CN105218071A - A kind of New-type bamboo charcoal pottery water purification inner bag and preparation method thereof - Google Patents
A kind of New-type bamboo charcoal pottery water purification inner bag and preparation method thereof Download PDFInfo
- Publication number
- CN105218071A CN105218071A CN201510595369.6A CN201510595369A CN105218071A CN 105218071 A CN105218071 A CN 105218071A CN 201510595369 A CN201510595369 A CN 201510595369A CN 105218071 A CN105218071 A CN 105218071A
- Authority
- CN
- China
- Prior art keywords
- inner bag
- bamboo charcoal
- water
- new
- water purification
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of New-type bamboo charcoal pottery water purification inner bag, it comprises following component, bamboo charcoal particle 45-55 part, raw ore purple clay 25-30 part, bamboo charcoal powder 5-15 part, medical stone 5-15 part, silica powder 3-5 part, Zijin soil 2-5 part, potter's clay 2-5 part and carbon fiber 1-3 part, its preparation method comprises and said components is added water is blended into slurry, described slurry is made inner bag blank in a mold, inner bag blank is put into totally-enclosed electric furnace sinter molding.The present invention can purify domestic running water, increases water quality.
Description
Technical field
The invention belongs to family and quote tap water purifying field, be specifically related to a kind of bamboo charcoal ceramic water purification inner bag and preparation method thereof.
Background technology
The main Drinking water of China is tap water, and National urban about 100,000,000 population tap water does not meet drinking water standard according to investigations, and rural area about has harmful substance contents in 1.9 hundred million population tap water to exceed standard, and very easily cause the popular of disease, drinking water safety causes anxiety.According to statistics, the subject matter that current Drinking Water in China exists has: 1. the pollution of microorganism and heavy metal 2. cholorination bring new pollution 3. tap water pipe network pollution 4. Highrise buildings secondary pollution in water supply 5. artificially there is water hygiene event.
Boccaro is a kind of silicate minerals, and boccaro type is opaque mud salt, and be silty sand argillaceous texture, iron content is more.Rock mainly contains quartzy flour sand and glues together its clay mineral composition, and quartz grains distributes in the structure isolatedly, becomes base type cementing.Can observe between boccaro granule by microscope, the linear porosity between single mineral and granule such as quartz, clay, and the fine pores of granule inside, boccaro is different from common potter's clay, and common potter's clay is single crystal structure, and boccaro is dual air hole structure.Dual air hole structure makes product have high stomatal frequency and certain void content.Compared with other fictile, purple-clay product has quality exquisiteness, water-intake rate is little, and void content is high, is mainly used in tea set or can container in daily life, in addition boccaro make haydite or ceramic honey comb shape pottery with may be used for filtering water, but mainly play filter suspended substance, colloid substances; Obvious filteration is not had to the heavy metal in water, and poor to the filter effect of bacterium in water.
Bamboo charcoal is with 3 years above high mountain mao bamboons of life for raw material, through a kind of charcoal of nearly thousand degree of high-temperature firings.Bamboo charcoal has vesicular structure, and the fine and closely woven porous of its molecule, quality is hard.Have very strong adsorptive power, can purify air, eliminate peculiar smell, bamboo charcoal has superpower adsorptive power and bacteriostatic action, discharges the negative ion useful to human body.The adsorption surface area of bamboo charcoal is very large, and every gram reaches standard basketball court size.Chlorine residue in water, heavy metal ion all can by its strong adsorptions; It is obvious that next improves water quality, through the water taste and sweet mouthfeel, soft of bamboo charcoal purification.But bamboo charcoal water-purifying material such as bamboo-carbon fibre or bamboo charcoal cellular material are easy consumption material, need regularly to carry out professional cleaning and replacing.
Summary of the invention
Goal of the invention: object of the present invention, mainly for the deficiencies in the prior art, provides one to purify domestic running water, the New-type bamboo charcoal of increasing water quality pottery water purification inner bag and preparation method thereof.
Technical scheme: in order to solve the problems of the technologies described above, a kind of New-type bamboo charcoal pottery water purification inner bag of the present invention, calculate by weight, it comprises following component,
The particle diameter of described bamboo charcoal particle is 0.5-2.5mm.
The particle diameter of described bamboo charcoal powder is 20-120 μm, and specific surface area is 250-400m
2/ g.
A kind of New-type bamboo charcoal pottery water purification inner bag preparation method, it comprises the following steps,
(1) said components is added water and be blended into slurry;
(2) described slurry is made inner bag blank in a mold, dry 12-36 hour at lower than the temperature of 100 DEG C;
(3) inner bag blank is put into totally-enclosed electric furnace sinter molding, in 30-60 minute, be heated to 80 DEG C, insulation 1-2 hour; With the heat-up rate of 15 DEG C/min, be heated to 500 DEG C, insulation 1-2 hour; With the heat-up rate of 25 DEG C/min, be heated to 1000 DEG C, be incubated 3 hours, furnace cooling.
Beneficial effect: the present invention compared with prior art, its remarkable advantage is: the present invention is by each component high-temperature firing, shaping inner bag intensity is high, can heavy metal in active adsorption tap water, the objectionable impurities such as chlorine residue and bacterium, only need tap water or bottled water be added in inner bag, water slowly oozes out from wall of inner container, infiltrate in boccaro cylinder body, water is in process of osmosis, chlorine residue wherein, heavy metal ion and organism and bacterium etc. are adsorbed, and to the suppressed growth of microorganism in water, water correction clearly, filtered water security, health, healthy, can directly quote, the present invention adopts natural material to make, and the not electricity consumption when purifying waste water, do not pressurize, do not consume the energy, do not need to change annex, single purchase, long term benefit, and it is simple to operate, only need to add water in inner bag, as long as inner bag is proposed to soak and to clean from cylinder during cleaning, without dismounting, install, that cleans is loaded down with trivial details.
