CN105231523B - Efficient protecting mask taking triboelectric nano power generator as filtering layer - Google Patents
Efficient protecting mask taking triboelectric nano power generator as filtering layer Download PDFInfo
- Publication number
- CN105231523B CN105231523B CN201510643870.5A CN201510643870A CN105231523B CN 105231523 B CN105231523 B CN 105231523B CN 201510643870 A CN201510643870 A CN 201510643870A CN 105231523 B CN105231523 B CN 105231523B
- Authority
- CN
- China
- Prior art keywords
- pole plate
- woven fabrics
- friction
- friction pole
- deionized water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses an efficient protecting mask taking a triboelectric nano power generator as a filtering layer. The efficient protecting mask is formed by arranging the triboelectric nano power generator in a ventilation cover of the protecting mask, the triboelectric nano power generator is composed of an upper friction pole plate and a lower friction pole plate, the upper friction pole plate is formed by growing a ZnO nano array on one side of nonwoven cloth and serves as a friction layer obtaining electrons, nano Ag conductive ink coats the other side of the nonwoven cloth to serve as an output electrode, the lower friction pole plate is formed by magnetron sputtering of metal Al on one side of a copper net with 200 meshes and serves as a friction layer losing electrons, the other side of the copper net serves as an output electrode, and the lower friction pole plate of the triboelectric nano power generator is fixed to a bottom ventilation plate of the ventilation cover. The efficient protecting mask has the advantages that surface treatment is performed on the nonwoven cloth, so that physical adsorption efficiency of the nonwoven cloth is maintained while the electrostatic adsorption effect is improved without changing breathability; electric charge generated on the surface and high voltage between the friction pole plates have a bacterial killing and inhibiting effect, and the efficient protecting mask has a remarkable technical effect.
Description
Technical field
The invention belongs to high efficiency filter technology, it is particularly a kind of with the electric nano generator that rubs be the high efficient protected of filter layer
Mouth mask.
Background technology
The technology of preparing of friction nanometer power generator has reached its maturity, and its open-circuit voltage and short circuit current are from initial several volts
Special (V) and a few nas (nA), be developed to it is present reached open-circuit voltage V up to ten thousand, several mA of short circuit current, or even to the level of A.
Its application field, also from acoustic energy, the low-frequency vibration in initial driving portable electric appts, sensor, collection switching environment
Mechanical energy, tide energy, wind energy etc. are extended to the research of bio-compatible friction nanometer power generator and possible biomedical applications, and
Show wide application prospect.
Used as developing power, fossil energy (such as coal, oil, natural gas) efficiency of combustion is low, is always city for China
What city developed is denounced, and with the enhancing of China's national power, living standards of the people are increasingly improved, and versatility automobile has come into thousand
Ten thousand families, but influence of the thing followed haze to people's life and quality of life is increasing.From some big or middle urban environments
The time ratio that Monitoring Data can be seen that serious haze weather has reached 66.6%.Such weather seriously threatens people
It is healthy, especially in air particle diameter less than 0.3 μm of particle, once more likely penetrate blood oxygen barrier in suction lung,
Produce lesion.Equally, it is even more the puzzlement for enduring " silicosis " to the fullest extent for the workman for being worked in dust atmosphere throughout the year.Therefore, based on body
The consideration of body health, increasing people have selected and wear masks.Conventionally produced mouth mask, its dust-proof approach is relied primarily on
The mechanism such as Direct Acquisition, inertial deposition, gravity sedimentation and diffusional deposition, can the larger dust granules of filter sizes, and for
Particle diameter is in the particle of 0.3-1.0 μ m in size, and its filter efficiency is not ideal enough.So, the mankind are a kind of new in the urgent need to seeking
Strobe utility, and the excellent protective mask of strainability is prepared, meet special industrial and civilian demand.
At present, it is only confined in overcoat for the research of Electrostatic Absorption filter face mask and adds single layer of electret material,
However, decay because electret Electrostatic Absorption ability in itself can be raised with temperature, and due to the electricity distribution on electret
Limited, when the charged particle of absorption reaches certain electricity, the adsorption effect of electret is just greatly reduced, so that mouth mask is removed
Dirt effect is not ideal enough.Therefore, with reference to the development opportunity of current friction electric generator, stomodaeum cover filtering material-non-woven fabrics is entered
Row nano surface is modified, and adds the modified copper mesh of another nano aluminum as frictional layer pole plate, and design and exploitation one kind are with the electricity that rubs
Nano generator is the high efficiency dustproof filtering mouth mask of filter layer, and improves its tolerance.The mentality of designing of this gauze mask and
Preparation method has no relevant report both at home and abroad at present.
