CN105254987A - 吹塑聚乙烯薄膜 - Google Patents
吹塑聚乙烯薄膜 Download PDFInfo
- Publication number
- CN105254987A CN105254987A CN201510813041.7A CN201510813041A CN105254987A CN 105254987 A CN105254987 A CN 105254987A CN 201510813041 A CN201510813041 A CN 201510813041A CN 105254987 A CN105254987 A CN 105254987A
- Authority
- CN
- China
- Prior art keywords
- parts
- blow
- thin film
- methyl
- blow moulding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种吹塑聚乙烯薄膜,按重量份计由以下组分组成:1~2份十二烷基硫酸钠,25份聚乙烯微粉,3~4份石油磺酸盐,2~3份硬脂酸甘油酯,4~5份甲基三乙氧基硅烷,1~2份烷基苯磺酸酯,2~3份甲基硅油,5~6份月桂酰氨乙基硫酸钠,1~2份氧化聚乙烯蜡。本发明吹塑聚乙烯薄膜,透明度、耐热性、拉伸强度好,不易发皱。
Description
技术领域
本发明涉及吹塑聚乙烯薄膜。
背景技术
现有的吹塑聚乙烯薄膜,其透明度、耐热性、拉伸强度都有待改进,且易发皱。
发明内容
本发明的目的在于提供一种吹塑聚乙烯薄膜,其透明度、耐热性、拉伸强度好,不易发皱。
为实现上述目的,本发明的技术方案是设计一种吹塑聚乙烯薄膜,按重量份计由以下组分组成:
1~2份十二烷基硫酸钠,
25份聚乙烯微粉,
3~4份石油磺酸盐,
2~3份硬脂酸甘油酯,
4~5份甲基三乙氧基硅烷,
1~2份烷基苯磺酸酯,
2~3份甲基硅油,
5~6份月桂酰氨乙基硫酸钠,
1~2份氧化聚乙烯蜡。
优选的,吹塑聚乙烯薄膜,按重量份计由以下组分组成:
2份十二烷基硫酸钠,
25份聚乙烯微粉,
4份石油磺酸盐,
3份硬脂酸甘油酯,
5份甲基三乙氧基硅烷,
2份烷基苯磺酸酯,
3份甲基硅油,
6份月桂酰氨乙基硫酸钠,
2份氧化聚乙烯蜡。
优选的,吹塑聚乙烯薄膜,按重量份计由以下组分组成:
1份十二烷基硫酸钠,
25份聚乙烯微粉,
3份石油磺酸盐,
2份硬脂酸甘油酯,
4份甲基三乙氧基硅烷,
1份烷基苯磺酸酯,
2份甲基硅油,
5份月桂酰氨乙基硫酸钠,
1份氧化聚乙烯蜡。
优选的,吹塑聚乙烯薄膜,按重量份计由以下组分组成:
1.2份十二烷基硫酸钠,
25份聚乙烯微粉,
3.4份石油磺酸盐,
2.3份硬脂酸甘油酯,
4.5份甲基三乙氧基硅烷,
1.2份烷基苯磺酸酯,
2.3份甲基硅油,
5.6份月桂酰氨乙基硫酸钠,
1.2份氧化聚乙烯蜡。
本发明的优点和有益效果在于:提供一种吹塑聚乙烯薄膜,其透明度、耐热性、拉伸强度好,不易发皱。
具体实施方式
下面结合实施例,对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是:
实施例1
吹塑聚乙烯薄膜,按重量份计由以下组分组成:
2份十二烷基硫酸钠,
25份聚乙烯微粉,
4份石油磺酸盐,
3份硬脂酸甘油酯,
5份甲基三乙氧基硅烷,
2份烷基苯磺酸酯,
3份甲基硅油,
6份月桂酰氨乙基硫酸钠,
2份氧化聚乙烯蜡。
实施例2
吹塑聚乙烯薄膜,按重量份计由以下组分组成:
1份十二烷基硫酸钠,
25份聚乙烯微粉,
3份石油磺酸盐,
2份硬脂酸甘油酯,
4份甲基三乙氧基硅烷,
1份烷基苯磺酸酯,
2份甲基硅油,
5份月桂酰氨乙基硫酸钠,
1份氧化聚乙烯蜡。
实施例3
吹塑聚乙烯薄膜,按重量份计由以下组分组成:
1.2份十二烷基硫酸钠,
25份聚乙烯微粉,
3.4份石油磺酸盐,
2.3份硬脂酸甘油酯,
4.5份甲基三乙氧基硅烷,
1.2份烷基苯磺酸酯,
2.3份甲基硅油,
5.6份月桂酰氨乙基硫酸钠,
1.2份氧化聚乙烯蜡。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (4)
1.吹塑聚乙烯薄膜,其特征在于,按重量份计由以下组分组成:
1~2份十二烷基硫酸钠,
25份聚乙烯微粉,
3~4份石油磺酸盐,
2~3份硬脂酸甘油酯,
4~5份甲基三乙氧基硅烷,
1~2份烷基苯磺酸酯,
2~3份甲基硅油,
5~6份月桂酰氨乙基硫酸钠,
1~2份氧化聚乙烯蜡。
2.根据权利要求1所述的吹塑聚乙烯薄膜,其特征在于,按重量份计由以下组分组成:
2份十二烷基硫酸钠,
25份聚乙烯微粉,
4份石油磺酸盐,
3份硬脂酸甘油酯,
5份甲基三乙氧基硅烷,
2份烷基苯磺酸酯,
3份甲基硅油,
6份月桂酰氨乙基硫酸钠,
2份氧化聚乙烯蜡。
3.根据权利要求1所述的吹塑聚乙烯薄膜,其特征在于,按重量份计由以下组分组成:
1份十二烷基硫酸钠,
25份聚乙烯微粉,
3份石油磺酸盐,
2份硬脂酸甘油酯,
4份甲基三乙氧基硅烷,
1份烷基苯磺酸酯,
2份甲基硅油,
5份月桂酰氨乙基硫酸钠,
1份氧化聚乙烯蜡。
4.根据权利要求1所述的吹塑聚乙烯薄膜,其特征在于,按重量份计由以下组分组成:
1.2份十二烷基硫酸钠,
25份聚乙烯微粉,
3.4份石油磺酸盐,
2.3份硬脂酸甘油酯,
4.5份甲基三乙氧基硅烷,
1.2份烷基苯磺酸酯,
2.3份甲基硅油,
5.6份月桂酰氨乙基硫酸钠,
1.2份氧化聚乙烯蜡。