CN105218907A - Rubber cemented shoe - Google Patents
Rubber cemented shoe Download PDFInfo
- Publication number
- CN105218907A CN105218907A CN201510774101.9A CN201510774101A CN105218907A CN 105218907 A CN105218907 A CN 105218907A CN 201510774101 A CN201510774101 A CN 201510774101A CN 105218907 A CN105218907 A CN 105218907A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- heel
- half sole
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of rubber cemented shoe.Comprise half sole and heel, described half sole comprises following component by weight: chloroprene rubber 80 ~ 120 parts, 2 ~ 6 parts, magnesium oxide, stearic acid 0.3 ~ 0.7 part, semi-reinforcing hydrocarbon black 3 ~ 7 parts, 3 ~ 7 parts, zinc oxide, Vulcanization accelerator TMTD-II 0.15 ~ 0.55 part, antioxidant NBC 0.2 ~ 1 part; Described heel comprises following component by weight: chloroprene rubber 80 ~ 120 parts, 2 ~ 6 parts, magnesium oxide, stearic acid 0.3 ~ 0.7 part, semi-reinforcing hydrocarbon black 3 ~ 7 parts, 3 ~ 7 parts, zinc oxide, accelerator CBS 0.3 ~ 0.7 part, antioxidant NBC 0.2 ~ 1 part.The invention has the beneficial effects as follows: half sole and heel adopt the promotor of inhomogeneity, Different Weight part, reach whole footwear curing time consistent, namely the rubber of heel thicker position accelerates vulcanization rate, the rubber of half sole thinner position slows down vulcanization rate, makes the rubber at two positions by same curing time, that same temperature reaches curing time is identical.
Description
Technical field
The present invention relates to a kind of rubber cemented shoe.
Background technology
Aborning, in certain temperature, under mold pressing, elasticity is become from plasticity in order to make sizing material, and reach cross-linking density maximization, physical and mechanical properties optimizing time used is rubber item curing time, rubber vulcanization time depends primarily on temperature, but individual product due to rubber thickness uneven, cause curing time inconsistent, affect into the actual using function of footwear, for example, the thinner curing time of half sole is corresponding shorter, heel is thicker, curing time is also just corresponding longer, but as determined curing time according to thinner half sole curing time in actual production, the thicker position rubber of heel rubber then can be caused to owe sulphur, cause functional deficiency, if and the thicker heel curing time of employing determines curing time, then cause half sole position overlong time, form rubber over cure aging, also waste product can be caused to produce.
Summary of the invention
For the deficiencies in the prior art, the problem to be solved in the present invention is, provide a kind of rubber cemented shoe, half sole is consistent with heel curing time.
Technical scheme provided by the invention is, rubber cemented shoe, comprise half sole and heel, described half sole comprises following component by weight: chloroprene rubber 80 ~ 120 parts, 2 ~ 6 parts, magnesium oxide, stearic acid 0.3 ~ 0.7 part, semi-reinforcing hydrocarbon black 3 ~ 7 parts, 3 ~ 7 parts, zinc oxide, Vulcanization accelerator TMTD-II 0.15 ~ 0.55 part, antioxidant NBC 0.2 ~ 1 part;
Described heel comprises following component by weight: chloroprene rubber 80 ~ 120 parts, 2 ~ 6 parts, magnesium oxide, stearic acid 0.3 ~ 0.7 part, semi-reinforcing hydrocarbon black 3 ~ 7 parts, 3 ~ 7 parts, zinc oxide, accelerator CBS 0.3 ~ 0.7 part, antioxidant NBC 0.2 ~ 1 part.
Further, described half sole comprises following component by weight: chloroprene rubber 90 ~ 110 parts, 3 ~ 5 parts, magnesium oxide, stearic acid 0.4 ~ 0.6 part, semi-reinforcing hydrocarbon black 4 ~ 6 parts, 4 ~ 6 parts, zinc oxide, Vulcanization accelerator TMTD-II 0.25 ~ 0.45 part, antioxidant NBC 0.4 ~ 0.8 part;
Described heel comprises following component by weight: chloroprene rubber 90 ~ 110 parts, 3 ~ 5 parts, magnesium oxide, stearic acid 0.4 ~ 0.6 part, semi-reinforcing hydrocarbon black 4 ~ 6 parts, 4 ~ 6 parts, zinc oxide, accelerator CBS 0.4 ~ 0.6 part, antioxidant NBC 0.4 ~ 0.8 part.
Preferably, described half sole comprises following component by weight: chloroprene rubber 100 parts, 4 parts, magnesium oxide, stearic acid 0.5 part, semi-reinforcing hydrocarbon black 5 parts, 5 parts, zinc oxide, Vulcanization accelerator TMTD-II 0.35 part, antioxidant NBC 0.6 part;
Described heel comprises following component by weight: chloroprene rubber 100 parts, 4 parts, magnesium oxide, stearic acid 0.5 part, semi-reinforcing hydrocarbon black 5 parts, 5 parts, zinc oxide, accelerator CBS 0.5 part, antioxidant NBC 0.6 part.