The content of the invention
The purpose of the present invention is directed to the current problem that protective mask filter efficiency is low, service life is short, there is provided it is a kind of with
The electric nano generator of friction is the high efficient protected mouth mask of filter layer, and the protective mask is not only obviously improved electro static filtering performance, and
And antibacterial for electrostatic also have remarkable result.
Technical scheme:
A kind of is the high efficient protected mouth mask of filter layer with the electric nano generator that rubs, and is set by protective mask range hood
Friction susceptance rice generating set is into the electric nano generator of friction is made up of upper friction pole plate and lower friction pole plate, upper friction
Pole plate be non-woven fabrics one side grown ZnO nano array as electronics frictional layer, non-woven fabrics another side coating receives
Used as output electrode, the internal diameter of non-woven fabrics is 2-4cm to rice Ag electrically conductive inks, external diameter is 10-14cm, and thickness is 1-4mm, and coating is received
The thickness of rice Ag electrically conductive inks is 2-6 μm;Lower friction pole plate is the face magnetron sputtering metal Al in the copper mesh of 200 mesh as mistake
The frictional layer of electronics, used as output electrode, copper mesh mesh number >=200 mesh, size is internal diameter 2-4cm, external diameter 10- to the another side of copper mesh
14cm, the thickness of magnetron sputtering metal Al layer is 40-80 μm, and the lower friction pole plate of the electric nano generator of friction is changed with protective mask
The bottom ventilation plate of gas hood is fixed.
It is a kind of it is described be the preparation method of the high efficient protected mouth mask of filter layer with the electric nano generator that rubs, step is as follows:
(1) preparation of the pole plate that rubbed on
1) commercially available thickness is cut into the toroidal of internal diameter 2-4cm, external diameter 10-14cm for the non-woven fabrics of 1-4mm, is put into
20-40min is impregnated with and be cleaned by ultrasonic in deionized water completely, deionized water will be changed before cleaning every time, by non-woven fabrics repeatedly
After cleaning 2-4 times, then with the ultrasonically treated 30-50min of alcohol of mass percent concentration >=99.75%, then in 100-120
DEG C, 2-4h is dried in the vacuum drying chamber of≤1Pa air pressure, obtain cleaned non-woven fabrics;
2) mixed solution is obtained in acetic acid zinc powder being added into absolute ethyl alcohol, is placed in 90-100 DEG C of water bath with thermostatic control and is incubated
30-60min, then to adding LiOHH in mixed solution2O, ultrasonic vibration 1-3h is completely dissolved lithium hydroxide, after suction filtration
To adding 3-5 times that the solution is diluted to absolute ethyl alcohol original mixed liquor volume in mixed solution, then agitating heating
To fluidized state and lasting 1-10min, now occur obvious dregs in solution, be cooled to after room temperature be placed in refrigerator stand >=
24h, obtains colloidal sol, the acetic acid zinc powder, absolute ethyl alcohol and LiOHH2The amount ratio of O is 3-5g:100-300mL:1-3g;
3) by step 1) cleaned non-woven fabrics lifted in above-mentioned colloidal sol, formed uniformly with nonwoven surface
Crystal seed layer, is then vacantly placed on dried process 5-10min in 60-80 DEG C of baking oven by the non-woven fabrics after lifting, repeats above-mentioned
Process three times, then dries 15-30min in an oven by non-woven fabrics, obtains being coated with the non-woven fabrics of ZnO crystal seed layers;
4) by Zn (NO3)2·6H2O and hexamethylenetetramine are dissolved in the deionized water of 100-400mL respectively, treat Zn
(NO3)2·6H2After O and hexamethylenetetramine are completely dissolved, two kinds of solution are mixed and ultrasound 10-30min obtains mixing molten
Liquid, then by through step 3) non-woven fabrics that obtains for the treatment of is dipped vertically into the open containers equipped with mixed solution, uses preservative film
