CN105236299A - High-strength base for hoister - Google Patents
High-strength base for hoister Download PDFInfo
- Publication number
- CN105236299A CN105236299A CN201510733871.9A CN201510733871A CN105236299A CN 105236299 A CN105236299 A CN 105236299A CN 201510733871 A CN201510733871 A CN 201510733871A CN 105236299 A CN105236299 A CN 105236299A
- Authority
- CN
- China
- Prior art keywords
- support tube
- high strength
- elevator high
- group
- strength base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-strength base for a hoister. The high-strength base comprises a cross beam and a set of supporting pipes. The supporting pipes are perpendicularly arranged on the cross beam, and a set of reinforcing beams are further arranged between the supporting pipes. The high-strength base for the hoister is simple and reasonable in structure, easy to produce, high in adaptability, high in strength and rigidity, high in weight and pressure bearing capacity and long in service life.
Description
Technical field
The invention belongs to flight-line maintenance field, particularly a kind of elevator high strength base.
Background technology
China is an automobile consumption big country, and during the nearly last ten years, the quantity of each city automobile constantly rises, along with time lapse, and the having automobile amount and also can constantly rise of later city.But the maintenance of automobile, maintenance etc. are as the past-sale service of automobile, repair plant or automobile 4s shop all essential.
Auto hoist refers to that automobile maintenance industry protects equipment for the vapour of vehicle hoisting.Lifting machine plays vital effect in vehicle maintenance and repair maintenance, no matter car load overhaul, or routine maintenance, all be unable to do without it.But due to auto hoist itself bulky, complex structure, product property, the quality of elevator also directly can affect the property safety of vehicle and the personal safety of maintainer.Lifting machine, as a kind of vehicle maintenance and repair and maintenance of equipment, must ensure its safety in use, should protect the property safety of vehicle, more will protect the personal safety of service personnel.
Summary of the invention
Goal of the invention: in order to overcome above deficiency, the object of this invention is to provide a kind of elevator high strength base, it is simple and reasonable for structure, is easy to produce, and applicability is wide, and strength and stiffness are high, and resistance to heavy bearing capacity is strong, long service life.
Technical scheme: a kind of elevator high strength base, comprises crossbeam and support tube, described crossbeam is vertically provided with one group of support tube, is also provided with one group of strength beam between described support tube, and described strength beam is X-type strength beam.A kind of elevator high strength base of the present invention, its structure is simple, reasonable in design, is easy to produce, and applicability is wide, fixed.Its center member is secured by bolts on ground, by arranging strength beam between support tube, effectively increases the resistance to heavy bearing capacity of base.The strength beam uniform force of X-type, stable, resistance to heavy bearing capacity is strong, and may be used for heavy motor vehicle, applicability is wide.
Further, above-mentioned elevator high strength base, is provided with one group of support beam in described support tube, described support beam described support tube is divided into one group of cross-sectional plane be " " square type support tubule.By arranging multiple support beam inside support tube, continuous print support beam effectively can improve the bearing capacity of base, improves device security.
Further, above-mentioned elevator high strength base, is also provided with one group and strengthens rib in described support tubule.Support in tubule and also strengthen rib, increase the resistance to heavy bearing capacity of base further.Strengthening rib coordinates support beam that vehicle steadily can be made to fix on elevator, improves the safety of whole operating process, and stable performance.
Further, above-mentioned elevator high strength base, described reinforcement rib is that wave mode strengthens rib, and distributes alternatively up and down along described support tubule.Wherein the dispersion of wave mode reinforcement rib actv. is stressed, improves the Rigidity and strength of base, effectively prevents base generation deformation or fracture.Namely, when overload makes base generation deformation or fractures, wave mode strengthens rib can serve as base connection temporarily, and the alteration of form of base is little, improves the safety of equipment.Substep makes the uniform force of base further alternatively up and down, on the basis ensureing rigidity, intensity, alleviates the weight of whole base, can save material by actv. simultaneously, reduce manufacturing cost.
As a modification of the present invention, above-mentioned elevator high strength base, described support tube surface is also provided with reinforced rib, and described reinforced rib is X-type reinforced rib.Support tube arranges reinforced rib on the surface, can ensure the stability of understructure further, improve its bearing capacity.Vehicle steadily can be made to be fixed on elevator, to improve the safety of whole operating process, and stable performance.In addition, the reinforced rib uniform force of X-type, stable, resistance to heavy bearing capacity is strong.
Further, above-mentioned elevator high strength base, is provided with boss between described crossbeam and support tube.Also be provided with fixed mount boss between crossbeam and support tube, effectively increase the rigidity that base is connected with fixed mount, make stressedly more to disperse simultaneously.Boss coordinates strength beam and reinforced rib that vehicle steadily can be made to be fixed on elevator, improves the safety of whole operating process, and stable performance.