The invention has the beneficial effects as follows: half sole and heel adopt the promotor of inhomogeneity, Different Weight part, reach whole footwear curing time consistent, namely the rubber of heel thicker position accelerates vulcanization rate, the rubber of half sole thinner position slows down vulcanization rate, makes the rubber at two positions by same curing time, that same temperature reaches curing time is identical.
Embodiment
Describe embodiments of the present invention in detail below with reference to specific embodiment, to the present invention, how utilisation technology means solve technical problem whereby, and the implementation procedure reaching technique effect can fully understand and implement according to this.
Embodiment 1: rubber cemented shoe, comprise half sole and heel, half sole comprises following component by weight: chloroprene rubber 80 ~ 120 parts, 2 ~ 6 parts, magnesium oxide, stearic acid 0.3 ~ 0.7 part, semi-reinforcing hydrocarbon black 3 ~ 7 parts, 3 ~ 7 parts, zinc oxide, Vulcanization accelerator TMTD-II 0.15 ~ 0.55 part, antioxidant NBC 0.2 ~ 1 part; Heel comprises following component by weight: chloroprene rubber 80 ~ 120 parts, 2 ~ 6 parts, magnesium oxide, stearic acid 0.3 ~ 0.7 part, semi-reinforcing hydrocarbon black 3 ~ 7 parts, 3 ~ 7 parts, zinc oxide, accelerator CBS 0.3 ~ 0.7 part, antioxidant NBC 0.2 ~ 1 part.
Embodiment 2: rubber cemented shoe, comprises half sole and heel, and half sole comprises following component by weight: chloroprene rubber 80 parts, magnesium oxide 2, stearic acid 0.3 part, semi-reinforcing hydrocarbon black 3 parts, 3 parts, zinc oxide, Vulcanization accelerator TMTD-II 0.15 part, antioxidant NBC 0.2 part; Heel comprises following component by weight: chloroprene rubber 80 parts, 2 parts, magnesium oxide, stearic acid 0.3 part, semi-reinforcing hydrocarbon black 3 parts, 3 parts, zinc oxide, accelerator CBS 0.3 part, antioxidant NBC 0.2 part.
Embodiment 3: rubber cemented shoe, comprises half sole and heel, and described half sole comprises following component by weight: chloroprene rubber 100 parts, 4 parts, magnesium oxide, stearic acid 0.5 part, semi-reinforcing hydrocarbon black 5 parts, 5 parts, zinc oxide, Vulcanization accelerator TMTD-II 0.35 part, antioxidant NBC 0.6 part; Described heel comprises following component by weight: chloroprene rubber 100 parts, 4 parts, magnesium oxide, stearic acid 0.5 part, semi-reinforcing hydrocarbon black 5 parts, 5 parts, zinc oxide, accelerator CBS 0.5 part, antioxidant NBC 0.6 part.
Embodiment 4: rubber cemented shoe, comprises half sole and heel, and described half sole comprises following component by weight: chloroprene rubber 90 parts, 3 parts, magnesium oxide, stearic acid 0.4 part, semi-reinforcing hydrocarbon black 4 parts, 4 parts, zinc oxide, Vulcanization accelerator TMTD-II 0.25 part, antioxidant NBC 0.4 part; Described heel comprises following component by weight: chloroprene rubber 90 parts, 3 parts, magnesium oxide, stearic acid 0.4 part, semi-reinforcing hydrocarbon black 4 parts, 4 parts, zinc oxide, accelerator CBS 0.4 part, antioxidant NBC 0.4 part.
Embodiment 5: rubber cemented shoe, comprises half sole and heel, and half sole comprises following component by weight: chloroprene rubber 110 parts, 5 parts, magnesium oxide, stearic acid 0.6 part, semi-reinforcing hydrocarbon black 6 parts, 6 parts, zinc oxide, Vulcanization accelerator TMTD-II 0.45 part, antioxidant NBC 0.8 part; Heel comprises following component by weight: chloroprene rubber 110 parts, 5 parts, magnesium oxide, stearic acid 0.6 part, semi-reinforcing hydrocarbon black 6 parts, 6 parts, zinc oxide, accelerator CBS 0.6 part, antioxidant NBC 0.8 part.
Embodiment 6: rubber cemented shoe, comprises half sole and heel, and half sole comprises following component by weight: chloroprene rubber 85 parts, 2.5 parts, magnesium oxide, stearic acid 0.35 part, semi-reinforcing hydrocarbon black 3.5 parts, 3.5 parts, zinc oxide, Vulcanization accelerator TMTD-II 0.2 part, antioxidant NBC 0.3 part; Heel comprises following component by weight: chloroprene rubber 85 parts, 2.5 parts, magnesium oxide, stearic acid 0.35 part, semi-reinforcing hydrocarbon black 3.5 parts, 3.5 parts, zinc oxide, accelerator CBS 0.35 part, antioxidant NBC 0.3 part.
