CN105218408A - 一种聚氧乙烯醚磺酸盐及其合成方法 - Google Patents
一种聚氧乙烯醚磺酸盐及其合成方法 Download PDFInfo
- Publication number
- CN105218408A CN105218408A CN201410314818.0A CN201410314818A CN105218408A CN 105218408 A CN105218408 A CN 105218408A CN 201410314818 A CN201410314818 A CN 201410314818A CN 105218408 A CN105218408 A CN 105218408A
- Authority
- CN
- China
- Prior art keywords
- sulfonic acid
- acid salt
- sulphite
- add
- soxylat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明是一种聚氧乙烯磺酸盐及其合成方法,聚氧乙烯磺酸盐由烯丙基衍生物和亚硫酸盐按组分含量的重量%比1:1.1磺化反应而成,其中烯丙基衍生物由聚氧乙烯醚和氧丙烃按重量%比1:1.2与NaOH反应而成。其制备步骤是先溶解氢氧化钠,通入N2,在120℃~150℃下加入聚氧乙烯醚和氧丙烃混合搅拌1~2小时,然后加入亚硫酸盐搅拌4~6小时。本发明的产品外观为琥珀色粘稠液体,固相含量为50%,PH值适用范围广,在水相和非水相介质中均发泡性能优良。这种表活性剂耐高温,抗矿盐性也明显优于石油磺酸盐等烷基芳基磺酸盐,适用于高温稠油降粘化学辅助。
Description
技术领域
本发明涉及稠油高温开采化学辅助降粘剂中的表面活性剂技术领域,是一种聚氧乙烯磺酸盐及其合成方法。
背景技术
由于采油地层越来越深,表面活性剂的使用温度越来越高、水质矿化度也越来越高。普通的非离子表面活性剂的缺点是浊点低,不仅不能用于温度超过浊点的地层,而且浊点还随着水中含盐量的增加而降低。为克服上述非离子表面活性剂的弱点。将两种不同性质的亲水基团(非离子基团和阴离子基团)设计在同一个表面活性剂分子中,能兼具阴离子型和非离子型表面活性剂的优点。聚氧乙烯醚磺酸盐是一种抗矿盐的表面活性剂,兼具阴离子和非离子的结构特点,因此选择此种表面活性剂作为降粘剂的主要配方,除此之外,降粘剂中还需要加入少量的其它表面活性剂和助剂,以保证乳化降粘效果。
发明内容
本发明的目的在于提供一种适用SAGD开采稠油油藏化学辅助增效的化学增效剂重要组成表面活性剂之一的一种聚氧乙烯磺酸盐及其合成方法,提高稠油高温开采过程中的降粘效果。
本发明采用如下技术方案:一种聚氧乙烯磺酸盐,由烯丙基衍生物和亚硫酸盐按组分含量的重量%比1:1.1磺化反应而成。都是在通入N2下反应的,温度120℃-150℃。亚硫酸盐是亚硫酸钠、亚硫酸钾、亚硫酸铵等中的一种或一种以上。
本发明提供一种聚氧乙烯磺酸盐的制备方法,主要分为二步:
首先将聚氧乙烯醚和氧丙烃与NaOH反应转变为烯丙基衍生物I:第二步,产物I和亚硫酸氢钠进行磺化反应。反应过程如下:
R—O—(CH2CH2O)n—H+ClCH2CH=CH2+NaOH→
R—O—(CH2CH2O)n—CH2CH=CH2+NaCl+H2O(1)
R—O—(CH2CH2O)n—CH2CH=CH2+NaHOS3→
R—O—(CH2CH2O)n—CH2CH2CH2OS3(2)
反应过程中温度控制在120-150℃,其中(1)中投料比1:1.2,(2)中投料比1:1.1。具体步骤是:是先溶解氢氧化钠,通入N2,在120℃~150℃下加入聚氧乙烯醚和氧丙烃混合搅拌1~2小时,然后加入亚硫酸盐搅拌4~6小时。
本发明产品外观为琥珀色粘稠液体,固相含量为50%,PH值适用范围广,在水相和非水相介质中均发泡性能优良。这种表活性剂耐高温,抗矿盐性也明显优于石油磺酸盐等烷基芳基磺酸盐。
实施案例
本发明不受下述实施例的限制,可根据上述本发明的技术方案和实际情况来确定具体的实施方式。下面结合具体实施例对本发明做进一步描述。
实施例1:先取5g氢氧化钠溶解于100ml蒸馏水中,通入N2,在150℃下加入10g聚氧乙烯醚和12g氧丙烃混合搅拌1~2小时,然后加入23.2亚硫酸钠搅拌4~6小时,得产物1。
实施例2:先取5g氢氧化钠溶解于100ml蒸馏水中,通入N2,在150℃下加入10g聚氧乙烯醚和12g氧丙烃混合搅拌1~2小时,然后加入23.2亚硫酸钾搅拌4~6小时,得产物2。
实施例3:先取10g氢氧化钠溶解于100ml蒸馏水中,通入N2,在150℃下加入10g聚氧乙烯醚和12g氧丙烃混合搅拌1~2小时,然后加入23.2亚硫酸钠搅拌4~6小时,得产物3。
实施例4:先取10g氢氧化钠溶解于100ml蒸馏水中,通入N2,在150℃下加入10g聚氧乙烯醚和12g氧丙烃混合搅拌1~2小时,然后加入23.2亚硫酸钾搅拌4~6小时,得产物4。
取产物1进行性能测试,如下:
1、合成表面活性剂的特征
用液膜压片方法制作红外分析样本,在红外光谱仪上,摄取红外光谱图对所制备的表面活性剂进行结构分析。
从所合成表面活性剂的红外光谱图可以看出,3338cm-1处的吸收峰为酚轻基的伸缩振动吸收峰,1612cm-1和1513cm-1,处的吸收峰为C=C伸缩振动吸收峰,829cm-1处的吸收峰为C-H弯曲振动吸收峰,1738.95cm-1处吸收峰为c=o伸缩振动吸收峰,1543cm-1,和1398cm-1处出现了翅酸盐的反对称伸缩振动吸收峰,1184cm-1,和1143cm-1处出现了磺酸盐的特征吸收峰。
2、降粘效果评价
取某油田稠油测试结果表明,本发明产物1浓度0.5-1%时,形成的水外相乳状液粘度较原油粘度降低了95%以上。
Claims (5)
1.一种聚氧乙烯磺酸盐,由烯丙基衍生物和亚硫酸盐按组分含量的重量%比1:1.1磺化反应而成。
2.根据权利要求1所述的一种聚氧乙烯磺酸盐,其特征在于烯丙基衍生物由聚氧乙烯醚和氧丙烃按重量%比1:1.2与NaOH反应而成。
3.根据权利要求1或2所述的一种聚氧乙烯磺酸盐,其特征在于亚硫酸盐是亚硫酸钠、亚硫酸钾、亚硫酸铵等中的一种或一种以上。
4.根据权利要求1或2所述的一种聚氧乙烯磺酸盐,其特征在于都是在通入N2下反应的,温度120℃-150℃。
5.一种聚氧乙烯磺酸盐的制备方法,其制备步骤是:是先溶解氢氧化钠,通入N2,在120℃~150℃下加入聚氧乙烯醚和氧丙烃混合搅拌1~2小时,然后加入亚硫酸盐搅拌4~6小时。