CN105200280A - 一种具有高耐磨性的液压阀体 - Google Patents

一种具有高耐磨性的液压阀体 Download PDF

Info

Publication number
CN105200280A
CN105200280A CN201510678038.9A CN201510678038A CN105200280A CN 105200280 A CN105200280 A CN 105200280A CN 201510678038 A CN201510678038 A CN 201510678038A CN 105200280 A CN105200280 A CN 105200280A
Authority
CN
China
Prior art keywords
percent
hydraulic valve
raw material
rare earth
earth element
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510678038.9A
Other languages
English (en)
Inventor
杨龙兴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuxi Yanggong Machinery Manufacturing Co Ltd
Original Assignee
Wuxi Yanggong Machinery Manufacturing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuxi Yanggong Machinery Manufacturing Co Ltd filed Critical Wuxi Yanggong Machinery Manufacturing Co Ltd
Priority to CN201510678038.9A priority Critical patent/CN105200280A/zh
Publication of CN105200280A publication Critical patent/CN105200280A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种具有高耐磨性的液压阀体，所述液压阀体通过铸造制成，所述液压阀体铸造原料按质量百分比包括以下组分：Fe：0.7-0.8%，Co：0.4-0.45%，Si：0.8-0.9%，Cu：0.07-0.08%，Ti：0.1-0.12%，B：0.05-0.06%，Ni：0.5-1.0%，Re：0.01-0.03%，Mn：0.1-0.2%，Zn：0.6-0.7%，本发明所公开的一种具有高耐磨性的液压阀体，原料配比合理，能够有效提高液压阀阀体的耐磨性。Mg：0.7-0.9%，Li：0.01-0.03%，Pt：0.06-0.08%，N：0.01-0.02%，C：0.02-0.04%，P：0.01-0.03%，S：0.008-0.010%，残余元素：0.05-0.20%，稀土元素：0.2-0.8%，其余为铝。本发明所公开的一种具有高耐磨性的液压阀体，原料配比合理，能够有效提高液压阀阀体的耐磨性。