Embodiment
The invention will be further elaborated by the following examples.
Embodiment 1:
A kind of New-type bamboo charcoal pottery water purification inner bag of the present invention, calculate by weight, it comprises following component,
The particle diameter of described bamboo charcoal particle is 1mm.
The particle diameter of described bamboo charcoal powder is 60 μm, and specific surface area is 300m
2/ g.
A kind of New-type bamboo charcoal pottery water purification inner bag preparation method, it comprises the following steps,
(1) said components is added water and be blended into slurry;
(2) described slurry is made inner bag blank in a mold, drying 18 hours at the temperature of 50 DEG C;
(3) inner bag blank is put into totally-enclosed electric furnace sinter molding, in 35 minutes, be heated to 80 DEG C, be incubated 1 hour; With the heat-up rate of 15 DEG C/min, be heated to 500 DEG C, be incubated 1 hour; With the heat-up rate of 25 DEG C/min, be heated to 1000 DEG C, be incubated 3 hours, furnace cooling.
Embodiment 2:
A kind of New-type bamboo charcoal pottery water purification inner bag of the present invention, calculate by weight, it comprises following component,
The particle diameter of described bamboo charcoal particle is 1.5mm.
The particle diameter of described bamboo charcoal powder is 80 μm, and specific surface area is 350m
2/ g.
A kind of New-type bamboo charcoal pottery water purification inner bag preparation method, it comprises the following steps,
(1) said components is added water and be blended into slurry;
(2) described slurry is made inner bag blank in a mold, drying 24 hours at the temperature of 70 DEG C;
(3) inner bag blank is put into totally-enclosed electric furnace sinter molding, in 45 minutes, be heated to 80 DEG C, be incubated 1 hour; With the heat-up rate of 15 DEG C/min, be heated to 500 DEG C, be incubated 1 hour; With the heat-up rate of 25 DEG C/min, be heated to 1000 DEG C, be incubated 3 hours, furnace cooling.
Embodiment 3:
A kind of New-type bamboo charcoal pottery water purification inner bag of the present invention, calculate by weight, it comprises following component,
The particle diameter of described bamboo charcoal particle is 2mm.
The particle diameter of described bamboo charcoal powder is 100 μm, and specific surface area is 380m
2/ g.
A kind of New-type bamboo charcoal pottery water purification inner bag preparation method, it comprises the following steps,
(1) said components is added water and be blended into slurry;
(2) described slurry is made inner bag blank in a mold, drying 32 hours at the temperature of 90 DEG C;
(3) inner bag blank is put into totally-enclosed electric furnace sinter molding, in 55 minutes, be heated to 80 DEG C, be incubated 2 hours; With the heat-up rate of 15 DEG C/min, be heated to 500 DEG C, be incubated 2 hours; With the heat-up rate of 25 DEG C/min, be heated to 1000 DEG C, be incubated 3 hours, furnace cooling.
The present invention is by each component high-temperature firing, shaping inner bag intensity is high, can heavy metal in active adsorption tap water, the objectionable impurities such as chlorine residue and bacterium, only need tap water or bottled water be added in inner bag, water slowly oozes out from wall of inner container, infiltrate in boccaro cylinder body, water is in process of osmosis, chlorine residue wherein, heavy metal ion and organism and bacterium etc. are adsorbed, and to the suppressed growth of microorganism in water, water correction clearly, filtered water security, health, healthy, can directly quote, the present invention adopts natural material to make, and the not electricity consumption when purifying waste water, do not pressurize, do not consume the energy, do not need to change annex, single purchase, long term benefit, and it is simple to operate, only need to add water in inner bag, as long as inner bag is proposed to soak and to clean from cylinder during cleaning, without dismounting, install, that cleans is loaded down with trivial details.
The invention provides a kind of thinking and method; the method and access of this technical scheme of specific implementation is a lot; the above is only the preferred embodiment of the present invention; should be understood that; for those skilled in the art, under the premise without departing from the principles of the invention, some improvements and modifications can also be made; these improvements and modifications also should be considered as protection scope of the present invention, and all available prior art of each integral part not clear and definite in the present embodiment is realized.
Claims (4)
1. a New-type bamboo charcoal pottery water purification inner bag, it is characterized in that: calculate by weight, it comprises following component,
2. New-type bamboo charcoal pottery water purification inner bag according to claim 1, is characterized in that: the particle diameter of described bamboo charcoal particle is 0.5-2.5mm.
3. New-type bamboo charcoal pottery water purification inner bag according to claim 1, is characterized in that: the particle diameter of described bamboo charcoal powder is 20-120 μm, and specific surface area is 250-400m
2/ g.
4. a New-type bamboo charcoal pottery water purification inner bag preparation method according to claim 1 and 2, is characterized in that: it comprises the following steps,
(1) said components is added water and be blended into slurry;
(2) described slurry is made inner bag blank in a mold, dry 12-36 hour at lower than the temperature of 100 DEG C;
(3) inner bag blank is put into totally-enclosed electric furnace sinter molding, in 30-60 minute, be heated to 80 DEG C, insulation 1-2 hour; With the heat-up rate of 15 DEG C/min, be heated to 500 DEG C, insulation 1-2 hour; With the heat-up rate of 25 DEG C/min, be heated to 1000 DEG C, be incubated 3 hours, furnace cooling.