Further, above-mentioned elevator high strength base, described crossbeam, support tube and strength beam surface are provided with anti-corrosion film.Described crossbeam, support tube and strength beam surface are provided with anti-corrosion film, effectively can improve the corrosion resistance of longeron, extend the service life of longeron.
Further, above-mentioned elevator high strength base, described anti-corrosion film comprises following components by weight percent:
Polyethylene 20-25 part
Poly-ester fibres 10-20 part
TiO
25-10 part
SiO
210-20 part
Epoxy resin 50-80 part
Kaolin 20-25 part
Polyether Modified Polysiloxanes Defoaming Agent 5-8 part.
The formula of this anti-corrosion film metal surface can be made to have anticorrosion impact resistance that antiwear and antifriction improves crossbeam, support tube and strength beam surface, improves the corrosion resistance of base further, effectively increases the service life.
Technique scheme can be found out, the present invention has following beneficial effect: elevator high strength base of the present invention, and it is simple and reasonable for structure, is easy to produce, and applicability is wide, and strength and stiffness are high, and resistance to heavy bearing capacity is strong, long service life.
Accompanying drawing explanation
Fig. 1 is the perspective view of elevator high strength base of the present invention;
Fig. 2 is the cross-sectional view of support tubule of the present invention;
Fig. 3 is the structural representation of the elevator high strength base of improvement of the present invention;
Fig. 4 is the perspective view with another kind of elevator high strength base of the present invention.
In figure: 1 crossbeam, 2 support tubes, 3 strength beams, 4 support beams, 5 support tubule, 6 and strengthen rib, 7 reinforced ribs, 8 bosses.
Detailed description of the invention
Below in conjunction with the drawings and specific embodiments, illustrate the present invention further.
Embodiment 1
Shown elevator high strength base as described in Figure 1, comprise crossbeam 1 and support tube 2, its center member 1 is secured by bolts on ground, described crossbeam 1 is vertically provided with one group of support tube 2.Boss 8 is provided with between described crossbeam 1 and support tube 2.In the present embodiment, described support tube 2 is two.Also be provided with one group of strength beam 3 between described support tube 2, described strength beam 3 is X-type strength beam 3.
As shown in Figure 2, be provided with a support beam 4 in described support tube 2, described support tube 2 is divided into two cross-sectional planes to be that the square type of " " supports tubule 5 by described support beam 4.Also be provided with one group in described support tubule 5 and strengthen rib 6.As shown in Figure 3, described reinforcement rib 6 is wave mode reinforcement rib 6, and distributes alternatively up and down along described support tubule 5.
In addition, described crossbeam 1, support tube 2 and strength beam 3 surface are provided with anti-corrosion film, effectively can improve the corrosion resistance of longeron, extend the service life of longeron.
Wherein, described anti-corrosion film comprises following components by weight percent:
Polyethylene 20 parts
Poly-ester fibres 10 parts
TiO
25 parts
SiO
210 parts
Epoxy resin 50 parts
Kaolin 20 parts
Polyether Modified Polysiloxanes Defoaming Agent 5 parts.
Embodiment 2
Shown elevator high strength base as described in Figure 3, comprise crossbeam 1 and support tube 2, its center member 1 is secured by bolts on ground, described crossbeam 1 is vertically provided with one group of support tube 2.Boss 8 is provided with between described crossbeam 1 and support tube 2.In the present embodiment, described support tube 2 is two.Also be provided with one group of strength beam 3 between described support tube 2, described strength beam 3 is X-type strength beam 3.Described support tube 2 surface is also provided with reinforced rib 7, and described reinforced rib 7 is X-type reinforced rib 7.
As shown in Figure 2, be provided with a support beam 4 in described support tube 2, described support tube 2 is divided into two cross-sectional planes to be that the square type of " " supports tubule 5 by described support beam 4.As described in be also provided with one group in support tubule 5 and strengthen rib 6.Shown in Fig. 3, described reinforcement rib 6 is wave mode reinforcement rib 6, and distributes alternatively up and down along described support tubule 5.
In addition, described crossbeam 1, support tube 2 and strength beam 3 surface are provided with anti-corrosion film, effectively can improve the corrosion resistance of longeron, extend the service life of longeron.
Wherein, described anti-corrosion film comprises following components by weight percent:
Polyethylene 25 parts
Poly-ester fibres 20 parts
TiO
210 parts
SiO
220 parts
Epoxy resin 80 parts
Kaolin 25 parts
Polyether Modified Polysiloxanes Defoaming Agent 8 parts.