Description

一种具有高耐磨性的液压阀体
技术领域
本发明涉及液压件零部件的加工工艺技术领域，具体涉及一种具有高耐磨性的液压阀体。
背景技术
液压阀阀体作为液压阀的主要零件，其材质选择首先应考虑到液压阀阀体工作介质的物理性能（温度、压力）和化学性能（腐蚀性）等。同时，还应了解介质的清洁程度（有无固体颗粒）。除此之外，还要参照国家和使用部门的有关规定和要求。许多种材料可以满足液压阀阀体在多种不同工况的使用要求。但是，正确、合理的选择液压阀阀体的材料，可以获得液压阀阀体最经济的使用寿命和最佳的性能。
发明内容
为解决现有技术中存在的上述问题，本发明提供了一种具有高耐磨性的液压阀体。
本发明的技术效果通过以下技术方案实现：
一种具有高耐磨性的液压阀体，所述液压阀体通过铸造制成，所述液压阀体铸造原料按质量百分比包括以下组分：Fe：0.7-0.8%，Co：0.4-0.45%，Si：0.8-0.9%，Cu：0.07-0.08%，Ti：0.1-0.12%，B：0.05-0.06%，Ni：0.5-1.0%，Re：0.01-0.03%，Mn：0.1-0.2%，Zn：0.6-0.7%，Mg：0.7-0.9%，Li：0.01-0.03%，Pt：0.06-0.08%，N：0.01-0.02%，C：0.02-0.04%，P：0.01-0.03%，S：0.008-0.010%，残余元素：0.05-0.20%，稀土元素：0.2-0.8%，其余为铝。
进一步的，所述的稀土元素按质量百分比计包括以下组分：铈：5-6%，钬：3-4%，镝：19-22%，饵：5-5.5%，镧：1-2%，铽：8-9%，铕：5-6%，钐：8-10%，余量为镧系元素。
进一步的，所述液压阀体铸造原料按质量百分比包括以下组分：Fe：0.7%，Co：0.45%，Si：0.9%，Cu：0.08%，Ti：0.1%，B：0.06%，Ni：0.8%，Re：0.02%，Mn：0.15%，Zn：0.6%，Mg：0.8%，Li：0.02%，Pt：0.07%，N：0.01%，C：0.03%，P：0.02%，S：0.009%，残余元素：0.15%，稀土元素：0.6%，其余为铝，所述的稀土元素按质量百分比计包括以下组分：铈：6%，钬：4%，镝：20%，饵：5.5%，镧：1%，铽：8%，铕：6%，钐：9%，余量为镧系元素。
本发明的有益效果是：
本发明所公开的一种具有高耐磨性的液压阀体，原料配比合理，能够有效提高液压阀阀体的耐磨性。
具体实施方式
本发明通过以下具体实施方式实现：
一种具有高耐磨性的液压阀体，所述液压阀体通过铸造制成，所述液压阀体铸造原料按质量百分比包括以下组分：Fe：0.7-0.8%，Co：0.4-0.45%，Si：0.8-0.9%，Cu：0.07-0.08%，Ti：0.1-0.12%，B：0.05-0.06%，Ni：0.5-1.0%，Re：0.01-0.03%，Mn：0.1-0.2%，Zn：0.6-0.7%，Mg：0.7-0.9%，Li：0.01-0.03%，Pt：0.06-0.08%，N：0.01-0.02%，C：0.02-0.04%，P：0.01-0.03%，S：0.008-0.010%，残余元素：0.05-0.20%，稀土元素：0.2-0.8%，其余为铝。
进一步的，所述的稀土元素按质量百分比计包括以下组分：铈：5-6%，钬：3-4%，镝：19-22%，饵：5-5.5%，镧：1-2%，铽：8-9%，铕：5-6%，钐：8-10%，余量为镧系元素。
具体的，所述液压阀体铸造原料按质量百分比包括以下组分：Fe：0.7%，Co：0.45%，Si：0.9%，Cu：0.08%，Ti：0.1%，B：0.06%，Ni：0.8%，Re：0.02%，Mn：0.15%，Zn：0.6%，Mg：0.8%，Li：0.02%，Pt：0.07%，N：0.01%，C：0.03%，P：0.02%，S：0.009%，残余元素：0.15%，稀土元素：0.6%，其余为铝，所述的稀土元素按质量百分比计包括以下组分：铈：6%，钬：4%，镝：20%，饵：5.5%，镧：1%，铽：8%，铕：6%，钐：9%，余量为镧系元素。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (3)

1.一种具有高耐磨性的液压阀体，所述液压阀体通过铸造制成，其特征在于：所述液压阀体铸造原料按质量百分比包括以下组分：Fe：0.7-0.8%，Co：0.4-0.45%，Si：0.8-0.9%，Cu：0.07-0.08%，Ti：0.1-0.12%，B：0.05-0.06%，Ni：0.5-1.0%，Re：0.01-0.03%，Mn：0.1-0.2%，Zn：0.6-0.7%，Mg：0.7-0.9%，Li：0.01-0.03%，Pt：0.06-0.08%，N：0.01-0.02%，C：0.02-0.04%，P：0.01-0.03%，S：0.008-0.010%，残余元素：0.05-0.20%，稀土元素：0.2-0.8%，其余为铝。
2.根据权利要求1所述的一种具有高耐磨性的液压阀体，其特征在于：所述的稀土元素按质量百分比计包括以下组分：铈：5-6%，钬：3-4%，镝：19-22%，饵：5-5.5%，镧：1-2%，铽：8-9%，铕：5-6%，钐：8-10%，余量为镧系元素。
3.根据权利要求2所述的一种具有高耐磨性的液压阀体，其特征在于：所述液压阀体铸造原料按质量百分比包括以下组分：Fe：0.7%，Co：0.45%，Si：0.9%，Cu：0.08%，Ti：0.1%，B：0.06%，Ni：0.8%，Re：0.02%，Mn：0.15%，Zn：0.6%，Mg：0.8%，Li：0.02%，Pt：0.07%，N：0.01%，C：0.03%，P：0.02%，S：0.009%，残余元素：0.15%，稀土元素：0.6%，其余为铝，所述的稀土元素按质量百分比计包括以下组分：铈：6%，钬：4%，镝：20%，饵：5.5%，镧：1%，铽：8%，铕：6%，钐：9%，余量为镧系元素。
CN201510678038.9A 2015-10-20 2015-10-20 一种具有高耐磨性的液压阀体 Pending CN105200280A (zh)