Behind sealing container opening, the above-mentioned container equipped with mixed solution is placed in >=95 DEG C of water bath with thermostatic control in 3-5h, hanging on appearance
Non-woven fabrics growth ZnO in device, is rinsed 3-6 times repeatedly after the completion of growth with deionized water positive and negative, is subsequently placed in vacuum drying
12-24h is dried at 60-80 DEG C of case, obtains growing the non-woven fabrics of ZnO nano array, the Zn (NO3)2·6H2O and deionized water
Amount ratio be 1-3g:100-400mL, hexamethylenetetramine is 1-4g with the amount ratio of deionized water:100-400mL;
5) silver-colored electrically conductive ink is preheated to >=40 DEG C, the non-woven fabrics being uniformly coated to hairbrush after above-mentioned growth ZnO
Another side, each coating thickness is 1-3 μm, then vacuum drying >=12h, this coating-drying process weight at 50-80 DEG C of temperature
It is multiple 4-6 times, upper friction pole plate is obtained;
(2) preparation of the pole plate that rubbed under
1) by copper mesh be cut into it is in the same size with upper friction pole plate after, be put into ultrasonic vibration cleaning 20- in deionized water
60min, changes deionized water repeated washing 2-4 times, then with the alcohol ultrasonic vibration of mass percent concentration >=99.75%
30-60min, and dry 2-4h in the vacuum drying chamber of≤1Pa air pressure;
2) copper mesh obtained above is utilized into magnetron sputtering metal Al layer, purity >=99.99% of aluminium target, magnetic control splashes
The parameter penetrated be sputtering power 30-45w, sputtering time 30-50min, operating current 0.089-1A, operating voltage 320-400V,
Background vacuum≤4.0 × 10-4Pa, working vacuum degree≤1.7pa, argon flow amount 30-50cm3/ s, obtains splash-proofing sputtering metal Al layers
Copper mesh as lower friction pole plate, copper mesh lower floor is in close contact with sputtering target, and another surface is played a good protection;
(3) assembling of the electric nano generator of friction and implantation mouth mask
By it is upper friction pole plate ZnO nano array face with it is lower friction pole plate Al coat sides it is relative insert in range hood, work
For the copper mesh of lower friction pole plate is fixed on the bottom of range hood ventilation plate, upper friction pole plate is placed in lower friction pole plate and can be free
Motion, it is the high efficient protected mouth mask of filter layer to be obtained with the electric nano generator that rubs.
It is an advantage of the invention that:
Be surface-treated for the raw material non-woven fabrics for manufacturing common mouth mask by the present invention, is keeping its physical absorption efficiency
While, increase Electrostatic Absorption effect;Additionally, the high voltage between the electric charge of surface generation and friction pole plate also acts as bactericidal
Effect;While above-mentioned advantage is had concurrently, its gas permeability will not change mouth mask prepared by the present invention, obvious technical effects.
Brief description of the drawings
Fig. 1 are with the electric nano generator as the structural representation of the high efficient protected mouth mask of filter layer that rubs.
Fig. 2 is friction susceptance rice filter generator Rotating fields schematic diagram.
Fig. 3 is to emulate schematic diagram during filter generator layer is implanted into mouth mask.
Fig. 4 is friction susceptance rice filter generator layer schematic diagram.
Fig. 5 is that the electric nano generator of friction rubs the surface treatment effect figure of pole plate up and down, in figure:A, b are on non-woven fabrics
Growth ZnO;C, b are the magnetron sputtering Al on copper mesh.
In figure:1. range hood, 2. on rub pole plate, 3. lower friction pole plate, 4. bottom ventilation plate.
Specific embodiment
Instantiation described below is intended to understand objective purposes of the invention in detail and in order that reader has intuitively
Understand.In addition, it is to be understood that after the content for having read instruction of the present invention, those skilled in the art can make various to the present invention
Change or change, these equivalent form of values equally fall within the application appended claims limited range.
