CN105200767A - Durability anti-crease finishing agent - Google Patents
Durability anti-crease finishing agent Download PDFInfo
- Publication number
- CN105200767A CN105200767A CN201510696667.4A CN201510696667A CN105200767A CN 105200767 A CN105200767 A CN 105200767A CN 201510696667 A CN201510696667 A CN 201510696667A CN 105200767 A CN105200767 A CN 105200767A
- Authority
- CN
- China
- Prior art keywords
- crease
- finishing agent
- finishing
- agent
- durability
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a durability anti-crease finishing agent, which comprises the following main components in parts by weight: dimethylol urea resin, bis (hydroxymethyl) triazone, methylol melamine, butyl acrylate, ammonium citrate, maleic acid-acrylic acid copolymer, poly-carboxylate, fatty alcohol-polyoxyethylene ether, nanometer titania, a dispersing agent and a penetrating agent. The anti-crease finishing liquid is nanometer resin finishing liquid, the dimethylol urea resin, the excess bis (hydroxymethyl) triazone and the methylol melamine are compounded to serve as a finishing agent, and meanwhile, nanometer oxide with a catalytic effect or a synergistic effect is added to prepare the durability anti-crease finishing agent; when the durability anti-crease finishing agent is used for anti-crease finishing of cotton fabrics, while the anti-crease effect is ensured, the problem that anti-crease finishing strength loss and abrasive resistance loss are great in the past is improved; meanwhile, the fabrics have no yellowing phenomenon.
Description
Technical field
The present invention relates to textile dyeing and finishing process technology, be specially a kind of durability crease-shedding finishing agent.
Background technology
Along with human society progress, science and technology development and growth in the living standard, people wear consumption idea and the market demand there occurs marked change.From the status both at home and abroad of market fabric development and research, its emphasis mainly concentrates on comfortableness, health, the aspect such as safety and the feature of environmental protection of product.
Natural fabric comes from nature, meets the demand of people to comfortableness and environment protection health, deeply by consumers.Wherein, cotton fiber is a kind of with a long history, widely used natural fabric, is known as " green fiber " by people.Pure cotton fabric as natural fabric product, because it has soft feel, good moisture permeability, excellent wearing comfortable, and quality plentiful abundant, there is the characteristics such as better whiteness, natural environmental protection, receive the welcome of people.But COTTON FABRIC and other cellulose base fiber fabrics in use also exist poor flexibility, yielding, crease easily, wash after need the defects such as flatiron, cause cotton and other cellulose base fiber fabrics after washing and take in process and can not keep smooth outward appearance.Therefore, in order to improve cotton and the outward appearance of other cellulose base fiber fabrics in wearing process, keeping the stability of its form, improving its wearability, need to carry out anti-crease finishing in the dyeing and finishing process of textile and other cellulose fibre garment materials.
At present, crease-shedding finishing agent (or anti-crease finishing liquid) conventional in described anti-crease finishing, still based on urea aldehyde derivatives resinoid finishing agent, namely contains N-hydroxymethyl derivative structure in structure, e.g., and 2D or modification 2D resinoid etc.Fabric after this kind of resin finishing agent arranges more or less all also exists release formaldehyde problem.People usually according to crease-shedding finishing agent release formaldehyde number this resinoid is divided into low formaldehyde resin and Superlow Formaldehyde Resin.But along with the enhancing of people's environmental consciousness, awareness of safety, need safer crease-shedding finishing agent, occur formaldehyde-free anti-crease finish thus.Wherein, study more formaldehyde-free anti-crease finish and mainly contain tetrabasic carboxylic acid butane (BTCA), citric acid (CA) and tricarballylic acid (PTCA), maleic acid (MA) etc.But the N-methylol amide class finishing agent of formaldehydeless finishing agent all with traditional in reactivity, price and raw material sources etc. is mutually far short of what is expected, is therefore also difficult to replace this resinoid (as 2D or modification 2D resinoid etc.) in combination property.
Experiment shows, after modification 2D resinoid dressing liquid anti-crease finishing, strength loss that is cotton and other cellulose base fiber fabrics is very large, has had a strong impact on its wearability.Research finds, causing the powerful reason declined to mainly contain two: reason is that this kind of finishing agent defines in cotton and other cellulose fibre inside in molecule with intermolecular crosslinked, limit the mobility of cellulose macromolecule segment in cotton and other cellulose fibres, cause stress to concentrate; Another reason is that the catalyst used in conventional finish method is mostly acid or latent acidic catalyst, and acidic catalyst can cause the degraded of cellulose macromolecule chain, causes the Acid damages of cotton and other cellulose fibres.In order to improve the elastic performance of cotton and other cellulose base fiber fabrics, anti-crease finishing causes the former of powerful decrease reason inevitable; For this reason, using composite as finishing agent to dihydroxymethyl carbamide resin, excessive dihydroxymethyl triazinone and melamine methylol, add the nano-oxide with catalytic effect or cooperative effect simultaneously and make, anti-crease finishing for COTTON FABRIC is processed, while guarantee anti-wrinkle effect, improve the problem that anti-crease finishing is powerful and ABRASION RESISTANCE loss is larger in the past, fabric is without yellowing phenomenon simultaneously, has no patent or bibliographical information up to now.
