CN105200858A - Cigarette packaging paper capable of reducing tar - Google Patents
Cigarette packaging paper capable of reducing tar Download PDFInfo
- Publication number
- CN105200858A CN105200858A CN201510494544.2A CN201510494544A CN105200858A CN 105200858 A CN105200858 A CN 105200858A CN 201510494544 A CN201510494544 A CN 201510494544A CN 105200858 A CN105200858 A CN 105200858A
- Authority
- CN
- China
- Prior art keywords
- slurry
- tar
- cigarette
- packaging paper
- hydrogen peroxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses cigarette packaging paper capable of reducing tar. The preparing process includes the steps of pulp preparing, pulp mixing and packaging paper coating at a filter tip. The processing process is natural, safe and nontoxic. Bamboo fibers have natural antibacterial performance and natural air permeability; when a cigarette is lighted, the amount of oxygen can be increased, and generated carbon monoxide can be reduced. As wood is replaced by bamboos, fell trees are reduced, the environment is protected, and ecological balance is maintained; due to use of waste wood, waste can be turned into wealth, and cost can be saved; as the raw materials are pretreated through white rot fungi, time for removing lignin with hydrogen-peroxide is shortened, the amount of hydrogen peroxide for removing lignin is decreased, the packaging paper can be further sterilized and bleached by the hydrogen peroxide, and multiple purposes are achieved; as the lignin is removed through the white rot fungi and the hydrogen peroxide, the safe effect and the nontoxic effect are achieved, and the environment is protected; as tar catalysts are contained in the packaging paper, splitting decomposition of the tar can be catalyzed; as a silica gel powder coating layer is additionally arranged inside the portion, at the filter tip, of the packaging paper, harmful substances such as the tar in the cigarette can be adsorbed, and harm to a smoker is greatly reduced.
Description
Technical field
The present invention relates generally to a kind of wrapping paper, particularly relates to a kind of cigarette wrapper reducing tar.
Background technology
Packaging has two large functions: one is that protection commodity do not damage, never degenerate in manufacture, transport, storage, sales process; Two is play decoration to commodity, beautify, publicize and value-added effect, has also beautified the life of people, has met the material and cultural needs that consumers in general are growing, promoted and pulled consumption.Wrapping paper, as a kind of important packaging material, has been widely used in the packing of product of every profession and trade, and it contains boxboard and fluting medium, white board and art post paperboard, soft package of beverage paper, special packing paper etc.
Tobacco product, such as cigarette or cigar, in combustion, harmful substance in multiple 5068 can be produced, wherein 96 kinds is carcinogenic and short cancer material, has that to report into material the most harmful in cigarette be not nicotine, but tar, tar be in cigarette organic substance under anoxic conditions imperfect combustion produce, tar is the complex mixture of the oxide of multiple hydro carbons and hydrocarbon, sulfide and nitride.In tarry matters in smoke, the material of 99.4% is harmful, and 0.2% is carcinogenic initator, and 0.4% is the synergist of cancer.In tar, the content of polycyclic aromatic hydrocarbon is maximum, and all there is strong carcinogenesis, as BaP, hexichol pyrrole, dibenzanthracene, after these materials enter human body, can induce the aryl hydrocarbon hydroxylase in tissue, can polycyclic aromatic hydrocarbon metabolism for can there is covalently bound carcinogenic substance with DNA molecular in this enzyme.
In the wrapping paper of cigarette, add tar catalyst and adsorbent, effectively can reduce the tar content in cigarette, reduce cigarette to the body harm of smoker.
Summary of the invention
In order to make up the defect of prior art, the object of this invention is to provide a kind of cigarette wrapper reducing tar.
Reduce a cigarette wrapper for tar, comprise following raw material: bamboo 80% ~ 85%, scoot 15% ~ 20%.
Reduce a preparation method for the cigarette wrapper of tar, comprise the following steps:
(1) bamboo and scoot are pulverized, add water, make particle and moisture content be 1:3 ~ 3.5, temperature is 28 ~ 30 DEG C, obtains slurry;
(2) in plant slurry, access whiterot fungi, concentration is 5% ~ 8% of slurry weight, carries out bioanalysis delignification 15 ~ 20 days;
(3) by 2) slurry adopt interval displacement cooking after, adjustment slurry solid-to-liquid ratio be 1:5 ~ 8, the addition of hydrogen peroxide is 1% ~ 2% of slurry weight, utilizes hydrogen peroxide delignification 10 ~ 12 hours;
(4) by 3) slurry and catalyst mix, the addition of catalyst is 3% ~ 5% of slurry weight;
(5) utilize 4) slurry carry out copy paper, paper is shaping;
(6) 200 order C type silica whites are mixed with the aqueous solution that solid content is 2% ~ 4%, are coated on 5) the filter tip place of wrapping paper inside, coating weight is 23 ~ 25g/m
2.