Embodiment:
It is a kind of with the electric nano generator that rubs be the high efficient protected mouth mask of filter layer, as Figure 1-3, by commercially available protection
The susceptance rice generating set that rubs is set in mouth mask range hood 1 into the electric nano generator of friction is rubbed by upper friction pole plate 2 with
Wipe pole plate 3 constitute, it is upper friction pole plate 2 be non-woven fabrics one side grown ZnO nano array as electronics frictional layer, nothing
The another side coated with nano Ag electrically conductive inks of cloth are spun as output electrode, the internal diameter of non-woven fabrics is 3cm, external diameter is 11cm, thickness
It is 2mm, the thickness of coated with nano Ag electrically conductive inks is 5 μm;Lower friction pole plate 3 is a face magnetron sputtering of the copper mesh in 200 mesh
Metal Al as betatopic frictional layer, the another side of copper mesh is 200 mesh as output electrode, copper mesh mesh number, and size is internal diameter
3cm, external diameter 11cm, the thickness of magnetron sputtering metal Al layer are 50 μm, the lower friction pole plate 3 of the electric nano generator of friction and protection
The bottom ventilation plate 4 of mouth mask range hood 1 is fixed.
Above-mentioned is the preparation method of the high efficient protected mouth mask of filter layer with the electric nano generator that rubs, and step is as follows:
(1) preparation of the pole plate that rubbed on
1) commercially available thickness is cut into the toroidal of internal diameter 3cm, external diameter 13cm for the non-woven fabrics of 3mm, deionization is put into
40min is impregnated with and be cleaned by ultrasonic in water completely, deionized water will be changed before cleaning every time, after non-woven fabrics is cleaned into 2 times repeatedly,
Again with the ultrasonically treated 40min of alcohol that mass percent concentration is 99.75%, then at 110 DEG C, the vacuum drying of 1Pa air pressure
4h is dried in case, cleaned non-woven fabrics is obtained;
2) mixed solution is obtained in 6g acetic acid zinc powder being added into 600mL absolute ethyl alcohols, is placed in 94 DEG C of waters bath with thermostatic control and is protected
Warm 60min, then to addition 3g LiOHH in mixed solution2O, ultrasonic vibration 3h is completely dissolved lithium hydroxide, after suction filtration
To adding 4 times that the solution is diluted to absolute ethyl alcohol original mixed liquor volume in mixed solution, then it is stirred and heated to
, now there are obvious dregs in fluidized state and persistently 1min in solution, be cooled to after room temperature to be placed in 45h is stood in refrigerator, obtain
To colloidal sol;
3) by step 1) cleaned non-woven fabrics lifted in above-mentioned colloidal sol, formed uniformly with nonwoven surface
Crystal seed layer, is then placed on dried process 10min in 80 DEG C of baking oven by the non-woven fabrics after lifting is hanging, repeats said process three
It is secondary, non-woven fabrics is then dried into 30min in an oven, obtain being coated with the non-woven fabrics of ZnO crystal seed layers;
4) by 3g Zn (NO3)2·6H2O and 6g hexamethylenetetramines are dissolved in the deionized water of 300mL respectively, treat Zn
(NO3)2·6H2After O and hexamethylenetetramine are completely dissolved, two kinds of solution are mixed and ultrasound 20min obtains mixed solution, so
Afterwards by step 3) non-woven fabrics of ZnO crystal seed layers that is coated with that obtains is dipped vertically into the beaker equipped with mixed solution, uses preservative film
After sealed beaker, 3h in 95 DEG C of water bath with thermostatic control is placed in, the non-woven fabrics growth ZnO in container is hung on is used after the completion of growth
Deionized water positive and negative is rinsed 4 times repeatedly, is subsequently placed at 60 DEG C of vacuum drying chamber and is dried 12h, obtains growing ZnO nano array
Non-woven fabrics;
5) silver-colored electrically conductive ink is preheated to 40 DEG C, the non-woven fabrics being uniformly coated to hairbrush after above-mentioned growth ZnO it is another
Simultaneously, each coating thickness is 2 μm, then vacuum drying >=12h at 50-80 DEG C of temperature, this coating-drying process repetition 5
It is secondary, upper friction pole plate is obtained;
(2) preparation of the pole plate that rubbed under
1) by copper mesh be cut into it is in the same size with upper friction pole plate after, be put into ultrasonic vibration cleaning 40min in deionized water,
Deionized water repeated washing is changed 4 times, then with the alcohol ultrasonic vibration 340min of mass percent concentration 99.75% ensuring
The greasy dirt and dust on removal copper mesh surface, then dry 4h in the vacuum drying chamber of 0.7Pa air pressure at 80 DEG C completely;
2) copper mesh obtained above is utilized into magnetron sputtering metal Al layer, the purity 99.99% of aluminium target, magnetron sputtering
Parameter be sputtering power 30w, sputtering time 30min, operating current 1A, operating voltage 320V, background vacuum 4.0 × 10- 4Pa, working vacuum degree 1.7pa, argon flow amount 30cm3/ s, obtains splash-proofing sputtering metal Al layers of copper mesh as lower friction pole plate, copper mesh
Lower floor is in close contact with sputtering target, and another surface is played a good protection;
(3) assembling of the electric nano generator of friction and implantation mouth mask
By it is upper friction pole plate ZnO nano array face with it is lower friction pole plate Al coat sides it is relative insert in range hood, work
For the copper mesh of lower friction pole plate is fixed on the bottom of range hood ventilation plate, upper friction pole plate is placed in lower friction pole plate and can be free
Motion, it is the high efficient protected mouth mask of filter layer to be obtained with the electric nano generator that rubs.
