add a small amount of stopping composition to reduce costs. and experiment proves, in the stopping composition of numerous cheapness, the impact of water-ground limestone on glossiness is minimum.
Further, in order to strengthen the antiseptic property of emulsion paint, also comprise P-123 fungicidal preservative 2 parts.
Further, described synthetic emulsion benzene emulsion adopts TL-615 benzene emulsion.
A kind of manufacture craft of the interior wall matt latex paint based on ASE class thickening material, add 180 parts, water, TritonCo-630 wetting agent 1 part, CPA dispersion agent 4 parts, FG-5 suds suppressor 1 part, sharp titanium white 100 parts, calcined kaolin 100 parts, water-ground limestone 255 parts successively, then high speed dispersion is after 20 minutes, slow down stirring velocity, add successively: 140 parts, water, TL-615 benzene emulsion 180 parts, AMP-19 defoamer 2 parts, MC-201 acrylic thickener 2 parts, MC-35 associative thickener 7 parts.
The present invention adopts the stability in order to emulsion paint, and selection and the consumption of dispersion agent have great significance.Poly-acids dispersion agent generally has better effect to stability, acid is then slightly poor in this respect with the multipolymer of hydrophobic or hydrophilic monomer. with ASE and ASE class thickening material with the use of time, dispersant dosage is slightly higher than color stuffing good distribution aequum in high speed dispersion, also higher with the consumption in the emulsion paint of conventional fibre element thickening than general.Therefore, when adopting acrylic thickener, these ASE thickening materials of associative thickener, the present invention adopts CPA dispersion agent, and the hot storage stability of CPA dispersion agent is excellent, can not occur bad phenomenon because of the increase of dispersant dosage in storage process.
Concrete system component of the present invention is as shown in the table:
Table 1
Formula constant of the present invention is:
Dry coating film thickness: 35uM
Coating theoretical density: 1.41KG/L;
Brushing area: 10.54M2/KG;
Quality solid content: 55.39%;
Volume solids content: 36.88%;
Resin-pigment ratio: 4.6:1;
PVC:59.53%；
PH value: 8.8;
Scrubbing resistance number of times: >5000 time;
Mobility: excellent;
Can opening effect: without layering, stirs delayed sense well.
The above, just preferred embodiment of the present invention, the present invention is not limited to above-mentioned embodiment, as long as it reaches technique effect of the present invention with identical means, all should belong to protection scope of the present invention.
Claims (7)
1. the interior wall matt latex paint based on ASE class thickening material, it is characterized in that, the parts by weight of each component are: 320 parts, water, TritonCo-630 wetting agent 1 part, CPA dispersion agent 4 parts, FG-5 suds suppressor 1 part, white light color stuffing 355 parts, Texanol film coalescence aid 10 parts, benzene emulsion 180 parts, PH conditioning agent 6 parts, defoamer 2 parts, acrylic thickener 2 parts, associative thickener 7 parts.
2. a kind of interior wall matt latex paint based on ASE class thickening material according to claim 1, is characterized in that: described acrylic thickener is MC-201 acrylic thickener.
3. a kind of interior wall matt latex paint based on ASE class thickening material according to claim 1, is characterized in that: described associative thickener is MC-35 associative thickener.
4. a kind of interior wall matt latex paint based on ASE class thickening material according to claim 1, is characterized in that: described white light color stuffing is made up of sharp titanium white 100 parts, calcined kaolin 100 parts and water-ground limestone 255 parts.
5. a kind of interior wall matt latex paint based on ASE class thickening material according to claim 1, is characterized in that: also comprise P-123 fungicidal preservative 2 parts.
6. a kind of interior wall matt latex paint based on ASE class thickening material according to claim 1, is characterized in that: described synthetic emulsion benzene emulsion adopts TL-615 benzene emulsion.
7. the manufacture craft based on the interior wall matt latex paint of ASE class thickening material, it is characterized in that: add 180 parts, water, TritonCo-630 wetting agent 1 part, CPA dispersion agent 4 parts, FG-5 suds suppressor 1 part, sharp titanium white 100 parts, calcined kaolin 100 parts, water-ground limestone 255 parts successively, then high speed dispersion is after 20 minutes, slow down stirring velocity, add successively: 140 parts, water, TL-615 benzene emulsion 180 parts, AMP-19 defoamer 2 parts, MC-201 acrylic thickener 2 parts, MC-35 associative thickener 7 parts.