Summary of the invention
For the deficiencies in the prior art, the technical problem that quasi-solution of the present invention is determined is to provide a kind of durability crease-shedding finishing agent.This anti-crease finishing liquid is a kind of nano-resin dressing liquid, using composite as finishing agent to dihydroxymethyl carbamide resin, excessive dihydroxymethyl triazinone and melamine methylol, add the nano-oxide with catalytic effect or cooperative effect simultaneously and make, anti-crease finishing for COTTON FABRIC is processed, while guarantee anti-wrinkle effect, improve the problem that anti-crease finishing is powerful and ABRASION RESISTANCE loss is larger in the past, fabric is without yellowing phenomenon simultaneously.
To achieve these goals, the present invention adopts following technical scheme: a kind of durability crease-shedding finishing agent, comprises following key component: with parts by weight,
Dihydroxymethyl carbamide resin 15-20
Dihydroxymethyl triazinone 18-30
Melamine methylol 12-15
Butyl acrylate 2-5
Ammonium citrate 7-10
Maleic acid-acrylic acid copolymer 3-6
Polycarboxylate 1-1.5
Fatty alcohol-polyoxyethylene ether 2-5
Nano titanium oxide 0.5-3
Dispersant 1-2
Bleeding agent 3-6;
The preparation process of described dihydroxymethyl carbamide resin is as follows: in ceramic reactor, add the formalin that mass percent is 37-40%, regulate the pH value of formalin to be 7.5-9.0 by the NaOH solution of mass percent 10%, stir 30-40min and pH value is tended towards stability; Under agitation evenly and lentamente adding with formaldehyde mole ratio is afterwards the urea of 1:1.6-1.8, starts to be heated to connect backflow when temperature is 50-60 DEG C, and control temperature is 80-100 DEG C, insulation, and the reaction time is 30-60min; After condensation reaction completes, add frozen water keeps temperature of charge below 4 DEG C, is stirred to resin initial reduced body and is fully dissolved in the water, then leave standstill a few hours, take out supernatant liquor.
Preferably, described a kind of durability crease-shedding finishing agent, comprises following key component: with parts by weight,
Dihydroxymethyl carbamide resin 18
Dihydroxymethyl triazinone 24
Melamine methylol 13
Butyl acrylate 4
Ammonium citrate 9
Maleic acid-acrylic acid copolymer 5
Polycarboxylate 1.2
Fatty alcohol-polyoxyethylene ether 3
Nano titanium oxide 2
Dispersant 1.5
Bleeding agent 5.
The present invention also provides a kind of anti-crease finishing method of cellulose base fiber fabric, and this anti-crease finishing method uses the durability crease-shedding finishing agent described in claim 1, adopts two leachings two to roll finishing technique and carries out anti-crease finishing to cellulose base fiber fabric; The parameter that finishing technique is rolled in described two leachings two is: pick-up rate is 75-80%; Preliminary drying 1-3min at 80-90 DEG C; 2-5min is baked at 120-180 DEG C.
Beneficial effect
The present invention is using composite as finishing agent to dihydroxymethyl carbamide resin, excessive dihydroxymethyl triazinone and melamine methylol, add the nano-oxide with catalytic effect or cooperative effect simultaneously and make, anti-crease finishing for COTTON FABRIC is processed, while guarantee anti-wrinkle effect, improve the problem that anti-crease finishing is powerful and ABRASION RESISTANCE loss is larger in the past, fabric is without yellowing phenomenon simultaneously.
Meanwhile, in composite RESIN FINISH liquid, add the nano-oxide with catalytic effect or cooperative effect and make, there is the cross-linking efficiency promoted between compound resin and cellulose, reducing reaction condition, reducing the feature of fibre damage.The purposes of this dressing liquid uses this dressing liquid to the anti-crease finishing method of cellulose base fiber fabric, this method for sorting is on the basis not changing traditional anti-crease finishing technique, namely can improve wrinkle resistance and the brute force of cotton and other cellulose base fiber fabrics, effectively improve the wearability of cellulose base fiber fabric after anti-crease finishing.
Detailed description of the invention
Below by embodiment, technical scheme of the present invention is described in further detail.