Embodiment 3
Shown elevator high strength base as described in Figure 4, comprise crossbeam 1 and support tube 2, its center member 1 is secured by bolts on ground, described crossbeam 1 is vertically provided with one group of support tube 2.Boss 8 is provided with between described crossbeam 1 and support tube 2.In the present embodiment, described support tube 2 is four.Also be provided with one group of strength beam 3 between described two support tubes 2, described strength beam 3 is X-type strength beam 3.
As shown in Figure 2, be provided with a support beam 4 in described support tube 2, described support tube 2 is divided into two cross-sectional planes to be that the square type of " " supports tubule 5 by described support beam 4.As described in be also provided with one group in support tubule 5 and strengthen rib 6.Shown in Fig. 3, described reinforcement rib 6 is wave mode reinforcement rib 6, and distributes alternatively up and down along described support tubule 5.
In addition, described crossbeam 1, support tube 2 and strength beam 3 surface are provided with anti-corrosion film, effectively can improve the corrosion resistance of longeron, extend the service life of longeron.
Wherein, described anti-corrosion film comprises following components by weight percent:
Polyethylene 23 parts
Poly-ester fibres 15 parts
TiO
28 parts
SiO
215 parts
Epoxy resin 60 parts
Kaolin 23 parts
Polyether Modified Polysiloxanes Defoaming Agent 6 parts.
Embodiment 4
A kind of elevator high strength base, comprise crossbeam 1 and support tube 2, its center member 1 is secured by bolts on ground, described crossbeam 1 is vertically provided with one group of support tube 2.Boss 8 is provided with between described crossbeam 1 and support tube 2.In the present embodiment, described support tube 2 is two.Also be provided with one group of strength beam 3 between described support tube 2, described strength beam 3 is X-type strength beam 3.Described support tube 2 surface is also provided with reinforced rib 7, and described reinforced rib 7 is X-type reinforced rib 7.
As shown in Figure 2, be provided with three support beams 4 in described support tube 2, described support tube 2 is divided into four cross-sectional planes to be that the square type of " " supports tubule 5 by described support beam 4.As shown in Figure 3, be also provided with one group in described support tubule 5 and strengthen rib 6.Described reinforcement rib 6 is wave mode reinforcement rib 6, and distributes alternatively up and down along described support tubule 5.
In addition, described crossbeam 1, support tube 2 and strength beam 3 surface are provided with anti-corrosion film, effectively can improve the corrosion resistance of longeron, extend the service life of longeron.
Wherein, described anti-corrosion film comprises following components by weight percent:
Polyethylene 20 parts
Poly-ester fibres 15 parts
TiO
210 parts
SiO
210 parts
Epoxy resin 60 parts
Kaolin 20 parts
Polyether Modified Polysiloxanes Defoaming Agent 5 parts.
The above is only the preferred embodiment of the present invention, it should be pointed out that for those skilled in the art, under the premise without departing from the principles of the invention, can also make some improvement, and these improvement also should be considered as protection scope of the present invention.
Claims (8)
1. an elevator high strength base, comprise crossbeam (1) and support tube (2), described crossbeam (1) is vertically provided with one group of support tube (2), it is characterized in that: be also provided with one group of strength beam (3) between described support tube (2), described strength beam (3) is X-type strength beam (3).
2. elevator high strength base according to claim 1, it is characterized in that: in described support tube (2), be provided with one group of support beam (4), described support beam (4) described support tube (2) is divided into one group of cross-sectional plane be " " square type support tubule (5).
3. elevator high strength base according to claim 2, is characterized in that: be also provided with one group in described support tubule (5) and strengthen rib (6).
4. elevator high strength base according to claim 3, is characterized in that: described reinforcement rib (6) is wave mode reinforcement rib (6), and distributes alternatively up and down along described support tubule (5).
5. elevator high strength base according to claim 1, is characterized in that: described support tube (2) surface is also provided with reinforced rib (7), and described reinforced rib (7) is X-type reinforced rib (7).
6. elevator high strength base according to claim 1, is characterized in that: be provided with boss (8) between described crossbeam (1) and support tube (2).
7. elevator high strength base according to claim 1, is characterized in that: described crossbeam (1), support tube (2) and strength beam (3) surface are provided with anti-corrosion film.
8. elevator high strength base according to claim 7, is characterized in that: described anti-corrosion film comprises following components by weight percent:
Polyethylene 20-25 part
Poly-ester fibres 10-20 part
TiO
25-10 part
SiO
210-20 part
Epoxy resin 50-80 part
Kaolin 20-25 part
Polyether Modified Polysiloxanes Defoaming Agent 5-8 part.