Working mechanism of the invention:Referring to Fig. 4, Fig. 5
The concentration of PM2.5 remains high in current surrounding environment, and mouth mask is used as work of the alleviation haze to human injury at present
Tool, its strainability is always focus of concern.But General Physics strobe utility is difficult particle diameter at 0.3 μm -1.0 μm
Little particle effectively filter out.Principle by Electrostatic Absorption of the invention, people is worn in the respiratory of mouth mask, and air-flow passes through nonwoven
Cloth film can produce certain air pressure to non-woven fabrics.On the other hand, our lower frictional layers using 200 mesh copper mesh, due to this two
Planting material has different elastic modelling quantity, will be separate in oral inhalation, air blowing process is come from, and thus can
Produce relative motion between two materials, because non-woven fabrics belongs to the electronic shell that is easy to get, and the copper mesh after sputtered aluminum have it is volatile
The characteristics of electronics, so charge adsorption will be produced in nonwoven surface due to electrostatic friction.Even neutral little particle, is entering
Enter to generator in the middle of friction pole plate when, due to the electric high-tension feature of nano generator of friction, neutral particle also can be by pole
Change, so can also be attracted to filtering layer surface.Simultaneously because non-woven fabrics silk quality fiber surface has the ZnO nano battle array for preparing
Row, are also that one kind is obviously improved for the physical filtering performance of non-woven fabrics while increase is to frictional layer area.Pass through simultaneously
Experiment finds that the non-woven fabrics that grown ZnO has good hydrophobicity, and this can further keep flexible friction nano generator again
The Electrostatic Absorption performance of filter layer.
Claims (2)
1. it is a kind of with the electric nano generator that rubs be the high efficient protected mouth mask of filter layer, it is characterised in that:Changed by protective mask
Friction susceptance rice generating set is set in gas hood into the electric nano generator of friction is by upper friction pole plate and lower friction pole plate group
Into, it is upper friction pole plate be non-woven fabrics one side grown ZnO nano array as electronics frictional layer, non-woven fabrics it is another
Used as output electrode, the internal diameter of non-woven fabrics is 2-4cm to face coated with nano Ag electrically conductive inks, external diameter is 10-14cm, and thickness is 1-
4mm, the thickness of coated with nano Ag electrically conductive inks is 2-6 μm;Lower friction pole plate is copper mesh of the mesh number more than or equal to 200 mesh, copper
One face magnetron sputtering metal Al of net as betatopic frictional layer, used as output electrode, the size of copper mesh is internal diameter to another side
The disk of 2-4cm, external diameter 10-14cm, the thickness of magnetron sputtering metal Al layer is 40-80 μm, under the electric nano generator of friction
Friction pole plate is fixed with the bottom ventilation plate of protective mask range hood.
