CN105200419A - Phosphorization treatment method for surface of entertainment equipment - Google Patents
Phosphorization treatment method for surface of entertainment equipment Download PDFInfo
- Publication number
- CN105200419A CN105200419A CN201510700657.3A CN201510700657A CN105200419A CN 105200419 A CN105200419 A CN 105200419A CN 201510700657 A CN201510700657 A CN 201510700657A CN 105200419 A CN105200419 A CN 105200419A
- Authority
- CN
- China
- Prior art keywords
- workpiece
- recreation facility
- parts
- entertainment equipment
- phosphating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a phosphorization treatment method for a surface of entertainment equipment. The method comprises the following steps: (1) immersing the entertainment equipment to be installed in a NaOH solution, and carrying out the surface degreasing; (2) washing a workpiece after the surface degreasing, and polishing and grinding to remove rust; (3) ultrasonically washing the workpiece treated in the step (2) for 20 to 30 minutes; (4) immersing the workpiece after being ultrasonically treated in a phosphorization solution for 5 to 10 minutes to form a phosphorization film of 4 to 6 micrometers on the surface of the workpiece; (5) taking out the workpiece, and drying the workpiece in a drying machine. The phosphorization film of 4 to 6 micrometers is formed on the surface of the entertainment equipment, so that the environment resistance of the entertainment equipment is greatly improved, the entertainment equipment is unlikely to corrode and rust, and the high structural strength of the entertainment equipment still can be guaranteed after the entertainment equipment is exposed in an outdoor environment for a long time.
Description
Technical field
The invention belongs to recreation facility and manufacture field, specifically a kind of recreation facility surface phosphating method.
Background technology
Parkerizing method makes metal and phosphoric acid or phosphoric acid salt produce chemical reaction, thus form the treatment process that one deck stablizes phosphatize phosphate coat in metallic surface.
Phosphatize phosphate coat is for recreation facility, and especially outdoor recreation facility has the effect of very weight, not only can improve the erosion resistance of Whole Equipment, can also improve the tack of equipment list paint.
But manufacture field at recreation facility, the phosphatize phosphate coat that current method for bonderizing is formed is after equipment cold extrusion, and phosphatize phosphate coat easily produces strip and comes off, and resistance to feeding habits are poor, and equipment surface gets rusty easily.
Summary of the invention
Goal of the invention: the object of the invention is for the deficiencies in the prior art, provides a kind of recreation facility surface phosphating method, improves erosion resistance and the stability of phosphatize phosphate coat.
Technical scheme: recreation facility surface phosphating method of the present invention, comprises the steps:
(1) recreation facility workpiece to be installed is immersed in NaOH solution, carry out surperficial degreasing;
(2) workpiece after surperficial degreasing is washed, and ramming polishing rust cleaning;
(3) workpiece after step (2) being processed carries out ultrasonic wave water washing 20 ~ 30 minutes;
(4) workpiece after ultrasonication soaks 5 ~ 10 minutes in Phosphating Solution, forms the phosphatize phosphate coat of 4 ~ 6um at workpiece surface;
(5) take out workpiece and put into drying machine drying.
The present invention further preferably technical scheme is, described in step (1), NaOH solution is 40%NaOH solution, and recreation facility workpiece to be installed immerses in 40%NaOH solution and soaks 30 ~ 60 seconds, carries out surperficial degreasing.
Preferably, workpiece is inserted in the water of 60 ~ 80 DEG C in step (3), carry out ultrasonic wave water washing.
Preferably, described in step (4), Phosphating Solution comprises:
SODIUM PHOSPHATE, MONOBASIC 1.5 ~ 2.5 parts;
Zinc nitrate 2.2 ~ 2.4 parts;
Phosphatase 11 ~ 1.5 part;
Fluoroboric acid receives 0.5 ~ 0.8 part;
Iron nitrate 0.1 ~ 0.3 part
Ammonium molybdate 0.1 ~ 0.3 part,
Each component is with parts by weight.
Further, described in step (4), Phosphating Solution comprises:
SODIUM PHOSPHATE, MONOBASIC 2 parts;
Zinc nitrate 2.3 parts;
Phosphatase 11 .2 part;
Fluoroboric acid receives 0.6 part;
Iron nitrate 0.2 part
Ammonium molybdate 0.2 part,
Each component is with parts by weight.
Beneficial effect: the present invention forms the phosphatize phosphate coat of 4 ~ 6um on recreation facility surface, improves the opposing environment capacity of recreation facility greatly, not perishable, not easily gets rusty, guarantees that recreation facility still can ensure higher structural strength under being chronically exposed to outdoor environment; Phosphatize phosphate coat of the present invention can improve the sticking power of recreation facility lacquer painting simultaneously, and table paint difficult drop-off, long-term outdoor uses, and still can keep the color of recreation facility.