Each weight ratio of constituents of the catalyst of described step 4) is nickel-base catalyst 30% ~ 35%, dolomite 15% ~ 20%, aluminium oxide 10% ~ 15%, zeolite 10% ~ 15%, olivine 10% ~ 15%, swelling 10% ~ 15%, sepiolite 5% ~ 10%, light burnt powder 5% ~ 10%, and granularity is 0.1 ~ 0.3 micron.
Advantage of the present invention is: a kind of cigarette wrapper reducing tar provided by the invention, and whole process is natural, safe, nontoxic; It processes raw material as bamboo and scoot, and bamboo fibre has natural antibiotic property and gas permeability, can increase the amount of oxygen during igniting cigarette, reduces the generation of carbon monoxide; Replace timber with bamboo, avoid the felling to trees, protection of the environment, maintain the ecological balance, the use of scoot can be turned waste into wealth, cost-saving; The collocation of bamboo fibre and xylon uses, and significantly improves intensity and the pliability of paper; Delignification's process first uses whiterot fungi to carry out preliminary treatment to raw material, decreases hydrogen peroxide delignified time and consumption, and hydrogen peroxide can also carry out disinfection to wrapping paper and bleach, and achieves many things at one stroke, cost-saving; Use whiterot fungi and hydrogen peroxide delignification safety non-toxic, can not to environment; Containing tar catalyst in wrapping paper, can the cracking of catalytic tar, uncracked tar can be adsorbed simultaneously, silica white coating layer is turn increased in the wrapping paper inside at filter tip place, again can adsorb the harmful substances such as the tar in cigarette, greatly reduce the harm to smoker, silica white can regenerate, and recycles.
Detailed description of the invention
With specific embodiment, the present invention is described below.
Embodiment 1
Reduce a cigarette wrapper for tar, comprise following raw material: bamboo 80%, scoot 20%.
Reduce a preparation method for the cigarette wrapper of tar, comprise the following steps:
(1) bamboo and scoot are pulverized, add water, make particle and moisture content be 1:3, temperature is 28 DEG C, obtains slurry;
(2) in plant slurry, access whiterot fungi, concentration is 5% of slurry weight, carries out bioanalysis delignification 15 days;
(3) by 2) slurry adopt interval displacement cooking after, adjustment slurry solid-to-liquid ratio be 1:5, the addition of hydrogen peroxide is 1% of slurry weight, utilizes hydrogen peroxide delignification 10 hours;
(4) by 3) slurry and catalyst mix, the addition of catalyst is 3% of slurry weight, each weight ratio of constituents of catalyst is nickel-base catalyst 32%, dolomite 16%, aluminium oxide 11%, zeolite 11%, olivine 10%, swelling 10%, sepiolite 5%, light burnt powder 5%, and granularity is 0.1 micron;
(5) utilize 4) slurry carry out copy paper, paper is shaping;
(6) 200 order C type silica whites are mixed with the aqueous solution that solid content is 2%, are coated on 5) the filter tip place of wrapping paper inside, coating weight is 23g/m
2.
Embodiment 2
Reduce a cigarette wrapper for tar, comprise following raw material: bamboo 83%, scoot 17%.
Reduce a preparation method for the cigarette wrapper of tar, comprise the following steps:
(1) bamboo and scoot are pulverized, add water, make particle and moisture content be 1:3.3, temperature is 29 DEG C, obtains slurry;
(2) in plant slurry, access whiterot fungi, concentration is 7% of slurry weight, carries out bioanalysis delignification 18 days;
(3) by 2) slurry adopt interval displacement cooking after, adjustment slurry solid-to-liquid ratio be 1:7, the addition of hydrogen peroxide is 1.5% of slurry weight, utilizes hydrogen peroxide delignification 11 hours;
(4) by 3) slurry and catalyst mix, the addition of catalyst is 4% of slurry weight, each weight ratio of constituents of catalyst is nickel-base catalyst 30%, dolomite 16%, aluminium oxide 11%, zeolite 11%, olivine 11%, swelling 11%, sepiolite 5%, light burnt powder 5%, and granularity is 0.2 micron;
(5) utilize 4) slurry carry out copy paper, paper is shaping;
(6) 200 order C type silica whites are mixed with the aqueous solution that solid content is 3%, are coated on 5) the filter tip place of wrapping paper inside, coating weight is 24g/m
2.
