CN105199575A - Special solar coating and preparation method thereof - Google Patents
Special solar coating and preparation method thereof Download PDFInfo
- Publication number
- CN105199575A CN105199575A CN201510626477.5A CN201510626477A CN105199575A CN 105199575 A CN105199575 A CN 105199575A CN 201510626477 A CN201510626477 A CN 201510626477A CN 105199575 A CN105199575 A CN 105199575A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- solvent
- oxide
- prepared
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses special solar coating and a preparation method thereof. The special solar coating is composed of a light absorption agent, an adhesive, a solvent and an auxiliary agent, wherein the light absorption agent can be prepared from, by weight, 33 parts of ferric oxide, 10 parts of cadmium red, 1.5 parts of copper oxide, 1.7 parts of manganese oxide and 2 parts of iron oxide red; the adhesive can be prepared from, by weight, 53 parts of polyurethane resin; the solvent can be prepared from, by weight, xylene; the auxiliary agent can be prepared from, by weight, 5 parts of cobalt naphthenate solution. The special solar coating can be used for solar thermal absorption coatings of building walls of houses, schools, guesthouses, hotels, office buildings and the like, has characteristics of freeness of toxicity and odors, flame retardancy, convenience and simplicity in construction, effectiveness in heat absorption and the like and has the advantages of high adhesive power, resistance to washing, acids, alkalis and ageing, fire retardancy, long service life and the like.
Description
Technical field
The present invention relates to paint field, be specifically related to a kind of building coating, can be used for the sun power speciality coating of the construction wall solar energy heat absorbing coatings such as family, school, hotel, hotel, office building, there is the features such as nontoxic, tasteless, fire-retardant, easy construction, endothermic effect are good, and there is strong adhesion, scrubbing resistance; Acid and alkali-resistance, anti-aging, fire-retardant fireproof, the advantages such as the life-span is long.
Background technology
Speciality coating refers to the new coating having essential distinction with traditional coating, and speciality coating gives object with various exceptional function.Different speciality coatings, has different characteristics.Speciality coating refers to the coating of various special purpose, refers to except protective effect, and this kind of coating also has that some is extraordinary especially, to meet the speciality coating of the needs in coated product design concurrently.Speciality coating is of a great variety, of many uses, is forming a large-scale hi-tech industry group, is having very wide market outlook and very important strategic importance.Research and development and the application of speciality coating are all attached great importance in countries in the world.Specific function coating be have absorb decompose hazardous and noxious substances, the function such as waterproof, fire prevention, antifouling, conduction, shielding electromagnetic wave, anti-electrostatic, mildew-resistant, sterilization, anti-marine organisms are sticked, high temperature resistant, temperature indicating and temperature marker, luminescence, absorption and infra-red-emitting, absorption sun power, shielding ray, flag colors, anti-skidding, self-lubricating, chip resistant splashing and antinoise, damping, antisweat.Functional special coating can differently be classified, if classified by its function, then mainly contains several as follows: one, hot functional paint: comprise high-temperature resistant coating, frie retardant coating, thermal insulating coating etc.Two, functional Energy-Saving Architectural Coatings: comprise Sunscreen paint, thermal insulation coatings, glass heat-insulating coating etc.Three, chemical functional coating: comprise the etching ground of resistance to special medium, high-temperature corrosion resistance coating, ultrahigh-temperature object antioxidizing paint etc.Four, function solenoid coating: be mainly high-temperature insulating paint.Five, mechanical function coating: be mainly wear-resistant paint.Six, interface function coating: comprise chalking paint, icephobic coating, snow defence coating, the attached coating of high-temperature adhesion resistant etc.Seven, optical function coating: comprise luminous reflectance coating, ir radiation heat radiation coating, high-temperature-resistant far infrared radiation coating etc.
Summary of the invention
The object of the present invention is to provide a kind of building coating, can be used for the sun power speciality coating of the construction wall solar energy heat absorbing coatings such as family, school, hotel, hotel, office building, there is the features such as nontoxic, tasteless, fire-retardant, easy construction, endothermic effect are good, and there is strong adhesion, scrubbing resistance; Acid and alkali-resistance, anti-aging, fire-retardant fireproof, the advantages such as the life-span is long.
Present invention employs such technical scheme: the material in described sun power speciality coating and weight proportion respectively: optical absorbing agent, cakingagent, solvent, auxiliary agent.
In the present invention, optical absorbing agent can select ferric oxide 33 parts, Se deposit 10 parts, cupric oxide 1.5 parts, manganese oxide 1.7 parts, red iron oxide 2 parts; Cakingagent can select urethane resin 53 parts; Solvent can select dimethylbenzene 9 parts; Auxiliary agent can select cobalt naphthenate solution 5 parts.
The present invention is specifically related to a kind of building coating, can be used for the sun power speciality coating of the construction wall solar energy heat absorbing coatings such as family, school, hotel, hotel, office building.
The advantages such as this product has the features such as nontoxic, tasteless, fire-retardant, easy construction, endothermic effect are good, and has strong adhesion, scrubbing resistance, acid and alkali-resistance, anti-aging, fire-retardant fireproof, and the life-span is long.
Embodiment
Present invention employs such technical scheme: in described sun power speciality coating, material and weight proportion are respectively: optical absorbing agent, cakingagent, solvent, auxiliary agent.
In the present invention, optical absorbing agent can select ferric oxide 33 parts, Se deposit 10 parts, cupric oxide 1.5 parts, manganese oxide 1.7 parts, red iron oxide 2 parts; Cakingagent can select urethane resin 53 parts; Solvent can select dimethylbenzene 9 parts; Auxiliary agent can select cobalt naphthenate solution 5 parts.
Its preparation method is following steps:
Step one), add optical absorbing agent, cakingagent in a reservoir, abundant mixing and stirring, be ground to after qualified fineness for subsequent use through shredder;
Step 2), by step one) institute obtains in material and adds solvent, auxiliary agent, stir, after filtration finished product.
Claims (2)
1. a sun power speciality coating, is characterized in that, material and weight proportion respectively: optical absorbing agent, cakingagent, solvent, auxiliary agent; In the present invention, optical absorbing agent can select ferric oxide 33 parts, Se deposit 10 parts, cupric oxide 1.5 parts, manganese oxide 1.7 parts, red iron oxide 2 parts; Cakingagent can select urethane resin 53 parts; Solvent can select dimethylbenzene 9 parts; Auxiliary agent can select cobalt naphthenate solution 5 parts.
2. according to sun power speciality coating according to claim 1, it is characterized in that, its preparation method, preparation method is following steps: step one), add optical absorbing agent, cakingagent in a reservoir, abundant mixing and stirring, is ground to after qualified fineness for subsequent use through shredder;
Step 2), by step one) institute obtains in material and adds solvent, auxiliary agent, stir, after filtration finished product.