Embodiment
Below technical solution of the present invention is described in detail, but protection scope of the present invention is not limited to described embodiment.
embodiment 1:a kind of recreation facility surface phosphating method, comprises the steps:
(1) soak in recreation facility workpiece to be installed immersion 40%NaOH solution 30 seconds, carry out surperficial degreasing;
(2) workpiece after surperficial degreasing is washed, and ramming polishing rust cleaning;
(3) workpiece after step (2) being processed is inserted in the water of 60 DEG C, carries out ultrasonic wave water washing 20 minutes;
(4) workpiece after ultrasonication soaks 5 minutes in Phosphating Solution, and form the phosphatize phosphate coat of 4um at workpiece surface, this Phosphating Solution comprises:
SODIUM PHOSPHATE, MONOBASIC 1.5 parts;
Zinc nitrate 2.2 parts;
Phosphatase 11 part;
Fluoroboric acid receives 0.5 part;
Iron nitrate 0.1 part
Ammonium molybdate 0.1 part,
Each component is with parts by weight;
(5) take out workpiece and put into drying machine drying.
embodiment 2:a kind of recreation facility surface phosphating method, comprises the steps:
(1) soak in recreation facility workpiece to be installed immersion 40%NaOH solution 60 seconds, carry out surperficial degreasing;
(2) workpiece after surperficial degreasing is washed, and ramming polishing rust cleaning;
(3) workpiece after step (2) being processed is inserted in the water of 80 DEG C, carries out ultrasonic wave water washing 30 minutes;
(4) workpiece after ultrasonication soaks 10 minutes in Phosphating Solution, and form the phosphatize phosphate coat of 6um at workpiece surface, this Phosphating Solution comprises:
SODIUM PHOSPHATE, MONOBASIC 2.5 parts;
Zinc nitrate 2.4 parts;
Phosphatase 11 .5 part;
Fluoroboric acid receives 0.8 part;
Iron nitrate 0.3 part
Ammonium molybdate 0.3 part,
Each component is with parts by weight;
(5) take out workpiece and put into drying machine drying.
embodiment 3:a kind of recreation facility surface phosphating method, comprises the steps:
(1) soak in recreation facility workpiece to be installed immersion 40%NaOH solution 45 seconds, carry out surperficial degreasing;
(2) workpiece after surperficial degreasing is washed, and ramming polishing rust cleaning;
(3) workpiece after step (2) being processed is inserted in the water of 70 DEG C, carries out ultrasonic wave water washing 25 minutes;
(4) workpiece after ultrasonication soaks 8 minutes in Phosphating Solution, and form the phosphatize phosphate coat of 5um at workpiece surface, this Phosphating Solution comprises:
SODIUM PHOSPHATE, MONOBASIC 2 parts;
Zinc nitrate 2.3 parts;
Phosphatase 11 .2 part;
Fluoroboric acid receives 0.6 part;
Iron nitrate 0.2 part
Ammonium molybdate 0.2 part,
Each component is with parts by weight;
(5) take out workpiece and put into drying machine drying.
As mentioned above, although represented with reference to specific preferred embodiment and described the present invention, it shall not be construed as the restriction to the present invention self.Under the spirit and scope of the present invention prerequisite not departing from claims definition, various change can be made in the form and details to it.
Claims (5)
1. a recreation facility surface phosphating method, is characterized in that comprising the steps:
(1) recreation facility workpiece to be installed is immersed in NaOH solution, carry out surperficial degreasing;
(2) workpiece after surperficial degreasing is washed, and ramming polishing rust cleaning;
(3) workpiece after step (2) being processed carries out ultrasonic wave water washing 20 ~ 30 minutes;
(4) workpiece after ultrasonication soaks 5 ~ 10 minutes in Phosphating Solution, forms the phosphatize phosphate coat of 4 ~ 6um at workpiece surface;
(5) take out workpiece and put into drying machine drying.
2. recreation facility surface phosphating method according to claim 1, it is characterized in that, described in step (1), NaOH solution is 40%NaOH solution, and recreation facility workpiece to be installed immerses in 40%NaOH solution and soaks 30 ~ 60 seconds, carries out surperficial degreasing.
3. recreation facility surface phosphating method according to claim 1, is characterized in that, is inserted by workpiece in the water of 60 ~ 80 DEG C, carry out ultrasonic wave water washing in step (3).
4. recreation facility surface phosphating method according to claim 1, is characterized in that, described in step (4), Phosphating Solution comprises:
SODIUM PHOSPHATE, MONOBASIC 1.5 ~ 2.5 parts;
Zinc nitrate 2.2 ~ 2.4 parts;
Phosphatase 11 ~ 1.5 part;
Fluoroboric acid receives 0.5 ~ 0.8 part;
Iron nitrate 0.1 ~ 0.3 part
Ammonium molybdate 0.1 ~ 0.3 part,
Each component is with parts by weight.
5. recreation facility surface phosphating method according to claim 4, is characterized in that, described in step (4), Phosphating Solution comprises:
SODIUM PHOSPHATE, MONOBASIC 2 parts;
Zinc nitrate 2.3 parts;
Phosphatase 11 .2 part;
Fluoroboric acid receives 0.6 part;
Iron nitrate 0.2 part
Ammonium molybdate 0.2 part,
Each component is with parts by weight.