Embodiment 3
Reduce a cigarette wrapper for tar, comprise following raw material: bamboo 85%, scoot 15%.
Reduce a preparation method for the cigarette wrapper of tar, comprise the following steps:
(1) bamboo and scoot are pulverized, add water, make particle and moisture content be 1:3.5, temperature is 30 DEG C, obtains slurry;
(2) in plant slurry, access whiterot fungi, concentration is 8% of slurry weight, carries out bioanalysis delignification 20 days;
(3) by 2) slurry adopt interval displacement cooking after, adjustment slurry solid-to-liquid ratio be 1:8, the addition of hydrogen peroxide is 2% of slurry weight, utilizes hydrogen peroxide delignification 12 hours;
(4) by 3) slurry and catalyst mix, the addition of catalyst is 5% of slurry weight, each weight ratio of constituents of catalyst is nickel-base catalyst 31%, dolomite 15%, aluminium oxide 11%, zeolite 11%, olivine 10%, swelling 10%, sepiolite 6%, light burnt powder 6%, and granularity is 0.1 ~ 0.3 micron;
(5) utilize 4) slurry carry out copy paper, paper is shaping;
(6) 200 order C type silica whites are mixed with the aqueous solution that solid content is 4%, are coated on 5) the filter tip place of wrapping paper inside, coating weight is 25g/m
2.
The cigarette wrapper of minimizing tar of the present invention and other cigarette wrapper the key technical indexes are contrasted, the results are shown in Table 1.
Table 1: cigarette wrapper and other cigarette wrapper the key technical indexes of minimizing tar of the present invention contrast
| Project | Cigarette wrapper of the present invention | Usual cigarette wrapper |
| Tar/mg/ props up | 4.6 | 16.7 |
| BaP/ng/ props up | 19.3 | 25.1 |
| CO/mg/ props up | 13.1 | 16.4 |
| Nicotine/mg/ props up | 0.8 | 1.2 |
Show from the result of table 1, the cigarette wrapper of minimizing tar provided by the invention, good to the lytic effect of tar, while removal tar, the content of the BaP in cigarette smoke, CO and nicotine also has certain decline, shows that the cigarette wrapper of minimizing tar of the present invention can reduce the harmful substance in cigarette.
Claims (3)
1. reduce a cigarette wrapper for tar, it is characterized in that, comprise following raw material: bamboo 80% ~ 85%, scoot 15% ~ 20%.
2. a kind of preparation method reducing the cigarette wrapper of tar as claimed in claim 1, is characterized in that, comprise the following steps:
(1) bamboo and scoot are pulverized, add water, make particle and moisture content be 1:3 ~ 3.5, temperature is 28 ~ 30 DEG C, obtains slurry;
(2) in plant slurry, access whiterot fungi, concentration is 5% ~ 8% of slurry weight, carries out bioanalysis delignification 15 ~ 20 days;
(3) by 2) slurry adopt interval displacement cooking after, adjustment slurry solid-to-liquid ratio be 1:5 ~ 8, the addition of hydrogen peroxide is 1% ~ 2% of slurry weight, utilizes hydrogen peroxide delignification 10 ~ 12 hours;
(4) by 3) slurry and catalyst mix, the addition of catalyst is 3% ~ 5% of slurry weight;
(5) utilize 4) slurry carry out copy paper, paper is shaping;
(6) 200 order C type silica whites are mixed with the aqueous solution that solid content is 2% ~ 4%, are coated on 5) the filter tip place of wrapping paper inside, coating weight is 23 ~ 25g/m
2.
3. a kind of preparation method reducing the cigarette wrapper of tar as claimed in claim 2, it is characterized in that, each weight ratio of constituents of the catalyst of described step 4) is nickel-base catalyst 30% ~ 35%, dolomite 15% ~ 20%, aluminium oxide 10% ~ 15%, zeolite 10% ~ 15%, olivine 10% ~ 15%, swelling 10% ~ 15%, sepiolite 5% ~ 10%, light burnt powder 5% ~ 10%, and granularity is 0.1 ~ 0.3 micron.