CN105200886A - Self-luminous colorful pavement and construction method - Google Patents
Self-luminous colorful pavement and construction method Download PDFInfo
- Publication number
- CN105200886A CN105200886A CN201510615415.4A CN201510615415A CN105200886A CN 105200886 A CN105200886 A CN 105200886A CN 201510615415 A CN201510615415 A CN 201510615415A CN 105200886 A CN105200886 A CN 105200886A
- Authority
- CN
- China
- Prior art keywords
- layer
- self
- luminous
- basal plane
- pavement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a self-luminous colorful pavement and a construction method thereof. The self-luminous colorful pavement sequentially comprises a base face, a base coating, an elastic pavement layer and a finishing coat layer from bottom to top; the base face is coated with the base coating, the elastic pavement layer is divided into multiple layers and paved on the surface of the base coating, and the surface of the elastic pavement layer is coated with the finishing coat layer. The construction method comprises the steps that floating dust on the base face is cleaned away, the bottom coating is coated, the elastic pavement layer is divided into the multiple layers and sequentially paved on the base coating according to the thickness requirement, and finishing coat layer colloid is sprayed on the surface of the elastic pavement layer after the elastic pavement layer is solidified. According to the self-luminous colorful pavement, energy-storage luminous particle materials and high-molecular polymer latex are adopted to be combined to form the finishing coat layer, so that the pavement absorbs the energy in the day and shines at night, and the energy can be effectively saved. The construction efficiency is high, the pavement is formed well and is not prone to cracking, breakage, seepage and aging, the anti-skid effect is achieved, and the driving safety is facilitated. The self-luminous colorful pavement can be widely applied to pavements such as city sidewalks, residential area roads, fitness sites and ball courts, and the effects of beautifying, guiding, safety warning and the like are achieved.
Description
Technical field
The present invention relates to road traffic technical field, particularly a kind of self-luminous road surface and construction method thereof.
Background technology
On urban road, some location does not have street lamp or illuminance level deficiency, and road surface is unclear, makes troubles, there is potential safety hazard yet to vehicle traveling and pedestrian's walking.
Recently have current research both domestic and external, propose the technical scheme of self illuminous sign board, this scheme is only only to provide sign board or tag line.Publication number is that the Chinese patent of CN201116356 discloses a kind of self-luminescence road surface brick, its technical scheme " comprises brick body and the lenticular deck being located at brick body upper surface, described lenticular deck comprise several can self luminous striped, projection or both combinations, the linear arranged distribution of described striped, each striped traverses the upper surface of brick body parallel to each other, striped cross section is protruding arc, between adjacent stripes, there is arc groove, the side of described projection is smooth ramp or arcuation inclined-plane, each projection parallelly traverses the arranged in a straight line of brick body upper surface along several respectively ", " described luminescent layer is the planar lamina primarily of wear-resisting cement and self-luminescent material mixing composition." obviously, this structure can only be arranged on both sides of the road, compared with the self-luminous road surface designed by the present invention, obviously limited in the scope of application, safety etc.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of self-luminous colored road surface and construction method, overcomes existing road surface and indicates safely not enough defect.
For solving the problems of the technologies described above, the present invention first proposed a kind of self-luminous colored road surface, and order comprises basal plane, scratch coat, elasticity pave-load layer, top coat layer from the bottom up; Described basal plane has been the plane of base support, is positioned at most bottom surface; Described scratch coat, is coated on described basal plane upper strata; Described elasticity pave-load layer, point two-layer coating is in described scratch coat upper strata, and thickness is 3 ~ 6mm; Described top coat layer, for being coated in described elasticity pave-load layer surface, solidifying the coating of rear formation.
With the addition of light-accumulated luminous granular material in described top coat layer colloid, there is the characteristic on " daytime energy-absorbing, illuminating at night ".
The present invention proposes a kind of construction method of described self-luminous colored road surface simultaneously, comprises the following steps:
Described basal plane applies subbing, is oxidized for preventing described basic unit and fixes remaining dust granule in basic unit; Treat that described subbing solidifies formation scratch coat;
Put the first floor epoxide-resin glue body elasticity pave-load layer of flow-like at described scratch coat upslide, wait for that it solidifies, thickness is 1-2mm;
According to design thickness requirement, point multilayer pouring high molecular polymer colloid elasticity pave-load layer, until meet design thickness, solidifies rear formation elasticity pave-load layer;
Energy-accumulating luminous granular material colloid mixture is mixed with to described elasticity pave-load layer surface spraying.
Before described basal plane applies subbing, tackle described basal plane and carry out coarsen treatment, cleaning basal plane dust.
Self-luminous road surface provided by the present invention have employed the top coat layer being mixed with energy-accumulating luminous granular material, make road surface accumulate solar energy by day, in dark surrounds, continue self-luminous, and lighting source need not be set on road, can effective energy conservation, and meet the requirement of environmental protection.Above-mentioned self-luminescent material adopts special light-accumulated luminous granular material, and this road surface, can at continuous illumination more than eight hours at night by day through solar radiation after ten five to two ten minutes.
Meanwhile, the construction method on self-luminous colored road surface that the present invention proposes, adopt successively integral construction engineering method, efficiency of construction is high, and pavement forming is good, and road surface is not easy to crack, damaged, seep water and aging, and anti-skidding, is conducive to traffic safety.