Embodiment 7: rubber cemented shoe, comprises half sole and heel, and half sole comprises following component by weight: chloroprene rubber 95 parts, 3.5 parts, magnesium oxide, stearic acid 0.45 part, semi-reinforcing hydrocarbon black 4.5 parts, 4.5 parts, zinc oxide, Vulcanization accelerator TMTD-II 0.3 part, antioxidant NBC 0.5 part; Heel comprises following component by weight: chloroprene rubber 95 parts, 3.5 parts, magnesium oxide, stearic acid 0.45 part, semi-reinforcing hydrocarbon black 4.5 parts, 4.5 parts, zinc oxide, accelerator CBS 0.45 part, antioxidant NBC 0.5 part.
Embodiment 8: rubber cemented shoe, comprises half sole and heel, and half sole comprises following component by weight: chloroprene rubber 105 parts, 4.5 parts, magnesium oxide, stearic acid 0.55 part, semi-reinforcing hydrocarbon black 5.5 parts, 5.5 parts, zinc oxide, Vulcanization accelerator TMTD-II 0.4 part, antioxidant NBC 0.7 part; Heel comprises following component by weight: chloroprene rubber 105 parts, 4.5 parts, magnesium oxide, stearic acid 0.55 part, semi-reinforcing hydrocarbon black 5.5 parts, 5.5 parts, zinc oxide, accelerator CBS 0.55 part, antioxidant NBC 0.7 part.
Embodiment 9: rubber cemented shoe, comprises half sole and heel, and half sole comprises following component by weight: chloroprene rubber 115 parts, 5.5 parts, magnesium oxide, stearic acid 0.65 part, semi-reinforcing hydrocarbon black 6.5 parts, 6.5 parts, zinc oxide, Vulcanization accelerator TMTD-II 0.5 part, antioxidant NBC 0.9 part; Heel comprises following component by weight: chloroprene rubber 115 parts, 5.5 parts, magnesium oxide, stearic acid 0.65 part, semi-reinforcing hydrocarbon black 6.5 parts, 6.5 parts, zinc oxide, accelerator CBS 0.65 part, antioxidant NBC 0.9 part.
Embodiment 10: rubber cemented shoe, comprises half sole and heel, and half sole comprises following component by weight: chloroprene rubber 120 parts, 6 parts, magnesium oxide, stearic acid 0.7 part, semi-reinforcing hydrocarbon black 7 parts, 7 parts, zinc oxide, Vulcanization accelerator TMTD-II 0.55 part, antioxidant NBC 1 part; Heel comprises following component by weight: chloroprene rubber 120 parts, 6 parts, magnesium oxide, stearic acid 0.7 part, semi-reinforcing hydrocarbon black 7 parts, 7 parts, zinc oxide, accelerator CBS 0.7 part, antioxidant NBC 1 part.
Claims (3)
1. rubber cemented shoe, comprises half sole and heel, it is characterized in that:
Described half sole comprises following component by weight: chloroprene rubber 80 ~ 120 parts, 2 ~ 6 parts, magnesium oxide, stearic acid 0.3 ~ 0.7 part, semi-reinforcing hydrocarbon black 3 ~ 7 parts, 3 ~ 7 parts, zinc oxide, Vulcanization accelerator TMTD-II 0.15 ~ 0.55 part, antioxidant NBC 0.2 ~ 1 part;
Described heel comprises following component by weight: chloroprene rubber 80 ~ 120 parts, 2 ~ 6 parts, magnesium oxide, stearic acid 0.3 ~ 0.7 part, semi-reinforcing hydrocarbon black 3 ~ 7 parts, 3 ~ 7 parts, zinc oxide, accelerator CBS 0.3 ~ 0.7 part, antioxidant NBC 0.2 ~ 1 part.
2. rubber cemented shoe according to claim 1, is characterized in that:
Described half sole comprises following component by weight: chloroprene rubber 90 ~ 110 parts, 3 ~ 5 parts, magnesium oxide, stearic acid 0.4 ~ 0.6 part, semi-reinforcing hydrocarbon black 4 ~ 6 parts, 4 ~ 6 parts, zinc oxide, Vulcanization accelerator TMTD-II 0.25 ~ 0.45 part, antioxidant NBC 0.4 ~ 0.8 part;
Described heel comprises following component by weight: chloroprene rubber 90 ~ 110 parts, 3 ~ 5 parts, magnesium oxide, stearic acid 0.4 ~ 0.6 part, semi-reinforcing hydrocarbon black 4 ~ 6 parts, 4 ~ 6 parts, zinc oxide, accelerator CBS 0.4 ~ 0.6 part, antioxidant NBC 0.4 ~ 0.8 part.
3. rubber cemented shoe according to claim 2, is characterized in that:
Described half sole comprises following component by weight: chloroprene rubber 100 parts, 4 parts, magnesium oxide, stearic acid 0.5 part, semi-reinforcing hydrocarbon black 5 parts, 5 parts, zinc oxide, Vulcanization accelerator TMTD-II 0.35 part, antioxidant NBC 0.6 part;
Described heel comprises following component by weight: chloroprene rubber 100 parts, 4 parts, magnesium oxide, stearic acid 0.5 part, semi-reinforcing hydrocarbon black 5 parts, 5 parts, zinc oxide, accelerator CBS 0.5 part, antioxidant NBC 0.6 part.