2. a kind of is as claimed in claim 1 the preparation method of the high efficient protected mouth mask of filter layer with the electric nano generator that rubs,
It is characterized in that step is as follows:
(1) preparation of the pole plate that rubbed on
1) by commercially available thickness for the non-woven fabrics of 1-4mm is cut into the toroidal of internal diameter 2-4cm, external diameter 10-14cm, be put into from
20-40min is impregnated with and be cleaned by ultrasonic in sub- water completely, deionized water will be changed before cleaning every time, non-woven fabrics is cleaned repeatedly
After 2-4 times, then with the ultrasonically treated 30-50min of alcohol of mass percent concentration >=99.75%, then at 100-120 DEG C ,≤
2-4h is dried in the vacuum drying chamber of 1Pa air pressure, cleaned non-woven fabrics is obtained;
2) mixed solution is obtained in acetic acid zinc powder being added into absolute ethyl alcohol, is placed in 90-100 DEG C of water bath with thermostatic control and is incubated 30-
60min, then to adding LiOHH in mixed solution2O, ultrasonic vibration 1-3h is completely dissolved lithium hydroxide, and suction filtration is mixed backward
3-5 times that the solution is diluted to absolute ethyl alcohol original mixed liquor volume is added in conjunction solution, boiling is then stirred and heated to
State and persistently 1-10min are risen, now occur obvious dregs in solution, standing >=24h in refrigerator is placed in after being cooled to room temperature,
Obtain colloidal sol, the acetic acid zinc powder, absolute ethyl alcohol and LiOHH2The amount ratio of O is 3-5g:100-300mL:1-3g;
3) by step 1) cleaned non-woven fabrics lifted in above-mentioned colloidal sol, and uniform crystal seed is formed with nonwoven surface
Layer, is then vacantly placed on dried process 5-10min in 60-80 DEG C of baking oven by the non-woven fabrics after lifting, repeats said process
Three times, non-woven fabrics is then dried into 15-30min in an oven, obtain being coated with the non-woven fabrics of ZnO crystal seed layers;
4) by Zn (NO3)2·6H2O and hexamethylenetetramine are dissolved in the deionized water of 100-400mL respectively, treat Zn (NO3)
2·6H2After O and hexamethylenetetramine are completely dissolved, two kinds of solution are mixed and ultrasound 10-30min obtains mixed solution, then
By through step 3) non-woven fabrics that obtains for the treatment of is dipped vertically into the open containers equipped with mixed solution, uses preservative film sealing container
Behind opening, the above-mentioned container equipped with mixed solution is placed in >=95 DEG C of water bath with thermostatic control in 3-5h, the nothing in container is hung on
Cloth growth ZnO is spun, is rinsed 3-6 times repeatedly with deionized water positive and negative after the completion of growth, be subsequently placed in 60-80 DEG C of vacuum drying chamber
Under dry 12-24h, obtain grow ZnO nano array non-woven fabrics, the Zn (NO3)2·6H2The amount ratio of O and deionized water
It is 1-3g:100-400mL, hexamethylenetetramine is 1-4g with the amount ratio of deionized water:100-400mL;
5) silver-colored electrically conductive ink is preheated to >=40 DEG C, the non-woven fabrics being uniformly coated to hairbrush after above-mentioned growth ZnO it is another
Face, each coating thickness is 1-3 μm, then vacuum drying >=12h at 50-80 DEG C of temperature, this coating-drying process repetition 4-
6 times, upper friction pole plate is obtained;
(2) preparation of the pole plate that rubbed under
1) by copper mesh be cut into it is in the same size with upper friction pole plate after, be put into ultrasonic vibration cleaning 20-60min in deionized water,
Deionized water repeated washing is changed 2-4 times, then with the alcohol ultrasonic vibration 30- of mass percent concentration >=99.75%
60min, and dry 2-4h in the vacuum drying chamber of≤1Pa air pressure;
2) by copper mesh obtained above utilize magnetron sputtering metal Al layer, purity >=99.99% of aluminium target, magnetron sputtering
Parameter is sputtering power 30-45w, sputtering time 30-50min, operating current 0.089-1A, operating voltage 320-400V, background
Vacuum≤4.0 × 10-4Pa, working vacuum degree≤1.7pa, argon flow amount 30-50cm3/ s, obtains splash-proofing sputtering metal Al layers of copper
Net is in close contact with sputtering target, another surface is played a good protection as lower friction pole plate, copper mesh lower floor;
(3) assembling of the electric nano generator of friction and implantation mouth mask
By it is upper friction pole plate ZnO nano array face with it is lower friction pole plate Al coat sides it is relative insert in range hood, under
The copper mesh of the pole plate that rubs is fixed on the bottom of range hood ventilation plate, and upper friction pole plate is placed in lower friction pole plate and can freely transport
Dynamic, it is the high efficient protected mouth mask of filter layer to be obtained with the electric nano generator that rubs.