Embodiment one:
A kind of durability crease-shedding finishing agent, comprises following key component: with parts by weight,
Dihydroxymethyl carbamide resin 18
Dihydroxymethyl triazinone 24
Melamine methylol 13
Butyl acrylate 4
Ammonium citrate 9
Maleic acid-acrylic acid copolymer 5
Polycarboxylate 1.2
Fatty alcohol-polyoxyethylene ether 3
Nano titanium oxide 2
Dispersant 1.5
Bleeding agent 5;
The preparation process of described dihydroxymethyl carbamide resin is as follows: in ceramic reactor, add the formalin that mass percent is 37-40%, regulate the pH value of formalin to be 7.5 by the NaOH solution of mass percent 10%, stir 30-40min and pH value is tended towards stability; Under agitation evenly and lentamente adding with formaldehyde mole ratio is afterwards the urea of 1:1.6, starts to be heated to connect backflow when temperature is 50-60 DEG C, and control temperature is 80-100 DEG C, insulation, and the reaction time is 45min; After condensation reaction completes, add frozen water keeps temperature of charge below 4 DEG C, is stirred to resin initial reduced body and is fully dissolved in the water, then leave standstill a few hours, take out supernatant liquor.
Embodiment two:
A kind of durability crease-shedding finishing agent, comprises following key component: with parts by weight,
Dihydroxymethyl carbamide resin 15
Dihydroxymethyl triazinone 18
Melamine methylol 12
Butyl acrylate 2
Ammonium citrate 7
Maleic acid-acrylic acid copolymer 3
Polycarboxylate 1
Fatty alcohol-polyoxyethylene ether 2
Nano titanium oxide 0.5
Dispersant 1
Bleeding agent 3;
The preparation process of described dihydroxymethyl carbamide resin is as follows: in ceramic reactor, add the formalin that mass percent is 37-40%, regulate the pH value of formalin to be 9.0 by the NaOH solution of mass percent 10%, stir 30-40min and pH value is tended towards stability; Under agitation evenly and lentamente adding with formaldehyde mole ratio is afterwards the urea of 1:1.8, starts to be heated to connect backflow when temperature is 50-60 DEG C, and control temperature is 80-100 DEG C, insulation, and the reaction time is 60min; After condensation reaction completes, add frozen water keeps temperature of charge below 4 DEG C, is stirred to resin initial reduced body and is fully dissolved in the water, then leave standstill a few hours, take out supernatant liquor.
Anti-wrinkle effect is tested:
With reference to crease recovery of fabrics: reply horn cupping (AATCC66-1998) testing standard and method, after testing, fabric elasticity creasy recovery angle improves more than 30 °, and ultimate strength and the equal not damaged of tearing brute force, whiteness does not reduce.
The above; be only the specific embodiment of the present invention; but protection scope of the present invention is not limited thereto; any those of ordinary skill in the art are in the technical scope disclosed by the present invention; the change can expected without creative work or replacement, all should be encompassed within protection scope of the present invention.Therefore, the protection domain that protection scope of the present invention should limit with claims is as the criterion.
Claims (2)
1. a durability crease-shedding finishing agent, is characterized in that: comprise following key component: with parts by weight,
Dihydroxymethyl carbamide resin 15-20
Dihydroxymethyl triazinone 18-30
Melamine methylol 12-15
Butyl acrylate 2-5
Ammonium citrate 7-10
Maleic acid-acrylic acid copolymer 3-6
Polycarboxylate 1-1.5
Fatty alcohol-polyoxyethylene ether 2-5
Nano titanium oxide 0.5-3
Dispersant 1-2
Bleeding agent 3-6;
The preparation process of described dihydroxymethyl carbamide resin is as follows: in ceramic reactor, add the formalin that mass percent is 37-40%, regulate the pH value of formalin to be 7.5-9.0 by the NaOH solution of mass percent 10%, stir 30-40min and pH value is tended towards stability; Under agitation evenly and lentamente adding with formaldehyde mole ratio is afterwards the urea of 1:1.6-1.8, starts to be heated to connect backflow when temperature is about 50-60 DEG C, and control temperature is 80-100 DEG C, insulation, and the reaction time is about 30-60min; After condensation reaction completes, add frozen water keeps temperature of charge below 4 DEG C, is stirred to resin initial reduced body and is fully dissolved in the water, then leave standstill a few hours, take out supernatant liquor.
2. a kind of durability crease-shedding finishing agent according to claim 1, is characterized in that: comprise following key component: with parts by weight,
Dihydroxymethyl carbamide resin 18
Dihydroxymethyl triazinone 24
Melamine methylol 13
Butyl acrylate 4
Ammonium citrate 9
Maleic acid-acrylic acid copolymer 5
Polycarboxylate 1.2
Fatty alcohol-polyoxyethylene ether 3
Nano titanium oxide 2
Dispersant 1.5
Bleeding agent 5.