Accompanying drawing explanation
Below in conjunction with the drawings and specific embodiments, technical scheme of the present invention is further described in detail.
Fig. 1 is road surface of the present invention sectional drawing.
Wherein: 1-top coat layer; 2-second layer elasticity pave-load layer; 3-first floor elasticity pave-load layer; 4-scratch coat; 5-foundation base.
Detailed description of the invention
As shown in Figure 1, self-luminous colored road surface from the bottom up order comprises basal plane 5, scratch coat 4, comprises the multilayer elastic pave-load layer of first floor elasticity pave-load layer 3, second layer elasticity pave-load layer 2, top coat layer 1.Basal plane 5 has been the plane of base support, and be positioned at most bottom surface, scratch coat 4 is coated on basal plane 5 upper strata, and for preventing basic unit be oxidized and fix remaining dust granule in basic unit, first, second elasticity pave-load layer 3,2 paves successively on scratch coat 4, gross thickness 3 ~ 6mm.Adopt the construction technology of two-layer elasticity pave-load layer, can difficulty of construction be simplified, improve the compression elasticity of pave-load layer simultaneously.Top coat layer 1 is for being mixed with the colloid mixture of light-accumulated luminous granular material, and top coat layer 1 thickness is 0.5-1.5mm.
Above-mentioned self-luminous colored road surface have employed and is mixed with light-accumulated luminous granular material colloid mixture top coat layer, makes road surface continue self-luminous in dark surrounds, and need not arrange lighting source on road, can effective energy conservation, and meets the requirement of environmental protection.
The construction method on above-mentioned self-luminous road surface, comprises the following steps:
Coarsen treatment is carried out to basal plane, cleaning basal plane dust;
Basal plane applies subbing, prevents basic unit be oxidized and fix remaining dust granule in basic unit; Treat that subbing solidifies formation scratch coat;
Put the first floor epoxide-resin glue body elasticity pave-load layer of flow-like at scratch coat upslide, wait for that it solidifies, it is 1-2mm that first floor epoxy resin colloid solidifies rear thickness;
According to the thickness requirement of design gross thickness 3 ~ 6mm, divide the high molecular polymer elasticity pave-load layer that paves at many levels, until meet thickness requirement;
Be mixed with light-accumulated luminous granular material colloid mixture to elasticity pave-load layer surface spraying, solidify rear forming surface enamelled coating.
The all technical of the self-luminous colored ground surface material under present embodiment is shown in as following table 1.
The self-luminous colored pavement technique index of table 1
Test item | Technical standard |
Gel time | ≥30min |
Adhesive tensile resistance intensity | ≥1.2MPa |
Pressure-proof elasticity modulus | ≤500MPa |
Planeness | Be not less than original road surface |
Thickness | Design load ± 1mm |
The construction method on above-mentioned self-luminous road surface, adopt successively integral construction engineering method, efficiency of construction is high, and pavement forming is good, and road surface is not easy to crack, damaged, infiltration and aging, and anti-skidding, is conducive to traffic safety.
It should be noted last that, above detailed description of the invention is only in order to illustrate technical scheme of the present invention and unrestricted, although with reference to preferred embodiment to invention has been detailed description, those of ordinary skill in the art is to be understood that, can modify to technical scheme of the present invention or equivalent replacement, and not departing from the spirit and scope of technical solution of the present invention, it all should be encompassed in the middle of right of the present invention.
Claims (5)
1. a self-luminous colored road surface, is characterized in that, order comprises basal plane, scratch coat, elasticity pave-load layer, top coat layer from the bottom up;
Described basal plane has been the plane of base support, is positioned at the bottom;
Described scratch coat, is coated on described basal plane upper strata;
Described elasticity pave-load layer divides multilayer pouring, and first floor paves in base coating surface, and the second layer paves in first floor surface, needs to select suitable thickness according to difference, can multilayer pouring, gross thickness 3 ~ 6mm;
Described top coat layer, for being coated in described elasticity pave-load layer surface, solidifying the coating of rear formation.
2. self-luminous colored road surface according to claim 1, is characterized in that, described elasticity material of paving course is high molecular polymer colloid.
3. self-luminous colored road surface according to claim 1, is characterized in that, with the addition of energy-accumulating luminous granular material in described top coat layer, has the characteristic on " daytime energy-absorbing, illuminating at night "; In finish paint, binder has light transmission and certain adhesion strength.
4. the construction method on self-luminous colored road surface according to claim 1, comprises the following steps:
Described basal plane applies subbing, remaining particle on consolidation basal plane, and elastic layer and basal plane are bonded together;
Put the first floor high molecular polymer colloid of flow-like at described scratch coat upslide, the second layer of can constructing after it solidifies, described first floor high molecular polymer colloid thickness is 1-2mm;
According to design thickness requirement, point multilayer paves high molecular polymer colloid successively, until meet design thickness, jointly forms elasticity pave-load layer;
Be mixed with energy-accumulating luminous granular material colloid mixture to described elasticity pave-load layer surface spraying, wait for that it solidifies rear forming surface enamelled coating.
5. the construction method on self-luminous colored road surface according to claim 4, is characterized in that, before described basal plane applies subbing, carries out coarsen treatment to described basal plane, cleaning basal plane dust.